CN106927784A - Jing Dezhen health pottery mud and the glaze of energy anion releasing - Google Patents
Jing Dezhen health pottery mud and the glaze of energy anion releasing Download PDFInfo
- Publication number
- CN106927784A CN106927784A CN201710131440.4A CN201710131440A CN106927784A CN 106927784 A CN106927784 A CN 106927784A CN 201710131440 A CN201710131440 A CN 201710131440A CN 106927784 A CN106927784 A CN 106927784A
- Authority
- CN
- China
- Prior art keywords
- parts
- pottery mud
- anion
- health
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to ceramic technology field, it is related to Jing Dezhen health pottery mud and the glaze of a kind of energy anion releasing.It includes pottery mud, and the anion component that can produce anion is added with described pottery mud, and the pottery made by the pottery mud.The present invention adds anion component by mud of making pottery, and obtains a kind of health pottery mud, and the vessel made of health pottery mud can directly produce anion, without subsequently carrying out anion coating, be conducive to simplifying subsequent technique.
Description
Technical field
The invention belongs to ceramic technology field, it is related to Jing Dezhen health pottery mud and the glaze of a kind of energy anion releasing.
Background technology
It is known that material is molecular in physics, molecule is molecular by original, and atom is by atom
The electronics composition that core and enclosing is rotated about, obtains aobvious elecrtonegativity during electronics, loses aobvious electropositive during electronics, and we are positron-electron
Motion artifacts are referred to as：Ionic phenomenon.Under nature, the polarity of air molecule is in neutrality, i.e.,：Neutral.But penetrated in universe
Under the effects such as line, ultraviolet, micro- radiation, Lightning strike, air molecule can lose part and be rotated most around atomic nucleus
Outer-shell electron, ionizes air, and the electronics of escape atomic nucleus constraint is referred to as：Free electron, it is negatively charged.Work as free electron
After being combined with other neutral gas molecules, negatively charged negative aeroion is just formed.Above is what is produced in natural phenomena is negative
Ion.
The presence in the township of Bama of Guangxi world longevity allows anion to have obtained preferably proving to the health-care effect of human body, research
It was found that, why high population rate at the age of one hundred years old in Bama area is, it is important that a reason be exactly local negative ion concentration high, up to 30,000
Individual/cm3.In bar horse, a diabetes, hypertension even cancer patient are almost can not find, most of old man dies without known cause, and sugared
Urine patient lives more than the moon at this point, just substantially can be without beating insulin again.The negative oxygen in the magic hole of bar horse anion highest hundred
Ion concentration is up to 170,000/cm3, it is many obtained cancer patients pay breathe anion herein.Effect based on anion,
It has the title of " air vitamin " again.Countless clinical researches find that anion can improve neurasthenia, insomnia, unobstructed heart and brain
Blood vessel, reduces blood viscosity, improves body immunity, to improving insomnia, asthma, alleviates the persistent ailments such as hypertension, diabetes tool
There is significant curative effect.
Chinese patent literature discloses a kind of negative ion ceramic mud gadget [application number：201520582556.6], including by making pottery
The body that mud is made, the outer wall of the body is coated with anion layer, and the body is in hollow structure, the inwall of the body with
Outer wall is equipped with bar shaped lines and/or netted lines, and the inwall of the body is also coated with anion layer, is opened up on the body
There is through hole.The surface area that the program solves existing negative ion ceramic mud gadget coating anion layer small causes clean-up effect not good
Problem.But carefully analyze, it has been found that the negative ion ceramic mud gadget is substantially to be coated with the vessel being made in pottery mud
One layer of anion layer, the anion layer is located at ceramic surface, and during use, the anion layer can wear and tear, so as to cause
Anion yield declines.
The content of the invention
Regarding the issue above, the present invention provides a kind of Jing Dezhen health pottery mud of energy anion releasing.
It is a further object of the present invention to provide a kind of Jing Dezhen health glaze of energy anion releasing.
