CN101412561A - Pearl calcium ion particle and preparation thereof - Google Patents
Pearl calcium ion particle and preparation thereof Download PDFInfo
- Publication number
- CN101412561A CN101412561A CNA2007101631896A CN200710163189A CN101412561A CN 101412561 A CN101412561 A CN 101412561A CN A2007101631896 A CNA2007101631896 A CN A2007101631896A CN 200710163189 A CN200710163189 A CN 200710163189A CN 101412561 A CN101412561 A CN 101412561A
- Authority
- CN
- China
- Prior art keywords
- pearl
- calcium ion
- powder
- shell
- pearl calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses pearl calcium ion particles and a production method thereof. 8 to 12 weight percent of pearl, 58 to 62 weight percent of coral, 8 to 12 weight percent of pearl shell, 8 to 12 weight percent of shrimp shell, and 8 to 12 weight percent of crab shell are evenly mixed according to the proportion, are stirred, are calcined and dried for 12 hours at high temperature of between 1,100 and 1,250 DEG C to remove unnecessary impurities, and then are cooled; then the sintered substance is ground, is then placed into a container for oxidation, and then is cooled to obtain finished pearl calcium ion powder; in addition, the powder is mixed with pottery clay for pelleting, calcination and temperature reduction to finish another finished product, namely the pearl calcium ion particles, thereby ensuring that calcium ion components can be released and alkaline calcium ion water can be obtained when the powder or the particles containing 85 to 95 percent of pearl calcium ions are placed into water.
Description
Technical field
The present invention relates to a kind of pearl calcium ion particle and manufacture method thereof.
Background technology
Because, contain impurity or water purification chemicals in the employed tap water in the general life, other adds that its water pipe can dissolved gradually corrosion, and not the cleaning of storage tanks in the apartment, often all can cause and contain filth and bacterium in the water, therefore, the tap water of general family is many now can install strainer and R.0 pass through filter against oozing
Though can eliminate the foreign odor of tap water, but time fine bacterium and doubtful organic chloride with carinogenicity in the tap water but do not have too big effect, therefore, most machine more can be seen the reproductive patterns of general bacterium when the filterability activated carbon layer is trapped in the water.
Because public hazards pollution, water quality and the general acidification of air, the pure white rice and flour that add that life is nervous and add beverage such as a large amount of phosphoric acid salt, asccharin and compatriots' hobby are with carnivorous, a large amount of calcareously be excreted for many acidic substance that neutralize, absorb difficulty because of the calcareous mating type in the food again, lack factors such as calcareous in the soil, calcium deficiency phenomenon ubiquity is people's main purpose today if the abundant supply of will keeping fit is easy to calcium ion.
Summary of the invention
At the deficiencies in the prior art, the objective of the invention is to: a kind of pearl calcium ion composition grain and manufacture method thereof are provided, and the pearl calcium ion particle that makes has highly purified calcium content.
Pearl calcium ion composition grain of the present invention, be prepared from by pearl calcium ion composition powder 65-75wt% of the present invention and potter's clay 35-25wt%, and pearl calcium ion composition powder of the present invention is prepared from by following compositions: pearl 8-12wt%, coral 58-62wt%, pearl shell 8-12wt%, shrimp shell 8-12wt% and crab shell 8-12wt%.
A kind of manufacture method of pearl calcium ion composition grain, it is characterized in that, may further comprise the steps: at first with pearl (8-12wt%), coral (58-62wt%), pearl shell (8-12wt%), shrimp shell (8-12wt%) uniformly mixes with crab shell (8-12wt%) composition, and carry out 12 hours calcination drying with 1100 ℃ of-1250 ℃ of high temperature, to remove unwanted impurity, lower the temperature again and institute's agglutinating matter is ground, insert again carry out oxidation in the container after, generate the pearl calcium ion composition powder through cooling, then mix mutually with potter's clay (35-25wt%) and carry out drying-granulating with pearl calcium ion composition powder (65-75wt%), calcination and cooling and generate the pearl calcium ion composition grain, obtain containing the powder or the particle of calcium oxide (more than 90%), insert in the water when it and can discharge the pearl calcium ion composition, make water quality can obtain alkalescence.
Compared with prior art; the beneficial effect that the present invention has is: when the pearl calcium ion composition powder that the present invention is made or particle are immersed in the water; the powder of its pearl calcium ion or particle can discharge alkaline calcium ion composition or powder is dissolved in the water; for can level off to alkalescence than sour water quality, can change than tart physique.
Description of drawings
Fig. 1 is one of manufacturing flow chart of the present invention;
Fig. 2 is two of a manufacturing flow chart of the present invention.
Description of reference numerals: A-mixes stirring; B-calcination drying; The C-cooling; D-grinds; E-pearl calcium ion composition powder; The F-pearl calcium ion particle; The a-coral; The b-pearl; The c-pearl shell; D-shrimp shell; E-crab shell.
