CN108751934A - A kind of tableware base soil of selenium-rich health and preparation method thereof - Google Patents
A kind of tableware base soil of selenium-rich health and preparation method thereof Download PDFInfo
- Publication number
- CN108751934A CN108751934A CN201810698114.6A CN201810698114A CN108751934A CN 108751934 A CN108751934 A CN 108751934A CN 201810698114 A CN201810698114 A CN 201810698114A CN 108751934 A CN108751934 A CN 108751934A
- Authority
- CN
- China
- Prior art keywords
- selenium
- mud
- preparation
- rich
- base soil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of tableware base soil of selenium-rich health and preparation method thereof, and the preparation method includes：Dispensing → calcining → finely ground → six ring mountain flours are produced → screen → talcum material modulation → wet-milling → mixes and be let down → secondary wet-milling → pH value adjustment → stirring is mixed → finished product.Selenium-rich ore and six ring mountain flours are added in a kind of tableware base soil with the selenium-rich health for activating water purification function of the present invention, selenium element and anion can be discharged for a long time, improve the Se content in the food that tableware is held, to increase intake of the user to selenium, selenium element has natural anti-oxidation effect, maintain cell normal function, improve heart gland vascular circulation and renal function, modulability glandular secretion, anti-aging is promoted longevity, and is enhanced human immunity, it can effectively improve the immunity of the human body and prevent disease, improve the health and safety of diet.
Description
Technical field
The invention belongs to tableware base soil preparing process field, more particularly to the tableware base soil of a kind of selenium-rich health and its preparation
Method.
Background technology
With the continuous improvement of people's living condition, people more pursue the body element of good living environment and health
Matter more pursues the yearning to promoting longevity, and selenium is to safeguard the indispensable trace element of human life activity, when selenium deficiency
When, human immunological competence's decline is just easily lead to, human health and more than 40 kinds of disease of life is threatened all to be lacked with human body
Selenium is related, such as cancer, cardiovascular disease, hepatopathy, cataract, pancreatic disease, diabetes, genital system diseases symptom, the whole world
There are a countries and regions more than 40 to belong to selenium deficiency area, China is a selenium deficiency big country, therefore the supplement of selenium is highly desirable, rich
Selenium tableware has very important significance for the supplement of the daily selenium of people, and many benefits are obtained when can make people using tableware
Place is conducive to people's lives health, for this purpose, the present invention proposes a kind of tableware base soil of selenium-rich health and preparation method thereof.
Invention content
It is of the existing technology in order to solve the problems, such as, the present invention provides a kind of tableware base soil of selenium-rich health and its prepare
Method adds selenium-rich ore in tableware base soil, has the function of discharging selenium element, be taken the photograph when can make people using selenium-rich tableware
Selenium element is taken, people's lives health is conducive to.
To achieve the goals above, the present invention is to realize by the following technical solutions：A kind of tableware of selenium-rich health
Base soil and preparation method thereof, the preparation method comprises the following steps：
Step 1：Dispensing；Take high feldspar 18%, quartz 19%, kaolin 20%, talcum 28%, six ring mountain flours 10%, selenium-rich ore
5%, and above-mentioned raw materials are removed into impurity；
Step 2：Calcining；Quartz raw material and talcum raw material are put into kiln and calcined, its structure is destroyed, is conducive to follow-up
It is finely ground；
Step 3：It is finely ground；High feldspar, kaolin, selenium-rich ore and the quartz calcined are carried out with talcum respectively it is finely ground, then
It is separated in suitable containers for future use；
Step 4：Six ring mountain flours are produced；A certain amount of six rings stone raw ore is chosen, six ring stone raw ores are removed into impurity and is pulverized
Last shape is spare；
Step 5：Screening；The powder of high feldspar, quartz, kaolin, talcum, six ring mountain flours and selenium-rich ore is sieved respectively
It selects, and takes the various raw materials of constant weight according to the proportioning of step 1；
Step 6：Talcum material is modulated；Talcum powder is positioned in suitable container, the weight of talcum powder is compared, in talcum powder
30% water is added and is mixed, 0.3% a small amount of bentonite is added, to improve plasticity, improves processability, is added 0.2%
Sodium carbonate, to improve the performance of mud, 0.4% hydrochloric acid, which is added, makes mud agglomerate, for use after being mixed again；
Step 7：Wet-milling；Wet-milling is carried out using wet milk to the mud in step 6, so that it can be sufficiently mixed, avoids adding
The bentonite and sodium carbonate entered influences the sophistication of mud；
Step 8：It mixes and is let down；Remaining raw material powder is sequentially added in mud, and is stirred and adds in the process
Water is let down；
Step 9：Secondary wet-milling；Mud in step 8 is subjected to secondary wet-milling using wet milk, on the one hand can increase mud
Sophistication, on the other hand can make mud various composition mixing evenly；
Step 10：PH value adjustment；The pH value of mud is detected, and carries out adjusting appropriate；
Step 11：Finished product；Uniformly mixed mud is stood into a period of time, it is then spare.
