CN107354715A - 一种棉质织物的持久抗菌防汗迹免烫整理液及整理工艺 - Google Patents
一种棉质织物的持久抗菌防汗迹免烫整理液及整理工艺 Download PDFInfo
- Publication number
- CN107354715A CN107354715A CN201710505371.9A CN201710505371A CN107354715A CN 107354715 A CN107354715 A CN 107354715A CN 201710505371 A CN201710505371 A CN 201710505371A CN 107354715 A CN107354715 A CN 107354715A
- Authority
- CN
- China
- Prior art keywords
- cotton fabric
- parts
- extract
- sweat mark
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于纺织品抗菌整理技术领域，尤其涉及一种棉质织物的持久抗菌防汗迹免烫整理液及整理工艺。整理液采用壳聚糖和中草药提取物、纳米氧化锌、纳米银粉及其他助剂复配，壳聚糖天然无毒可降解、生物相容性好、抗菌性能优异，表面含大量活性基团，有利于防缩抗皱效果；阿拉伯胶成膜包裹金银花提取物、鱼腥草提取物、石榴皮提取物和纳米氧化锌、纳米银粉抗菌剂，达到缓释和持久抗菌的效果，复配壳聚糖，赋予了棉质织物良好的抗皱性、免烫性、抗菌性能，提高了棉质织物手感、强力和耐洗性；经整理后的织物抗菌性、耐性、抗皱性和免烫性好，汗迹可以瞬间吸收和挥发，透气性良好，服用舒适；振荡式烘干避免带压力的轧辊式设备影响织物的透气性。
Description
技术领域
本发明属于纺织品抗菌整理技术领域，尤其涉及一种棉质织物的持久抗菌防汗迹免烫整理液及整理工艺。
背景技术
棉质织物具有穿着舒适、天然环保等优点深受人们的喜爱，但在穿着和洗涤过程中存在容易起皱、不易打理等缺陷，给人们的生活带来了诸多不便。随着生活质量和健康产品技术的提高，人们对天然与健康产品的持续追求越来越强烈，抗菌等功能性最受市场欢迎；同时随着户外运动的大量普及，人们对吸湿排汗功能的服饰需求大幅增加。现有技术中的抗菌整理剂种类很多，有无机抗菌整理剂、有机抗菌整理剂、生物抗菌整理剂、天然抗菌整理剂等。但是目前的棉质织物的抗菌整理剂及整理工艺的抗菌效果不好，不能有效的抑制金黄色葡萄球菌和白色念珠菌，耐洗性能较差，抗菌性能不能持久有效，面料的服用性能较差；汗迹不仅影响衣服的美观，而且很容易使衣服泛黄，大大降低服装的使用寿命，现有技术中的服饰的防汗迹整理效果不好。
发明内容
发明目的：为了克服以上问题，本发明的目的是提供一种棉质织物的持久抗菌防汗迹免烫整理液及整理工艺。
技术方案：本发明的一个目的在于提供一种棉质织物的持久抗菌防汗迹免烫整理液，包括以下重量份的原料：金银花提取物20-30份、鱼腥草提取物20-30份、石榴皮提取物20-30份、阿拉伯胶2-3份、纳米氧化锌5-10份、纳米银粉5-10份、壳聚糖4-6份、柔软剂3-5份、羧甲基纤维素3-6份、渗透剂1-2份、防水剂4-6份、粘合剂2-4份。
优选地，所述的金银花提取物为金银花烘干粉碎后与20％乙醇溶液在料液比1:10、温度60℃回流提取两次，每次1h，离心后合并提取液浓缩即得。
优选地，所述的鱼腥草提取物为鱼腥草切段后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
