CN1072111A - J111均孔弱酸阳离子交换树脂及工艺 - Google Patents
J111均孔弱酸阳离子交换树脂及工艺 Download PDFInfo
- Publication number
- CN1072111A CN1072111A CN 91108224 CN91108224A CN1072111A CN 1072111 A CN1072111 A CN 1072111A CN 91108224 CN91108224 CN 91108224 CN 91108224 A CN91108224 A CN 91108224A CN 1072111 A CN1072111 A CN 1072111A
- Authority
- CN
- China
- Prior art keywords
- water
- hour
- accounts
- hours
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
J111均孔弱酸阳离子交换树脂及其生产工艺。
成分配比，丙烯酸甲酯0.14，甲苯0.03，二乙烯苯
0.03，过氧化苯甲酰0.03，丙烯腈0.004，水0.715，氯
化钠0.071，羟乙基纤维素0.003，极其微量的次甲
蓝，甲基丙烯酸甲酯0.04。生产工艺分配油相，配水
箱，将温度分别控制在65℃，75℃，95℃保温反应2
小时、8小时，再进入水解生产工艺。具有结构均匀、
交换树脂快、交换容量高(全交换≥11.3，体积交换≥
4.0)，外观透明，密度0.75/毫升(湿)，膨胀度≤
75％，含水量55％，pH使用范围8—14。使用温度
100℃，粒度20—60目。
Description
本发明给出的是一种J111均孔弱酸阳离子交换树脂及其聚合生产工艺。
弱酸阳树脂的生产是在强酸阳树脂之后，第一代弱酸树脂是凝胶型结构的产品。这类产品骨架结构类似凝胶，十分紧密、孔隙窄小，使用离子交换速度很慢，使用性能不够理想。为改进上述性能，就在合成珠体骨架过程中加入致孔剂，以产生扩大孔道，加快交换速度（所得珠体由骨架凝胶部分和孔道两部分组成），大孔型树脂使用时交换速度大大加快，但其缺陷是大孔型树脂还要紧密，所以在使用时常产生离子的“滞后”即“带尾巴”现象，直接影响二交容量和再生剂用量，大孔型树脂一般称为第二代树脂。
本发明的目的在于克服上述缺陷，提出第三代树脂及其生产工艺-J111均孔弱酸阳离子交换树脂及其它的生产工艺。
本发明的技术解决方案：
J111均孔弱酸阳离子交换树脂，它的配比成份及聚合生产工艺。
配比：丙烯酸甲脂占0.14，甲苯占0.03，二乙烯苯占0.03，过氧化苯甲酰占0.03，丙烯晴占0.004，水占0.715，氯化钠占0.071，羟乙基纤维占0.003，次甲兰极其微量（0.7×10-7），甲基丙烯酸甲脂占0.04;
生产操作工艺：配油相，依次将丙烯酸甲脂、甲苯、二乙烯苯，丙烯晴、甲基丙烯酸甲脂投入配油相釜，搅拌15分钟后再投入过氧化苯甲酰，再搅拌半小时后投入水相釜。配水相，羟乙基纤维素在前一天泡好，投水、食盐（氯化钠），在温度45℃中搅拌0.5小时，温度再升到50℃投油相;用0.5小时将温度升至65℃，保温反应2小时。用0.5小时将温度升至75℃，保温反应2小时。用0.5小时将温度升至95℃，保温反应8小时。离子利用70℃热水冲洗二遍，再用冷水（自来水）冲洗至水清，球烘干、过筛，取20-60目送水介。
水介生产工艺：配比（1000L釜），取110Kg球，烧碱（2.2-2.4N）800Kg，甲醇20Kg;操作工艺：投入碱、球、甲醇，用1小时升至75℃保温反应1小时。用1小时升至92℃保温反应至球心消失，再维持反应1小时，保温3小时后取样观察，可用0.1N盐酸滴球，见光球由大→小至球心即为水介透，反应毕降温至30℃，离子放置过滤器内，抽去母液作下次套用，球用水洗至中性，停止水洗，滤干即得成品。
本发明具有结构均匀，交换树脂快、交换容量大。均孔型树脂的性能指标如下：
外观，微黄透明至半透明球粒，粒度20-60目，密度0.75克/毫升（湿），全交换容量≥11.3毫克当量/克（干）树脂，体积交换容量≥4.0毫克当量/毫升（湿）树脂，膨胀度≤75%，含水量55%，PH使用范围8-14，使用温度100℃。
Claims (1)
1、J111均孔弱酸阳离子交换树脂，其特征是它的配比成份及聚合生产工艺为：
配比，丙烯酸甲脂占0.14，甲苯占0.03，二乙烯苯占0.03，过氧化苯甲酰占0.03，丙烯晴占0.004，水占0.715，氯化钠占0.071，羟乙基纤维占0.003，次甲兰极其微量(0.7×10-7)，甲基丙烯酸甲脂占0.04；
生产操作工艺：
(1)、配油相，依次将丙烯酸甲脂、甲苯、二乙烯苯，丙烯晴、甲基丙烯酸甲脂投入配油相釜，搅拌15分钟后再投入过氧化苯甲酰，再搅拌半小时后投入水相釜；
(2)、配水相，羟乙基纤维素在前一天泡好，投水，食盐(氯化钠)，在温度45℃中搅拌0.5小时，温度再升到50℃投油相，
(3)、用0.5小时将温度升至65℃，保温反应2小时，
(4)、用0.5小时将温度升至75℃，保温反应2小时，
(5)、用0.5小时将温度升至95℃，保温反应8小时，
(6)、离子利用70℃热水冲洗二遍，再用冷水(自来水)冲洗至水清，
(7)、球烘干、过筛，取20-60目送水介；
水介生产工艺：
(1)、配比(1000L釜)，取110Kg球，烧碱(2.2-2.4N)800Kg，甲醇20Kg；
a、投入碱、球、甲醇，用1小时升至75℃保温反应1小时，
b、用1小时升至92℃，保温反应至球心消失，再维持反应1小时，保温3小时后取样观察，可用0.1N盐酸滴球，见光球由大→小至球心即为水介透，
c、反应毕降温至30℃，离子放置过滤器内，抽去母液作下次套用，球用水洗至中性，停止水洗，滤干即得成品。