As a kind of preferred embodiment of the present invention, the finely ground process in the step 3 and step 4 is first coarse crushing, then is made
With ball mill grinding at powdered.
As a kind of preferred embodiment of the present invention, the mud moisture content after adding water to be let down in the step 8 is 30-34%.
As a kind of preferred embodiment of the present invention, the pH value of mud should be greater than 8.6 after pH value adjustment in the step 10.
First all devices should be cleared up, avoid original before prepared by tableware base soil as a kind of preferred embodiment of the present invention
It is mixed into impurity in material, influences the quality of finished product.
As a kind of preferred embodiment of the present invention, each material fineness in the step 3 and step 4 is more than 10000-hole sieve
0.1-0.2%。
Beneficial effects of the present invention are：
1, the present invention adds selenium-rich ore in tableware base soil, can discharge selenium element for a long time, improves the food that tableware is held
In Se content, to increase intake of the user to selenium, selenium element has natural anti-oxidation effect, the maintenance normal work(of cell
Can, improve heart gland vascular circulation and renal function, modulability glandular secretion, anti-aging are promoted longevity, enhanced human immunity, energy
It is enough effectively to improve the immunity of the human body and prevent disease.
2 and the present invention six ring mountain flours are also added in tableware base soil, anion and far infrared can be discharged for a long time
Line can eliminate the harmful bacteria in the food that tableware is held, and achieve the purpose that bactericidal, purification food, and make in food
Water become alkaline ionized water, water clusters become smaller, and are more suitable for human internal environment, be convenient for absorption of human body, human body can be adjusted
The faintly acid sub-health state of interior environment is weak base sexual health status, so that human body is had more resistance and immunity, improves diet
Health and safety.
3, the present invention, which uses, screens and takes various raw materials again after finely ground, substantially increases the accuracy of raw material proportioning, energy
Enough losses for effectively avoiding causing raw material during finely ground make the quality of tableware base soil to cause proportioning inaccurate
It being affected, wet-milling twice can effectively improve the sophistication of tableware base soil and the mixed uniformity, and step of the present invention is succinct,
The preparation of tableware base soil is set to facilitate controllable, wide adaptability.
Description of the drawings
Fig. 1 is a kind of tableware base soil of selenium-rich health and preparation method thereof flow chart.
Specific implementation mode
To make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, with reference to
Specific implementation mode, the present invention is further explained.
Referring to Fig. 1, the present invention provides a kind of technical solution：A kind of tableware base soil of selenium-rich health and preparation method thereof,
The preparation method comprises the following steps：
Step 1：Dispensing；Take high feldspar 18%, quartz 19%, kaolin 20%, talcum 28%, six ring mountain flours 10%, selenium-rich ore
5%, and above-mentioned raw materials are removed into impurity；
Step 2：Calcining；Quartz raw material and talcum raw material are put into kiln and calcined, its structure is destroyed, is conducive to follow-up
It is finely ground；
Step 3：It is finely ground；High feldspar, kaolin, selenium-rich ore and the quartz calcined are carried out with talcum respectively it is finely ground, then
It is separated in suitable containers for future use；
Step 4：Six ring mountain flours are produced；A certain amount of six rings stone raw ore is chosen, six ring stone raw ores are removed into impurity and is pulverized
Last shape is spare；
Step 5：Screening；The powder of high feldspar, quartz, kaolin, talcum, six ring mountain flours and selenium-rich ore is sieved respectively
It selects, and takes the various raw materials of constant weight according to the proportioning of step 1；
Step 6：Talcum material is modulated；Talcum powder is positioned in suitable container, the weight of talcum powder is compared, in talcum powder
30% water is added and is mixed, 0.3% a small amount of bentonite is added, to improve plasticity, improves processability, is added 0.2%
Sodium carbonate, to improve the performance of mud, 0.4% hydrochloric acid, which is added, makes mud agglomerate, for use after being mixed again；
Step 7：Wet-milling；Wet-milling is carried out using wet milk to the mud in step 6, so that it can be sufficiently mixed, avoids adding
The bentonite and sodium carbonate entered influences the sophistication of mud；
Step 8：It mixes and is let down；Remaining raw material powder is sequentially added in mud, and is stirred and adds in the process
Water is let down；
Step 9：Secondary wet-milling；Mud in step 8 is subjected to secondary wet-milling using wet milk, on the one hand can increase mud
Sophistication, on the other hand can make mud various composition mixing evenly；
Step 10：PH value adjustment；The pH value of mud is detected, and carries out adjusting appropriate；
Step 11：Finished product；Uniformly mixed mud is stood into a period of time, it is then spare.
