CN106917170A - A kind of mould carbon fiber polyester thread of anti-soil and its production method - Google Patents

A kind of mould carbon fiber polyester thread of anti-soil and its production method Download PDF

Info

Publication number
CN106917170A
CN106917170A CN201710260708.4A CN201710260708A CN106917170A CN 106917170 A CN106917170 A CN 106917170A CN 201710260708 A CN201710260708 A CN 201710260708A CN 106917170 A CN106917170 A CN 106917170A
Authority
CN
China
Prior art keywords
carbon fiber
yarn
polyster fibre
combed cotton
polyester thread
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710260708.4A
Other languages
Chinese (zh)
Inventor
吴磊
朱德胜
何冲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei Ren Ren Textile Technology Co Ltd
Original Assignee
Hubei Ren Ren Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hubei Ren Ren Textile Technology Co Ltd filed Critical Hubei Ren Ren Textile Technology Co Ltd
Priority to CN201710260708.4A priority Critical patent/CN106917170A/en
Publication of CN106917170A publication Critical patent/CN106917170A/en
Pending legal-status Critical Current

Abstract

The invention belongs to textile production technical field, and in particular to a kind of mould carbon fiber polyester thread of anti-soil and its production method.The yarn is the union twist yarn of carbon fiber/combed cotton blended yarn and carbon fiber/polyster fibre mixed yarn.Its production method includes：Three-level blending, pad, dry and bake and bank up with earth.The mould carbon fiber polyester thread of anti-soil provided by the present invention is by carbon fiber, combed cotton and the polyster fibre reasonably combined yarn produced of these three fibers, it is not only durable durable, and with relatively smooth feel, several scenes can be applied to as a kind of high performance yarn with oil-stain-preventing, easy to clean.