To reach above-mentioned purpose, present invention employs following technical proposal：A kind of Jing Dezhen health of energy anion releasing
Pottery mud, including pottery mud, the anion component that can produce anion is added with described pottery mud.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, this health pottery mud is respectively including mass fraction
68-117 parts and 10-20 parts of pottery mud and anion component.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, described anion component includes Tourmaline, wheat
In meal stone and Gu Hai sedimentary rocks any one or it is several.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, described anion component includes following mass parts
Several components：
1 part of Tourmaline；
1 part of medical stone；
Ancient 1 part of the sedimentary rock in sea.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, described pottery mud include feldspar, clay, talcum,
Quartz and calcium carbonate.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, described pottery mud includes the group of following mass fraction
Point：
Feldspar 15-30 parts, clay 30-50 parts, talcum 2-4 parts, 20-30 parts, calcium carbonate 1-3 parts of quartz；
Or, feldspar 15-30 parts, clay 20-40 parts, talcum 10-25 parts, 20-30 parts, calcium carbonate 1-3 parts of quartz.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, described pottery mud includes the group of following mass fraction
Point：
Sericite 25-35 parts, clay 20-30 parts, talcum 1-4 parts, 30-45 parts, calcium carbonate 1-3 parts of quartz.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, described pottery mud includes the group of following mass fraction
Point：
Animal bone powder 30-50 parts, clay 25-35 parts, feldspar 5-20 parts, 15-30 parts of quartz.
In the Jing Dezhen health pottery mud of above-mentioned energy anion releasing, described anion component be in the grinding of pottery mud or
It is added to Tao Nizhong in person's mechanical milling process, and is sufficiently mixed with pottery mud, so as to forms health pottery mud.
Present invention also offers a kind of porcelain made using above-mentioned health pottery mud.
Present invention also offers it is a kind of can anion releasing Jing Dezhen health pottery mud, including following mass fraction group
Point：
Compared with prior art, the advantage of the invention is that：Anion component is added by mud of making pottery, a breeding is obtained
Raw pottery mud, the vessel of mud making of being made pottery with the health can directly produce anion, without subsequently carrying out anion coating, be conducive to
Simplify subsequent technique.
Because anion component be well mixed with pottery mud, therefore after making vessel with pottery mud, the component of generation anion
Inside vessel, anion concentration reduction will not be thus resulted in because of originals such as abrasions.
Specific embodiment
Reagent used in following embodiments, unless otherwise specified, can be commercially available from routine biochemistry reagent shop.With
Quantitative data in lower embodiment, is respectively provided with three repetitions and tests, results averaged.
Embodiment 1
A kind of anion component is present embodiments provided, specifically, including anion component includes Tourmaline.
Tourmaline is a kind of natural crystal, also makes tourmaline, releasing far infrared, the anion of energy contain lot of trace unit
Element, can produce 0.06ma bioelectricities, can improve water quality, be put into the water of Tourmaline, be the water of weakly alkaline subset, most suitable
People is closed to drink.Water quality is presented alkalescent, with antioxidation, is conducive to health.
Above-mentioned Tourmaline can be powder, or microballoon.
Medical stone, Chinese medicine name.Scientific name is：Quartz monzonite.Medical stone is to biological nontoxic, harmless and with certain biological living
The complex mineral or medicinal rock of property.With detoxicating and resolving a mass, remove necrosis and promote granulation, except cold clearing damp, beneficial liver and strengthening stomach, promoting blood circulation and removing blood stasis, diuresis
Fossil, the effect of promoting longevity.