As a kind of preferred embodiment of the present invention, the finely ground process in the step 3 and step 4 is first coarse crushing, then is made
With ball mill grinding at powdered.
As a kind of preferred embodiment of the present invention, the mud moisture content after adding water to be let down in the step 8 is 30-34%.
As a kind of preferred embodiment of the present invention, the pH value of mud should be greater than 8.6 after pH value adjustment in the step 10.
First all devices should be cleared up, avoid original before prepared by tableware base soil as a kind of preferred embodiment of the present invention
It is mixed into impurity in material, influences the quality of finished product.
As a kind of preferred embodiment of the present invention, each material fineness in the step 3 and step 4 is more than 10000-hole sieve
0.1-0.2%。
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from the present invention spirit or
In the case of essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that come within the meaning and range of equivalency of the claims in the present invention
It is interior.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (6)
1. a kind of tableware base soil of selenium-rich health and preparation method thereof, which is characterized in that the preparation method comprises the following steps：
Step 1：Dispensing；Take high feldspar 18%, quartz 19%, kaolin 20%, talcum 28%, six ring mountain flours 10%, selenium-rich ore
5%, and above-mentioned raw materials are removed into impurity；
Step 2：Calcining；Quartz raw material and talcum raw material are put into kiln and calcined, its structure is destroyed, is conducive to follow-up
It is finely ground；
Step 3：It is finely ground；High feldspar, kaolin, selenium-rich ore and the quartz calcined are carried out with talcum respectively it is finely ground, then
It is separated in suitable containers for future use；
Step 4：Six ring mountain flours are produced；A certain amount of six rings stone raw ore is chosen, six ring stone raw ores are removed into impurity and is pulverized
Last shape is spare；
Step 5：Screening；The powder of high feldspar, quartz, kaolin, talcum, six ring mountain flours and selenium-rich ore is sieved respectively
It selects, and takes the various raw materials of constant weight according to the proportioning of step 1；
Step 6：Talcum material is modulated；Talcum powder is positioned in suitable container, the weight of talcum powder is compared, in talcum powder
30% water is added and is mixed, 0.3% a small amount of bentonite is added, to improve plasticity, improves processability, is added 0.2%
Sodium carbonate, to improve the performance of mud, 0.4% hydrochloric acid, which is added, makes mud agglomerate, for use after being mixed again；
Step 7：Wet-milling；Wet-milling is carried out using wet milk to the mud in step 6, so that it can be sufficiently mixed, avoids adding
The bentonite and sodium carbonate entered influences the sophistication of mud；
Step 8：It mixes and is let down；Remaining raw material powder is sequentially added in mud, and is stirred and adds in the process
Water is let down；
Step 9：Secondary wet-milling；Mud in step 8 is subjected to secondary wet-milling using wet milk, on the one hand can increase mud
Sophistication, on the other hand can make mud various composition mixing evenly；
Step 10：PH value adjustment；The pH value of mud is detected, and carries out adjusting appropriate；
Step 11：Finished product；Uniformly mixed mud is stood into a period of time, it is then spare.
2. a kind of tableware base soil and preparation method thereof of selenium-rich health according to claim 1, which is characterized in that the step
Rapid three and step 4 in finely ground process be first coarse crushing, reuse ball mill grinding at powdered.
3. a kind of tableware base soil and preparation method thereof of selenium-rich health according to claim 1, which is characterized in that the step
Mud moisture content after adding water to be let down in rapid eight is 30-34%.
4. a kind of tableware base soil and preparation method thereof of selenium-rich health according to claim 1, which is characterized in that the step
The pH value of mud should be greater than 8.6 after pH value adjustment in rapid ten.
5. a kind of tableware base soil and preparation method thereof of selenium-rich health according to claim 1, which is characterized in that tableware base
Before prepared by soil, first all devices should be cleared up, avoid being mixed into impurity in raw material, influence the quality of finished product.
6. a kind of tableware base soil and preparation method thereof of selenium-rich health according to claim 1, which is characterized in that the step
Rapid three and step 4 in each material fineness be 10000-hole sieve more than 0.1-0.2%.