CN107415355A - 一种防火阻燃复合防火门 - Google Patents

一种防火阻燃复合防火门 Download PDF

Info

Publication number
CN107415355A
CN107415355A CN201710621023.8A CN201710621023A CN107415355A CN 107415355 A CN107415355 A CN 107415355A CN 201710621023 A CN201710621023 A CN 201710621023A CN 107415355 A CN107415355 A CN 107415355A
Authority
CN
China
Prior art keywords
fire
door
layer
parts
flame retarding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710621023.8A
Other languages
English (en)
Inventor
汪中奇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Iraq Door And Window Co Ltd
Original Assignee
Hefei Iraq Door And Window Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Iraq Door And Window Co Ltd filed Critical Hefei Iraq Door And Window Co Ltd
Priority to CN201710621023.8A priority Critical patent/CN107415355A/zh
Publication of CN107415355A publication Critical patent/CN107415355A/zh
Withdrawn legal-status Critical Current

Abstract

本发明属于门窗技术领域，提供了一种防火阻燃复合防火门，所述防火阻燃复合防火门包括三层，由上到下分别为第一层、中间层、第二层，所述第一层为防火门面板、所述中间层为防火门芯板、所述第二层为防火门背板，所述复合防火门由防火门面板、防火门芯板、防火门背板复合而成。本发明的复合防火门，该复合防火门由防火门面板、防火门芯板、防火门背板复合而成，所述的防火门面板、防火门芯板、防火门背板材料均添加了具有阻燃防火功能的成分，对防火门的防火阻燃功能进行加强，并通过涂胶、热压的工艺制成，制成的复合防火门具有优异的防火阻燃性能。

