CN107419812A - 一种防水型建筑外墙保温结构及其施工方法 - Google Patents
一种防水型建筑外墙保温结构及其施工方法 Download PDFInfo
- Publication number
- CN107419812A CN107419812A CN201710582889.2A CN201710582889A CN107419812A CN 107419812 A CN107419812 A CN 107419812A CN 201710582889 A CN201710582889 A CN 201710582889A CN 107419812 A CN107419812 A CN 107419812A
- Authority
- CN
- China
- Prior art keywords
- heat
- wall
- coat
- mortar
- insulation layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种防水型建筑外墙保温结构，包括基层墙体，以及由内往外依次为找平层、保温层、防护层、饰面层；所述基层墙体上覆盖涂抹环氧聚合物砂浆形成找平层；所述找平层上覆盖涂抹双组分聚氨酯胶黏剂粘贴岩棉板形成保温层；所述保温层上铺设玻璃纤维网格布，涂抹聚合物抹面抗裂砂浆形成防护层；所述防护层上覆盖涂抹装饰涂料形成饰面层。本发明的一种防水型建筑外墙保温结构，具有节能环保，结构简单的特点，有效地解决了墙体外的保温、隔热、抗风压、耐冻融、防水、防裂等问题，其防水性能、抗裂性能、耐老化性能，阻燃性能优良；另外具有保温层安装牢固、施工方便等优点。
Description
技术领域
本发明属于外墙保温技术领域，具体涉及一种防水型建筑外墙保温结构及其施工方法。
背景技术
外墙保温是采用节能保温材料覆盖于墙体的外侧，在夏季，防止室外阳光照射引起室内温度升；在冬季，防止室内热量散失到室外，主要保障夏季降温设备的降温效果和冬天暖气的供暖效果，从而节约能源消耗，提高能源利用率；同时外墙保温不占用室内空间，提高建筑使用面积，因此外墙保温在建筑保温、隔热应用中最广泛，其效果最为突出，已成为我国建筑墙体保温主要施工方法。
近年来,由于外墙外保温材料选择不当造成的火灾令人触目惊心，给人民群众生命财产安全造成极大的损失。外墙保温材料有些采用泡沫材料，具有填缝、粘结、密封、隔热、吸音等多种效果，是一种环保节能，使用方便的优点，但由于受到季节温度的使用限制、平整度效果差、易燃安全性差，因此不是最佳的选材。岩棉制品以其优异的防火保温特性是国际上公认的"第五常规能源"中的主要节能材料。在建筑上每使用1吨岩棉制品进行保温，一年至少可节省相当于1吨石油的能量,符合低碳、节能、减排趋势，已成为理想的建筑保温材料。岩棉是一种多孔纤维状材料，具有非常好的保温绝热性能，透气性能，吸音性能，也有效地减少建筑墙体发霉情况。但目前制作的岩棉保温板，粘贴到墙体上之后，由于岩棉具有可压缩性，这样的结构，存在抗拉抗压能力弱，稳定性差，墙体保温易损坏、开裂，保温层易脱落，保温效果差等问题。
发明内容
本发明主要针对现有技术中存在的缺陷，而提供的一种防水型建筑外墙保温结构及其施工方法，能够解决墙体保温易损坏、开裂、易脱落，保温效果差的问题，并且具有环保、阻燃、防水功能于一体等优点。
技术方案：