Ancient sea sedimentary rock --- sea-gull stone, English name：Health.Main component is CaO, SiO2And variable valency metal Fe；
Internal structure has the hole of 20-60nm, therefore possesses powerful adsorption function；When moisture in air enters micro- inside sea-gull stone
Kong Shi, hydrone is appraised at the current rate the electric microfield ionization of iron generation, produces natural negative ion, and negative oxygen ion concentration is up to 1700/cm3,
A small amount of TiO is contained in sea-gull stone inside simultaneously2, therefore with photoelectrocatalysis effect, the harmful bacteria in air, virus can be killed,
According to experiment, sea-gull stone to staphylococcus aureus, Escherichia coli, Candida albicans, withered grass bacterium antibiotic rate be up to 90% with
On.
One of ancient sea sedimentary rock is opal stone, and also known as Ou Po, opal, classification is noncrystalline, belongs to opal bijouterie.Egg
Bai Shi has unique natural nano level microcellular structure, has powerful adsorption function, while discharging natural air anion.
The two of ancient sea sedimentary rock are six ring stones, are created on the Ordovician system (away from modern 200,000,000 4 thousand ten thousand years).With clean structure, can be certainly
So emitting far-infrared, normal emittance is up to 0.88, the biological Electricity Functional for having uniqueness.It is that a kind of adsorptivity is powerful, anti-electromagnetism
Ripple, anti-chemotherapy, antitumor, AIDS virus resisting ancient sedimentary rock, six ring stones are rich in calcium, magnesium, sodium, potassium, iron, selenium, zinc, strontium, copper
And nutrient necessary to the human body such as noble metal germanium, and permanent anion releasing.
Three attapulgites of ancient sea sedimentary rock, are a kind of link layer also known as palygorskite (Palygorskite) or ripple thread thin white silk used in ancient China stone
The clay ore of magnesium silicate containing Shuifu County of shape structure.Because attapulgite clay has unique crystal structure, with good
Caking property and stronger adsorption function, and characteristic that is deodorant, purifying.
Embodiment 2
A kind of anion component is present embodiments provided, specifically, anion component includes Tourmaline and medical stone.
Wherein, Tourmaline and medical stone are with 2:1 mass ratio mixing, grind into powder is well mixed.
Embodiment 3
A kind of anion component is present embodiments provided, specifically, anion component includes Tourmaline, medical stone and Gu
Extra large sedimentary rock.
Wherein, Tourmaline, medical stone and Gu Hai sedimentary rocks are with 1:1:1 mass ratio mixing, grind into powder, mixing is equal
It is even.
In the present embodiment, ancient sea sedimentary rock includes following components：In sea-gull stone, opal stone, six ring stones and attapulgite
Any one and it is several.
Embodiment 4
A kind of anion component is present embodiments provided, specifically, anion component includes Tourmaline, medical stone and Gu
Extra large sedimentary rock.
Wherein, Tourmaline, medical stone and Gu Hai sedimentary rocks are with 2:1:1 mass ratio mixing, grind into powder, mixing is equal
It is even.
Embodiment 5
Present embodiments provide a kind of pottery mud, specifically, the pottery mud include 15 parts of feldspar, 30 parts of clay, 4 parts of talcum,
Quartzy 30 parts, 3 parts of calcium carbonate, the pottery mud are applied to making tableware, tea set and all kinds of workmanships.
Embodiment 6
Present embodiments provide a kind of pottery mud, specifically, the pottery mud include 30 parts of feldspar, 50 parts of clay, 2 parts of talcum,
Quartzy 20 parts, 1 part of calcium carbonate, the pottery mud are applied to making tableware, tea set and all kinds of workmanships.
Embodiment 7
Present embodiments provide a kind of pottery mud, specifically, the pottery mud include 25 parts of feldspar, 40 parts of clay, 3 parts of talcum,
Quartzy 25 parts, 2 parts of calcium carbonate, the pottery mud are applied to making tableware, tea set and all kinds of workmanships.
Embodiment 8
Present embodiments provide a kind of pottery mud, specifically, the pottery mud include 15 parts of feldspar, 20 parts of clay, 25 parts of talcum,
Quartzy 30 parts, 3 parts of calcium carbonate, the pottery mud are applied to making tableware, tea set and all kinds of workmanships.