Description

一种防火阻燃复合防火门
技术领域
本发明属于门窗技术领域，具体地，涉及一种防火阻燃复合防火门。
背景技术
防火门，是用来维持走火通道的耐火完整性及提供逃生途径的门。其目的是要确保在一段合理时间（通常是逃生时间）内，保护走火通道内正在逃生的人免受火灾的威胁，包括阻隔浓烟及热力。
防火门种类很多，有木质防火门、钢质防火门、钢木防火门、其他防火门等；其中，木质防火门用难燃木材或难燃木材制品作门框、门扇骨架、门扇面板；钢质防火门用钢质材料制作门框、门扇骨架和门扇面板，门扇内若填充材料，则填充对人体无毒无害的防火隔热材料，并配以防火五金配件所组成的具有一定耐火性能的门；钢木质防火门是用钢质和难燃木质材料或难燃木材制品制作门框、门扇骨架、门扇面板。
其中，《钢质、木质防火门产品型式认可补充细则》第三条规定，木质防火门生产企业必须配备木材阻燃处理设备。但由于部分生产企业在工厂认证和型式检验认证时提交的技术文件中称木材未进行阻燃处理，木材不进行阻燃处理，又不用防火涂料或不燃材料进行保护，防火门的耐火极限肯定达不到甲级防火门的要求。
因此，本发明提供一种防火阻燃性能高的复合防火门，以满足市场的需要。
发明内容
针对现有技术中的缺陷，本发明的目的是提供一种防火阻燃复合防火门。
本发明提供一种防火阻燃复合防火门，所述防火阻燃复合防火门包括三层，由上到下分别为第一层、中间层、第二层，所述第一层为防火门面板、所述中间层为防火门芯板、所述第二层为防火门背板，所述复合防火门由防火门面板、防火门芯板、防火门背板复合而成；
其中，所述防火门面板表层为阻燃层、中间层为木质层、底层为阻燃层；
所述防火门芯板的材料包括如下重量份的原料：甲基硅酸钠1-3.5份、聚丙烯纤维1.3-3.5份、白炭黑2-6份、无机粘结剂0.1-2.5份、硅灰3-12份、棕榈纤维0.9-2.5份、硫酸石膏3-9份、酚醛树脂2.1-5.9份、氮化硅11-21份、镁铝合金粉3-7份、氧化锆空心球0.1-2.5份。
优选地，所述防火门面板表层阻燃层由三聚氰胺密胺盐、多聚磷酸铵、润滑剂、偶联剂和二氧化钛复配而成。
优选地，所述润滑剂为硬脂酸、硬脂酸锌或硬脂酸钙任一种。
优选地，所述防火门面板底层阻燃层由白碳黑、三氧化二锑、氢氧化铝复配而成。
优选地，所述白碳黑、三氧化二锑、氢氧化铝质量比为1:1-1.5:1。
优选地，所述无机粘结剂成份包括硫酸钙和硫酸铝钾。
优选地，所述硫酸钙和硫酸铝钾的质量比为1:1-2。
优选地，所述防火阻燃复合防火门的制备方法如下：
（1）、将发泡胶均匀地刮涂在防火门面板上，然后迅速地将除去表面浮尘的防火门芯板紧密地压放在涂胶完成的防火门面板上，再将完成涂胶的防火门背板耦合压放在防火门芯板的另一面上，完成涂胶工艺；
（2）、将完成涂胶工艺的防火门进行热压即可，其中，所述热压工艺控制参数是：热压温度：40-84℃；热压时间：14-32min。
优选地，所述发泡胶为水固性防火发泡胶。
与现有技术相比，本发明具有如下的有益效果：
1、本发明提供的一种防火阻燃复合防火门，该复合防火门由防火门面板、防火门芯板、防火门背板复合而成，所述的防火门面板、防火门芯板、防火门背板材料均添加了具有阻燃防火功能的成分，对防火门的防火阻燃功能进行加强，并通过涂胶、热压的工艺制成，制成的复合防火门具有优异的防火阻燃性能。
2、本发明提供的一种防火阻燃复合防火门，防火门芯板材料中的白炭黑、硅灰、氮化硅、镁铝合金粉具有优异的阻燃作用，各成分协同作用，提高了防火门芯板的阻燃作用，此外，添加的聚丙烯纤维、棕榈纤维加强了防护门的强度和延展性。
3、本发明提供的一种防火阻燃复合防火门，阻燃层中的各组分不损害防火门的的物理机械性能，不降低防火门的热变形温度和机械强度，阻燃效果显著，发烟量少、质量损失速率小，环保高效。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述，本发明的其它特征、目的和优点将会变得更明显：
图1为本发明提供的一种防火阻燃复合防火门结构示意图。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
结合图1，本实施例提供的一种防火阻燃复合防火门，所述防火阻燃复合防火门包括三层，由上到下分别为第一层1、中间层2、第二层3，所述第一层1为防火门面板、所述中间层2为防火门芯板、所述第二层3为防火门背板，所述复合防火门由防火门面板、防火门芯板、防火门背板复合而成；
其中，所述防火门面板表层为阻燃层、中间层为木质层、底层为阻燃层；
所述防火门芯板的材料包括如下重量份的原料：甲基硅酸钠3.5份、聚丙烯纤维1.3份、白炭黑6份、无机粘结剂0.1份、硅灰12份、棕榈纤维0.9份、硫酸石膏9份、酚醛树脂2.1份、氮化硅21份、镁铝合金粉3份、氧化锆空心球2.5份。
