CN108793989A - A kind of ceramic blank soil and preparation method thereof with activation water purification function - Google Patents
A kind of ceramic blank soil and preparation method thereof with activation water purification function Download PDFInfo
- Publication number
- CN108793989A CN108793989A CN201810699593.3A CN201810699593A CN108793989A CN 108793989 A CN108793989 A CN 108793989A CN 201810699593 A CN201810699593 A CN 201810699593A CN 108793989 A CN108793989 A CN 108793989A
- Authority
- CN
- China
- Prior art keywords
- mud
- soil
- talcum
- preparation
- ceramic blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ceramic blank soil and preparation method thereof with activation water purification function, and the preparation method includes：Dispensing → talcum calcining → finely ground → talcum material modulation → secondary finely ground → screening and mixing → preparation → six ring mountain flours are produced → stir and are mixed → pH value adjustment → finished product.Six ring mountain flours are added in a kind of ceramic blank soil with activation water purification function of the present invention, anion can eliminate the harmful bacteria in water caused by six ring mountain flours, achieve the purpose that bactericidal, purified water, and drinking water is made to become alkaline ionized water（PH value is 7.4-8）Water clusters become smaller, it is more suitable for human internal environment, convenient for absorption of human body, so as to be purified and activated to drinking water, the faintly acid sub-health state that human internal environment is adjusted through the six purified water of ring stone in drinking water is weak base sexual health status, and human body is made to have more resistance and immunity, human body is set to invigorate, it is more healthy.
Description
Technical field
The invention belongs to ceramic blank soil preparing process field, more particularly to a kind of ceramic blank soil with activation water purification function
And preparation method thereof.
Background technology
Ceramics are one of most common utensils in people's daily life, and ceramic is widely used, and ceramics in the market are a variety of
Various, function is also not quite similar, and ceramic blank soil is the raw material of firing ceramics, and the quality of ceramic blank soil decides the matter of ceramic
Amount and effect, still, ceramic blank soil currently on the market all do not have the function of activating water purification function, can not be to being contained in ceramics
Water in product is sterilized, and ceramic blank soil in the market cannot generate specific benefits to human body, if it is possible to make ceramics
Base soil has the function of antibacterial and sterilization, then obtains many benefits when can make people using ceramic, be conducive to people's
Life health, for this purpose, the present invention proposes a kind of ceramic blank soil and preparation method thereof with activation water purification function.
Invention content
Of the existing technology in order to solve the problems, such as, the present invention provides a kind of ceramic blank soil with activation water purification function
And preparation method thereof, six ring mountain flours are added in ceramic blank soil, have the function of activation and purified water, and people can be made to use pottery
Many benefits are obtained when ceramic products, are conducive to people's lives health.
To achieve the goals above, the present invention is to realize by the following technical solutions：One kind having activation water purification work(
The ceramic blank soil and preparation method thereof of energy, the preparation method comprises the following steps：
Step 1：Dispensing；Talcum 70% is taken, feldspar 6% builds soil 4%, long by precious native 16%, bentonite 2%, barium carbonate 2%, and will
Above-mentioned raw materials remove impurity；
Step 2：Talcum is calcined；Talcum raw material is put into kiln and is calcined, its laminated structure is destroyed, is conducive to subsequent
It is finely ground；
Step 3：It is finely ground；The talcum calcined progress is finely ground, it is put into after then screening talcum powder standby in suitable container
With；
Step 4：Talcum material is modulated；According to the weight of talcum, 30% water is added and is mixed, 0.3% a small amount of bentonite is added,
To improve plasticity, improves processability, 0.2% sodium carbonate is added, to improve the performance of mud, 0.4% salt is added
Acid makes mud agglomerate, for use after being mixed again；
Step 5：It is secondary finely ground；The weight of talcum and the proportioning of raw material are taken in comparison, by the feldspar of corresponding weight, build soil, long
Precious soil, bentonite and barium carbonate carry out finely ground respectively；
Step 6：Screening and mixing；By finely ground good feldspar, construction soil, long precious soil, bentonite and barium carbonate addition talcum material mud
In slurry and it is mixed；
Step 7：It prepares；Water is added to be let down in mixed mud, it is then spare；
Step 8：Six ring mountain flours are produced；A certain amount of six rings stone raw ore is chosen, six ring stone raw ores are removed into impurity, by six ring stones
It is ground into powder, is then screened；
Step 9：Stirring is mixed；Six ring mountain flours after screening are added in mud, and are again stirring for uniformly, so as to six ring mountain flours
It can be uniformly dispersed in mud；
Step 10：PH value adjustment；The pH value of mud is detected, adjusting appropriate is then carried out；
Step 11：Finished product；Uniformly mixed mud is stood into a period of time, it is then spare.
