CN106521749A - Radiation-proof terylene covering yarn and preparation method thereof - Google Patents

Radiation-proof terylene covering yarn and preparation method thereof Download PDF

Info

Publication number
CN106521749A
CN106521749A CN201611016518.XA CN201611016518A CN106521749A CN 106521749 A CN106521749 A CN 106521749A CN 201611016518 A CN201611016518 A CN 201611016518A CN 106521749 A CN106521749 A CN 106521749A
Authority
CN
China
Prior art keywords
covering yarn
flax fiber
radiation
pearl powder
modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611016518.XA
Other languages
Chinese (zh)
Inventor
刘鹏飞
严林泉
金明强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Peng Long Garments Co Ltd
Original Assignee
Huzhou Peng Long Garments Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Peng Long Garments Co Ltd filed Critical Huzhou Peng Long Garments Co Ltd
Priority to CN201611016518.XA priority Critical patent/CN106521749A/en
Publication of CN106521749A publication Critical patent/CN106521749A/en
Pending legal-status Critical Current

Abstract

The invention provides a radiation-proof terylene covering yarn and a preparation method thereof. The covering yarn is obtained by blending polyester fibers and modified linen fibers, the modified effect is good, and the covering yarn not only has the original advantages of terylene, but also has better radiation-proof properties, mold resistance, anti-ultraviolet properties and healthcare functions. By means of a process of freezing before vacuum treatment, the penetration effect of pearl powder is improved, a certain destructive effect is achieved on the original structures of the linen fibers, skin needling feelings of the surfaces of the linen fibers are reduced and the wearing comfort is better. The pearl powder and the linen fibers both have certain anti-bacterial functions, after the pearl powder and the linen fibers are treated with the method, the anti-bacterial effects of the covering yarn are much better than that of the covering yarn prepared by independent use of the pearl powder or the linen fibers, and synergistic effects are achieved. After the nanometer pearl powder evenly permeates into the linen fibers, the anti-ultraviolet effects are much better than that of the untreated nanometer pearl powder; after nanometer ferric oxide powder is added, and a very good shielding effect on electromagnetic waves are achieved.

