CN102898120A - Water filter material and preparation process thereof as well as corresponding water filter device - Google Patents
Water filter material and preparation process thereof as well as corresponding water filter device Download PDFInfo
- Publication number
- CN102898120A CN102898120A CN2012104171791A CN201210417179A CN102898120A CN 102898120 A CN102898120 A CN 102898120A CN 2012104171791 A CN2012104171791 A CN 2012104171791A CN 201210417179 A CN201210417179 A CN 201210417179A CN 102898120 A CN102898120 A CN 102898120A
- Authority
- CN
- China
- Prior art keywords
- water
- tourmalinite
- chitin
- kaolin
- medical stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of daily life, and particularly designs a drinking water filter material and a preparation process thereof as well as a corresponding water filter device. The water filter material is prepared by sintering a filter component powder substance and a clay powder substance, wherein the filter component at least comprises a substance which can generate atomic groups with positive electricity and negative electricity. Due to adopting the technical scheme, the pH value of pure water is adjusted to be weakly alkaline, a sterilization function is achieved, macroelements such as potassium, sodium, calcium, magnesium, phosphorus and trace elements such as zinc, iron, selenium, strontium, iodine, fluorine, metasilicic acid and the like, which are beneficial to the human body, are released, two negative ions such as hydroxidion and hydronium ions are produced, immunity and natural healing capacity of the human body for harmful substances can be improved, the water molecular groups can be reduced by utilizing the produced negative ions, and the water molecules and trace elements can be conveniently absorbed by the human body.
Description
Technical field
The invention belongs to the daily life technical field, a kind of Drinking Water Filtration material of special design and preparation technology thereof, and corresponding water filtering device.
Background technology
Water is Source of life, and the mankind have left water and just can't survive.Along with socioeconomic development and people improve constantly the requirement of standard of living, the requirement of tap water is also improved constantly.But, contain in the natural water much to person harmful microorganism, and along with the development of industry, a large amount of industrial refuses also causes severe contamination to the water source that the mankind depend on for existence, and the contaminated water source of these rounds of long-term drinking can cause to the mankind's health great injury.
At present, the tap water of municipal administration supply has all passed through purifying treatment, and the treatment process of taking has coarse filtration and reverse osmosis technology of fine filtering usually.The coarse filtration water technology can only carry out simple process to water, its advantage is to remove large granular impurity, bacterium and the virus in the water, and microorganism, having kept in the water healthy and helpful mineral substance and trace element, the pH value of purifying waste water after the filtration is weakly alkaline; The shortcoming of coarse filtration technology is to remove the impurity such as the chemical pollutant that contains in the water, heavy metal, and the security of water can not be guaranteed.The advantage of reverse osmosis Fine Filtration Technology is and can carries out fine processing to water, the large granular impurity that contains in the water, bacterium, virus, microorganism and the 96% above impurity such as heavy metal can be filtered, the pure safety of water quality, shortcoming is substantially not contain any material in the water, particularly can be filtered out simultaneously healthy and helpful mineral substance and trace element, pure water pH value after the filtration is slightly acidic, the pure water that this slightly acidic of long-term drinking does not contain mineral substance and trace element can cause the physique acidification, disappearance mineral substance and trace element in the health can be to the health injuries of health.At present, the municipal tap water is contained more impurity usually, such as chlorinated lime of remnants etc., need to boil and just can drink afterwards; And commercially available pure water adopts the reverse osmosis Fine Filtration Technology to process more, wherein lacks the necessary mineral substance of human body and trace element, can not make the pH value of pure water be weakly alkaline simultaneously.
A lot of Drinking Water Filtration materials are also arranged in the prior art, although have the function that water purifies, mineralization ability a little less than, and pH regulator ability can't be regulated water pH value to weakly alkaline.In order to satisfy better people to the demand of healthy water use, just need a kind of functions such as purification, mineralising that both had on the market, take charge of again to regulate pure water pH value and be weakly alkaline filtering material, the deficiency that exists to remedy prior art.
Summary of the invention
For solving above-mentioned problems of the prior art, the purpose of this invention is to provide a kind of have water purification, mineralization function, and can regulate water pH value to weakly alkaline Drinking Water Filtration material and preparation technology thereof, and use the water filtering device of described water filtration material.
For achieving the above object, the invention provides following technical scheme
The water filtration material is formed by the meal that filters component and the meal sintering of kaolin, wherein, comprises chitin in the described filtration component.
Described water filtration material, wherein, described filtration component also comprises at least a material that can produce with the atomic group of positive and negative electricity in water.