优选地，所述的石榴皮提取物为石榴皮切条后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
优选地，所述的柔软剂为非离子柔软剂。
优选地，所述的渗透剂为非离子型渗透剂JFC。
优选地，所述的防水剂为防水剂EF-24。
优选地，所述的粘合剂为低温固着型水性聚丙烯酸酯。
优选地，所述的抗菌防汗迹免烫整理液的制备方法，包括以下步骤：
1)金银花提取物、鱼腥草提取物和石榴皮提取物制备；
2)将阿拉伯胶加到去离子水中制成浓度为1％的溶液，45℃搅拌完全溶解得混合液；
3)按配方量称取纳米氧化锌和纳米银粉，将其均匀分散于水中后和步骤1)中制备的金银花提取物、鱼腥草提取物和石榴皮提取物一同加入到步骤2)中的混合液中混合均匀后加入配方量壳聚糖、柔软剂、羧甲基纤维素、渗透剂、防水剂和粘合剂充分搅拌混合均匀，直至粘度达到10000-13000厘泊即得整理液。
本发明的另一目的在于提供上述所述的抗菌防汗迹免烫整理液用于棉质织物的持久抗菌防汗迹免烫整理工艺，包括以下步骤：
1.将棉质织物采用喷雾方法使其含水量保持在30％后放入到90-100℃热水中预煮后130-140℃下进行轧压；
2.再将棉质织物经过布棍、分丝辊、纠偏装置、压辊进入印花机的运布导带上，根据工艺设定调整网目、磁棒、速度，最后经过涂覆整理液的棉质织物将进入160-170℃的印花机烘房内以25-26m/min的速度运行，最后落布，整理液涂层厚度为0.03-0.05mm；
3.防汗迹检测合格后继续下一道工序，否则调整工艺，每一匹料布至少检测10个点；
4.采用振荡式烘干，整理后的棉质织物为保证抗菌和防汗迹牢固度，进行二次焙烘，焙烘温度为150-160℃，速度为25-26m/min。
优选地，所述的印花机为圆网印花机，网目大小为120-150目，磁棒粗细为1.0-1.5cm，压力为0.3-0.5kg/cm2。
优选地，所述的棉质织物为纯棉织物或者棉与纤维混纺面料，其中棉的含量为30-100wt％。
上述技术方案可以看出，本发明具有如下有益效果：本发明所述的棉质织物的持久抗菌防汗迹免烫整理液，采用壳聚糖和中草药提取物、纳米氧化锌、纳米银粉以及其他助剂复配作为整理液，壳聚糖为天然生物高分子多糖，天然无毒可降解、生物相容性好、抗菌性能优异，壳聚糖表面含有大量的羟基和氨基等活性基团，有利于提高整理液的防缩抗皱效果；阿拉伯胶成膜包裹金银花提取物、鱼腥草提取物、石榴皮提取物和纳米氧化锌、纳米银粉抗菌剂，达到缓释和持久抗菌的效果，加上壳聚糖复配，赋予了棉质织物良好的抗皱性、免烫性、抗菌性能，提高了棉质织物手感、强力和耐洗性；经整理后的织物抗菌性、耐性、抗皱性和免烫性好，汗迹可以瞬间吸收和挥发，透气性良好，服用舒适；振荡式烘干避免带压力的轧辊式设备影响织物的透气性。
具体实施方式
下面结合具体实施例，进一步阐明本发明。
实施例1
一种棉质织物的持久抗菌防汗迹免烫整理液，包括以下重量份的原料：金银花提取物30份、鱼腥草提取物30份、石榴皮提取物30份、阿拉伯胶3份、纳米氧化锌10份、纳米银粉10份、壳聚糖6份、非离子柔软剂5份、羧甲基纤维素6份、非离子型渗透剂JFC2份、防水剂EF-24 6份、低温固着型水性聚丙烯酸酯4份。
所述的金银花提取物为金银花烘干粉碎后与20％乙醇溶液在料液比1:10、温度60℃回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的鱼腥草提取物为鱼腥草切段后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的石榴皮提取物为石榴皮切条后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的抗菌防汗迹免烫整理液的制备方法，包括以下步骤：
