CN109943953A - A kind of imitative denim fabric of antibacterial - Google Patents
A kind of imitative denim fabric of antibacterial Download PDFInfo
- Publication number
- CN109943953A CN109943953A CN201910290209.9A CN201910290209A CN109943953A CN 109943953 A CN109943953 A CN 109943953A CN 201910290209 A CN201910290209 A CN 201910290209A CN 109943953 A CN109943953 A CN 109943953A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- fiber
- antibacterial
- imitates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibacterials to imitate denim fabric, it contains the following parts by weight: 200-320 parts of blended cellulosic fibres, 50-80 parts of bamboo charcoal fiber, 60-90 parts of terylene, 5-10 parts of spandex, 35-60 parts of conductive fiber, 25-35 parts of copper ammonia fiber, 10-15 parts of silicone Quaternary Ammonium Salt Antimicrobial Agent, blended cellulosic fibres are 1:(1-2 by mass ratio) cotton and tencel blended form, it is mixed by spinning color master batch with fiber stoste, high-temperature fusion extrusion spinning, the processes such as face weave form fabric, improve the color fastness of fabric, the anti-microbial property of fabric is further increased by antibiotic finish process again.Antibacterial of the invention imitates denim fabric, has the advantages that comfortably soft, moisture absorption is breathed freely, high-efficiency antimicrobial.
Description
Technical field
The present invention relates to functional fabric technical field, in particular to a kind of antibacterial imitates denim fabric.
Background technique
Clothes three elements include style, fabric, color, and fabric is for making clothes as one of clothes three elements
Material, can not only annotate the style and characteristic of clothes, but also be directly related to the expression effect of the color of clothes, moulding.
As the improvement of people's living standards, people propose the requirement of more and more functional aspects to fabric, pass
The non-cotton fiber of the denim fabric of system is mainly weaved by starching after warp dyeing, then obtains denim fabric by washing to arrange.
One kind is developed in recent years using cellulose fibres such as cotton, viscose rayons as warp thread, and the fine imitative cowboy face for weft yarn is closed with terylene etc.
Material, is mainly dyed using the dyeability difference of different fibers, reaches the fabric of imitative cowboy style, while also greatly rich
The rich colour system of fabric.
Existing application publication number is the Chinese patent of CN105780554A, discloses a kind of colored imitative cowboy style fabric
Production method, including sizing, weaving, piece dyeing finishing, the washing techniques such as desizing and arrangement, specific steps include: with cellulose
Fiber is the raw yarn of main material after warping, carries out starching using the slurry for mixing acquirement of sizing mixing with colour splitting agent by high gelatinized starch,
To obtain dressed warp；Dressed warp with wash or terylene covered weft yarn is weaved entirely, obtain fabric；By fabric using work
One of property dyestuff, bipseudoindoxyl dye or reducing dye dye it；The fabric after dyeing is carried out using amylase
Biological desizing；Using singing, be formed and preshrinking process arranges fabric after desizing.
Imitative denim fabric in prior art is although rich in color, color fastness is higher, but due to only considering
The color and style of fabric do not make improvements the functional aspect of fabric, especially in terms of antibacterial agent permeability also
It is lacking, is reduced so as to cause the wearing comfort of wearer, but also the functional aspect of fabric is restricted.
Summary of the invention
The purpose of the present invention is to provide a kind of antibacterials to imitate denim fabric, and there is comfortable soft, moisture absorption to breathe freely and have
Good antibacterial effect.
To achieve the above object, the present invention provides the following technical scheme that a kind of antibacterial imitates denim fabric, comprising following heavy
Measure the component of part:
200-320 parts of blended cellulosic fibres, 50-80 parts of bamboo charcoal fiber, 60-90 parts of terylene, 5-10 parts of spandex, conductive fiber
35-60 parts, 25-35 parts of copper ammonia fiber, 10-15 parts of antibacterial agent.