Description

A kind of mould carbon fiber polyester thread of anti-soil and its production method
Technical field
The invention belongs to textile production technical field, and in particular to a kind of mould carbon fiber polyester thread of anti-soil and its producer Method.
Background technology
Antifouling and easy decontamination processing is the opposite processing of two effects.On the one hand, textile by three-prevention finishing it is latter as In the case of dirt be difficult contamination, but dirt once be infected with it is upper after because three anti-textiles are difficult to soak in itself so that contamination On dirt be difficult to remove；On the other hand, if textile has done soil-releasing finiss, general hydrophily is higher, is difficult to do again Soil resistant finish with better effects.But the antifouling soil-releasing finishing agent of a new generation has done very big improvement on molecular structure, There is hydrophilic radical and water repellent group (Rf) simultaneously on its strand, be exposed to when by the textile of antifouling soil-releasing finiss Water repellent group is aligned in fibrous external when in air, and hydrophilic radical is curled in fibrous inside, so as to show " refusing dirt " Performance, and when it is placed in water, the locus where hydrophilic radical and water repellent group overturns, fabric exhibits go out hydrophilic Performance, so as to embody soil release performance energy.So, antifouling and soil-releasing finiss (SG-SR) can just unite, and can accomplish Have substantially no effect on respective performance.
Cotton is easily contaminated as traditional textile material, therefore generally not using it as antipollution weaving face fabric material. But, due to its good sense of touch, and mostly people are favored, so, the skill of anti-soil weaving face fabric is produced as material using cotton Art exploitation is necessary.Meanwhile, the material based on carbon fiber has many good performances, and it is applied to every field, is a kind of Improve the potential material of yarn property.
The content of the invention
To solve the deficiencies in the prior art, the invention provides a kind of mould carbon fiber polyester thread of anti-soil and its production method. The mould carbon fiber polyester thread of anti-soil provided by the present invention is not only durable durable, and with relatively smooth feel, can be with grease proofing It is dirty, easy to clean.
Technical scheme provided by the present invention is as follows：
A kind of mould carbon fiber polyester thread of anti-soil, is carbon fiber/combed cotton blended yarn and carbon fiber/polyster fibre mixed yarn Union twist yarn.
Specifically, the density of carbon fiber/combed cotton blended yarn is 250~255/10cm, carbon fiber/polyster fibre blending The density of yarn is 215~220/10cm.
Specifically, the number of carbon fiber/combed cotton blended yarn is 9.0~9.2tex, carbon fiber/polyster fibre mixed yarn Number is 9.2~9.5tex.
Specifically, in carbon fiber/combed cotton blended yarn, carbon fiber is 40~45 with the blending ratio of combed cotton：45~50；Carbon In each yarns of fiber/polyster fibre mixed yarn, carbon fiber is 40~45 with the blending ratio of polyster fibre：45~50.
Specifically, carbon fiber/combed cotton blended yarn is 32~37 with the blending ratio of carbon fiber/polyster fibre mixed yarn：42 ~45.
Present invention also offers a kind of production method of the mould carbon fiber polyester thread of anti-soil, comprise the following steps：
1) carbon fiber with it is combed cotton blended, obtain carbon fiber/combed cotton blended yarn；
2) carbon fiber and polyster fibre blending, obtain carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn and carbon fiber/polyster fibre mixed yarn blending, obtain union twist yarn；
4) to step 3) union twist yarn that obtains pads；
5) 1~2min will be dried under the conditions of 150~160 DEG C by the union twist yarn for padding；
6) 3~4min will be bakeed under the conditions of 165~175 DEG C by the union twist yarn of drying, obtains the mould carbon fiber of anti-soil and wash Synthetic fibre line.
Specifically, step 1) in：
Carbon fiber is 40~45 with the blending ratio of combed cotton：45~50；
The density of the carbon fiber for obtaining/combed cotton blended yarn is 250~255/10cm；
The number of the carbon fiber for obtaining/combed cotton blended yarn is 9.0~9.2tex.
Specifically, step 2) in：
Carbon fiber is 40~45 with the blending ratio of polyster fibre：45~50；
The density of the carbon fiber for obtaining/polyster fibre mixed yarn is 215~220/10cm；
The number of the carbon fiber for obtaining/polyster fibre mixed yarn is 9.2~9.5tex.
Specifically, step 3) in：Carbon fiber/combed cotton blended yarn is with the blending ratio of carbon fiber/polyster fibre mixed yarn 32~37：42~45.
The mould carbon fiber polyester thread of anti-soil provided by the present invention is by these three fibers of carbon fiber, combed cotton and polyster fibre The reasonably combined yarn produced, it is not only durable durable, and with relatively smooth feel, can be with oil-stain-preventing, easy to clean, can Apply to several scenes as a kind of high performance yarn.
Specific embodiment
Principle of the invention and feature are described below, illustrated embodiment is served only for explaining the present invention, is not intended to Limit the scope of the present invention.
Embodiment 1
The production method of the mould carbon fiber polyester thread 1 of anti-soil, comprises the following steps：
