CN106904579A - 一种制备二硒化钼量子点的方法 - Google Patents

一种制备二硒化钼量子点的方法 Download PDF

Info

Publication number
CN106904579A
CN106904579A CN201710041917.XA CN201710041917A CN106904579A CN 106904579 A CN106904579 A CN 106904579A CN 201710041917 A CN201710041917 A CN 201710041917A CN 106904579 A CN106904579 A CN 106904579A
Authority
CN
China
Prior art keywords
selenizing molybdenum
quantum dots
ultrasound
selenizing
preparing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710041917.XA
Other languages
English (en)
Inventor
李学铭
唐利斌
鲁朝宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yunnan University YNU
Yunnan Normal University
Original Assignee
Yunnan Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yunnan Normal University filed Critical Yunnan Normal University
Priority to CN201710041917.XA priority Critical patent/CN106904579A/zh
Publication of CN106904579A publication Critical patent/CN106904579A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种简单易行的制备二硒化钼量子点的方法。该方法以二硒化钼粉末为原料，先称取一定量的二硒化钼在研钵中充分研磨，接着量取适量的氮甲基吡咯烷酮（NMP）加入到研磨好的样品中，放到超声仪中超声，将超声后的溶液静置，吸取悬浮溶液进行离心，最后收集上层棕色澄清溶液即为二硒化钼量子点。本发明可一步制得二硒化钼量子点，具有制备工艺简单、操作安全、成本低廉、绿色环保、可重复性好等优点，且制备得到的二硒化钼量子点具有分散性好，尺寸均匀，结晶度高的优点。在光电器件、太阳能光催化制氢、电解水等领域拥有极大的商业前景。

Description

一种制备二硒化钼量子点的方法
技术领域
本发明涉及一种纳米材料制备方法，具体涉及二硒化钼量子点的一种制备方法。
背景技术
二硒化钼是一种具有层状结构的物质，与石墨烯类似，其原子之间靠共价键紧密连接，层与层之间是较弱的范德华力作用，常作为固体润滑剂使用，可有效减少设备的表面磨损和运转阻力，降低设备能耗，延长使用寿命。层状二硒化钼表面的硒、钼原子具有良好的化学活性，在电催化制氢方面有显著的电催化析氢性能，有望在太阳能光催化制氢中作为廉价析氢电催化材料大规模推广应用，获得的氢气作为一种高能效、无污染理想的能源，有望解决日益严重的环境污染问题。
二硒化钼量子点高的比表面积和层状结构边缘产生的大量悬挂键增加了氢原子的吸附点，可明显增强催化产氢效果。当二硒化钼为单原子层厚度时，材料从间接带隙半导体变为直接带隙半导体，可以大幅度提高半导体光电转换效率。二硒化钼量子点具有的优异性能引起了研究者的关注，在光电器件领域极具商业价值。但目前为止，尚未有二硒化钼量子点材料制备的相关报道。
本发明提供一种制备二硒化钼量子点材料的方法，通过以下步骤制备：
第一步，在研钵中把一定量的二硒化钼充分研磨。
第二步，取适量的氮甲基吡咯烷酮（NMP）加到研磨好的样品中，并放入超声仪中超声。
第三步，将超声后的溶液静置，吸取上层悬浮液进行离心，离心结束后收集上层棕色澄清溶液，即为二硒化钼量子点。
上述制备二硒化钼量子点材料具体步骤为，第一步，研磨二硒化钼粉末；第二步，向研磨好的粉末样品加入NMP，使其浓度为0.1 g/mL~0.2 g/mL，置于功率为400 W~800 W的超声仪超声，第三步，超声后将溶液静置15~30分钟，取悬浮液在离心机中以5000~10000r/min离心20~45分钟。
本发明制备二硒化钼量子点的工艺有以下优点：
（1）二硒化钼量子点尺寸均匀，结晶度好，且具有良好的的荧光特性。
（2）制备工艺简单，绿色环保，成本低廉，重复性好，水溶性量子点分散性强，稳定性高，便于规模化生产。
附图说明
图1为二硒化钼量子点透射电镜图。
图2为二硒化钼量子点拉曼测试图。
图3为二硒化钼量子点的光电子能谱图（Se 3d XPS）。
图4为二硒化钼量子点的光电子能谱图（Mo 3d XPS）。
具体实施方式
取0.5 g二硒化钼粉末放在研钵中充分研磨。
将研磨后的样品放到烧杯中，加入50 ML 氮甲基吡咯烷酮（NMP），并用超声仪超声4小时。
将超声后的溶液离心，收集上层棕色澄清液体，即为二硒化钼量子点。

Claims (4)

1.一种制备二硒化钼量子点的方法，包括如下步骤：（1）称取适量二硒化钼粉末在研钵里充分研磨；（2）量取适量氮甲基吡咯烷酮（NMP），并放入研磨好的样品中，进行超声；（3）将超声好的悬浮液离心，收集上层棕色澄清溶液。
2.根据权利要求1所述的一种制备二硒化钼量子点的方法，其特征在于：步骤（1）中，称取二硒化钼粉末0.5 g，充分研磨。
3.根据权利要求1所述的一种制备二硒化钼量子点的方法，其特征在于：步骤（2）中，加入氮甲基吡咯烷酮50 mL ,在超声仪中超声。
4.根据权利要求1所述的一种制备二硒化钼量子点的方法，其特征在于：步骤（3）中，将超声后的溶液静置，取悬浮液在离心机中离心。
CN201710041917.XA 2017-01-20 2017-01-20 一种制备二硒化钼量子点的方法 Pending CN106904579A (zh)