CN106801204A - 一种抗拉强度增强的轴承 - Google Patents

一种抗拉强度增强的轴承 Download PDF

Info

Publication number
CN106801204A
CN106801204A CN201510835293.XA CN201510835293A CN106801204A CN 106801204 A CN106801204 A CN 106801204A CN 201510835293 A CN201510835293 A CN 201510835293A CN 106801204 A CN106801204 A CN 106801204A
Authority
CN
China
Prior art keywords
bearing
tensile strength
enhanced
steel
lanthanum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510835293.XA
Other languages
English (en)
Inventor
徐文萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510835293.XA priority Critical patent/CN106801204A/zh
Publication of CN106801204A publication Critical patent/CN106801204A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种抗拉强度增强的轴承，它是由这样的轴承钢制成的，所述轴承钢的组成为(以重量％计)：0.25％至0.29％的碳；0.10％至1.20％的锰；0.09％至0.13％的磷；0.10％至0.19％的硫；0.60％至1.00％的硅；≤0.09％的铝；≤0.01％的氮；0.45％至0.83％的铬；0.04％至0.07％的铌；≤0.50％的铜；0.25％至0.70％的镧；0.2％至2.00％的铈；0.2％至0.4％的钒；0.0075％至0.0095％的钨；0.010％至0.050％的钛：其余为铁和不可避免的杂质。本发明所述的轴承具有增强的抗拉强度，可以广泛用于生产。

Description

一种抗拉强度增强的轴承
技术领域
本发明涉及轴承领域，具体地说，涉及一种抗拉强度增强的轴承。
背景技术
轴承是生产中最常用的零部件，但是由于目前对于轴承的要求越来越高，目前的一些轴承已经满足不了要求。
发明内容
本发明的目的是提供一种抗拉强度增强的轴承。
为了实现本发明的目的，本发明提供一种抗拉强度增强的轴承，它是由这样的轴承钢制成的，所述轴承钢的组成为(以重量％计)：
0.25％至0.29％的碳；
0.10％至1.20％的锰；
0.09％至0.13％的磷；
0.10％至0.19％的硫；
0.60％至1.00％的硅；
≤0.09％的铝；
≤0.01％的氮；
0.45％至0.83％的铬；
0.04％至0.07％的铌；
≤0.50％的铜；
0.25％至0.70％的镧；
0.2％至2.00％的铈；
0.2％至0.4％的钒；
0.0075％至0.0095％的钨；
0.010％至0.050％的钛：
其余为铁和不可避免的杂质。
优选地，所述轴承钢的组成为(以重量％计)：
0.27％的碳；
0.60％的锰；
0.10％的磷；
0.16％的硫；
0.80％的硅；
0.03％的铝；
0.005％的氮；
0.57％的铬；
0.05％的铌；
0.30％的铜；
0.55％的镧；
1.00％的铈；
0.3％的钒；
0.0085％的钨；
0.035％的钛：
其余为铁和不可避免的杂质。
本发明所述的轴承具有增强的抗拉强度，可以广泛用于生产
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
实施例1轴承的制备
抗拉强度增强的轴承钢的组成为(以重量％计)：
0.27％的碳；
0.60％的锰；
0.10％的磷；
0.16％的硫；
0.80％的硅；
0.03％的铝；
0.005％的氮；
0.57％的铬；
0.05％的铌；
0.30％的铜；
0.55％的镧；
1.00％的铈；
0.3％的钒；
0.0085％的钨；
0.035％的钛：
其余为铁和不可避免的杂质。
将具有上述成分组成的30kg钢料在高频真空熔炉中熔融，随后进行浇铸，在该浇铸中冷却速度为1.9℃/min以形成锭料。将锭料在950℃下保持12小时，然后在500℃下保持90分钟。此后使用500吨锤式锻造机进行热锻，这样制得轴承钢。将轴承钢在锻造机中压制成型以制造轴承1。
实施例2轴承的制备
按照和实施例1相同的方式制备轴承2，不同之处在于不使用铈。
实施例3轴承的制备
按照和实施例1相同的方式制备轴承3，不同之处在于不使用钨。
实施例4轴承的制备
按照和实施例1相同的方式制备轴承4，不同之处在于不使用镧。
实验例1
根据GB/T 228-2002测定抗拉强度。结果如下：轴承1的抗拉强度Rm为1183兆帕，轴承2的抗拉强度Rm为758兆帕，轴承3的抗拉强度Rm为778兆帕，轴承4的抗拉强度Rm为612兆帕。

Claims (2)

1.一种抗拉强度增强的轴承，其特征在于，它是由这样的轴承钢制成的，所述轴承钢的组成为(以重量％计)：
0.25％至0.29％的碳；
0.10％至1.20％的锰；
0.09％至0.13％的磷；
0.10％至0.19％的硫；
0.60％至1.00％的硅；
≤0.09％的铝；
≤0.01％的氮；
0.45％至0.83％的铬；
0.04％至0.07％的铌；
≤0.50％的铜；
0.25％至0.70％的镧；
0.2％至2.00％的铈；
0.2％至0.4％的钒；
0.0075％至0.0095％的钨；
0.010％至0.050％的钛：
其余为铁和不可避免的杂质。
2.根据权利要求1所述的抗拉强度增强的轴承，其特征在于，所述轴承钢的组成为(以重量％计)：
0.27％的碳；
0.60％的锰；
0.10％的磷；
0.16％的硫；
0.80％的硅；
0.03％的铝；
0.005％的氮；
0.57％的铬；
0.05％的铌；
0.30％的铜；
0.55％的镧；
1.00％的铈；
0.3％的钒；
0.0085％的钨；
0.035％的钛：
其余为铁和不可避免的杂质。
CN201510835293.XA 2015-11-26 2015-11-26 一种抗拉强度增强的轴承 Pending CN106801204A (zh)