Described water filtration material wherein, also comprises at least a material that can produce hydroxyl ion or oxonium ion in the described filtration component, make water form small-micelle water.
Described water filtration material, wherein: the described material that can produce in water with the atomic group of positive and negative electricity is medical stone powdery thing, and the described material that can produce hydroxyl ion or oxonium ion is tourmalinite powdery thing.
Described water filtration material, wherein, described water filtration material is that the meal sintering with chitin, MUSYUSHI, medical stone, tourmalinite, kaolin forms, the shared weight percent of each component is respectively: chitin 20-40%, MUSYUSHI 5-25%, medical stone 5-25%, tourmalinite 15-40%, kaolin 10-15%.
Described water filtration material, wherein, the shared weight percent of described each component is: chitin 30%, MUSYUSHI 15%, medical stone 15%, tourmalinite 30%, kaolin 10%.
Described water filtration material, wherein, the granular size of described chitin, MUSYUSHI, medical stone, tourmalinite, kaolin meal is the 80-300 order, described water filtration material sinters the spherical of 2-8mm into.
Described water filtration material preparation technique comprises step:
1), chitin, MUSYUSHI, medical stone, tourmalinite, kaolin are put into respectively ball mill be crushed to 80-300 purpose meal, stand-by;
2), be chitin 20-40% according to weight percent, MUSYUSHI 5-25%, medical stone 5-25%, tourmalinite 15-40%, the ratio of kaolin 10-15% is with step 1) in the meal of preparation put into stirrer and stir, stand-by;
3), to step 2) in add pure water in the compound after stirring, stirring makes it become material-mud, stand-by;
4), with step 3) in the material-mud of preparation make the sphere material of diameter 2-8mm by apparatus for making pearl ball, oven dry, stand-by;
5), with step 4) in the sphere material of preparation put into 1000-1200 ℃ High Temperature Furnaces Heating Apparatus and heated roasting 2-3 hour, the cooling of ceasing fire can be come out of the stove and be made finished product.
The weight percent of each component is chitin 30% described water filtration material preparation technique, wherein: step 2), MUSYUSHI 15%, medical stone 15%, tourmalinite 30%, kaolin 10%.
Water filtering device comprises the shell with entrance and exit, wherein: above-mentioned water filtration material is set in the described shell.
(3) beneficial effect: technical scheme provided by the invention discloses a kind of water filtration material and preparation technology thereof, corresponding water treatment device.When pure water during by water filtration material provided by the present invention, the water filtration material can discharge calcium carbonate in pure water, can increase calcium ion content in the water, regulate the pure water pH value and be weakly alkaline, have antibacterial, sterilizing function, the potassium that release is useful to human body, sodium, calcium, magnesium, phosphorus major element and zinc, iron, selenium, copper, strontium, iodine, fluorine, the trace elements such as metasilicic acid, produce hydroxyl ion and two kinds of negative ions of oxonium ion, can improve human body to resistibility and the natural curability of objectionable impurities, utilize the negative ion that produces to dwindle water clusters, be convenient to absorption of human body water molecules and trace element.
Embodiment
Below in conjunction with preferred embodiment the present invention is described in further details.
Embodiment one
A kind of Drinking Water Filtration material is formed by the meal that filters component and the meal sintering of kaolin, and wherein, described filtration component comprises a kind of material that can produce with the atomic group of positive and negative electricity at least in water.
Described water filtration material wherein, also comprises the material that can produce hydroxyl ion or oxonium ion in the described filtration component, makes water form small-micelle water.
Described water filtration material, wherein, the described material that can produce in water with the atomic group of positive and negative electricity is medical stone powdery thing, the described material that can produce hydroxyl ion or oxonium ion is tourmalinite powdery thing.
Described water filtration material, wherein, its component comprises the meal of chitin, MUSYUSHI, medical stone, tourmalinite, kaolin, the meal of above-mentioned component is made by apparatus for making pearl ball formed by high temperature sintering after spherical.
Described chitin be a kind of from the shell of the crustaceans such as shrimp shell, crab shell, shell, extract meal, have restraining and sterilizing bacteria, antitumor, the effect that improves body immunity and liver detoxification, and contain calcium carbonate in the chitin, can increase calcium ion in the water.In the described water filtration material of present embodiment, add chitinous composition, the calcium ion that can carry out sterilization and disinfection and provide human body to need water quality.And researchist of the present invention finds that in research process chitin has the ability of pH value in the very strong adjusting water, and the pH value that can regulate pure water is weakly alkaline, and the weakly alkaline water of long-term drinking is of value to the health of human body.