By using above-mentioned technical proposal, cellulose fibre be by special process to the cellulosic molecules of natural materials into
A kind of staple fibre that row remodeling obtains, cellulose fibre have good gas permeability, moisture absorbing and sweat releasing, and the fabric pro-skin being made into is relaxed
It is suitable, there is certain natural bacteriostatic health-care effect；On the other hand, cellulose fibre hygroscopicity is strong, therefore has excellent dyeing
Performance, color fastness is high, and it is complete can to dye chromatography.
Bamboo charcoal fiber is the tencel with honeycomb microporous structure formed using moso bamboo as Raw material processing, has and inhales
Penetrable ventilated, bacteriostasis antibiosis, anti-ultraviolet effect are ideal antibacterial fabric fibers.
Terylene is one of three big conjunction fibres, and processing technology is mature, fibrous elasticity is good, is unlikely to deform, is corrosion-resistant, imitative
Terylene is added in denim fabric can increase the wearability and durability of fabric.
Spandex is a kind of elastomer, and line density is small, chemically-resistant degradation, wearability is good, can be improved fabric elasticity and
Wearability.
By blended implantable conductive fiber in fabric, it can effectively improve the antistatic property of fabric, subtract to play
Electrostatic phenomenon in few clothes wearing process, while can also effectively reduce and be easy showing for absorption dust because fabric generates electrostatic
As.
The fibre section of copper ammonia fiber is rounded, no skin-core structure, and fiber can bear high elongation, monofilament obtained compared with
Carefully, the feel and pliability of fabric can be improved；On the other hand, the good hygroscopicity of copper ammonia fiber can be in blended addition fabric
Further increase the sucting wet air permeability of fabric.
Antibacterial agent can make antibacterial agent be absorbed and fixed at fiber surface and fiber by being added in fabric finishing process
Inside, to achieve the effect that further increase fabric entirety antibiotic property.
The present invention is further arranged to, and the cellulose fibre is 1:(1-2 by mass ratio) cotton and tencel blended form.
By using above-mentioned technical proposal, tencel be by wood pulp, water and solvent oxidation amine mix, it is heated dissolution, removal of impurities,
Direct fabrics and the fiber formed, are a kind of environmentally protective fibers.The pliability and sense of touch of tencel can match in excellence or beauty silk, hygroscopicity
It is more preferable than cotton, it is frivolous easy to wash easily dry, it is not easy to shrink, and have good bacteriostasis property.It is blended by being carried out with cotton, it can be improved
The antibacterial effect of fabric and ventilative comfort.
The present invention is further arranged to, the conductive fiber be one of Carbon fibe, metal compound fibres or
Two kinds.
By using above-mentioned technical proposal, Carbon fibe has the advantages that light weight, intensity are big, conducts electricity very well, and can incite somebody to action
The electrostatic charge that fabric generates is conducted, and is avoided static charge buildup on fabric and is generated electric discharge phenomena, while decreasing face
The phenomenon that material adsorbs dust because of electrostatic, improves the cleanliness and fungistatic effect of fabric；The fiber of metal compound fibres compared with
Gently, flexible good, there is good durable antistatic, the antistatic property of fabric can be improved.
The present invention is further arranged to, and the antibacterial agent is silicone Quaternary Ammonium Salt Antimicrobial Agent.
By using above-mentioned technical proposal, organosilicon quaternary ammonium salt is the ideal antibacterial agent of a kind of comprehensive performance, finish fabric
When such antibacterial agent do not need high temperature baking, just can produce lasting antibacterial effect after general drying, the fabric after arrangement is not only
With excellent anti-microbial property, and be also equipped with good water suction absorption of perspiration, flexibility, flatness, resilience, static electricity resistance and
Resistance tocrocking.
The present invention is further arranged to, the antibacterial imitate denim fabric preparation method the following steps are included:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 2%-4%, is added extruder type spinning machine after mixing, produces colored cotton fibre through high-temperature fusion extrusion spinning
Dimension；The Masterbatch of 3%-5% is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；In tencel slurry
The middle Masterbatch that 1%-3% is added carries out extrusion spinning using same method；
S2, scribbled: dyed cotton, dyeing tencel and conductive fiber are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 165- on sectional warper
185m/min, beaming speed are 110-130m/min；
S5, face weave: warp thread and weft yarn that S4 step obtains are weaved；
S6, antibiotic finish: configuration quality percentage concentration is the silicone Quaternary Ammonium Salt Antimicrobial Agent solution of 10%-15%, by S5 step
Fabric be impregnated in antimicrobial, bath raio be (4:1)-(5:1), dip time be 45-60 minutes, in 70-80 after dipping
It is dried under degree Celsius, drying time is 18-30 minutes；
S7, final finishing: the fabric of S6 step is subjected to final finishing.