Description

A kind of radiation-proof polyester covering yarn and preparation method thereof
Technical field
The present invention relates to functional type garment material field, more particularly to a kind of radiation-proof polyester covering yarn and its preparation side Method.
Background technology
Used as most widely used chemical fibre, which has good fibre-forming performance and mechanical performance, intensity to polyster fibre High, fast light, heat-resisting and resistance to acids and bases is good, with good processability and Yi Fangxing, pure can spin, blending and intertexture.Polyester fabric Washable and wearable, ironing and anti-crease, clothing, home textile, decoration and product with etc. field be widely used.However, polyster fibre is also deposited Hygroscopicity is poor, absorbing sweat, dress do not have the shortcomings that feeling of oppression and heat, anti-static ability difference and easily stain dust, therefore make significantly fabric The about application and development of polyster fibre.For improving the snugness of fit of polyster fibre, the application added value of polyster fibre is improved, The improvement of chemically or physically aspect, and then the higher moisture absorbing and sweat releasing property of endowing terylene fiber is typically carried out to polyster fibre, is carried High dacron wearing comfort.
The present invention is easypro to improve taking for polyster fibre by way of polyster fibre is made covering yarn with flax fiber Adaptive simultaneously gives the more preferable shielding property of yarn, anti-microbial property, anti-ultraviolet property and health care.
The content of the invention
In view of this, it is an object of the invention to provide a kind of radiation-proof polyester covering yarn and preparation method thereof.
Caulis et Folium Lini is one of natural fiber that the mankind use earliest, away from modern existing more than 10,000 years history.Flax fiber is A kind of rare natural fiber, only accounts for the 1.5% of natural fiber total amount.Due to the natural, simple and unsophisticated, rare of it, color nature and height It is expensive, it is described as " the fiber queen in natural fiber ".
Flax fiber textile has good health care.It has unique suppression bacterial action.Linum Yin Xiang sections Plant, can distribute a kind of indistinct fragrance.Expert thinks that this abnormal smells from the patient can kill many antibacterials, and can suppress various parasites Growth.Proved with the scientific experimentss done by contact method:Lingerie has significant bacteriostasis, and to bacillus pyocyaneus, white is read The bacteriostasis rate of the international standard bacterial strain such as pearl bacterium exceeds to the bacteriostasis rate of escherichia coli and gold-coloured staphylococci pearl up to more than 65% More than 90%.The mummy of ancient egypt Pharaoh is rolled in surprising solid fine linen, be allowed to intactly to preserve to It is modern.
With homoiothermic, antiallergic, antistatic, antibacterial function, due to the good hygroscopicity of Caulis et Folium Lini, can absorb equivalent to itself The moisture that 20 times of weight, so sodolin feel is dry and comfortable, nowadays, the birth of wrinkle resistant, non-ironing lingerie and blending product Occur, the market of flax product is further expanded.In the world, the weaving of Caulis et Folium Lini mostly is gripper shuttle loom and rapier loom, Product includes delicate linen handkerchief, skyteens, crepe, fancy dyed yarn product, sportswear and numb wool blended yarn. Household products then include:Curtain, wall paper, tablecloth, bedding etc..Industry product then includes:Painting canvas, luggage tent, insulation Cloth, filter cloth and aviation product.
A kind of radiation-proof polyester covering yarn, with polyster fibre as core, is wrapped in outer layer with modified flax fiber, obtains cored Yarn;
Described modified flax fiber is modified through Margarita powder.
Preferably, in described modified flax fiber, the content of Margarita powder is 1-3%.
Preferably, in described radiation-proof polyester covering yarn, the percentage by weight of polyster fibre is 75-85%;Modified Asia The mass fraction of flaxen fiber is 15-25%.
A kind of preparation method of radiation-proof polyester covering yarn, is carried out as steps described below:
A, the flax fiber by moisture content in 8-15% freeze 24-30h under the subzero 20 DEG C of low temperature of subzero 30-, high at 80-90 DEG C Thawed under temperature rapidly and dried;
B, flax fiber is carried out into shredding scutching cotton and cotton carding;
C, flax fiber is transferred in vacuum laboratory box, evacuation, and injects nanometer pearl powder solution, keeping temperature is 60-80 DEG C, process 3-5h;
D, flax fiber is taken out after, washed and dried, obtained modified flax fiber, and recovery and rinsing liquid;
E, blending is carried out to polyster fibre and modified flax fiber using Technology of Air Vortex Spinning, wherein with polyster fibre as core, to change Property flax fiber be wrapped in outer layer, form covering yarn.
Preferably, the cleanout fluid in described step D can obtain nanometer pearl powder solution after treatment, and repeat Utilize.
Preferably, described nanometer pearl powder solution, including the composition of following percentage by weight:
Nanometer pearl powder 8-15%
Nanoscale iron powder 6-10%
Dispersant 0.1-0.3%
Deionized water surplus.
Preferably, described dispersant is BYK-180 dispersants.
It is an advantage of the current invention that:
1st, a kind of radiation-proof polyester covering yarn provided by the present invention and preparation method thereof, by polyster fibre and modified flax fiber Blending is carried out, covering yarn is obtained, modified effect is good, covering yarn not only possesses the original advantage of terylene, be also equipped with preferably anti- Radiance, anti-microbial property, ultraviolet resistance and health care;
2nd, using vacuum treated mode is first freezed again, the infiltration effect of Margarita powder is not only improved, and it is former to flax fiber Some structures have certain destruction, reduce the surface spikes sense of flax fiber, and after dress, comfortableness is more preferably;
3rd, Margarita powder and flax fiber are respectively provided with certain antibacterial functions, and after being processed using the method for the present invention, antibacterial effect will It is well more many than Margarita powder or flax fiber is used alone, with cooperative effect;