Embodiment
See also shown in Figure 1ly, the present invention is a kind of manufacture method of pearl calcium ion particle, and its manufacturing step is:
(1) at first pearl b (8-12wt%), coral a (58-62wt%), pearl shell c (8-12wt%), shrimp shell d (8-12wt%) are mixed stirring A mutually with crab shell e compositions such as (8-12wt%), make the mutual uniform mixing of each composition:
(2) then carry out 12 hours the dry B of calcination with 1100 ℃ of-1250 ℃ of temperature, to remove unwanted impurity:
(3) C that lowers the temperature again;
(4) grind the D step;
(5) then insert and pour into the higher oxygen of purity in the container again to carry out oxidation, finish through overcooling get final product pearl calcium ion composition powder E, described pearl calcium ion composition powder E contains the calcium contents more than 90% at least.
(6) see also shown in Figure 2ly, with the prepared pearl calcium ion composition powder of manufacturing process Fig. 1 E (65-75wt%) and potter's clay (35-25wt%) mixing granulation mutually, and through super-dry calcination and cooling, and obtain pearl calcium ion composition grain F.
The present invention is as follows with the following example explanation:
At first the pearl b (8-12wt%) in the raw material, coral a (58-62wt%), pearl shell c (8-12wt%), shrimp shell d (8-12wt%) are mixed in proportion mutually with crab shell e (8-12wt%) and stir A, its phase raw materials mixed is the lime carbonate composition, known to theory, the lime carbonate calcium content is about 40%, behind described lime carbonate process high-temperature calcination, can get the calcium oxide composition, and the calcium content of described calcium oxide contains 70% at least:
And five kinds of raw materials among the present invention, process screening earlier before the remix, and through behind the dry B of 1100 ℃, 1250 ℃ temperature calcination, will be calcination has the atrament of being once more through screening, and through lowering the temperature and grinding, insert again at last in the container to carry out oxidation and cooling, enable to obtain pearl calcium ion powder E, the product that its tool calcium content is high, the trial report shown in annex one, the calcium amount is that 41850mg/L accounts for content 98%, and it has quite highly purified calcium content.
Again, five kinds of raw materials in the invention described above mix in proportion mutually, and process screening earlier before mixing, and remove through being the atrament screening behind the high-temperature calcination once more, and through cooling and grinding, insert again at last and cool off in the container and oxidation, make the subject of knowledge and the object of knowledge obtain pearl calcium ion powder E, when it is immersed in it in the water, and can discharge the composition of calcium ion, shown in the survey report of annex two, in the water calcium content at 1.42mg/L, and plumbous (Pb), cadmium (Cd), arsenic (As) and mercury (Hg) are all in the scope of drinking, and shown in the survey report of annex three, calcium content is at 68.4mg/L in the water, and its cadmium content is 0.0017mg/L, and plumbous, arsenic and mercury are all in the scope of drinking, again, by above-mentioned steps (1), (2), (3), (4) with (5) add in addition step (6) completion as annex four for making alkaline ceramic particulate survey report, wherein in the water calcium content at 0.834mg/L, and cadmium, plumbous, arsenic and mercury are all in the scope of drinking.Again, insert in the water at pearl calcium ion particle F of the present invention and soak institute's survey report that obtains shown in annex five: it demonstrates aerobic plate count (CFU/g) is zero, and intestinal bacteria (MPN/g) are negative, and obviously its suitable fully people drink.
When the pearl calcium ion powder that the present invention is made or particle are immersed in the water; the powder of its pearl calcium ion or particle can discharge alkaline calcium ion composition or powder is dissolved in the water; for can level off to alkalescence than sour water quality, can change than tart physique.
More than explanation is just illustrative for the purpose of the present invention, and it is nonrestrictive, those of ordinary skills understand, under the situation of the spirit and scope that do not break away from claim and limited, can make many modifications, variation or equivalence, but but all will fall within the claim restricted portion of the present invention.
Claims (3)
1. pearl calcium ion composition grain, it is prepared from by pearl calcium ion composition powder 65-75wt% and potter's clay 35-25wt%, and described pearl calcium ion composition powder is formed by following feedstock production: pearl 8-12wt%, coral 58-62wt%, pearl shell 8-12wt%, shrimp shell 8-12wt% and crab shell 8-12wt%.
2. pearl calcium ion composition grain according to claim 1 is characterized in that: made pearl calcium ion powder or particle can be used on R0 and contraryly ooze by filter, open and draw the change as water quality such as machine.
3. the manufacture method of a pearl calcium ion particle is characterized in that: may further comprise the steps:
At first be with pearl (8-12wt%), coral (58-62wt%), pearl shell (8-12wt%), shrimp shell (8-12wt%) uniformly mixes mutually to scale with crab shell (8-12wt%) composition, and carry out 12 hours calcination drying with 1100 ℃ of-1250 ℃ of high temperature, to remove unwanted impurity, lower the temperature again and institute's agglutinating matter is ground, insert again carry out oxidation in the container after, finish the pearl calcium ion powder through cooling, then mix mutually with potter's clay (35-25wt%) and carry out drying-granulating with pearl calcium ion powder (65-75wt%), calcination and cooling and finish pearl calcium ion particle, make its tool contain the powder or the particle of high oxidation calcium (more than 90%), in inserting water, can discharge the pearl calcium ion composition, make water quality can obtain alkalescence.