By using above-mentioned technical proposal, Masterbatch is mixed with fiber stoste, then carry out hot melt extruded spinning, it can
So that pigment it is more uniform penetrate into fibrous inside, realize the high color fastness of stock-dye, also improve the uniform of dyeing
Property, by the way that the fiber after dyeing is weaved, improve the upper dye effect and color fastness of fabric；Organosilicon quaternary ammonium salt is a kind of
Safe and efficient broad spectrum antimicrobial agent can make antibacterial agent attachment infiltration to fiber by fabric by the antibiotic finish of antiseptic solution
Between internal and fiber nodes, to achieve the effect that further increase fabric anti-microbial property.
The present invention is further arranged to, in the S5 step weft yarn be terylene, it is spandex, copper ammonia fiber blended.
By using above-mentioned technical proposal, elasticity is good for polyester fiber, is unlikely to deform, is corrosion-resistant, adds in imitative denim fabric
Enter terylene, the wearability and durability of fabric can be increased；Spandex line density is small, with blend polyester as weft yarn, can be improved
The feel of fabric；Copper ammonia fiber can be further improved fabric pliability and feel, while the moisture absorption that fabric can be improved is ventilative
Property.
The present invention is further arranged to, and the terylene is the low elastic polyester filament and polyester elastic of 1:(1-1.5) by mass ratio
Silk composition.
By using above-mentioned technical proposal, dacron elasticity silk is cooperateed with polyester low stretch silk blend, so that imitative cowboy face
The elasticity of material is in an ideal state.
The present invention is further arranged to, and final finishing includes: washing, sizing, preshrunk in the S7 step.
By using above-mentioned technical proposal, washing can be removed the loose colour of web surface and impurity, pass through sizing, preshrunk
The washing contraction distortion in the subsequent use process of fabric can be reduced.
The present invention is further arranged to, in the S1 step Masterbatch be black, blackish green, green, purple, khaki,
One or more of blue, spinning master batch of brown.
By using above-mentioned technical proposal, spinning color master batch granules of pigments is fine and smooth, and concentration is high, and strong coloring force is heat-resisting, fast light
Property is good, and coloring effect can be improved.
In conclusion the invention has the following advantages:
1. the blended cellulosic fibres of the tencel blended formation of cotton in the present invention, good permeability, pliability is high, and has preferably
Natural bacteriostatic effect, improve the wearing comfort of fabric entirety；On the other hand, cellulose fibre hygroscopicity is strong, therefore has
Standby excellent dyeability, color fastness is high, and it is complete can to dye chromatography；
2. the bamboo charcoal fiber in the present invention is natural environmental-protective fiber, there is moisture absorption to breathe freely, bacteriostasis antibiosis, anti-ultraviolet effect,
It is ideal antibacterial fabric fiber；
3. the conductive fiber in the present invention, which has, stablizes lasting antistatic property, the antistatic effect for closing fine fiber can be improved
Fruit, the phenomenon that reducing the electrostatic phenomenon of fabric and adsorb dust；
4. carrying out spin dyeing using spinning color masterbatch in the present invention, the coloring effect of fiber is improved, without the later period again to fabric
It is dyed, while improving shade fabric and color fastness, also reduces cost of sewage disposal.
Specific embodiment
Invention is further described in detail with reference to embodiments.
Embodiment
Embodiment 1: a kind of imitative denim fabric of antibacterial contains the following parts by weight:
200 parts of blended cellulosic fibres, 50 parts of bamboo charcoal fiber, 60 parts of terylene, 5 parts of spandex, 35 parts of conductive fiber, copper ammonia fiber 25
Part, 10 parts of antibacterial agent.
