CN107385608A - A kind of slub and its processing technology - Google Patents
A kind of slub and its processing technology Download PDFInfo
- Publication number
- CN107385608A CN107385608A CN201610333051.5A CN201610333051A CN107385608A CN 107385608 A CN107385608 A CN 107385608A CN 201610333051 A CN201610333051 A CN 201610333051A CN 107385608 A CN107385608 A CN 107385608A
- Authority
- CN
- China
- Prior art keywords
- slub
- yarn
- ring
- terylene
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of slub and its processing technology, wherein described slub includes warp thread and weft yarn, the weft yarn winds a pine tag silk by the single yarn with knot shape and is made, the warp thread is non-elastic yarn, and the ring is the granular color fiber knot made of color textile fiber mutually winds afterturn.Ring is distributed with yarn, ring is made up of fiber, and ring mutually wound with textile fabric on yarn it is twisted together with, such structure improves adhesion between the two together with making the ring on knot yarns twisted with the fiber winding of spun yarn, the shortcomings that having prevented easily to scatter between the two, the intensity of yarn is added, while the slub made using above-mentioned technique has excellent antianaphylaxis, there is bacteriostasis, and deodorization function, anti-static function, and it is very environmentally friendly.
Description
Technical field
The invention belongs to a kind of manufacturing process of yarn, and in particular to a kind of slub and its processing technology.
Background technology
Today's society, textile clothing industry are followed the fashion in one, the polynary and period of high-quality, in recent years, band
There is the slub of nodule because its third dimension is strong, good permeability, it is comfortable and easy to wear to knit manufactured textile cloth using it
Property it is good and receive the extensive welcome of people.The slub of current people's production, mainly using one cored wire,
The nodule formed by the envelope curve coated in cored wire surface wrap, and this slub are distributed with cored wire
The nodule of upper formation is to be wrapped around the slub for forming, spinning in this way by continuous envelope curve
Not only cored wire and envelope curve are easily opened scattered, influence the use of subsequent handling, and the nodule of slub is single, no
The nodule with different fiber properties and different colours can be formed on a continuous knot yarns, this is one
Determine to have impact on use of the people to slub in degree.
The content of the invention
The technical problems to be solved by the invention are the shortcomings that presence for above prior art, propose a kind of operation
Simply, a kind of high slub of production efficiency and its processing technology, the slub that the fabrication process comes out
Fastness is strong, wear-resisting, and fancy is more, and good hand touch.
The technical solution adopted in the present invention is：A kind of slub, including warp thread and weft yarn, the weft yarn is by single
Yarn with Bamboo-shaped winds a pine tag silk and is made, and the warp thread is non-elastic yarn, the ring be by
Color textile fiber mutually winds granular color fiber knot made of afterturn.
In the present invention：The minimum 0.8cm of pitch of described slub.
A kind of processing technology of ring, comprises the following steps：
(1) polyester fiber and polyester fiber are selected as raw material, respectively by blowing and cotton carding；
(2) drafting：Raw material after blowing and cotton carding is subjected to drafting twice on drawing frame respectively, respectively obtains and washs
Synthetic fibre ripe bar and terylene ripe bar；Sliver exporting speed is 350~450m/min, and simultaneously proparea drawing-off is 4 times to head, and head is simultaneously
Back area draft is 2.7~3 times, and two and proparea drawing-off are 4~7 times, and two and back area draft are 1.8~2.3 times,
Head quantitative is 12~25g/3m, two and quantification of 15~22g/3m；
(3) rove：Terylene ripe bar and terylene ripe bar are subjected to drawing-off, twisting, coiling and molding on fly frame respectively
Step, respectively obtain terylene rove and terylene rove；Roving twist factor is 50~67, under official regain
Quantification of 5~7g/5m, axial winding density are 4.0~5.0 circles/cm；
(4) spun yarn step is carried out on spinning frame, spinning frame has front roller, middle roller and rear sieve set gradually
Draw；Terylene rove is fed from the horn mouth after rear roller, exports and carries out through middle roller, front roller successively
Twisting, twist factor are 4.0~6.0；After slub passes through the wire loop being enclosed on rings by guide steel, volume
It is wound on the bobbin being tightly placed on spindle, the spun yarn number of the slub is 18~28 tex, ramie yarn twist
For 600~1000 sth. made by twisting/m；
(5) winder：The slub that step (4) is obtained carries out winder, and winding speed is 20~40m/min.
In the present invention：When the step (3) carries out drawing-off, relative humidity 57-59%.