为了解决上述技术问题，本发明所述的一种防水型建筑外墙保温结构，包括基层墙体，以及由内往外依次为找平层、保温层、防护层、饰面层；所述基层墙体上覆盖涂抹环氧聚合物砂浆形成找平层；所述找平层上覆盖涂抹双组分聚氨酯胶黏剂粘贴岩棉板形成保温层；所述保温层上铺设玻璃纤维网格布，涂抹聚合物抹面抗裂砂浆形成防护层；所述防护层上覆盖涂抹装饰涂料形成饰面层。
所述保温层安装高度每间隔2米采用T型不锈钢制锚固件锚固，锚固件的高度与保温层的厚度一致。
所述装饰涂料通过以下方法制得，其各原料组分的重量份为：环氧树脂60～100份、纳米二氧化硅20～30份、纳米碳酸钙10～15份、抗氧剂BHT0.02～0.03份、阻燃剂辛酸亚锡0.5～0.6份、消泡剂聚二甲基硅氧烷3～6份、成膜助剂乙二醇0.5～0.8份、防霉剂0.3～0.6份、颜料3～10份；制备方法是将在带搅拌的搪瓷反应锅中分别投入环氧树脂、纳米二氧化硅、纳米碳酸钙，开启搅拌，加热升温，温度上升至65～75℃，搅拌速度为 800～1000r/min，搅拌60～90min；然后冷却温度至45～55℃，加入抗氧剂BHT、阻燃剂辛酸亚锡、消泡剂聚二甲基硅氧烷、成膜助剂乙二醇、防霉剂、颜料，继续搅拌30～40min；最后冷却温度至常温，经100目滤网过滤、检测，即得装饰涂料。
一种防水型建筑外墙保温结构的施工方法，具体步骤为：
（1）基层墙体处理：清除墙体表面的凸出、松动、风化及表面污染物，使得墙体表面清洁平整。
（2）找平砂浆配制：将环氧聚合物砂浆成分中A料摇匀，然后按A料与B料为1:4的质量配比混合，并充分搅拌成均匀的胶浆状即可使用。参考用量为2000kg/m3，配好的料宜在1～2h内用完。
（3）找平层施工：将步骤(2)制备的砂浆进行找平，对缺损部位用抹刀将配制好的胶泥涂抹在修补部位，涂抹时要边压实边抹光，固化保养7天；对整体墙面层时，施工厚度不应小于3mm，分两次进行施工，当进行第二次找平时，应一次抹平，不得反复抹压，每次施工的间隔不应少于24h。
（4）胶黏剂配制：将双组分聚氨酯胶黏剂中的甲组分和乙组分按6:1的质量配比混合，并充分搅拌成均匀即可使用。
（5）锚固件安装：在已固化干燥的找平层上，由下往上水平划线标识，相隔线距为2m，在水平划线标识位置上采用步骤(4)配置的双组分聚氨酯胶黏剂安装锚固件。
（6）保温层安装：将步骤(4)配置的双组分聚氨酯胶黏剂涂抹至岩棉板上，并将岩棉板粘贴到砂浆找平层上，使岩棉板上下紧靠在锚固件之间位置，岩棉板的粘贴顺序为由下而上、由左到右、水平横向粘贴，其中，双组分聚氨酯胶黏剂在岩棉板上采用上、下、左、右、背面层5个面涂抹的布胶方式；对于相邻岩棉板之间拼接缝间距大于3mm时，将岩棉板切割成所需形状塞入拼接缝内，并用找平砂浆抹平接缝；
（7）抗裂砂浆配制：将聚合物抹面抗裂砂浆中的干粉与水按4:1的质量配比混合，用电动搅拌器搅动3min，静止5min后再次搅动均匀即可使用。一次配制用量须在2h内用完，
（8）保护层施工：将步骤(7)配置的聚合物抹面抗裂砂浆均匀的涂抹在岩棉保温层和锚固件上，然后铺设玻璃纤维网格布，玻璃纤维网格布相互之间的搭接宽度为30～40mm，在底层抗裂砂浆凝结前，再次涂抹一道抗裂砂浆，保护层厚度为2～3mm。
（9）饰面层施工：抗裂砂浆完全固化后，在保护层上均匀覆盖涂刷2～3遍装饰涂料，每次墙体表面干透后，再涂刷下一遍，最后一次涂刷并干透，即完成建筑外墙保温结构的全部施工。
本发明的有益效果