1)金银花提取物、鱼腥草提取物和石榴皮提取物制备；
2)将阿拉伯胶加到去离子水中制成浓度为1％的溶液，45℃搅拌完全溶解得混合液；
3)按配方量称取纳米氧化锌和纳米银粉，将其均匀分散于水中后和步骤1)中制备的金银花提取物、鱼腥草提取物和石榴皮提取物一同加入到步骤2)中的混合液中混合均匀后加入配方量壳聚糖、非离子柔软剂、羧甲基纤维素、非离子型渗透剂、防水剂EF-24、低温固着型水性聚丙烯酸酯充分搅拌混合均匀，直至粘度达到10000厘泊即得整理液。
上述所述的抗菌防汗迹整理液用于棉质织物的持久抗菌防汗迹免烫整理工艺，包括以下步骤：
1.将棉质织物采用喷雾方法使其含水量保持在30％后放入到90℃热水中预煮后130℃下进行轧压；
2.再将棉质织物经过布棍、分丝辊、纠偏装置、压辊进入印花机的运布导带上，根据工艺设定调整网目、磁棒、速度，最后经过涂覆整理液的棉质织物将进入160℃的印花机烘房内以25m/min的速度运行，最后落布，整理液涂层厚度为0.03mm；
3.防汗迹检测合格后继续下一道工序，否则调整工艺，每一匹料布至少检测10个点；
4.采用振荡式烘干，整理后的棉质织物为保证抗菌和防汗迹牢固度，进行二次焙烘，焙烘温度为150℃，速度为25m/min。
所述的印花机为圆网印花机，网目大小为120目，磁棒粗细为1.0cm，压力为0.3kg/cm2。
所述的棉质织物为纯棉织物。
实施例2
一种棉质织物的持久抗菌防汗迹免烫整理液，包括以下重量份的原料：金银花提取物20份、鱼腥草提取物20份、石榴皮提取物20份、阿拉伯胶2份、纳米氧化锌5份、纳米银粉5份、壳聚糖4份、非离子柔软剂3份、羧甲基纤维素3份、非离子型渗透剂JFC1份、防水剂EF-24 4份、低温固着型水性聚丙烯酸酯2份。
所述的金银花提取物为金银花烘干粉碎后与20％乙醇溶液在料液比1:10、温度60℃回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的鱼腥草提取物为鱼腥草切段后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的石榴皮提取物为石榴皮切条后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的抗菌防汗迹免烫整理液的制备方法，包括以下步骤：
1)金银花提取物、鱼腥草提取物和石榴皮提取物制备；
2)将阿拉伯胶加到去离子水中制成浓度为1％的溶液，45℃搅拌完全溶解得混合液；
3)按配方量称取纳米氧化锌和纳米银粉，将其均匀分散于水中后和步骤1)中制备的金银花提取物、鱼腥草提取物和石榴皮提取物一同加入到步骤2)中的混合液中混合均匀后加入配方量壳聚糖、非离子柔软剂、羧甲基纤维素、非离子型渗透剂JFC、防水剂EF-24、低温固着型水性聚丙烯酸酯充分搅拌混合均匀，直至粘度达到13000厘泊即得整理液。
本发明的另一目的在于提供一种棉质织物的持久抗菌防汗迹免烫整理工艺，包括以下步骤：
1.将棉质织物采用喷雾方法使其含水量保持在30％后放入到100℃热水中预煮后140℃下进行轧压；
2.再将棉质织物经过布棍、分丝辊、纠偏装置、压辊进入印花机的运布导带上，根据工艺设定调整网目、磁棒、速度，最后经过涂覆整理液的棉质织物将进入170℃的印花机烘房内以26m/min的速度运行，最后落布，整理液涂层厚度为0.05mm；