Embodiment 9
Present embodiments provide a kind of pottery mud, specifically, the pottery mud include 30 parts of feldspar, 40 parts of clay, 10 parts of talcum,
Quartzy 20 parts, 1 part of calcium carbonate, it is adaptable to all face bricks for outdoor wall decorations.
Embodiment 10
Present embodiments provide a kind of pottery mud, specifically, the pottery mud include 25 parts of feldspar, 30 parts of clay, 15 parts of talcum,
Quartzy 25 parts, 2 parts of calcium carbonate, it is adaptable to all face bricks for outdoor wall decorations.
Embodiment 11
A kind of pottery mud is present embodiments provided, specifically, the pottery mud includes 25 parts of sericite, 30 parts of clay, talcum 4
Part, quartzy 30 parts, 1 part of calcium carbonate, it is adaptable to all face bricks for outdoor wall decorations.
Embodiment 12
A kind of pottery mud is present embodiments provided, specifically, the pottery mud includes 35 parts of sericite, 20 parts of clay, talcum 1
Part, quartzy 45 parts, 3 parts of calcium carbonate, tableware, tea set and all kinds of workmanships
Embodiment 13
A kind of pottery mud is present embodiments provided, specifically, the pottery mud includes 30 parts of sericite, 25 parts of clay, talcum 2
Part, quartzy 35 parts, 2 parts of calcium carbonate, tableware, tea set and all kinds of workmanships
Embodiment 14
A kind of pottery mud is present embodiments provided, specifically, the pottery mud includes 30 parts of animal bone powder, 25 parts of clay, feldspar
20 parts, 30 parts of quartz, manufacture china tableware, tea set, workmanship.
In the present embodiment, the bone of the animal bone powder animal such as including ox, sheep, pig, after oil refining, drying and crushing
Product.Specific composition：Most importantly hydroxyapatite crystals [Ca10(PO4)6(OH)2] and unformed calcium monohydrogen phosphate (CaHPO4),
Ca has also been adsorbed on its surface2+、Mg2+、Na+、Cl-、HCO3 -、F-And citrate plasma.What is more important, it is rich in bone meal
Rich Ca and P is macro minerals element needed by human, and without harmful lead and cadmium, long-term use has to health
Benefit.
Embodiment 15
A kind of pottery mud is present embodiments provided, specifically, the pottery mud includes 50 parts of animal bone powder, 35 parts of clay, feldspar 5
Part, 15 parts of quartz, manufacture china tableware, tea set, workmanship.
Embodiment 16
A kind of pottery mud is present embodiments provided, specifically, the pottery mud includes 40 parts of animal bone powder, 30 parts of clay, feldspar
15 parts, 20 parts of quartz, manufacture china tableware, tea set, workmanship.
Embodiment 17
Present embodiments provide a kind of Jing Dezhen health pottery mud of energy anion releasing, including embodiment 1-4 any one
Anion component, and embodiment 5-16 any one pottery mud.
Wherein the mass fraction of pottery mud and anion component is 68-117 parts and 10-20 parts.Anion component is in pottery mud
It is added to Tao Nizhong in grinding or mechanical milling process, and is sufficiently mixed with pottery mud, mixing can be mixed with high-speed mixer, so that shape
Into health pottery mud, the particle diameter and solid content, viscosity of mud of making pottery etc. are not limited in the present embodiment.The health pottery mud of the present embodiment
Form according to the difference of water content, can be made into plastic mass and slip casting blank, and the water content of plastic mass and slip casting blank
Belong to prior art, those skilled in the art can select the pottery of different water content according to different pottery and techniques are made
Mud, so as to obtain the blank of different forms.
Embodiment 18
Present embodiments provide a kind of Jing Dezhen health pottery mud of energy anion releasing, including embodiment 1-4 any one
Anion component, and embodiment 5-16 any one pottery mud.Wherein the mass fraction of pottery mud and anion component is 68 Hes
10 parts.Collocation method is with embodiment 17.