4th, after nanometer pearl powder uniformly penetrates into flax fiber, preventing ultraviolet effect is well more many than before processing.
5th, after testing, after adding nanoscale iron powder, the fabric pair that radiation-proof polyester covering yarn of the invention is made into The electromagnetic wave of 500-700MHz has extraordinary shield effectiveness.
Specific embodiment
Hereinafter embodiments of the invention are described in detail.
Embodiment 1
A kind of radiation-proof polyester covering yarn, with polyster fibre as core, is wrapped in outer layer with modified flax fiber, obtains covering yarn; Described modified flax fiber is modified through Margarita powder.
In described modified flax fiber, the content of Margarita powder is 2.
In described radiation-proof polyester covering yarn, the percentage by weight of polyster fibre is 82%;The matter of modified flax fiber Amount fraction is 18%.
A kind of preparation method of radiation-proof polyester covering yarn, is carried out as steps described below:
A, moisture content is freezed into 27h in 12% flax fiber under subzero 25 DEG C of low temperature, it is rapid under 85 DEG C of high temperature to thaw simultaneously Drying;
B, flax fiber is carried out into shredding scutching cotton and cotton carding;
C, flax fiber is transferred in vacuum laboratory box, evacuation, and injects nanometer pearl powder solution, keeping temperature is 75 DEG C, process 4h;
D, flax fiber is taken out after, washed and dried, obtained modified flax fiber, and recovery and rinsing liquid;
E, blending is carried out to polyster fibre and modified flax fiber using Technology of Air Vortex Spinning, wherein with polyster fibre as core, to change Property flax fiber be wrapped in outer layer, form covering yarn.
Described nanometer pearl powder solution, including the composition of following percentage by weight:
Nanometer pearl powder 12%
Nanoscale iron powder 8%
BYK-180 dispersants 0.2%
Deionized water surplus.
Embodiment 2
A kind of radiation-proof polyester covering yarn, with polyster fibre as core, is wrapped in outer layer with modified flax fiber, obtains covering yarn; Described modified flax fiber is modified through Margarita powder.
In described modified flax fiber, the content of Margarita powder is 3%.
In described radiation-proof polyester covering yarn, the percentage by weight of polyster fibre is 75%;The matter of modified flax fiber Amount fraction is 25%.
A kind of preparation method of radiation-proof polyester covering yarn, is carried out as steps described below:
A, the flax fiber by moisture content in 8-15% freeze 30h under subzero 20 DEG C of low temperature, are thawed under 90 DEG C of high temperature rapidly And dry;
B, flax fiber is carried out into shredding scutching cotton and cotton carding;
C, flax fiber is transferred in vacuum laboratory box, evacuation, and injects nanometer pearl powder solution, keeping temperature is 60 DEG C, process 5h;
D, flax fiber is taken out after, washed and dried, obtained modified flax fiber, and recovery and rinsing liquid;
E, blending is carried out to polyster fibre and modified flax fiber using Technology of Air Vortex Spinning, wherein with polyster fibre as core, to change Property flax fiber be wrapped in outer layer, form covering yarn.
Described nanometer pearl powder solution, including the composition of following percentage by weight:
Nanometer pearl powder 8%
Nanoscale iron powder 6%
BYK-180 dispersants 0.3%
Deionized water surplus.
Embodiment 3
A kind of radiation-proof polyester covering yarn, with polyster fibre as core, is wrapped in outer layer with modified flax fiber, obtains covering yarn; Described modified flax fiber is modified through Margarita powder.
In described modified flax fiber, the content of Margarita powder is 1%.
In described radiation-proof polyester covering yarn, the percentage by weight of polyster fibre is 85%;The matter of modified flax fiber Amount fraction is 15%.
A kind of preparation method of radiation-proof polyester covering yarn, is carried out as steps described below:
A, moisture content is freezed into 24h in 15% flax fiber under subzero 30 DEG C of low temperature, it is rapid under 80 DEG C of high temperature to thaw simultaneously Drying;
B, flax fiber is carried out into shredding scutching cotton and cotton carding;
C, flax fiber is transferred in vacuum laboratory box, evacuation, and injects nanometer pearl powder solution, keeping temperature is 80 DEG C, process 3h;
D, flax fiber is taken out after, washed and dried, obtained modified flax fiber, and recovery and rinsing liquid;
E, blending is carried out to polyster fibre and modified flax fiber using Technology of Air Vortex Spinning, wherein with polyster fibre as core, to change Property flax fiber be wrapped in outer layer, form covering yarn.
Described nanometer pearl powder solution, including the composition of following percentage by weight:
Nanometer pearl powder 15%
Nanoscale iron powder 10%
BYK-180 dispersants 0.1%
Deionized water surplus.
Reference examples
Modified flax fiber in comparative example 1 is replaced with through modified flax fiber, direct and polyester fibres Into covering yarn.
Below radiation-proof polyester covering yarn prepared by embodiment 1-3 is made into after fabric carries out properties test,
Detection project Embodiment 1 Embodiment 2 Embodiment 3 Reference examples
Anti-ultraviolet property 50+ 50+ 50+ 32
Dampness RET K/W 7.8 7.8 7.8 7.8
Biocidal property % (escherichia coli) 92 91 92 68
Biocidal property % (staphylococcus aureuses) 97 95 95 82
Biocidal property % (Candida albicans) 92 90 90 75
Each detection data from more than, radiation-proof polyester covering yarn prepared by embodiment 1-3 are compared through modified Caulis et Folium Lini Fiber and polyster fibre make covering yarn, and anti-ultraviolet property, anti-microbial property and moisture permeability are significantly increased.
Impact to various different factors to covering yarn is analyzed below:
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto, any Those familiar with the art the invention discloses technical scope in, technology according to the present invention scheme and its invention Design in addition equivalent or change, should all be included within the scope of the present invention.