本发明提供了一种防水型建筑外墙保温结构，具有节能环保，结构简单的特点，特别在找平层和保护层上分别采用环氧聚合物砂浆和聚合物抹面抗裂砂浆、有效地解决了墙体外的保温、隔热、抗风压、耐冻融、防水、防裂等问题，其防水性能、抗裂性能、耐老化性能，阻燃性能优良；另外具有保温层安装牢固、施工方便等优点。附图一说明:
图1为本发明的一种防水型建筑外墙保温结构示意图
图2为本发明中T型锚固件结构示意图
其中图中：
1、基层墙体，2、找平层，3、保温层，4、防护层，5、饰面层，6、锚固件，7、玻璃纤维网格布。
具体实施方式
以下通过具体实施方式对本发明作进一步的阐述。
一种防水型建筑外墙保温结构，包括基层墙体，以及由内往外依次为找平层、保温层、防护层、饰面层；所述基层墙体上覆盖涂抹环氧聚合物砂浆形成找平层；所述找平层上覆盖涂抹双组分聚氨酯胶黏剂粘贴岩棉板形成保温层；所述保温层上铺设玻璃纤维网格布，涂抹聚合物抹面抗裂砂浆形成防护层；所述防护层上覆盖涂抹装饰涂料形成饰面层。
一种防水型建筑外墙保温结构的施工方法，具体步骤为：
（1）基层墙体处理：采用钢制铲刀清除墙体表面的凸出、松动、风化及表面污染物，并用自来水冲刷，保证墙体表面清洁干净。
（2）找平砂浆配制：将环氧聚合物砂浆成分中A料摇匀，然后按A料与B料为1:4的质量配比混合，并用电动搅拌机充分搅拌成均匀的胶浆状待用。
（3）找平层施工：对墙体缺损部位用抹刀将配制好的环氧聚合物砂浆涂抹在修补部位，涂抹时边压实边抹光，固化保养7天；对整体墙面层时，分两次进行涂抹施工，第一次涂抹后，间隔24h再进行第二次涂抹找平，当进行第二次找平时，一次性抹平，确保找平层表面平整度控制在2～3mm，找平层厚度控制在3～6mm。
（4）胶黏剂配制：将双组分聚氨酯胶黏剂中的甲组分聚氨酯树脂和乙组分三羟甲基丙烷-T1按6:1的质量配比混合，并用电动搅拌机充分搅拌成均匀待用。
（5）锚固件安装：在已固化干燥的找平层上由下往上、相隔线距高度为2m水平划线标设，在水平划线标设位置上采用双组分聚氨酯胶黏剂安装T型锚固件。
（6）保温层安装：将配制的双组分聚氨酯胶黏剂涂抹在岩棉板的上、下、左、右、背面层5个面上，然后将岩棉板粘贴到砂浆找平层上，使岩棉板上下紧靠在锚固件之间位置，岩棉板的粘贴顺序为从底部位置开始，由下而上、由左到右、水平横向粘贴，当出现相邻岩棉板之间拼接缝间距大于3mm时，将岩棉板切割成所需形状塞入拼接缝内，并用找平砂浆抹平接缝；
（7）抗裂砂浆配制：将聚合物抹面抗裂砂浆中的干粉与水按4:1的质量配比混合，用电动搅拌器搅动3min，静止5min后再次搅动均匀待用。
（8）保护层施工：将配制的聚合物抹面抗裂砂浆均匀的涂抹在岩棉保温层和锚固件上，然后铺设玻璃纤维网格布，每件玻璃纤维网格布相互之间的搭接宽度为30～40mm，在底层抗裂砂浆凝结前，再次涂抹一道抗裂砂浆，保护层厚度控制在2～3mm。
（9）饰面层施工：待抗裂砂浆完全固化后，在保护层上均匀覆盖涂刷装饰涂料，每次墙体表面干透后，再涂刷下一遍，2～3遍涂刷并干透，即完成建筑外墙保温结构的全部施工。
本发明提供了一种思路及方法，具体实现该技术方案的方法和途径很多，以上所述仅是本发明的优选实施方式。应当指出，对于本技术领域的技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围内，本实施例中未明确的各组成部分均可用现有技术加以实现。
Claims (4)