1) carbon fiber presses blending ratio 45 with combed cotton：45 blending, obtain density be 255/10cm, number be 9.0tex Carbon fiber/combed cotton blended yarn；
2) carbon fiber presses blending ratio 45 with polyster fibre：45 blending, obtain density for 220/10cm, number are 9.2tex Carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn presses blending ratio 37 with carbon fiber/polyster fibre mixed yarn：42 blending, are mixed Spin；
4) to step 3) union twist yarn that obtains pads；
5) 1min will be dried under the conditions of 160 DEG C by the union twist yarn for padding；
6) 3min will be bakeed under the conditions of 175 DEG C by the union twist yarn of drying, obtains the mould carbon fiber polyester thread 1 of anti-soil.
Embodiment 2
The production method of the mould carbon fiber polyester thread 2 of anti-soil, comprises the following steps：
1) carbon fiber presses blending ratio 40 with combed cotton：50 blending, obtain density be 250/10cm, number be 9.2tex Carbon fiber/combed cotton blended yarn；
2) carbon fiber presses blending ratio 40 with polyster fibre：50 blending, obtain density for 215/10cm, number are 9.5tex Carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn presses blending ratio 32 with carbon fiber/polyster fibre mixed yarn：45 blending, are mixed Spin；
4) to step 3) union twist yarn that obtains pads；
5) 2min will be dried under the conditions of 150 DEG C by the union twist yarn for padding；
6) 4min will be bakeed under the conditions of 165 DEG C by the union twist yarn of drying, obtains the mould carbon fiber polyester thread 2 of anti-soil.
Embodiment 3
The production method of the mould carbon fiber polyester thread 3 of anti-soil, comprises the following steps：
1) carbon fiber presses blending ratio 45 with combed cotton：50 blending, obtain density be 250/10cm, number be 9.0tex Carbon fiber/combed cotton blended yarn；
2) carbon fiber presses blending ratio 45 with polyster fibre：50 blending, obtain density for 215/10cm, number are 9.2tex Carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn presses blending ratio 37 with carbon fiber/polyster fibre mixed yarn：45 blending, are mixed Spin；
4) to step 3) union twist yarn that obtains pads；
5) 1min will be dried under the conditions of 150 DEG C by the union twist yarn for padding；
6) 4min will be bakeed under the conditions of 175 DEG C by the union twist yarn of drying, obtains the mould carbon fiber polyester thread 3 of anti-soil.
Embodiment 4
The production method of the mould carbon fiber polyester thread 4 of anti-soil, comprises the following steps：
1) carbon fiber presses blending ratio 40 with combed cotton：45 blending, obtain density be 255/10cm, number be 9.2tex Carbon fiber/combed cotton blended yarn；
2) carbon fiber presses blending ratio 40 with polyster fibre：45 blending, obtain density for 220/10cm, number are 9.5tex Carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn presses blending ratio 32 with carbon fiber/polyster fibre mixed yarn：42 blending, are mixed Spin；
4) to step 3) union twist yarn that obtains pads；
5) 2min will be dried under the conditions of 160 DEG C by the union twist yarn for padding；
6) 3min will be bakeed under the conditions of 165 DEG C by the union twist yarn of drying, obtains the mould carbon fiber polyester thread 4 of anti-soil.
Embodiment 5
The production method of the mould carbon fiber polyester thread 5 of anti-soil, comprises the following steps：
1) carbon fiber presses blending ratio 42 with combed cotton：48 blending, obtain density be 258/10cm, number be 9.1tex Carbon fiber/combed cotton blended yarn；
2) carbon fiber presses blending ratio 43 with polyster fibre：8 blending, obtain density for 218/10cm, number are 9.4tex Carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn presses blending ratio 35 with carbon fiber/polyster fibre mixed yarn：43 blending, are mixed Spin；
4) to step 3) union twist yarn that obtains pads；
5) 1min will be dried under the conditions of 155 DEG C by the union twist yarn for padding；
6) 4min will be bakeed under the conditions of 170 DEG C by the union twist yarn of drying, obtains the mould carbon fiber polyester thread 5 of anti-soil.
Embodiment 6
The production method of the mould carbon fiber polyester thread 6 of anti-soil, comprises the following steps：
1) carbon fiber presses blending ratio 45 with combed cotton：45 blending, obtain density be 253/10cm, number be 9.2tex Carbon fiber/combed cotton blended yarn；
2) carbon fiber presses blending ratio 40 with polyster fibre：47 blending, obtain density for 220/10cm, number are 9.2tex Carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn presses blending ratio 35 with carbon fiber/polyster fibre mixed yarn：45 blending, are mixed Spin；
4) to step 3) union twist yarn that obtains pads；
5) 2min will be dried under the conditions of 150 DEG C by the union twist yarn for padding；
6) 3min will be bakeed under the conditions of 170 DEG C by the union twist yarn of drying, obtains the mould carbon fiber polyester thread 6 of anti-soil.
Decontamination is tested
5- spots are removed completely
4- vestiges are difficult to differentiate
3- vestiges can be differentiated
2- vestiges are easy to differentiate
1- vestiges cannot be removed
Fungus-proof test
Project Embodiment 1 Embodiment 2 Embodiment 3 Embodiment 4 Embodiment 5 Embodiment 6 Common fabric
Mildew Nothing Nothing Nothing Nothing Nothing Nothing Seriously
Musty Nothing It is extremely slight Nothing Nothing It is extremely slight Nothing Seriously
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all it is of the invention spirit and Within principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.

