CN1066694A - 现场冷拌填铺固化桥梁伸缩缝 - Google Patents
现场冷拌填铺固化桥梁伸缩缝 Download PDFInfo
- Publication number
- CN1066694A CN1066694A CN 92103722 CN92103722A CN1066694A CN 1066694 A CN1066694 A CN 1066694A CN 92103722 CN92103722 CN 92103722 CN 92103722 A CN92103722 A CN 92103722A CN 1066694 A CN1066694 A CN 1066694A
- Authority
- CN
- China
- Prior art keywords
- bridge
- component
- shop
- solidifying
- expansion joint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种现场冷拌填铺固化桥梁伸缩缝，在布设桥梁
伸缩缝处切出铺装槽，在槽底铺设调平层，调平层上
安装跨缝装置，在跨缝装置的上面铺设由双组分粘结
料(甲组分为聚氨酯，乙组分为煤焦油加硫化交联剂
MOCA)、橡胶粉和矿料组成的弹性混合料层，表面
涂刷有表面涂层。这种桥梁伸缩缝具有结构简单合
理、性能优良、施工方便、成本低等优点，便于推广应
用。
Description
本发明属于桥梁伸缩缝的连接技术领域。
目前桥梁伸缩缝的结构形式可分为钢板式、橡胶式、钢板橡胶组合式和橡胶沥青深埋式四种。前三种的平整度尚好，能满足变形要求，但均属装配类型，其构件均需在工厂预先加工制造，对加工精度要求高，安装也复杂，需要用混凝土浇注在桥面铺装层中固定，工期长，而且造价高，采用橡胶极易老化，因而造成松动脱落，直接影响行车，此外维修和更换也十分困难。第四种橡胶沥青深埋式伸缩缝，其变形量小，仅适用于跨径较小的桥梁和气温较高的地区。由于沥青属于热塑性材料，因此很难保证伸缩缝在夏季不出现拥起，在冬季不发生开裂。路面的平整度也差。
本发明的目的在于克服上述四种结构形式的桥梁伸缩缝的缺点，提供一种结构简单合理、性能优良、应用广泛的桥梁伸缩缝结构形式。
为达到上述目的，本发明采用的技术方案是：在布设桥梁伸缩缝处切出铺装槽，在槽底铺设调平层，跨缝装置安装在调平层上，在跨缝装置的上面铺设由双组分粘结料、橡胶粉和矿料组成的弹性混合料层，表面涂刷有表面涂层。
本发明弹性混合料层所采用的双组分粘结料是由甲、乙两组分混合而成，其中甲组分为聚氨酯，乙组分为煤焦油加硫化交联剂MOCA（3，3-二氯-4，4-二苯基甲烷二胺）。MOCA含量为煤焦油的4%。
本发明的双组分粘结料按下列比例混合：
在双组分粘结料中，甲组分占30～35%，乙组分占70～65%。
本发明与传统的几种结构形式桥梁伸缩缝相比，具有以下优点：
1、粘结性能好，与混凝土、金属、矿料等有极强的粘结力，能与桥面铺装层连成整体，防水性能好。
2、延伸率大，弹性、韧性和耐磨性较佳，能满足大跨径桥梁的伸缩变形要求。抗拉、抗压强度高，能满足行车舒适的要求。
3、高、低温性能好，高温不发软，不拥起;低温不变脆、不开裂。
4、结构简单、施工方便，在常温下拌和、摊铺、固化。
5、固化时间短，2～4小时即可开放交通。
6、适应性强，桥面铺装层无论是水泥混凝土还是沥青混凝土均适用。
7、维修和更换方便，费用低。
图1是本发明的双层结构图。
下面结合附图和实施例对本发明及其施工方法作进一步详细说明。
在图1所示的双层结构中，在桥梁伸缩缝2处的桥面铺装层8上面切割出铺装槽9，在铺装槽9的底部用快凝沙浆或细粒径弹性混合料铺设调平层3，使得跨缝钢板4能平稳地安置在桥梁主梁1上。在跨缝钢板4上铺设粗粒径弹性混合料层5。在粗粒径弹性混合料层5的上面铺设细粒径弹性混合料层6，其厚度为4～6厘米，表面涂刷一层2毫米厚的双组分粘结料，构成表面涂层7。
本实施例所用的粗粒径弹性混合料的配比是：15～20毫米的单一级配矿料占88～90%、双组分粘结料占12～10%。细粒径弹性混合料的配比是：2.5～5毫米的单一级配砂砾占75%、2.5～3.0毫米的橡胶粉占10%、双组分粘结料占15%。
本实施例的施工方法为：
1、用混凝土切割机在桥梁伸缩缝2处将桥面铺装层8切割出铺装槽9，用钢刷、砂纸打磨铺装槽9的两侧，并用气泵吹去铺装槽9两侧和底部的浮土、灰尘。
2、用快凝砂浆或细粒径弹性混合料在铺装槽9的底部铺设调平层3。
3、将跨缝钢板4安装在调平层3上。
4、在铺装槽9的两侧均匀地涂刷上一层双组分粘结料，使弹性混合料能与桥面铺装层8牢固地粘结在一起。
5、先将拌制好的粗粒径弹性混合料按量填入铺装槽9内的跨缝钢板4的上面，表面刮平，再将细粒径弹性混合料填入铺装槽9内的粗粒径弹性混合料层5的上面，使其高出桥面1.5厘米左右，表面刮平。
6、用4吨左右的压路机反复碾压数次使得已填铺的桥梁伸缩缝与桥面齐平。经2～4小时固化后，再在其表面涂刷一层双组分粘结料，固化后即可开放交通。
根据上述原理亦可将现场冷拌填铺固化桥梁伸缩缝设计成单层结构。
在图1所示的双层结构中，在铺装槽9内跨缝钢板4上面填铺的弹性混合料不再分成两层，而只填一层配比另行设计的弹性混合料，该单层结构的其它组成和施工方法与双层结构相同。
Claims (2)
1、一种现场冷拌填铺固化桥梁伸缩缝，在布设桥梁伸缩缝处切出铺装槽，在槽底铺设调平层，调平层上安装跨缝装置，在跨缝装置的上面铺设弹性混合料层和表面涂层，其特征在于：上述弹性混合料层是由双组分粘结料、橡胶粉和矿料组成。
2、按照权利要求1所述的现场冷拌填铺固化桥梁伸缩缝，其特征在于所说的双组分粘结料是由甲、乙两组分混合而成，甲组分为聚氨酯、乙组分为煤焦油加硫化交联剂MOCA（3，3-二氯-4，4-二苯基甲烷二胺）。