Wherein:
Blended cellulosic fibres are by the cotton that mass ratio is 1:1 and tencel blended form；
Terylene is made of the low elastic polyester filament that mass ratio is 1:1 and dacron elasticity silk；
Conductive fiber is one or both of Carbon fibe, metal compound fibres；
Antibacterial agent is silicone Quaternary Ammonium Salt Antimicrobial Agent.
A kind of preparation step that antibacterial imitates denim fabric is as follows:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 2%, is added extruder type spinning machine after mixing, produces coloured cotton fiber through high-temperature fusion extrusion spinning；?
3% Masterbatch is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；1% is added in tencel slurry
Masterbatch, using same method carry out extrusion spinning；Wherein, Masterbatch is black, blackish green, green, purple, the colour of loess
One or more of color, blue, spinning master batch of brown.
S2, scribbled: cotton, tencel and the conductive fiber after dyeing are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 165m/ on sectional warper
Min, beaming speed are 110m/min；
S5, face weave: warp thread and the weft yarn by terylene, spandex, copper ammonia fiber blended formation that S4 step obtains are knitted
It makes；
S6, antibiotic finish: the machine silicon quaternary ammonium salt antiseptic solution that configuration quality percentage concentration is 10% soaks the fabric of S5 step
Stain is in antimicrobial, bath raio 4:1, and dip time is 45 minutes, is dried under 70 degrees Celsius after dipping, when drying
Between be 18 minutes；
S7, final finishing: the fabric of S6 step is washed, is formed, the finishing process of preshrunk.
Embodiment 2: a kind of imitative denim fabric of antibacterial contains the following parts by weight:
240 parts of blended cellulosic fibres, 55 parts of bamboo charcoal fiber, 65 parts of terylene, 6 parts of spandex, 40 parts of conductive fiber, copper ammonia fiber 27
Part, 11 parts of antibacterial agent.
Wherein:
Blended cellulosic fibres are by the cotton that mass ratio is 1:1.5 and tencel blended form；
Terylene is made of the low elastic polyester filament that mass ratio is 1:1.5 and dacron elasticity silk；
Conductive fiber is one or both of Carbon fibe, metal compound fibres；
Antibacterial agent is silicone Quaternary Ammonium Salt Antimicrobial Agent.
A kind of preparation step that antibacterial imitates denim fabric is as follows:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 2.5%, is added extruder type spinning machine after mixing, produces coloured cotton fiber through high-temperature fusion extrusion spinning；
3.5% Masterbatch is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；It is added in tencel slurry
1.5% Masterbatch carries out extrusion spinning using same method；Wherein, Masterbatch be black, blackish green, green, purple,
One or more of khaki, blue, spinning master batch of brown.
S2, scribbled: cotton, tencel and the conductive fiber after dyeing are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 170m/ on sectional warper
Min, beaming speed are 115m/min；
S5, face weave: warp thread and the weft yarn by terylene, spandex, copper ammonia fiber blended formation that S4 step obtains are knitted
It makes；
S6, antibiotic finish: the machine silicon quaternary ammonium salt antiseptic solution that configuration quality percentage concentration is 11% soaks the fabric of S5 step
Stain is in antimicrobial, bath raio 4.5:1, and dip time is 50 minutes, is dried under 72 degrees Celsius after dipping, dries
Time is 20 minutes；
S7, final finishing: the fabric of S6 step is washed, is formed, the finishing process of preshrunk.
Embodiment 3: a kind of imitative denim fabric of antibacterial contains the following parts by weight:
260 parts of blended cellulosic fibres, 60 parts of bamboo charcoal fiber, 70 parts of terylene, 7 parts of spandex, 45 parts of conductive fiber, copper ammonia fiber 29
Part, 12 parts of antibacterial agent.
Wherein:
Blended cellulosic fibres are by the cotton that mass ratio is 1:1 and tencel blended form；
Terylene is made of the low elastic polyester filament that mass ratio is 1:1 and dacron elasticity silk；
Conductive fiber is one or both of Carbon fibe, metal compound fibres；
Antibacterial agent is silicone Quaternary Ammonium Salt Antimicrobial Agent.