3.防汗迹检测合格后继续下一道工序，否则调整工艺，每一匹料布至少检测10个点；
4.采用振荡式烘干，整理后的棉质织物为保证抗菌和防汗迹牢固度，进行二次焙烘，焙烘温度为160℃，速度为26m/min。
优选地，所述的印花机为圆网印花机，网目大小为150目，磁棒粗细为1.5cm，压力为0.5kg/cm2。
优选地，所述的棉质织物为棉与聚酯纤维混纺面料，其中棉的含量为30wt％。
实施例3
一种棉质织物的持久抗菌防汗迹免烫整理液，包括以下重量份的原料：金银花提取物25份、鱼腥草提取物25份、石榴皮提取物25份、阿拉伯胶2.5份、纳米氧化锌8份、纳米银粉8份、壳聚糖5份、非离子柔软剂4份、羧甲基纤维素5份、非离子型渗透剂JFC1.5份、防水剂EF-24 5份、低温固着型水性聚丙烯酸酯3份。
所述的金银花提取物为金银花烘干粉碎后与20％乙醇溶液在料液比1:10、温度60℃回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的鱼腥草提取物为鱼腥草切段后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的石榴皮提取物为石榴皮切条后与50％乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
所述的抗菌防汗迹免烫整理液的制备方法，包括以下步骤：
1)金银花提取物、鱼腥草提取物和石榴皮提取物制备；
2)将阿拉伯胶加到去离子水中制成浓度为1％的溶液，45℃搅拌完全溶解得混合液；
3)按配方量称取纳米氧化锌和纳米银粉，将其均匀分散于水中后和步骤1)中制备的金银花提取物、鱼腥草提取物和石榴皮提取物一同加入到步骤2)中的混合液中混合均匀后加入配方量壳聚糖、非离子柔软剂、羧甲基纤维素、非离子型渗透剂JFC、防水剂EF-24、低温固着型水性聚丙烯酸酯充分搅拌混合均匀，直至粘度达到12000厘泊即得整理液。
上述所述的抗菌防汗迹整理液用于棉质织物的持久抗菌防汗迹免烫整理工艺，包括以下步骤：
1.将棉质织物采用喷雾方法使其含水量保持在30％后放入到95℃热水中预煮后135℃下进行轧压；
2.再将棉质织物经过布棍、分丝辊、纠偏装置、压辊进入印花机的运布导带上，根据工艺设定调整网目、磁棒、速度，最后经过涂覆整理液的棉质织物将进入165℃的印花机烘房内以25m/min的速度运行，最后落布，整理液涂层厚度为0.04mm；
3.防汗迹检测合格后继续下一道工序，否则调整工艺，每一匹料布至少检测10个点；
4.采用振荡式烘干，整理后的棉质织物为保证抗菌和防汗迹牢固度，进行二次焙烘，焙烘温度为155℃，速度为25m/min。
优选地，所述的印花机为圆网印花机，网目大小为135目，磁棒粗细为1.3cm，压力为0.4kg/cm2。
优选地，所述的棉质织物为纯棉织物或者棉与纤维混纺面料，其中棉的含量为65wt％。
对实施例1-3整理后的棉质织物其免烫性能检测指标和国家标准GB/T 18863-2002《免烫纺织品》的对比结果及安装AATCC 79测试水洗前后的吸水性能，结果如表1所示；对金黄色葡萄球菌和白色念珠菌的抑制率如下表2所示；根据GB/T 3922-1995《纺织品耐汗渍色牢度试验方法》中要求，配制出两种试液，一种酸性，一种碱性。案子GB/T 21655.1-2008《纺织品吸湿速干性的评定》标准对产品滴水扩散时间进行测试，测试结果如下表3所示。
表1 实施例产品性能测试指标和国家标准对比表
表2 实施例产品对金黄色葡萄球菌和白色念珠菌的抑制率
| 金黄色葡萄球菌抑制率 | 白色念珠菌抑制率 | |
| 实施例1 | 90％ | 91％ |
