CN106723725A - 一种荧光人造水晶钻石及其制造方法 - Google Patents
一种荧光人造水晶钻石及其制造方法 Download PDFInfo
- Publication number
- CN106723725A CN106723725A CN201611096732.0A CN201611096732A CN106723725A CN 106723725 A CN106723725 A CN 106723725A CN 201611096732 A CN201611096732 A CN 201611096732A CN 106723725 A CN106723725 A CN 106723725A
- Authority
- CN
- China
- Prior art keywords
- fluorescence
- varnish
- coating
- diamond
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种荧光人造水晶钻石及其制造方法,一种荧光人造水晶钻石,包括顶部和底部,其中,底部表面设置有涂层,涂层由里向外分为荧光涂层和聚光涂层;荧光涂层由荧光涂料喷涂而成,荧光涂料按重量百分比计:AB混合漆30~40%,其中A清漆15~20%,B清漆15~20%;色荧光粉40~60%,珍珠粉10%。白色珠光有很强的保光效果,可以增长荧光时间,喷涂了此涂料后采光时间较未喷涂的发光时间增长15%以上,本发明要达到一种在吸光后,暗光条件下还能在一段时间内自发发光的效果,以便应用于特殊需要装饰品中去。
Description
技术领域
本发明属于水钻技术领域,具体的,本发明涉及一种夜光水钻及其制造方法。
背景技术
目前公知的人造水晶钻石基本都是仿效奥地利施华洛世奇公司的产品,不同形状规格采用不同的切割磨抛工艺,用于各类装饰上。由于荧光成分和玻璃的材料成分在化学制作方法上,目前尚不能制造出直接带有荧光效果的玻璃,荧光粉的基本成分为硫化盐和硝酸盐,与烧制水晶玻璃工艺的氧化物成分完全无法融合。所以需要寻求另外的方法去解决。
中国专利申请CN105942682A公开了一种夜光水钻及其制造方法,在夜光水钻亭面表面设置有夜光层,夜光层是由夜光涂料喷涂而成。该发明经夜光水钻亭面外表面设置了夜光层,夜光涂料的配方中使用合理比例的白色色精,在光亮环境下看具有暖白的效果,不使用白色色浆,白色色精遮盖力很弱,具有透光朦胧的观感,给人心旷 神怡的感觉,同时夜光粉的加入,在光亮环境下看具有一定的消光效果,增加朦胧的观感。但它并没有延时发光和功效。
发明内容
本发明提供一种能够涂层能有效长时间的附着在玻璃从而增强荧光效果的人造水晶钻石。
本发明同时还提供一种上述人造水晶钻石的制备方法。
本发明的技术方案是:一种荧光人造水晶钻石,包括顶部和底部,其中,底部表面设置有涂层,涂层由里向外分为荧光涂层和聚光涂层。
优选地,上述荧光涂层由荧光涂料喷涂而成,
所述荧光涂料按重量百分比计:
AB混合漆30~40%,其中A清漆15~20%,B清漆15~20%;色荧光粉40~60%,珍珠粉10%。
优选地,上述聚光涂层为白色珠光漆。
优选地,上述荧光涂料为绿色荧光剂,所述绿色荧光剂按重量百分比计:AB混合漆50%,其中A清漆25%,B清漆25%;绿色荧光粉40%,珍珠粉10%。
优选地,上述荧光涂料为蓝色荧光剂,所述蓝色荧光剂按重量百分比计: AB混合漆40%,其中A清漆20%,B清漆20%;蓝色荧光粉50%,珍珠粉10%。
优选地,上述荧光涂料为紫色荧光剂:AB混合漆30%,其中A清漆15%,B清漆15%;紫色荧光粉60%,珍珠粉10%。
优选地,上述荧光涂料为红色荧光剂:AB混合漆30%,其中A清漆15%,B清漆15%;红色荧光粉60%,珍珠粉10%。
一种用荧光水晶玻璃钻石制备方法,包括步骤:
①先将水晶玻璃钻石放置于金属清洗剂与5%浓度氢氧化钠溶液中洗净,出去油污;
②将水晶玻璃钻石有规律的吸附在透明的塑胶片上;
③将吸附与塑胶片上的水晶玻璃钻石用毛刷洗净;
④将吸附了水晶玻璃钻石的塑胶片置水烘箱内,把水分烤干;
⑤将搅拌充分的荧光涂料放置于有搅拌装置的桶内,用自动喷漆油漆枪将荧光涂料均匀的喷涂在水晶玻璃钻石的底侧;
⑥再用白色珠光漆喷涂于荧光漆表层。
本发明的有效效果是:本发明的有效效果是:白色珍珠粉有很强的保光效果,可以增长荧光时间。效果对比,喷涂了珍珠粉涂料和未添加珍珠粉的涂料,在同样的受光强度和时间下,喷涂了珍珠粉的涂料产品,发光可以增长15分钟。
本发明要达到一种在吸光后,暗光条件下还能在一段时间内自发发光的效果,以便应用于特殊需要装饰品中去。
附图说明
图1为尖底型人造水晶钻石的区域结构示意图;
图2为平底型人造水晶钻石的区域结构示意图;
附图标志为:1-顶部;2-腰部;3-底部。
具体实施方式
下面结合附图作进一步说明:
参见图1,图1中水晶玻璃钻石为尖底型,顶部1的顶端为平面型,底部2和顶部1的交叉部为腰部,底部2为涂层部份。
涂层部份分为两层,为荧光涂层和聚光涂层。
参见图2,图2除水晶玻璃钻石的底部为平面型外,其它和图2相同。
具体地,下面结合具体实施例对本发明作具体的说明
实施例1 一种用荧光水晶玻璃钻石制备方法,包括步骤:
①先将水晶玻璃钻石放置于金属清洗剂与5%浓度氢氧化钠溶液中洗净,出去油污;
②将水晶玻璃钻石有规律的吸附在透明的塑胶片上;
③将吸附与塑胶片上的水晶玻璃钻石用毛刷洗净;
④将吸附了水晶玻璃钻石的塑胶片置水烘箱内,把水分烤干;
⑤将搅拌充分的绿色荧光剂放置于有搅拌装置的桶内,用自动喷漆油漆枪将荧光涂料均匀的喷涂在水晶玻璃钻石的底侧;
其中:绿色荧光剂按重量百分比计:AB混合漆50%,其中A清漆25%,B清漆25%;绿色荧光粉40%,珍珠粉10%。
⑥再用白色珠光漆喷涂于荧光漆表层。
实施例2 荧光涂料为蓝色荧光剂,其中蓝色荧光剂按重量百分比计: AB混合漆40%,其中A清漆20%,B清漆20%;蓝色荧光粉50%,珍珠粉10%,其它和实施例1相同。
实施例3 荧光涂料为紫色荧光剂,其中紫色荧光剂按重量百分比计:AB混合漆30%,其中A清漆15%,B清漆15%;紫色荧光粉60%,珍珠粉10%,其它和实施例1相同。
实施例4荧光涂料为红色荧光剂,其中红色荧光剂按重量百分比计:AB混合漆30%,其中A清漆15%,B清漆15%;红色荧光粉60%,珍珠粉10%,其它和实施例1相同。
一、本发明中A漆为:环氧树脂70%,二甲苯30%;
B漆为:固化剂(苯酚磺酸)80%,二甲苯20%;
二.绿色,蓝色,紫色,红色荧光剂组成成分(按重量百分比):
绿色荧光剂:硫化钙55%、硫化钾1 %、硫化钠10%、硝酸钡12%、硝酸铟13%。
蓝色荧光剂:硫化钙63%、硫酸钠5 %、硫酸钾5 %、硫酸锶10%、氯化钠6 %、硝酸银1%、硫化镁10%。
紫色荧光剂:硫化钙63%、硫化镁26%、硫化钠10%、硝酸锶1 %。
红色荧光剂:硫酸钡55%、硫酸镁40%、磷酸锂2 %、硝酸铜3%。
三.白色珠光漆的成分(按重量百分比计)
AB漆80%(其中A漆40%,B漆40%),珍珠粉20%.
四.金属清洗剂成分(按重量百分比计):
丙二醇甲醚27%,二甲基硅氧烷13%,三乙醇胺15%,二氧化硅15%,甲基纤维素15%,硬脂酸25%;市场有销售,属于公知类产品。
本发明的产品可在增长荧光时间,也就是说本发明的荧光能够在延长发光时间约15分种。
Claims (6)
1.一种荧光人造水晶钻石,包括顶部和底部,其中,所述的底部表面设置有涂层,其特征在于,所述涂层由里向外分为荧光涂层和聚光涂层。
2.如权利要求 1 所述的荧光人造水晶钻石,其特征在于,所述荧光涂层由荧光涂料喷涂而成,所述荧光涂料按重量百分比计:
AB混合漆30~40%,其中A清漆15~20%,B清漆15~20%;色荧光粉40~60%,珍珠粉10%。
3.如权利要求 1 或2所述的荧光人造水晶钻石,其特征在于,所述聚光涂层为白色珠光漆,所述白色珠光漆的组份按重量百分比计为:AB漆80%,其中A漆40%,B漆40%,珍珠粉20%。
4. 如权利要求 1 或2所述的荧光人造水晶钻石,其特征在于,所述荧光涂料为绿色荧光剂,所述绿色荧光剂按重量百分比计:AB混合漆40%,其中A清漆20%,B清漆20%;绿色荧光粉40%,珍珠粉10%;
或所述荧光涂料为蓝色荧光剂,所述蓝色荧光剂按重量百分比计: AB混合漆40%,其中A清漆20%,B清漆20%;蓝色荧光粉50%,珍珠粉10%;
或所述荧光涂料为紫色荧光剂:AB混合漆30%,其中A清漆15%,B清漆15%;紫色荧光粉60%,珍珠粉10%;
或所述荧光涂料为红色荧光剂:AB混合漆30%,其中A清漆15%,B清漆15%;红色荧光粉60%,珍珠粉10%。
5.如权利要求4所述的荧光人造水晶钻石,其特征在于,
所述绿色荧光粉按重量百分比计:硫化钙55%、硫化钾1 %、硫化钠10%、硝酸钡12%、硝酸铟13%;
所述蓝色荧光粉按重量百分比计:硫化钙63%、硫酸钠5 %、硫酸钾5 %、硫酸锶10%、氯化钠6 %、硝酸银1 %、硫化镁10%;
所述紫色荧光粉按重量百分比计:硫化钙63%、硫化镁26%、硫化钠10%、硝酸锶1 %;
所述红色荧光粉按重量百分比计:硫酸钡55%、硫酸镁40%、磷酸锂2 %、硝酸铜3%。
6.一种用荧光水晶玻璃钻石制备方法,其特征在于,包括步骤:
①先将水晶玻璃钻石放置于金属清洗剂与5%浓度氢氧化钠溶液中洗净,出去油污;
②将水晶玻璃钻石有规律的吸附在透明的塑胶片上;
③将吸附与塑胶片上的水晶玻璃钻石用毛刷洗净;
④将吸附了水晶玻璃钻石的塑胶片置水烘箱内,把水分烤干;
⑤将搅拌充分的荧光涂料放置于有搅拌装置的桶内,用自动喷漆油漆枪将荧光涂料均匀的喷涂在水晶玻璃钻石的底侧;
⑥再用白色珠光漆喷涂于荧光漆表层。