1.一种防水型建筑外墙保温结构，其特征在于，包括基层墙体，以及由内往外依次为找平层、保温层、防护层、饰面层；所述基层墙体上覆盖涂抹环氧聚合物砂浆形成找平层；所述找平层上覆盖涂抹双组分聚氨酯胶黏剂粘贴岩棉板形成保温层；所述保温层上铺设玻璃纤维网格布，涂抹聚合物抹面抗裂砂浆形成防护层；所述防护层上覆盖涂抹装饰涂料形成饰面层。
2.根据权利要求1所述的一种防水型建筑外墙保温结构，其特征在于，所述的保温层安装高度每间隔2米采用T型不锈钢制锚固件锚固，锚固件高度与保温层厚度一致。
3.根据权利要求1所述的一种防水型建筑外墙保温结构，其特征在于，所述的装饰涂料通过以下方法制得：其各原料组分的重量份为：环氧树脂60～100份、纳米二氧化硅20～30份、纳米碳酸钙10～15份、抗氧剂BHT0.02～0.03份、阻燃剂辛酸亚锡0.5～0.6份、消泡剂聚二甲基硅氧烷3～6份、成膜助剂乙二醇0.5～0.8份、防霉剂0.3～0.6份、颜料3～10份；制备方法是将在带搅拌的搪瓷反应锅中分别投入环氧树脂、纳米二氧化硅、纳米碳酸钙，开启搅拌，加热升温，温度上升至65～75℃，搅拌速度为 800～1000r/min，搅拌60～90min；然后冷却温度至45～55℃，加入抗氧剂BHT、阻燃剂辛酸亚锡、消泡剂聚二甲基硅氧烷、成膜助剂乙二醇、防霉剂、颜料，继续搅拌30～40min；最后冷却温度至常温，经100目滤网过滤、检测，即得装饰涂料。
4.根据权利要求1所述的一种防水型建筑外墙保温结构的施工方法，其特征在于，它包括以下步骤：
（1）基层墙体处理：清除墙体表面的凸出、松动、风化及表面污染物，使得墙体表面清洁平整；
（2）找平砂浆配制：将环氧聚合物砂浆成分中A料摇匀，然后按A料与B料为1:4的质量配比混合，并充分搅拌成均匀的胶浆状即可使用；参考用量为2000kg/m3，配好的料宜在1～2h内用完；
（3）找平层施工：将步骤(2)制备的砂浆进行找平，对缺损部位用抹刀将配制好的胶泥涂抹在被修补部位，涂抹时要边压实边抹光，固化保养7天；对整体墙面层时，施工厚度不应小于3mm，分两次进行施工，当进行最后一次找平时，应一次抹平，不得反复抹压，每次施工的间隔不应少于24h；
（4）胶黏剂配制：将双组分聚氨酯胶黏剂中的甲组分和乙组分按 按6:1的质量配比混合，并充分搅拌成均匀即可使用；
（5）锚固件安装：在已固化干燥的找平层上由下往上水平划线，相隔线距为2m，在水平划线位置上采用步骤(4)配置的双组分聚氨酯胶黏剂安装T型锚固件，锚固件高度与保温层厚度一致；
（6）保温层安装：将步骤(4)配置的双组分聚氨酯胶黏剂涂抹至岩棉板上，并将岩棉板粘贴到砂浆找平层上，使岩棉板上下紧靠在锚固件之间位置，岩棉板的粘贴顺序为由下而上、由左到右、水平横向粘贴，其中，双组分聚氨酯胶黏剂在岩棉板上采用上、下、左、右、背面层5个面涂抹的布胶方式；对于相邻岩棉板之间拼接缝间距大于3mm时，将岩棉板切割成所需形状塞入拼接缝内，并用找平砂浆抹平接缝；
（7）抗裂砂浆配制：将聚合物抹面抗裂砂浆中的干粉与水按4:1的质量配合比例混合，用电动搅拌器搅动3min，静止5min后再次搅动均匀即可使用；一次配制用量须在2h内用完；
（8）保护层施工：将步骤(7)配置的聚合物抹面抗裂砂浆均匀的涂抹在岩棉保温层和锚固件上，然后铺设玻璃纤维网格布，每件玻璃纤维网格布之间的搭接宽度为30～40mm，在底层抗裂砂浆凝结前，再次涂抹一道抗裂砂浆，保护层厚度为2～3mm；
（9）饰面层施工：抗裂砂浆完全固化后，在保护层上均匀覆盖涂刷2～3遍装饰涂料，每次墙体表面干透后，再涂刷下一遍，最后一次涂刷并干透，即完成建筑外墙保温结构的全部施工。