A kind of preparation step that antibacterial imitates denim fabric is as follows:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 3%, is added extruder type spinning machine after mixing, produces coloured cotton fiber through high-temperature fusion extrusion spinning；?
4% Masterbatch is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；2% is added in tencel slurry
Masterbatch, using same method carry out extrusion spinning；Wherein, Masterbatch is black, blackish green, green, purple, the colour of loess
One or more of color, blue, spinning master batch of brown.
S2, scribbled: cotton, tencel and the conductive fiber after dyeing are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 175m/ on sectional warper
Min, beaming speed are 120m/min；
S5, face weave: warp thread and the weft yarn by terylene, spandex, copper ammonia fiber blended formation that S4 step obtains are knitted
It makes；
S6, antibiotic finish: the machine silicon quaternary ammonium salt antiseptic solution that configuration quality percentage concentration is 12% soaks the fabric of S5 step
Stain is in antimicrobial, bath raio 5:1, and dip time is 55 minutes, is dried under 74 degrees Celsius after dipping, when drying
Between be 22 minutes；
S7, final finishing: the fabric of S6 step is washed, is formed, the finishing process of preshrunk.
Embodiment 4: a kind of imitative denim fabric of antibacterial contains the following parts by weight:
280 parts of blended cellulosic fibres, 65 parts of bamboo charcoal fiber, 75 parts of terylene, 8 parts of spandex, 50 parts of conductive fiber, copper ammonia fiber 31
Part, 13 parts of antibacterial agent.
Wherein:
Blended cellulosic fibres are by the cotton that mass ratio is 1:1 and tencel blended form；
Terylene is made of the low elastic polyester filament that mass ratio is 1:1 and dacron elasticity silk；
Conductive fiber is one or both of Carbon fibe, metal compound fibres；
Antibacterial agent is silicone Quaternary Ammonium Salt Antimicrobial Agent.
A kind of preparation step that antibacterial imitates denim fabric is as follows:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 3.5%, is added extruder type spinning machine after mixing, produces coloured cotton fiber through high-temperature fusion extrusion spinning；
4.5% Masterbatch is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；It is added in tencel slurry
2.5% Masterbatch carries out extrusion spinning using same method；Wherein, Masterbatch be black, blackish green, green, purple,
One or more of khaki, blue, spinning master batch of brown.
S2, scribbled: cotton, tencel and the conductive fiber after dyeing are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 180m/ on sectional warper
Min, beaming speed are 125m/min；
S5, face weave: warp thread and the weft yarn by terylene, spandex, copper ammonia fiber blended formation that S4 step obtains are knitted
It makes；
S6, antibiotic finish: the machine silicon quaternary ammonium salt antiseptic solution that configuration quality percentage concentration is 13% soaks the fabric of S5 step
Stain is in antimicrobial, bath raio 4.5:1, and dip time is 60 minutes, is dried under 76 degrees Celsius after dipping, dries
Time is 24 minutes；
S7, final finishing: the fabric of S6 step is washed, is formed, the finishing process of preshrunk.
Embodiment 5: a kind of imitative denim fabric of antibacterial contains the following parts by weight:
300 parts of blended cellulosic fibres, 70 parts of bamboo charcoal fiber, 80 parts of terylene, 9 parts of spandex, 55 parts of conductive fiber, copper ammonia fiber 33
Part, 14 parts of antibacterial agent.
Wherein:
Blended cellulosic fibres are by the cotton that mass ratio is 1:1.5 and tencel blended form；
Terylene is made of the low elastic polyester filament that mass ratio is 1:1.5 and dacron elasticity silk；
Conductive fiber is one or both of Carbon fibe, metal compound fibres；
Antibacterial agent is silicone Quaternary Ammonium Salt Antimicrobial Agent.
A kind of preparation step that antibacterial imitates denim fabric is as follows:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 4%, is added extruder type spinning machine after mixing, produces coloured cotton fiber through high-temperature fusion extrusion spinning；?