Described MUSYUSHI is a kind of meal take the wooden fish ore as waste, the composition of wooden fish ore is limonite, except ferric oxide, other impurity often is phosphoric acid salt, also has a small amount of metasilicate, and more than the ten kind of trace element to the human body beneficial such as strontium, molybdenum, lithium, zinc, selenium, having the metabolism of balance the body, vessel softening prevents the function of arteriosclerosis.In the described water filtration material of present embodiment, add the MUSYUSHI composition, can increase the necessary trace element of human body and mineral substance in the water, make pure water after the filtration reach the standard of high quality mineral water.
Described medical stone is a kind of meal of being made by the subvolcano rock ore, contains more than 20 kind of potassium, sodium, calcium, magnesium, phosphorus major element and zinc, iron, selenium, copper, strontium, iodine, fluorine, metasilicic acid etc. to the HUMAN HEALTH healthy trace elements with household.Medical stone is porous, and adsorptive power is very strong, can absorbing pathogenic bacteria and bacterium, and be good whole food antistaling and antiseptic agent and refrigeration reodorant.When medical stone is used for water treatment, can be with absorption such as the chlorinated lime in the water and impurity, organism, miscellaneous bacterias, decompose, and in the feedwater with mineral substance and the necessary trace element of multiple human body.And medical stone can make a large amount of atomic group with positive and negative electricity of generation in the water, thereby can planar water middle reaches ion.In the described water filtration material of present embodiment, add the medical stone composition, the trace element and mineral substance in increasing water, can also adsorb the impurity such as chlorinated lime in the municipal tap water.
Described tourmalinite is a kind of meal take the Tourmaline ore as waste, and its major ingredient is borosilicate.Tourmalinite can be regulated pH value and the electroconductibility of water, make water deflection weakly alkaline, can produce two kinds of negative ions of hydroxyl ion and oxonium ion, make water form small-micelle water, compare with common macromolecular mass water, enter human body cell and be absorbed easilier, and so that the water-permeable of described water filtration material is better.Compare with ortho-water through the functional activation water that tourmalinite is processed, trace element and the mineral substance that can have greater concn, such as calcium, iron, zinc, selenium etc., thereby human body brought into play better physiology and medical care effect, long-term drinking just can improve human body to resistibility and the natural curability of objectionable impurities through the tourmalinite treated water.
Described kaolin is that a kind of aleuritic texture clay that forms take kaolinite, montmorillonite, quartz, feldspar is the meal of waste, can with other material mixing tool that fires pottery.
The described water filtration material that present embodiment provides, its crucial part is that the mix and match of described chitin, MUSYUSHI, medical stone, tourmalinite, kaolin uses, can either restraining and sterilizing bacteria, regulate the pH value to weakly alkaline, major element and trace element to the human body beneficial be can discharge again, hydroxyl ion and oxonium ion also produced simultaneously to promote human body to the absorption of trace element.
Described water filtration material, preferably, the granular size of described chitin, MUSYUSHI, medical stone, tourmalinite, kaolin is 200 orders.
Described water filtration material, preferably, wherein the weight percent of contained component is: chitin 30%, MUSYUSHI 15%, medical stone 15%, tourmalinite 30%, kaolin 10%.Water filtration material according to this proportional arrangement one-tenth, all be up to state standards bottle (bucket) the dress sanitary standard for drinking water of GB19298-2003 defined of the various indexs of the water after filtering, a plurality of indexs obviously are better than the technical indicator of existing pure water, and the design parameter of partial test project is as shown in the table.
| Interventions Requested | Standard value | Measured value | Interventions Requested | Standard value | Measured value |
| Colourity, (degree) | ≤10 | ＜1 | Turbidity, (degree) | ≤3 | 0.70 |
| Total number of bacterial colony, (cfu/mL) | ≤50 | 5 | Yeast, (cfu/mL) | ≤10 | ＜1 |
| Mould, (cfu/mL) | ≤10 | ＜1 | pH | 7.35 | |
| Calcium, (mg/kg) | 1.12 | Magnesium, (mg/kg) | 0.20 | ||
| Potassium, (mg/kg) | 0.95 | Zinc, (mg/kg) | ＜0.05 | ||
| Strontium, (mg/kg) | ＜0.05 | Iron, (mg/kg) | ＜0.05 |
| Iodine, (mg/kg) | 57.0 | Metasilicic acid, (mg/L) | 2.7 |
Embodiment two
A kind of water filtration material is compared with embodiment one, and its difference is:
Described water filtration material, preferably, the granular size of described chitin, MUSYUSHI, medical stone, tourmalinite, kaolin is 80 orders.
