CN101912186A - 一种夜光珍珠及其加工工艺 - Google Patents
一种夜光珍珠及其加工工艺 Download PDFInfo
- Publication number
- CN101912186A CN101912186A CN 201010244688 CN201010244688A CN101912186A CN 101912186 A CN101912186 A CN 101912186A CN 201010244688 CN201010244688 CN 201010244688 CN 201010244688 A CN201010244688 A CN 201010244688A CN 101912186 A CN101912186 A CN 101912186A
- Authority
- CN
- China
- Prior art keywords
- pearl
- pearl body
- coating
- transparent
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种夜光珍珠，包括珍珠本体，在珍珠本体表面包裹着一透明发光层；本发明公开了夜光珍珠的加工工艺，该工艺包括(1)、对珍珠本体进行烘干；(2)、在透明热固性粉末涂料中添加夜光粉，并对其搅拌混合，(3)、经搅拌混合后的涂料均匀的喷涂到经烘干后的珍珠本体表面，将珍珠本体完全包裹；(4)、将珍珠本体包裹后，放入烘箱内烘烤，经搅拌混合后的涂料被加热烘烤，使其熔融流平固化，固化后在珍珠本体表面形成一涂膜层；(5)、经烘烤后，拿出自然冷却，即为成品。采用上述结构以及工艺后，本发明透明发光层能在光线较暗的地方发光，且在光线的折射下衬托出珍珠本体的色泽，使佩带者在夜间也能突显珍珠装饰效果。
Description
技术领域
本发明公开了一种夜光珍珠及其加工工艺。
背景技术
珍珠象征着健康、纯洁、富有和幸福，自古以来作为饰品被人们佩带在身上，为人们所喜爱。它形状多样，有圆形、梨形、蛋形、泪滴形、纽扣形和任意形，其中以圆形为佳；颜色有白色、粉红色、淡黄色、淡绿色、淡蓝色、褐色、淡紫色、黑色等，以白色为主。但是，现在的珍珠因自身的局限，在黑暗的地方或夜间，也就是光线较暗的地方，自身不会发光，不能突显珍珠的装饰效果。
发明内容
为解决上述问题，本发明的目的在于提供一种能在光线较暗的地方发光，突显珍珠装饰效果的夜光珍珠以及该夜光珍珠的加工工艺。
本发明要解决其技术问题所采用的技术方案是：
一种夜光珍珠，包括珍珠本体，在珍珠本体表面包裹着一透明发光层。透明发光层可在光线较暗的地方发光，在光线的折射下衬托出珍珠本体的色泽，使佩带者在夜间(光线较暗的地方)也能突显珍珠装饰效果。
本发明进一步设置为：所述透明发光层为透明热固性粉末涂料层，该涂料层采用透明热固性粉末涂料；在透明热固性粉末涂料层中设有夜光粉，通过夜光粉使珍珠在光线较暗的地方发光。
一种夜光珍珠的加工工艺，包括珍珠本体，该工艺包括以下步骤：
(1)、对珍珠本体进行烘干，烘干温度为100℃～120℃，并对其保温18～22小时，经烘干后珍珠本体内的水分得到充分蒸发，防止在下述烘烤时，珍珠本体内含有水分而使下述透明发光层产生气泡。
(2)、在透明热固性粉末涂料中添加夜光粉，并对其搅拌混合，其中透明热固性粉末涂料含90％～97％(重量比)，夜光粉含3％～10％(重量比)，这两者配比的设置，既可保证夜光珍珠的亮度(根据夜光粉占有比例而定)，又可使透明热固性粉末涂料在珍珠本体表面充分流平(根据透明热固性粉末涂料占有比例而定)。
(3)、经搅拌混合后的涂料均匀的喷涂到经烘干后的珍珠本体表面，将珍珠本体完全包裹；
(4)、将珍珠本体包裹后，放入烘箱内烘烤，恒温为138℃～142℃，经搅拌混合的涂料被加热烘烤，使其熔融流平固化，流平固化时间为15～25分钟，流平固化后在珍珠本体表面形成一涂膜层，也就是透明发光层；
(5)、经烘烤后，拿出自然冷却，即为成品。
