CN107160296A - 一种高强度低温烧结微晶玻璃结合剂及其制备方法 - Google Patents
一种高强度低温烧结微晶玻璃结合剂及其制备方法 Download PDFInfo
- Publication number
- CN107160296A CN107160296A CN201710456315.0A CN201710456315A CN107160296A CN 107160296 A CN107160296 A CN 107160296A CN 201710456315 A CN201710456315 A CN 201710456315A CN 107160296 A CN107160296 A CN 107160296A
- Authority
- CN
- China
- Prior art keywords
- bonding agent
- glass
- oxide
- high intensity
- temperature sintering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (4)