After adopting the above technical scheme, beneficial effects of the present invention are：Ring, ring are distributed with yarn
Be made up of fiber, and ring mutually wound with textile fabric on yarn it is twisted together with, such structure makes
Ring on knot yarns improves adhesion between the two together with being twisted together with the fiber winding of spun yarn,
The shortcomings that having prevented easily to scatter between the two, the intensity of yarn is added, while made using above-mentioned technique
Slub there is excellent antianaphylaxis, have a bacteriostasis, and deodorization function, anti-static function, and very environmentally friendly.
Embodiment
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
A kind of slub, including warp thread and weft yarn, the weft yarn wind a pine by the single yarn with Bamboo-shaped
Lousiness is made, and the warp thread is non-elastic yarn, and the ring is mutually to wind afterturn system by color textile fiber
Into granular color fiber knot；The minimum 0.8cm of pitch of described slub.
A kind of processing technology of ring, comprises the following steps：
(1) polyester fiber and polyester fiber are selected as raw material, respectively by blowing and cotton carding；
(2) drafting：Raw material after blowing and cotton carding is subjected to drafting twice on drawing frame respectively, respectively obtains and washs
Synthetic fibre ripe bar and terylene ripe bar；Sliver exporting speed is 350~450m/min, and simultaneously proparea drawing-off is 4 times to head, and head is simultaneously
Back area draft is 2.7~3 times, and two and proparea drawing-off are 4~7 times, and two and back area draft are 1.8~2.3 times,
Head quantitative is 12~25g/3m, two and quantification of 15~22g/3m；
(3) rove：Terylene ripe bar and terylene ripe bar are subjected to drawing-off, twisting, coiling and molding on fly frame respectively
Step, respectively obtain terylene rove and terylene rove；Roving twist factor is 50~67, under official regain
Quantification of 5~7g/5m, axial winding density are 4.0~5.0 circles/cm；
(4) spun yarn step is carried out on spinning frame, spinning frame has front roller, middle roller and rear sieve set gradually
Draw；Terylene rove is fed from the horn mouth after rear roller, exports and carries out through middle roller, front roller successively
Twisting, twist factor are 4.0~6.0；After slub passes through the wire loop being enclosed on rings by guide steel, volume
It is wound on the bobbin being tightly placed on spindle, the spun yarn number of the slub is 18~28tex, ramie yarn twist
For 600~1000 sth. made by twisting/m；
(5) winder：The slub that step (4) is obtained carries out winder, and winding speed is 20~40m/min.
For a person skilled in the art, any equal modification and replacement to the technical program is all in this hair
Among bright scope.Therefore, the impartial conversion made without departing from the spirit and scope of the invention and modification,
It should all cover in the scope of the present invention.
Claims (4)
- A kind of 1. slub, it is characterised in that：Including warp thread and weft yarn, the weft yarn is by single with Bamboo-shaped Yarn winds a pine tag silk and is made, and the warp thread is non-elastic yarn, and the ring is by color textile fiber Granular color fiber knot mutually made of winding afterturn.
- A kind of 2. slub according to claim 1, it is characterised in that：The pitch of described slub is most Small is 0.8cm.
- A kind of 3. processing technology of ring, it is characterised in that：Comprise the following steps：(1) polyester fiber and polyester fiber are selected as raw material, respectively by blowing and cotton carding；(2) drafting：Raw material after blowing and cotton carding is subjected to drafting twice on drawing frame respectively, respectively obtains and washs Synthetic fibre ripe bar and terylene ripe bar；Sliver exporting speed is 350~450m/min, and simultaneously proparea drawing-off is 4 times to head, and head is simultaneously Back area draft is 2.7~3 times, and two and proparea drawing-off are 4~7 times, and two and back area draft are 1.8~2.3 times, Head quantitative is 12~25g/3m, two and quantification of 15~22g/3m；(3) rove：Terylene ripe bar and terylene ripe bar are subjected to drawing-off, twisting, coiling and molding on fly frame respectively Step, respectively obtain terylene rove and terylene rove；Roving twist factor is 50~67, under official regain Quantification of 5~7g/5m, axial winding density are 4.0~5.0 circles/cm；(4) spun yarn step is carried out on spinning frame, spinning frame has front roller, middle roller and rear sieve set gradually Draw；Terylene rove is fed from the horn mouth after rear roller, exports and carries out through middle roller, front roller successively Twisting, twist factor are 4.0~6.0；After slub passes through the wire loop being enclosed on rings by guide steel, volume It is wound on the bobbin being tightly placed on spindle, the spun yarn number of the slub is 18~28tex, ramie yarn twist For 600~1000 sth. made by twisting/m；(5) winder：The slub that step (4) is obtained carries out winder, and winding speed is 20~40m/min.
- A kind of 4. processing technology of slub according to claim 2, it is characterised in that：The step (3) When carrying out drawing-off, relative humidity 57-59%.