Described water filtration material, preferably, wherein the weight percent of contained component is: chitin 20%, MUSYUSHI 25%, medical stone 25%, tourmalinite 15%, kaolin 15%.Water filtration material according to this proportional arrangement one-tenth, all be up to state standards bottle (bucket) the dress sanitary standard for drinking water of GB19298-2003 defined of the various indexs of the water after filtering, a plurality of indexs obviously are better than the technical indicator of existing pure water, and the design parameter of partial test project is as shown in the table.
| Interventions Requested | Standard value | Measured value | Interventions Requested | Standard value | Measured value |
| Colourity, (degree) | ≤10 | ＜2 | Turbidity, (degree) | ≤3 | 0.90 |
| Total number of bacterial colony, (cfu/mL) | ≤50 | 6 | Yeast, (cfu/mL) | ≤10 | ＜2 |
| Mould, (cfu/mL) | ≤10 | ＜1.5 | pH | 7.15 | |
| Calcium, (mg/kg) | 1.5 | Magnesium, (mg/kg) | 0.25 | ||
| Potassium, (mg/kg) | 0.95 | Zinc, (mg/kg) | ＜0.05 | ||
| Strontium, (mg/kg) | ＜0.06 | Iron, (mg/kg) | ＜0.05 | ||
| Iodine, (mg/kg) | 59.0 | Metasilicic acid, (mg/L) | 2.8 |
Embodiment three
A kind of water filtration material is compared with embodiment one, and its difference is:
Described water filtration material, preferably, the granular size of described chitin, MUSYUSHI, medical stone, tourmalinite, kaolin is 300 orders.
Described water filtration material, preferably, wherein the weight percent of contained component is: chitin 40%, MUSYUSHI 5%, medical stone 5%, tourmalinite 40%, kaolin 10%.Water filtration material according to this proportional arrangement one-tenth, all be up to state standards bottle (bucket) the dress sanitary standard for drinking water of GB19298-2003 defined of the various indexs of the water after filtering, a plurality of indexs obviously are better than the technical indicator of existing pure water, and the design parameter of partial test project is as shown in the table.
| Interventions Requested | Standard value | Measured value | Interventions Requested | Standard value | Measured value |
| Colourity, (degree) | ≤10 | ＜2 | Turbidity, (degree) | ≤3 | 0.80 |
| Total number of bacterial colony, (cfu/mL) | ≤50 | 7 | Yeast, (cfu/mL) | ≤10 | ＜1.5 |
| Mould, (cfu/mL) | ≤10 | ＜3 | pH | 7.65 | |
| Calcium, (mg/kg) | 1.03 | Magnesium, (mg/kg) | 0.10 | ||
| Potassium, (mg/kg) | 0.35 | Zinc, (mg/kg) | ＜0.05 | ||
| Strontium, (mg/kg) | ＜0.04 | Iron, (mg/kg) | ＜0.06 | ||
| Iodine, (mg/kg) | 51.0 | Metasilicic acid, (mg/L) | 2.3 |
Embodiment four
A kind of water filtration material preparation technique, the water filtration material for the preparation of described in the embodiment one to three comprises the steps:
1, the meal of chitin, MUSYUSHI, medical stone, tourmalinite, kaolin is put into respectively ball mill and be crushed to more than 200 orders, stand-by;
2, be chitin 30% according to weight percent, MUSYUSHI 15%, medical stone 15%, tourmalinite 30%, the ratio of kaolin 10% is put into stirrer with the meal of preparation in the step 1 and stirred, and is stand-by;
3, add pure water in the compound after stirring in the step 2, stirring makes it become material-mud, stand-by;
4, the material-mud of preparation in the step 3 is made the sphere material of diameter 5mm by apparatus for making pearl ball, oven dry, stand-by;
5, the sphere material of preparation in the step 4 is put into the roasting 2.5 hours of heating of 1100 ℃ of High Temperature Furnaces Heating Apparatuss, the cooling of ceasing fire can be come out of the stove and be made finished product.
Embodiment five
A kind of water filtration material preparation technique, the water filtration material for the preparation of described in the embodiment one to three comprises the steps:
1, the meal of chitin, MUSYUSHI, medical stone, tourmalinite, kaolin is put into respectively ball mill and be crushed to more than 80 orders, stand-by;
2, be chitin 20% according to weight percent, MUSYUSHI 25%, medical stone 25%, tourmalinite 15%, the ratio of kaolin 15% is put into stirrer with the meal of preparation in the step 1 and stirred, and is stand-by;
3, add pure water in the compound after stirring in the step 2, stirring makes it become material-mud, stand-by;
4, the material-mud of preparation in the step 3 is made the sphere material of diameter 2mm by apparatus for making pearl ball, oven dry, stand-by;
5, the sphere material of preparation in the step 4 is put into the roasting 3 hours of heating of 1000 ℃ of High Temperature Furnaces Heating Apparatuss, the cooling of ceasing fire can be come out of the stove and be made finished product.