| 实施例2 | 91％ | 90％ |
| 实施例3 | 95％ | 94％ |
表3 实施例产品滴水扩散时间测试结果
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进，这些改进也应视为本发明的保护范围。
Claims (9)
1.一种棉质织物的持久抗菌防汗迹免烫整理液，其特征在于：包括以下重量份的原料：金银花提取物20-30份、鱼腥草提取物20-30份、石榴皮提取物20-30份、阿拉伯胶2-3份、纳米氧化锌5-10份、纳米银粉5-10份、壳聚糖4-6份、柔软剂3-5份、羧甲基纤维素3-6份、渗透剂1-2份、防水剂4-6份、粘合剂2-4份。
2.根据权利要求1所述的一种棉质织物的持久抗菌防汗迹免烫整理液，其特征在于：所述的金银花提取物为金银花烘干粉碎后与20%乙醇溶液在料液比1:10、温度60℃回流提取两次，每次1h，离心后合并提取液浓缩即得。
3.根据权利要求1所述的一种棉质织物的持久抗菌防汗迹免烫整理液，其特征在于：所述的鱼腥草提取物为鱼腥草切段后与50%乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
4.根据权利要求1所述的一种棉质织物的持久抗菌防汗迹免烫整理液，其特征在于：所述的石榴皮提取物为石榴皮切条后与50%乙醇溶液在料液比1:10、温度50℃条件下回流提取两次，每次1h，离心后合并提取液浓缩即得。
5.根据权利要求1所述的一种棉质织物的持久抗菌防汗迹免烫整理液，其特征在于：所述的柔软剂为非离子柔软剂；所述的渗透剂为非离子型渗透剂JFC；所述的防水剂为防水剂EF-24；所述的粘合剂为低温固着型水性聚丙烯酸酯。
6.根据权利要求1所述的一种棉质织物的持久抗菌防汗迹免烫整理液，其特征在于：所述的抗菌防汗迹免烫整理液的制备方法，包括以下步骤：
1）金银花提取物、鱼腥草提取物和石榴皮提取物制备；
2）将阿拉伯胶加到去离子水中制成浓度为1%的溶液，45℃搅拌完全溶解得混合液；
3）按配方量称取纳米氧化锌和纳米银粉，将其均匀分散于水中后和步骤1）中制备的金银花提取物、鱼腥草提取物和石榴皮提取物一同加入到步骤2）中的混合液中混合均匀后加入配方量壳聚糖、柔软剂、羧甲基纤维素、渗透剂、防水剂和粘合剂充分搅拌混合均匀，直至粘度达到10000-13000厘泊即得整理液。
7.一种如权利要求1-6任一项所述的抗菌防汗迹免烫整理液用于棉质织物的持久抗菌防汗迹免烫整理工艺，其特征在于：包括以下步骤：
1.将棉质织物采用喷雾方法使其含水量保持在30%后放入到90-100℃热水中预煮后130-140℃下进行轧压；
2.再将棉质织物经过布棍、分丝辊、纠偏装置、压辊进入印花机的运布导带上，根据工艺设定调整网目、磁棒、速度，最后经过涂覆整理液的棉质织物将进入160-170℃的印花机烘房内以25-26m/min的速度运行，最后落布，整理液涂层厚度为0.03-0.05mm；
3.防汗迹检测合格后继续下一道工序，否则调整工艺，每一匹料布至少检测10个点；
4.采用振荡式烘干，整理后的棉质织物为保证抗菌和防汗迹牢固度，进行二次焙烘，焙烘温度为150-160℃，速度为25-26m/min。
8.根据权利要求7所述的棉质织物的持久抗菌防汗迹免烫整理工艺，其特征在于：所述的印花机为圆网印花机，网目大小为120-150目，磁棒粗细为1.0-1.5cm，压力为0.3-0.5kg/cm2。
9.根据权利要求7所述的棉质织物的持久抗菌防汗迹免烫整理工艺，其特征在于：所述的棉质织物为纯棉织物或者棉与纤维混纺面料，其中棉的含量为30-100wt%。