Embodiment 19
Present embodiments provide a kind of Jing Dezhen health pottery mud of energy anion releasing, including embodiment 1-4 any one
Anion component, and embodiment 5-16 any one pottery mud.Wherein the mass fraction of pottery mud and anion component is 117 Hes
20 parts.Collocation method is with embodiment 17.
Embodiment 20
Present embodiments provide a kind of Jing Dezhen health pottery mud of energy anion releasing, including embodiment 1-4 any one
Anion component, and embodiment 5-16 any one pottery mud.Wherein the mass fraction of pottery mud and anion component is 68 Hes
20 parts.Collocation method is with embodiment 17.
Embodiment 21
Present embodiments provide a kind of Jing Dezhen health pottery mud of energy anion releasing, including embodiment 1-4 any one
Anion component, and embodiment 5-16 any one pottery mud.Wherein the mass fraction of pottery mud and anion component is 117 Hes
10 parts.Collocation method is with embodiment 17.
Embodiment 22
Present embodiments provide a kind of Jing Dezhen health pottery mud of energy anion releasing, including embodiment 1-4 any one
Anion component, and embodiment 5-16 any one pottery mud.Wherein the mass fraction of pottery mud and anion component is 89 Hes
11 parts.Collocation method is with embodiment 17.
Embodiment 23
A kind of Jing Dezhen health glaze of energy anion releasing is present embodiments provided,
Component including following mass fraction：
30 parts of feldspar, 2 parts of kaolin, 2 parts of talcum, 30 parts of quartz, 1 part of calcium carbonate, 5 parts of Tourmaline, 5 parts of medical stone is ancient
5 parts of extra large sedimentary rock.
Embodiment 24
A kind of Jing Dezhen health glaze of energy anion releasing is present embodiments provided,
Component including following mass fraction：15 parts of feldspar, 10 parts of kaolin, 4 parts of talcum, 20 parts of quartz, calcium carbonate 3
Part, 5 parts of Tourmaline, 5 parts of medical stone, ancient 5 parts of the sedimentary rock in sea.
Embodiment 25
A kind of Jing Dezhen health glaze of energy anion releasing is present embodiments provided,
Component including following mass fraction：20 parts of feldspar, 7 parts of kaolin, 3 parts of talcum, 25 parts of quartz, 2 parts of calcium carbonate,
5 parts of Tourmaline, 5 parts of medical stone, ancient 5 parts of the sedimentary rock in sea.
Application examples 1
Test environment：
With the anion component of embodiment 4, the pottery mud with embodiment 5, with mass ratio 12:92 mixing, are made ecological pottery mud,
The porcelain cup A made with ecology pottery mud, the porcelain cup B made with the pottery mud of embodiment 5.
Basicity is tested：Mutually synthermal pure water is put into simultaneously in porcelain cup A with ceramic cup B, stands 30 minutes, as a result
It is as follows：Porcelain cup A in water display pH value be 7.6 be in alkalescent, porcelain cup B in water display pH value be 6.4 in weak acid partially in
Property.
Understand to be filled with water in alkalescent by the porcelain cup after the fusion of anion component.After high temperature burns till, pottery mud
Crystal structure does not undergo phase transition, and is still hexagonal columnar crystal, so as to show that anion component is to be born health pottery mud
The main cause of ion function.
Application examples 2
With the anion component of embodiment 1-3 respectively with the pottery mud of embodiment 6-8, respectively with mass ratio 11:117、18:88
With 13:87 mixing, obtain ecological pottery mud, then are respectively prepared pottery cup, obtain pottery cup A, pottery cup B and pottery cup C, then with reality
The pottery mud for applying example 6 makes pottery cup D.