As a kind of preferred embodiment of the present invention, the finely ground process in the step 3 and step 5 is first coarse crushing, then is made
With ball mill grinding at powdered.
As a kind of preferred embodiment of the present invention, the mud moisture content after adding water to be let down in the step 7 is 34-36%.
As a kind of preferred embodiment of the present invention, the pH value of mud should be greater than 9 after pH value adjustment in the step 10.
First all devices should be cleared up before prepared by ceramic blank soil as a kind of preferred embodiment of the present invention.
As a kind of preferred embodiment of the present invention, mud and six ring mountain flour mixed proportions in the step 9 are 1:0.3.
Beneficial effects of the present invention are：
1, the present invention adds six ring mountain flours in ceramic blank soil, and anion can eliminate being harmful in water caused by six ring mountain flours
Bacterium achievees the purpose that bactericidal, purified water, and drinking water is made to become alkaline ionized water（PH value is 7.4-8）, hydrone
Group becomes smaller, and is more suitable for human internal environment, is convenient for absorption of human body, so as to be purified and activated to drinking water, drinking water warp
The faintly acid sub-health state that human internal environment is adjusted in the six purified water of ring stone is weak base sexual health status, and human body is made to have more
Resistance and immunity, make human body invigorate, more healthy.
2 and the present invention it is a kind of have activation water purification function ceramic blank soil can also permanent generating negative ions, have
Promote human metabolism, improve human immunological competence, enhance function of human body, adjust the effect of body function balance, and bears
Ion can reinforce the restoring force of life entity itself and natural healing ability, and then overcome disease, while can be emitting far-infrared,
To make the Marjoram Extract of human body, accelerate blood circulation, is conducive to removing blood vessel and hoards object and internal harmful substance, make again
Tissue is brought back to life, and ferment is promoted to generate, and is achieved the purpose that activate histocyte, is prevented aging, strengthening immune system ability, six ring stones
Also contain the micro- nutrients such as " germanium " and calcium needed by human, magnesium, sodium, potassium, iron, selenium, zinc in powder, and the present invention
A kind of ceramic blank soil with activation water purification function can also generate bioelectricity, and bioelectricity is transmitted to cerebral nerve and immune when use
System makes immunocyte enliven, and phagocytic activity enhancing can timely and effectively annihilate bacterium and the virus of invasion.
3, the present invention every time it is finely ground after all screened, can effectively improve the fine and smooth degree of ceramic blank soil, make mud
Slurry is not easy to be thickened, and enhances the mobility of mud, is conducive to the progress of slip casting, step of the present invention is succinct, makes the preparation of ceramic blank soil
It is convenient controllable, wide adaptability.
Description of the drawings
Fig. 1 is a kind of with the ceramic blank soil for activating water purification function and preparation method thereof flow chart.
Specific implementation mode
To make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, with reference to
Specific implementation mode, the present invention is further explained.
Referring to Fig. 1, the present invention provides a kind of technical solution：A kind of ceramic blank soil and its system with activation water purification function
Preparation Method, the preparation method comprises the following steps：
Step 1：Dispensing；Talcum 70% is taken, feldspar 6% builds soil 4%, long by precious native 16%, bentonite 2%, barium carbonate 2%, and will
Above-mentioned raw materials remove impurity；
Step 2：Talcum is calcined；Talcum raw material is put into kiln and is calcined, its laminated structure is destroyed, is conducive to subsequent
It is finely ground；
Step 3：It is finely ground；The talcum calcined progress is finely ground, it is put into after then screening talcum powder standby in suitable container
With；
Step 4：Talcum material is modulated；According to the weight of talcum, 30% water is added and is mixed, 0.3% a small amount of bentonite is added,
To improve plasticity, improves processability, 0.2% sodium carbonate is added, to improve the performance of mud, 0.4% salt is added
Acid makes mud agglomerate, for use after being mixed again；
Step 5：It is secondary finely ground；The weight of talcum and the proportioning of raw material are taken in comparison, by the feldspar of corresponding weight, build soil, long
Precious soil, bentonite and barium carbonate carry out finely ground respectively；
Step 6：Screening and mixing；By finely ground good feldspar, construction soil, long precious soil, bentonite and barium carbonate addition talcum material mud
In slurry and it is mixed；
Step 7：It prepares；Water is added to be let down in mixed mud, it is then spare；
Step 8：Six ring mountain flours are produced；A certain amount of six rings stone raw ore is chosen, six ring stone raw ores are removed into impurity, by six ring stones
It is ground into powder, is then screened；
Step 9：Stirring is mixed；Six ring mountain flours after screening are added in mud, and are again stirring for uniformly, so as to six ring mountain flours
It can be uniformly dispersed in mud；
Step 10：PH value adjustment；The pH value of mud is detected, adjusting appropriate is then carried out；
Step 11：Finished product；Uniformly mixed mud is stood into a period of time, it is then spare.