5% Masterbatch is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；3% is added in tencel slurry
Masterbatch, using same method carry out extrusion spinning；Wherein, Masterbatch is black, blackish green, green, purple, the colour of loess
One or more of color, blue, spinning master batch of brown.
S2, scribbled: cotton, tencel and the conductive fiber after dyeing are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 185m/ on sectional warper
Min, beaming speed are 130m/min；
S5, face weave: warp thread and the weft yarn by terylene, spandex, copper ammonia fiber blended formation that S4 step obtains are knitted
It makes；
S6, antibiotic finish: the machine silicon quaternary ammonium salt antiseptic solution that configuration quality percentage concentration is 14% soaks the fabric of S5 step
Stain is in antimicrobial, bath raio 4.5:1, and dip time is 60 minutes, is dried under 78 degrees Celsius after dipping, dries
Time is 26 minutes；
S7, final finishing: the fabric of S6 step is washed, is formed, the finishing process of preshrunk.
Embodiment 6: a kind of imitative denim fabric of antibacterial contains the following parts by weight:
320 parts of blended cellulosic fibres, 80 parts of bamboo charcoal fiber, 90 parts of terylene, 10 parts of spandex, 60 parts of conductive fiber, copper ammonia fiber
35 parts, 15 parts of antibacterial agent.
Wherein:
Blended cellulosic fibres are by the cotton that mass ratio is 1:1.5 and tencel blended form；
Terylene is made of the low elastic polyester filament that mass ratio is 1:1.5 and dacron elasticity silk；
Conductive fiber is one or both of Carbon fibe, metal compound fibres；
Antibacterial agent is silicone Quaternary Ammonium Salt Antimicrobial Agent.
A kind of preparation step that antibacterial imitates denim fabric is as follows:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 3%, is added extruder type spinning machine after mixing, produces coloured cotton fiber through high-temperature fusion extrusion spinning；?
4% Masterbatch is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；2% is added in tencel slurry
Masterbatch, using same method carry out extrusion spinning；Wherein, Masterbatch is black, blackish green, green, purple, the colour of loess
One or more of color, blue, spinning master batch of brown.
S2, scribbled: cotton, tencel and the conductive fiber after dyeing are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 185m/ on sectional warper
Min, beaming speed are 130m/min；
S5, face weave: warp thread and the weft yarn by terylene, spandex, copper ammonia fiber blended formation that S4 step obtains are knitted
It makes；
S6, antibiotic finish: the machine silicon quaternary ammonium salt antiseptic solution that configuration quality percentage concentration is 15% soaks the fabric of S5 step
Stain is in antimicrobial, bath raio 4.5:1, and dip time is 60 minutes, is dried at 80 degrees celsius after dipping, dries
Time is 30 minutes；
S7, final finishing: the fabric of S6 step is washed, is formed, the finishing process of preshrunk.
Comparative example
Comparative example 1: using the embodiment 1 in the Chinese invention patent application file application No. is CN103882601B as control,
A kind of processing method that cowboy's shirt antibacterial is non-ironing is washed, cleans, sprays or is impregnated finishing fluid by biological enzyme desizing, ferment, takes off
Water, preliminary drying, pressing are formed, bake, cooling down resurgence, cleaning, drying, and wherein finishing fluid takes water as a solvent, using formula as below: anti-
Microbial inoculum 0.5-2g/L, no-ironing resin 60-100g/L, fiber protection agent 10-25g/L, catalyst 13-25g/L, softening agent 10-
20g/L。
Performance detection
It is each to prepare the consistent sample fabric of 5 block specifications according to embodiment 1-6, the method for comparative example 1, and examine in accordance with the following methods
The properties of test specimens fabric, the test result of sample fabric as made from the same embodiment, comparative example are averaged, test
The results are shown in Table 1:
The performance test results of sample fabric made from 1 the above various embodiments of table
As can be seen from Table 1, pliability, grammes per square metre, tensile strength and tearing strength etc., 1-6 sample of embodiment of the present invention face
The detection of material and sample fabric in comparative example 1 was met quite；In terms of color fastness, 1-6 of the embodiment of the present invention will be substantially better than comparison
Testing result in example 1 is illustrated to be carried out extrusion spinning using spinning color master batch, then carries out color to coloured fiber and knit, and can effectively be mentioned
High fabric color fastness；In terms of antibiotic property, the antibiotic rate of 1-6 of the embodiment of the present invention is better than comparative example 1, since present invention introduces days
Silk, bamboo charcoal fiber, copper ammonia fiber etc. have the fiber of natural antibacterial performance, while using the solution conduct of machine silicon quaternary ammonium salt antiseptic
Antibiotic finishing solution effectively increases the anti-microbial property of fabric.