Pottery cup A, pottery cup B, pottery cup C and pottery cup D carry out combined radiation test and discharge test with anion solid,
Test result is as follows：
Pottery cup A：
Combined radiation value is：0.29usv/h；
8 test values of anion are：1566/cm3；
Pottery cup B：
Combined radiation value is：0.16usv/h；
8 test values of anion are：1278/cm3；
Pottery cup C：
Combined radiation value is：0.12usv/h；
8 test values of anion are：1038/cm3；
Pottery cup D：
Combined radiation value is：0.22usv/h；
8 test values of anion are：68/cm3。
Anionic textiles are detected using the negative ion concentration detector of Environmental Protection Technology Co., Ltd of Shanghai Anna Austria production, comprehensive
Radiation is closed using the detection of far infrared radiation detector.
From the foregoing, it will be observed that with the addition of the health pottery mud of anion component, the negative ion amount of release is much larger than and is not added with anion
The pottery mud of component.
The application example although schematically illustrate pottery cup, but do not represent this health pottery mud be only used for make pottery cup, this area
Technical staff can also make other pottery such as ceramic tile, tea set, toilet seat, shower houses etc. with it.
Specific embodiment described herein is only to the spiritual explanation for example of the present invention.Technology neck belonging to of the invention
The technical staff in domain can be made various modifications or supplement to described specific embodiment or be replaced using similar mode
Generation, but without departing from spirit of the invention or surmount scope defined in appended claims.
Claims (10)
1. the Jing Dezhen health pottery mud of a kind of energy anion releasing, including pottery mud, it is characterised in that be added with described pottery mud
The anion component of anion can be produced.
2. it is according to claim 1 can anion releasing Jing Dezhen health pottery mud, it is characterised in that this health is made pottery mud drum
Include the pottery mud and anion component of respectively 68-117 parts and 10-20 parts of mass fraction.
3. it is according to claim 2 can anion releasing Jing Dezhen health pottery mud, it is characterised in that described anion
Component includes any one in Tourmaline, medical stone and Gu Hai sedimentary rocks or several.
4. it is according to claim 3 can anion releasing Jing Dezhen health pottery mud, it is characterised in that described anion
Component includes the component of following mass fraction：
1 part of Tourmaline；
1 part of medical stone；
Ancient 1 part of the sedimentary rock in sea.
5. it is according to claim 2 can anion releasing Jing Dezhen health pottery mud, it is characterised in that described pottery mud drum
Include feldspar, clay, talcum, quartz and calcium carbonate.
6. it is according to claim 5 can anion releasing Jing Dezhen health pottery mud, it is characterised in that described pottery mud drum
Include the component of following mass fraction：
Feldspar 15-30 parts, clay 30-50 parts, talcum 2-4 parts, 20-30 parts, calcium carbonate 1-3 parts of quartz；
Or, feldspar 15-30 parts, clay 20-40 parts, talcum 10-25 parts, 20-30 parts, calcium carbonate 1-3 parts of quartz.
7. it is according to claim 2 can anion releasing Jing Dezhen health pottery mud, it is characterised in that described pottery mud drum
Include the component of following mass fraction：
Sericite 25-35 parts, clay 20-30 parts, talcum 1-4 parts, 30-45 parts, calcium carbonate 1-3 parts of quartz.
8. it is according to claim 2 can anion releasing Jing Dezhen health pottery mud, it is characterised in that described pottery mud drum
Include the component of following mass fraction：
Animal bone powder 30-50 parts, clay 25-35 parts, feldspar 5-20 parts, 15-30 parts of quartz.
9. it is according to claim 1 can anion releasing Jing Dezhen health pottery mud, it is characterised in that described anion
Component is to be added to Tao Nizhong in the grinding of pottery mud or mechanical milling process, and is sufficiently mixed with pottery mud, so as to form health pottery mud.
10. it is a kind of can anion releasing Jing Dezhen health pottery mud, it is characterised in that the component including following mass fraction：