本工艺进一步设置为：所述步骤3中经烘干后的珍珠本体放置在金属挂件上，经搅拌混合的涂料通过静电喷塑机均匀喷涂到经烘干后的珍珠本体表面，这时涂料带有静电，金属挂件的设置又可使珍珠本体表面产生电荷，并与涂料中的电荷极性相反，因此在静电作用下，涂料会均匀的吸附于珍珠本体表面，同时，随着喷上的涂料增多，电荷积聚也越多，当达到一定厚度时，由于产生静电排斥作用，便不继续吸附，从而使珍珠本体表面形成一定厚度且均匀的粉状涂层，经烘烤流平固化，形成的透明发光层平整光亮、厚度均匀，在夜光粉发出的光线折射下更能衬托出珍珠本体的色泽。
采用上述结构以及工艺后，本发明透明发光层在夜光粉作用下，能在光线较暗的地方发光，且在光线的折射下衬托出珍珠本体的色泽，使佩带者在夜间(光线较暗的地方)也能突显珍珠装饰效果。
附图说明
下面结合附图与具体实施方式对本发明作进一步详细说明。
图1是本发明的结构示意图。
具体实施方式
实施例1：参照图1，一种夜光珍珠，包括珍珠本体1，在珍珠本体1表面包裹着一透明发光层2，该透明发光层2为透明热固性粉末涂料层，并在透明热固性粉末涂料层中设有夜光粉3。
一种夜光珍珠的加工工艺，包括珍珠本体1，该工艺包括以下步骤：
(1)、对珍珠本体1进行烘干，烘干温度为100℃，并对其保温18小时；
(2)、在透明热固性粉末涂料中添加夜光粉，并对其搅拌混合，其中透明热固性粉末涂料含90％(重量比)，夜光粉含10％(重量比)；
(3)、经搅拌混合后的涂料通过静电喷塑机均匀的喷涂到经烘干后的珍珠本体1表面，将珍珠本体1完全包裹；
(4)、将珍珠本体1包裹后，放入烘箱内烘烤，恒温为138℃，经搅拌混合的涂料被加热烘烤，使其熔融流平固化，固化时间为15分钟，固化后在珍珠本体1表面形成一涂膜层，也就是透明发光层；
(5)、经烘烤后，拿出自然冷却，即为成品。
所述步骤3中经烘干后的珍珠本体放置在金属挂件上，经搅拌混合的涂料通过静电喷塑机均匀喷涂到经烘干后的珍珠本体表面，这时通过静电喷塑机使涂料带有静电，金属挂件的设置又可使珍珠本体表面产生电荷，并与涂料中的电荷极性相反，因此在静电作用下，涂料会均匀的吸附于珍珠本体表面，同时，随着喷上的涂料增多，电荷积聚也越多，当达到一定厚度时，由于产生静电排斥作用，便不继续吸附，从而使珍珠本体表面形成一定厚度且均匀的粉状涂层，经烘烤流平固化，形成的透明发光层平整光亮、厚度均匀，在夜光粉发出的光线折射下更能衬托出珍珠本体的色泽。
本发明所述透明热固性粉末涂料是采用环氧树脂及特别助剂，以特殊配方加工而成，本申请人可在市场上购得，它具有光泽度、透明度高；耐刮擦、耐酸碱、耐污染、冲击性好、硬度较高等优点。
按上述结构以及工艺所得夜光珍珠既可串接成项链使用，又可应用于首饰等装饰品上，在夜间，也就是光线较暗的地方发出微光，在光线的折射下衬托出珍珠本体的色泽，使佩带者在夜间也能突显珍珠装饰效果。
实施例2：参照图1，一种夜光珍珠，包括珍珠本体1，在珍珠本体1表面包裹着一透明发光层2，该透明发光层2为透明热固性粉末涂料层，并在透明热固性粉末涂料层中设有夜光粉3。
一种夜光珍珠的加工工艺，包括珍珠本体1，该工艺包括以下步骤：
(1)、对珍珠本体1进行烘干，烘干温度为110℃，并对其保温20小时；
(2)、在透明热固性粉末涂料中添加夜光粉，并对其搅拌混合，其中透明热固性粉末涂料含94％(重量比)，夜光粉含6％(重量比)；
(3)、经搅拌混合后的涂料通过静电喷塑机均匀的喷涂到经烘干后的珍珠本体1表面，将珍珠本体1完全包裹；
(4)、将珍珠本体1包裹后，放入烘箱内烘烤，恒温为140℃，经搅拌混合的涂料被加热烘烤，使其熔融流平固化，固化时间为20分钟，固化后在珍珠本体1表面形成一涂膜层，也就是透明发光层；
(5)、经烘烤后，拿出自然冷却，即为成品。
所述步骤3中经烘干后的珍珠本体放置在金属挂件上，经搅拌混合的涂料通过静电喷塑机均匀喷涂到经烘干后的珍珠本体表面，这时通过静电喷塑机使涂料带有静电，金属挂件的设置又可使珍珠本体表面产生电荷，并与涂料中的电荷极性相反，因此在静电作用下，涂料会均匀的吸附于珍珠本体表面，同时，随着喷上的涂料增多，电荷积聚也越多，当达到一定厚度时，由于产生静电排斥作用，便不继续吸附，从而使珍珠本体表面形成一定厚度且均匀的粉状涂层，经烘烤流平固化，形成的透明发光层平整光亮、厚度均匀，在夜光粉发出的光线折射下更能衬托出珍珠本体的色泽。