其中，所述防火门面板表层阻燃层由三聚氰胺密胺盐、多聚磷酸铵、润滑剂、偶联剂和二氧化钛复配而成。
其中，所述润滑剂为硬脂酸。
其中，所述防火门面板底层阻燃层由白碳黑、三氧化二锑、氢氧化铝复配而成。
其中，所述白碳黑、三氧化二锑、氢氧化铝质量比为1:1.5:1。
其中，所述无机粘结剂成份包括硫酸钙和硫酸铝钾。
其中，所述硫酸钙和硫酸铝钾的质量比为1:1。
其中，所述防火阻燃复合防火门的制备方法如下：
（1）、将发泡胶均匀地刮涂在防火门面板上，然后迅速地将除去表面浮尘的防火门芯板紧密地压放在涂胶完成的防火门面板上，再将完成涂胶的防火门背板耦合压放在防火门芯板的另一面上，完成涂胶工艺；
（2）、将完成涂胶工艺的防火门进行热压即可，其中，所述热压工艺控制参数是：热压温度：84℃；热压时间：14min。
其中，所述发泡胶为水固性防火发泡胶。
实施例2
结合图1，本实施例提供的一种防火阻燃复合防火门，所述防火阻燃复合防火门包括三层，由上到下分别为第一层1、中间层2、第二层3，所述第一层1为防火门面板、所述中间层2为防火门芯板、所述第二层3为防火门背板，所述复合防火门由防火门面板、防火门芯板、防火门背板复合而成；
其中，所述防火门面板表层为阻燃层、中间层为木质层、底层为阻燃层；
所述防火门芯板的材料包括如下重量份的原料：甲基硅酸钠1份、聚丙烯纤维3.5份、白炭黑2份、无机粘结剂2.5份、硅灰3份、棕榈纤维2.5份、硫酸石膏3份、酚醛树脂5.9份、氮化硅11份、镁铝合金粉7份、氧化锆空心球0.1份。
其中，所述防火门面板表层阻燃层由三聚氰胺密胺盐、多聚磷酸铵、润滑剂、偶联剂和二氧化钛复配而成。
其中，所述润滑剂为硬脂酸锌。
其中，所述防火门面板底层阻燃层由白碳黑、三氧化二锑、氢氧化铝复配而成。
其中，所述白碳黑、三氧化二锑、氢氧化铝质量比为1:1:1。
其中，所述无机粘结剂成份包括硫酸钙和硫酸铝钾。
其中，所述硫酸钙和硫酸铝钾的质量比为1:2。
其中，所述防火阻燃复合防火门的制备方法如下：
（1）、将发泡胶均匀地刮涂在防火门面板上，然后迅速地将除去表面浮尘的防火门芯板紧密地压放在涂胶完成的防火门面板上，再将完成涂胶的防火门背板耦合压放在防火门芯板的另一面上，完成涂胶工艺；
（2）、将完成涂胶工艺的防火门进行热压即可，其中，所述热压工艺控制参数是：热压温度：40℃；热压时间：32min。
其中，所述发泡胶为水固性防火发泡胶。
实施例3
结合图1，本实施例提供的一种防火阻燃复合防火门，所述防火阻燃复合防火门包括三层，由上到下分别为第一层1、中间层2、第二层3，所述第一层1为防火门面板、所述中间层2为防火门芯板、所述第二层3为防火门背板，所述复合防火门由防火门面板、防火门芯板、防火门背板复合而成；
其中，所述防火门面板表层为阻燃层、中间层为木质层、底层为阻燃层；
所述防火门芯板的材料包括如下重量份的原料：甲基硅酸钠2份、聚丙烯纤维2.5份、白炭黑5份、无机粘结剂1.5份、硅灰6份、棕榈纤维1.2份、硫酸石膏7份、酚醛树脂4.3份、氮化硅16份、镁铝合金粉5份、氧化锆空心球0.8份。
其中，所述防火门面板表层阻燃层由三聚氰胺密胺盐、多聚磷酸铵、润滑剂、偶联剂和二氧化钛复配而成。
其中，所述润滑剂为硬脂酸钙。
其中，所述防火门面板底层阻燃层由白碳黑、三氧化二锑、氢氧化铝复配而成。
其中，所述白碳黑、三氧化二锑、氢氧化铝质量比为1:1.4:1。
其中，所述无机粘结剂成份包括硫酸钙和硫酸铝钾。
其中，所述硫酸钙和硫酸铝钾的质量比为1:2。
其中，所述防火阻燃复合防火门的制备方法如下：
（1）、将发泡胶均匀地刮涂在防火门面板上，然后迅速地将除去表面浮尘的防火门芯板紧密地压放在涂胶完成的防火门面板上，再将完成涂胶的防火门背板耦合压放在防火门芯板的另一面上，完成涂胶工艺；
（2）、将完成涂胶工艺的防火门进行热压即可，其中，所述热压工艺控制参数是：热压温度：54℃；热压时间：18min。
其中，所述发泡胶为水固性防火发泡胶。
与现有技术相比，本发明具有如下的有益效果：
1、本发明提供的一种防火阻燃复合防火门，该复合防火门由防火门面板、防火门芯板、防火门背板复合而成，所述的防火门面板、防火门芯板、防火门背板材料均添加了具有阻燃防火功能的成分，对防火门的防火阻燃功能进行加强，并通过涂胶、热压的工艺制成，制成的复合防火门具有优异的防火阻燃性能。
2、本发明提供的一种防火阻燃复合防火门，防火门芯板材料中的白炭黑、硅灰、氮化硅、镁铝合金粉具有优异的阻燃作用，各成分协同作用，提高了防火门芯板的阻燃作用，此外，添加的聚丙烯纤维、棕榈纤维加强了防护门的强度和延展性。
3、本发明提供的一种防火阻燃复合防火门，阻燃层中的各组分不损害防火门的的物理机械性能，不降低防火门的热变形温度和机械强度，阻燃效果显著，发烟量少、质量损失速率小，环保高效。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。