As a kind of preferred embodiment of the present invention, the finely ground process in the step 3 and step 5 is first coarse crushing, then is made
With ball mill grinding at powdered.
As a kind of preferred embodiment of the present invention, the mud moisture content after adding water to be let down in the step 7 is 34-36%.
As a kind of preferred embodiment of the present invention, the pH value of mud should be greater than 9 after pH value adjustment in the step 10.
First all devices should be cleared up before prepared by ceramic blank soil as a kind of preferred embodiment of the present invention.
As a kind of preferred embodiment of the present invention, mud and six ring mountain flour mixed proportions in the step 9 are 1:0.3.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from the present invention spirit or
In the case of essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that come within the meaning and range of equivalency of the claims in the present invention
It is interior.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (6)
1. a kind of ceramic blank soil and preparation method thereof with activation water purification function, which is characterized in that the preparation method includes
Following steps：
Step 1：Dispensing；Talcum 70% is taken, feldspar 6% builds soil 4%, long by precious native 16%, bentonite 2%, barium carbonate 2%, and will
Above-mentioned raw materials remove impurity；
Step 2：Talcum is calcined；Talcum raw material is put into kiln and is calcined, its laminated structure is destroyed, is conducive to subsequent
It is finely ground；
Step 3：It is finely ground；The talcum calcined progress is finely ground, it is put into after then screening talcum powder standby in suitable container
With；
Step 4：Talcum material is modulated；According to the weight of talcum, 30% water is added and is mixed, 0.3% a small amount of bentonite is added,
To improve plasticity, improves processability, 0.2% sodium carbonate is added, to improve the performance of mud, 0.4% salt is added
Acid makes mud agglomerate, for use after being mixed again；
Step 5：It is secondary finely ground；The weight of talcum and the proportioning of raw material are taken in comparison, by the feldspar of corresponding weight, build soil, long
Precious soil, bentonite and barium carbonate carry out finely ground respectively；
Step 6：Screening and mixing；By finely ground good feldspar, construction soil, long precious soil, bentonite and barium carbonate addition talcum material mud
In slurry and it is mixed；
Step 7：It prepares；Water is added to be let down in mixed mud, it is then spare；
Step 8：Six ring mountain flours are produced；A certain amount of six rings stone raw ore is chosen, six ring stone raw ores are removed into impurity, by six ring stones
It is ground into powder, is then screened；
Step 9：Stirring is mixed；Six ring mountain flours after screening are added in mud, and are again stirring for uniformly, so as to six ring mountain flours
It can be uniformly dispersed in mud；
Step 10：PH value adjustment；The pH value of mud is detected, adjusting appropriate is then carried out；
Step 11：Finished product；Uniformly mixed mud is stood into a period of time, it is then spare.
2. a kind of ceramic blank soil and preparation method thereof with activation water purification function according to claim 1, feature exists
In the finely ground process in the step 3 and step 5 is first coarse crushing, reuses ball mill grinding at powdered.
3. a kind of ceramic blank soil and preparation method thereof with activation water purification function according to claim 1, feature exists
In the mud moisture content after adding water to be let down in the step 7 is 34-36%.
4. a kind of ceramic blank soil and preparation method thereof with activation water purification function according to claim 1, feature exists
In the pH value of mud should be greater than 9 after pH value adjustment in the step 10.
5. a kind of ceramic blank soil and preparation method thereof with activation water purification function according to claim 1, feature exists
Before prepared by, ceramic blank soil, first all devices should be cleared up.
6. a kind of ceramic blank soil and preparation method thereof with activation water purification function according to claim 1, feature exists
In mud and six ring mountain flour mixed proportions in the step 9 are 1:0.3.