Claims (7)

1. a kind of radiation-proof polyester covering yarn, it is characterised in that with polyster fibre as core, is wrapped up outside with modified flax fiber Layer, obtains covering yarn;Described modified flax fiber is modified through Margarita powder.
2. radiation-proof polyester covering yarn as claimed in claim 1, it is characterised in that Margarita powder in described modified flax fiber Content be 1-3%.
3. radiation-proof polyester covering yarn as claimed in claim 1, it is characterised in that in described radiation-proof polyester covering yarn, The percentage by weight of polyster fibre is 75-85%;The mass fraction of modified flax fiber is 15-25%.
4. a kind of preparation method of radiation-proof polyester covering yarn, it is characterised in that carry out as steps described below:
A, the flax fiber by moisture content in 8-15% freeze 24-30h under the subzero 20 DEG C of low temperature of subzero 30-, high at 80-90 DEG C Thawed under temperature rapidly and dried;
B, flax fiber is carried out into shredding scutching cotton and cotton carding;
C, flax fiber is transferred in vacuum laboratory box, evacuation, and injects nanometer pearl powder solution, keeping temperature is 60-80 DEG C, process 3-5h;
D, flax fiber is taken out after, washed and dried, obtained modified flax fiber, and recovery and rinsing liquid;
E, blending is carried out to polyster fibre and modified flax fiber using Technology of Air Vortex Spinning, wherein with polyster fibre as core, to change Property flax fiber be wrapped in outer layer, form covering yarn.
5. the preparation method of radiation-proof polyester covering yarn as claimed in claim 4, it is characterised in that in described step D Cleanout fluid can obtain nanometer pearl powder solution after treatment, and reuse.
6. the preparation method of radiation-proof polyester covering yarn as claimed in claim 4, it is characterised in that described nanometer level pearl Powder solution, including the composition of following percentage by weight:
Nanometer pearl powder 8-15%
Nanoscale iron powder 6-10%
Dispersant 0.1-0.3%
Deionized water surplus.
7. the preparation method of radiation-proof polyester covering yarn as claimed in claim 6, it is characterised in that described dispersant is BYK-180 dispersants.
CN201611016518.XA 2016-11-18 2016-11-18 Radiation-proof terylene covering yarn and preparation method thereof Pending CN106521749A (en)