本发明所述透明热固性粉末涂料是采用环氧树脂及特别助剂，以特殊配方加工而成，本申请人可在市场上购得，它具有光泽度、透明度高；耐刮擦、耐酸碱、耐污染、冲击性好、硬度较高等优点。
按上述结构以及工艺所得夜光珍珠既可串接成项链使用，又可应用于首饰等装饰品上，在夜间，也就是光线较暗的地方发出微光，在光线的折射下衬托出珍珠本体的色泽，使佩带者在夜间也能突显珍珠装饰效果。
实施例3：参照图1，一种夜光珍珠，包括珍珠本体1，在珍珠本体1表面包裹着一透明发光层2，该透明发光层2为透明热固性粉末涂料层，并在透明热固性粉末涂料层中设有夜光粉3。
一种夜光珍珠的加工工艺，包括珍珠本体1，该工艺包括以下步骤：
(1)、对珍珠本体1进行烘干，烘干温度为120℃，并对其保温22小时；
(2)、在透明热固性粉末涂料中添加夜光粉，并对其搅拌混合，其中透明热固性粉末涂料含97％(重量比)，夜光粉含3％(重量比)；
(3)、经搅拌混合后的涂料通过静电喷塑机均匀的喷涂到经烘干后的珍珠本体1表面，将珍珠本体1完全包裹；
(4)、将珍珠本体1包裹后，放入烘箱内烘烤，恒温为142℃，经搅拌混合的涂料被加热烘烤，使其熔融流平固化，固化时间为25分钟，固化后在珍珠本体1表面形成一涂膜层，也就是透明发光层；
(5)、经烘烤后，拿出自然冷却，即为成品。
所述步骤3中经烘干后的珍珠本体放置在金属挂件上，经搅拌混合的涂料通过静电喷塑机均匀喷涂到经烘干后的珍珠本体表面，这时通过静电喷塑机使涂料带有静电，金属挂件的设置又可使珍珠本体表面产生电荷，并与涂料中的电荷极性相反，因此在静电作用下，涂料会均匀的吸附于珍珠本体表面，同时，随着喷上的涂料增多，电荷积聚也越多，当达到一定厚度时，由于产生静电排斥作用，便不继续吸附，从而使珍珠本体表面形成一定厚度且均匀的粉状涂层，经烘烤流平固化，形成的透明发光层平整光亮、厚度均匀，在夜光粉发出的光线折射下更能衬托出珍珠本体的色泽。
本发明所述透明热固性粉末涂料是采用环氧树脂及特别助剂，以特殊配方加工而成，本申请人可在市场上购得，它具有光泽度、透明度高；耐刮擦、耐酸碱、耐污染、冲击性好、硬度较高等优点。
按上述结构以及工艺所得夜光珍珠既可串接成项链使用，又可应用于首饰等装饰品上，在夜间，也就是光线较暗的地方发出微光，在光线的折射下衬托出珍珠本体的色泽，使佩带者在夜间也能突显珍珠装饰效果。
Claims (4)
1.一种夜光珍珠，包括珍珠本体(1)，其特征在于：在珍珠本体(1)表面包裹着一透明发光层(2)。
2.如权利要求1所述的夜光珍珠，其特征在于：所述透明发光层(2)为透明热固性粉末涂料层，并在透明热固性粉末涂料层中设有夜光粉。
3.一种夜光珍珠的加工工艺，包括珍珠本体(1)、透明热固性粉末涂料，其特征在于：该工艺包括以下步骤：
(1)、对珍珠本体(1)进行烘干，烘干温度为100℃～120℃，并对其保温18～22小时；
(2)、在透明热固性粉末涂料中添加夜光粉，并对其搅拌混合，其中透明热固性粉末涂料含90％～97％(重量比)，夜光粉含3％～10％(重量比)；
(3)、经搅拌混合后的涂料均匀的喷涂到经烘干后的珍珠本体(1)表面，将珍珠本体(1)完全包裹；
(4)、将珍珠本体(1)包裹后，放入烘箱内烘烤，恒温为138℃～142℃，经搅拌混合的涂料被加热烘烤，使其熔融流平固化，流平固化时间为15～25分钟，流平固化后在珍珠本体(1)表面形成一涂膜层，也就是透明发光层；
(5)、经烘烤后，拿出自然冷却，即为成品。
4.如权利要求3所述的夜光珍珠的加工工艺，其特征在于：所述步骤3中经烘干后的珍珠本体放置在金属挂件上，经搅拌混合的涂料通过静电喷塑机均匀喷涂到经烘干后的珍珠本体(1)表面，在静电作用下，涂料会均匀的吸附于珍珠本体(1)表面，形成粉状涂层。