Embodiment six
A kind of water filtration material preparation technique, the water filtration material for the preparation of described in the embodiment one to three comprises the steps:
1, the meal of chitin, MUSYUSHI, medical stone, tourmalinite, kaolin is put into respectively ball mill and be crushed to more than 300 orders, stand-by;
2, be chitin 40% according to weight percent, MUSYUSHI 5%, medical stone 5%, tourmalinite 40%, the ratio of kaolin 10% is put into stirrer with the meal of preparation in the step 1 and stirred, and is stand-by;
3, add pure water in the compound after stirring in the step 2, stirring makes it become material-mud, stand-by;
4, the material-mud of preparation in the step 3 is made the sphere material of diameter 8mm by apparatus for making pearl ball, oven dry, stand-by;
5, the sphere material of preparation in the step 4 is put into the roasting 2 hours of heating of 1200 ℃ of High Temperature Furnaces Heating Apparatuss, the cooling of ceasing fire can be come out of the stove and be made finished product.
Embodiment seven
A kind of water filtering device comprises shell, inlet porting and outlet on the described shell, and key is, is provided with the water filtration material described in embodiment one, two, three in the described shell.
Above content is the explanation to preferred embodiment of the present invention, can help those skilled in the art to understand more fully technical scheme of the present invention.But these embodiment only illustrate, and can not assert that the specific embodiment of the present invention only limits to the explanation of these embodiment.Concerning the general technical staff of the technical field of the invention, without departing from the inventive concept of the premise, can also make some simple deductions and conversion, all should be considered as belonging to protection scope of the present invention.
Claims (10)
1. the water filtration material is formed by the meal that filters component and the meal sintering of kaolin, it is characterized in that, comprises chitin in the described filtration component.
2. water filtration material according to claim 1 is characterized in that, described filtration component also comprises at least a material that can produce with the atomic group of positive and negative electricity in water.
3. water filtration material according to claim 1 is characterized in that, also comprises at least a material that can produce hydroxyl ion or oxonium ion in the described filtration component, makes water form small-micelle water.
4. the described water filtration material of according to claim 1-3 each, it is characterized in that: the described material that can produce in water with the atomic group of positive and negative electricity is medical stone powdery thing, and the described material that can produce hydroxyl ion or oxonium ion is tourmalinite powdery thing.
5. water filtration material according to claim 4, it is characterized in that, described water filtration material is that the meal sintering with chitin, MUSYUSHI, medical stone, tourmalinite, kaolin forms, the shared weight percent of each component is respectively: chitin 20-40%, MUSYUSHI 5-25%, medical stone 5-25%, tourmalinite 15-40%, kaolin 10-15%.
6. water filtration material according to claim 4 is characterized in that, the shared weight percent of described each component is: chitin 30%, MUSYUSHI 15%, medical stone 15%, tourmalinite 30%, kaolin 10%.
7. water filtration material according to claim 4 is characterized in that, the granular size of described chitin, MUSYUSHI, medical stone, tourmalinite, kaolin meal is the 80-300 order, and described water filtration material sinters the spherical of 2-8mm into.
8. water filtration material preparation technique claimed in claim 1 comprises step:
1), chitin, MUSYUSHI, medical stone, tourmalinite, kaolin are put into respectively ball mill be crushed to 80-300 purpose meal, stand-by;
2), be chitin 20-40% according to weight percent, MUSYUSHI 5-25%, medical stone 5-25%, tourmalinite 15-40%, the ratio of kaolin 10-15% is with step 1) in the meal of preparation put into stirrer and stir, stand-by;
3), to step 2) in add pure water in the compound after stirring, stirring makes it become material-mud, stand-by;
4), with step 3) in the material-mud of preparation make the sphere material of diameter 2-8mm by apparatus for making pearl ball, oven dry, stand-by;
5), with step 4) in the sphere material of preparation put into 1000-1200 ℃ High Temperature Furnaces Heating Apparatus and heated roasting 2-3 hour, the cooling of ceasing fire can be come out of the stove and be made finished product.
9. preparation technology according to claim 8 is characterized in that: step 2) described in the weight percent of each component be chitin 30%, MUSYUSHI 15%, medical stone 15%, tourmalinite 30%, kaolin 10%.
10. water filtering device comprises the shell with entrance and exit, it is characterized in that: the water filtration material described in the claim 1 is set in the described shell.