Claims (9)

1. the mould carbon fiber polyester thread of a kind of anti-soil, it is characterised in that：It is that carbon fiber/combed cotton blended yarn and carbon fiber/terylene are fine Tie up the union twist yarn of mixed yarn.
2. the mould carbon fiber polyester thread of anti-soil according to claim 1, it is characterised in that：Carbon fiber/combed cotton blended yarn Density is 250~255/10cm, and the density of carbon fiber/polyster fibre mixed yarn is 215~220/10cm.
3. the mould carbon fiber polyester thread of anti-soil according to claim 1, it is characterised in that：Carbon fiber/combed cotton blended yarn Number is 9.0~9.2tex, and the number of carbon fiber/polyster fibre mixed yarn is 9.2~9.5tex.
4. the mould carbon fiber polyester thread of anti-soil according to claim 1, it is characterised in that：In carbon fiber/combed cotton blended yarn, Carbon fiber is 40~45 with the blending ratio of combed cotton：45~50；In each yarns of carbon fiber/polyster fibre mixed yarn, carbon is fine Dimension is 40~45 with the blending ratio of polyster fibre：45~50.
5. the mould carbon fiber polyester thread of anti-soil according to claim 1, it is characterised in that：Carbon fiber/combed cotton blended yarn with The blending ratio of carbon fiber/polyster fibre mixed yarn is 32~37：42~45.
6. the production method of the mould carbon fiber polyester thread of a kind of anti-soil, it is characterised in that comprise the following steps：
1) carbon fiber with it is combed cotton blended, obtain carbon fiber/combed cotton blended yarn；
2) carbon fiber and polyster fibre blending, obtain carbon fiber/polyster fibre mixed yarn；
3) carbon fiber/combed cotton blended yarn and carbon fiber/polyster fibre mixed yarn blending, obtain union twist yarn；
4) to step 3) union twist yarn that obtains pads；
5) 1~2min will be dried under the conditions of 150~160 DEG C by the union twist yarn for padding；
6) 3~4min will be bakeed under the conditions of 165~175 DEG C by the union twist yarn of drying, obtains the mould carbon fiber polyester thread of anti-soil.
7. the production method of the mould carbon fiber polyester thread of anti-soil according to claim 6, it is characterised in that：Step 1) in：
Carbon fiber is 40~45 with the blending ratio of combed cotton：45~50；
The density of the carbon fiber for obtaining/combed cotton blended yarn is 250~255/10cm；
The number of the carbon fiber for obtaining/combed cotton blended yarn is 9.0~9.2tex.
8. the production method of the mould carbon fiber polyester thread of anti-soil according to claim 6, it is characterised in that：Step 2) in：
Carbon fiber is 40~45 with the blending ratio of polyster fibre：45~50；
The density of the carbon fiber for obtaining/polyster fibre mixed yarn is 215~220/10cm；
The number of the carbon fiber for obtaining/polyster fibre mixed yarn is 9.2~9.5tex.
9. the production method of the mould carbon fiber polyester thread of anti-soil according to claim 6, it is characterised in that：Step 3) in：Carbon Fiber/combed cotton blended yarn is 32~37 with the blending ratio of carbon fiber/polyster fibre mixed yarn：42~45.
CN201710260708.4A 2017-04-20 2017-04-20 A kind of mould carbon fiber polyester thread of anti-soil and its production method Pending CN106917170A (en)