Claims (9)

1.一种防火阻燃复合防火门，其特征在于：所述防火阻燃复合防火门包括三层，由上到下分别为第一层、中间层、第二层，所述第一层为防火门面板、所述中间层为防火门芯板、所述第二层为防火门背板，所述复合防火门由防火门面板、防火门芯板、防火门背板复合而成；
其中，所述防火门面板表层为阻燃层、中间层为木质层、底层为阻燃层；
所述防火门芯板的材料包括如下重量份的原料：甲基硅酸钠1-3.5份、聚丙烯纤维1.3-3.5份、白炭黑2-6份、无机粘结剂0.1-2.5份、硅灰3-12份、棕榈纤维0.9-2.5份、硫酸石膏3-9份、酚醛树脂2.1-5.9份、氮化硅11-21份、镁铝合金粉3-7份、氧化锆空心球0.1-2.5份。
2.根据权利要求1所述的防火阻燃复合防火门，其特征在于：所述防火门面板表层阻燃层由三聚氰胺密胺盐、多聚磷酸铵、润滑剂、偶联剂和二氧化钛复配而成。
3.根据权利要求2所述的防火阻燃复合防火门，其特征在于：所述润滑剂为硬脂酸、硬脂酸锌或硬脂酸钙任一种。
4.根据权利要求1所述的防火阻燃复合防火门，其特征在于：所述防火门面板底层阻燃层由白碳黑、三氧化二锑、氢氧化铝复配而成。
5.根据权利要求4所述的防火阻燃复合防火门，其特征在于：所述白碳黑、三氧化二锑、氢氧化铝质量比为1:1-1.5:1。
6.根据权利要求1所述的防火阻燃复合防火门，其特征在于：所述无机粘结剂成份包括硫酸钙和硫酸铝钾。
7.根据权利要求6所述的防火阻燃复合防火门，其特征在于：所述硫酸钙和硫酸铝钾的质量比为1:1-2。
8.根据权利要求1所述的防火阻燃复合防火门，其特征在于：所述防火阻燃复合防火门的制备方法如下：
（1）、将发泡胶均匀地刮涂在防火门面板上，然后迅速地将除去表面浮尘的防火门芯板紧密地压放在涂胶完成的防火门面板上，再将完成涂胶的防火门背板耦合压放在防火门芯板的另一面上，完成涂胶工艺；
（2）、将完成涂胶工艺的防火门进行热压即可，其中，所述热压工艺控制参数是：热压温度：40-84℃；热压时间：14-32min。
9.根据权利要求8所述的防火阻燃复合防火门，其特征在于：所述发泡胶为水固性防火发泡胶。
CN201710621023.8A 2017-07-27 2017-07-27 一种防火阻燃复合防火门 Withdrawn CN107415355A (zh)