This specific embodiment is only explanation of the invention, is not limitation of the present invention, those skilled in the art
Member can according to need the modification that not creative contribution is made to the present embodiment after reading this specification, but as long as at this
All by the protection of Patent Law in the scope of the claims of invention.
Claims (9)
1. a kind of antibacterial imitates denim fabric, it is characterised in that: contain the following parts by weight:
200-320 parts of blended cellulosic fibres, 50-80 parts of bamboo charcoal fiber, 60-90 parts of terylene, 5-10 parts of spandex, conductive fiber
35-60 parts, 25-35 parts of copper ammonia fiber, 10-15 parts of antibacterial agent.
2. a kind of antibacterial according to claim 1 imitates denim fabric, it is characterised in that: the blended cellulosic fibres are by matter
It measures than the cotton for 1:(1-2) and tencel blended forms.
3. a kind of antibacterial according to claim 1 imitates denim fabric, it is characterised in that: the conductive fiber be Carbon fibe,
One or both of metal compound fibres.
4. a kind of antibacterial according to claim 1 imitates denim fabric, it is characterised in that: the antibacterial agent is organosilicone quaternary ammonium
Salt antibacterial agent.
5. a kind of antibacterial according to claim 1 imitates denim fabric, it is characterised in that: the antibacterial imitates the system of denim fabric
Preparation Method the following steps are included:
S1, stock-dye: cotton, tencel, terylene are dyed with Masterbatch respectively, specific steps are as follows: add in white cotton fiber
The Masterbatch for entering 2%-4%, is added extruder type spinning machine after mixing, produces coloured cotton fiber through high-temperature fusion extrusion spinning；
The Masterbatch of 3%-5% is added in terylene stoste, through extruder type spinning machine extrusion spinning after being uniformly mixed；It is added in tencel slurry
The Masterbatch of 1%-3% carries out extrusion spinning using same method；
S2, scribbled: cotton, tencel and the conductive fiber after dyeing are carried out blended；
S3, mercerising: the scribbled warp yarn mercerizing machine in S2 step is subjected to mercerization finish；
S4, warping weaving: the mercerized yarn that S3 step is obtained carries out warping, speed of beaming 165- on sectional warper
185m/min, beaming speed are 110-130m/min；
S5, face weave: warp thread and weft yarn that S4 step obtains are weaved；
S6, antibiotic finish: configuration quality percentage concentration is the machine silicon quaternary ammonium salt antiseptic solution of 10%-15%, by the face of S5 step
Material is impregnated in antimicrobial, and bath raio is (4:1)-(5:1), and dip time is 45-60 minutes, after dipping at 70-80 DEG C
It is dried, drying time is 18-30 minutes；
S7, final finishing: the fabric of S6 step is subjected to final finishing.
6. the preparation method that a kind of antibacterial according to claim 5 imitates denim fabric, it is characterised in that: in the S5 step
Weft yarn is terylene, spandex, copper ammonia fiber blended.
7. the preparation method that a kind of antibacterial according to claim 6 imitates denim fabric, it is characterised in that: the terylene is by matter
Amount is than the low elastic polyester filament and dacron elasticity silk composition for 1:(1-1.5).
8. the preparation method that a kind of antibacterial according to claim 7 imitates denim fabric, it is characterised in that: in the S7 step
Final finishing includes: washing, sizing, preshrunk.
9. the preparation method that a kind of antibacterial according to claim 5 imitates denim fabric, it is characterised in that: in the S1 step
Masterbatch is one or more of black, blackish green, green, purple, khaki, blue, the spinning master batch of brown.