CN106637180A - 一种银器发黑泡沫剂及其制备方法 - Google Patents
一种银器发黑泡沫剂及其制备方法 Download PDFInfo
- Publication number
- CN106637180A CN106637180A CN201710004779.8A CN201710004779A CN106637180A CN 106637180 A CN106637180 A CN 106637180A CN 201710004779 A CN201710004779 A CN 201710004779A CN 106637180 A CN106637180 A CN 106637180A
- Authority
- CN
- China
- Prior art keywords
- parts
- foaming agent
- silverware
- sodium
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种银器发黑泡沫剂，其包括以下重量份的组分：二巯基丙醇3‑5份，硫化钠2‑5份，次亚磷酸钠1‑3份，鞣花酸1‑2份，松醇油12‑15份，全氟辛烷磺酸钾12‑15份，水20‑25份，其制备方法为：将所述二巯基丙醇和松醇油在容器中搅拌混合，再加入全氟辛烷磺酸钾和水，搅拌15‑20min，最后加入所述硫化钠、次亚磷酸钠和鞣花酸，搅拌5‑10min即可。本发明泡沫剂使用方便，发黑效果好且储存稳定。
Description
技术领域
本发明涉及特色银器领域，具体涉及一种银器发黑泡沫剂及其制备方法。
背景技术
乌银是在银首饰上把银、硫的混合物融化，并以玻璃质状态形成覆盖层。乌银覆盖层疏松乌黑，与白银的光洁银白形成鲜明对比，产生特殊的视觉效果。由于经过了特殊的防旧处理，乌银首饰不仅长期不变色，表面硬度也大大增强，别具一格的质感和色泽，使这种首饰粗犷而古朴，受到很多时尚人士的喜爱。
现有技术制作乌银大多工艺复杂，成本较高，寻找一些简便可行且无污染的方法制作乌银成为许多科研工作者的研究对象，如中国专利申请201510023846.1公开了一种银器发黑剂，包括硫化钠1～3份，蛋氨酸2～5份，硫脲1～3份，氯化铵或硫酸铵1～5份，柠檬酸钠1～5份，硫酸钠10～20份，六偏磷酸钠1～2，十二烷基硫酸钠0.1～0.2份，该银器发黑剂为粉末剂，使用时需加水溶解成25～35％的水溶液，使用稍显不便。
发明内容
基于以上技术现状，本发明的目的是提供一种使用方便、发黑效果好且储存稳定的银器发黑泡沫剂，并进一步提供其制备方法。
本发明采用以下技术方案：
一种银器发黑泡沫剂，其包括以下重量份的组分：二巯基丙醇3-5份，硫化钠2-5份，次亚磷酸钠1-3份，鞣花酸1-2份，松醇油12-15份，全氟辛烷磺酸钾12-15份，水20-25份。
优选地，所述各组分的重量份数为：二巯基丙醇3份，硫化钠3份，次亚磷酸钠2份，鞣花酸1份，松醇油15份，全氟辛烷磺酸钾15份，水25份。
所述的银器发黑泡沫剂的制备方法为：将所述二巯基丙醇和松醇油在容器中搅拌混合，再加入全氟辛烷磺酸钾和水，搅拌15-20min，最后加入所述硫化钠、次亚磷酸钠和鞣花酸，搅拌5-10min即可。
优选地，所述搅拌的转速为150-200rpm。
本发明的有益效果为：
本发明中二巯基丙醇和鞣花酸对银单质具有强结合力，可使银单质失去电子成为银离子，并进一步与硫化钠反应生成硫化银而呈现出黑色，次亚磷酸钠可在硫化银表面形成镀层，使银器表面黑亮有光泽，并使生成的硫化银稳定附着在银器表面，不易脱落。松醇油和全氟辛烷磺酸钾在水体系中可形成稳定细腻的泡沫，使各组分均匀分散于体系中，储存稳定，50℃下储存30d或常温下储存12个月，性状及使用效果均基本无变化。
具体实施方式
下面用具体实施例来对本发明的技术方案进行详细说明。
实施例1
一种银器发黑泡沫剂，包括以下重量份的组分：二巯基丙醇3份，硫化钠3份，次亚磷酸钠2份，鞣花酸1份，松醇油15份，全氟辛烷磺酸钾15份，水25份。
所述银器发黑泡沫剂的制备方法为：将所述二巯基丙醇和松醇油在容器中搅拌混合，再加入全氟辛烷磺酸钾和水，200rpm搅拌15min，最后加入所述硫化钠、次亚磷酸钠和鞣花酸，搅拌150rpm 10min即可。
使用时，将本发明泡沫剂直接均匀涂抹于需要处理的银器表面，等待5分钟，银器表面即变黑，再用清水冲洗干净即可。
实施例2
一种银器发黑泡沫剂，包括以下重量份的组分：二巯基丙醇4份，硫化钠5份，次亚磷酸钠1份，鞣花酸1份，松醇油12份，全氟辛烷磺酸钾12份，水20份。
所述银器发黑泡沫剂的制备方法为：将所述二巯基丙醇和松醇油在容器中搅拌混合，再加入全氟辛烷磺酸钾和水，150rpm搅拌20min，最后加入所述硫化钠、次亚磷酸钠和鞣花酸，200rpm搅拌5min即可。
使用时，将本实施例泡沫剂直接涂抹于需要处理的银器表面，等待7分钟，银器表面即变黑，再用清水冲洗干净即可。
实施例3
一种银器发黑泡沫剂，包括以下重量份的组分：二巯基丙醇5份，硫化钠2份，次亚磷酸钠3份，鞣花酸2份，松醇油13份，全氟辛烷磺酸钾13份，水22份。
所述银器发黑泡沫剂的制备方法为：将所述二巯基丙醇和松醇油在容器中搅拌混合，再加入全氟辛烷磺酸钾和水，200rpm搅拌15min，最后加入所述硫化钠、次亚磷酸钠和鞣花酸，200rpm搅拌10min即可。
使用时，将本实施例泡沫剂直接涂抹于需要处理的银器表面，等待8分钟，银器表面即变黑，再用清水冲洗干净即可。
Claims (4)
1.一种银器发黑泡沫剂，其特征在于：其包括以下重量份的组分：二巯基丙醇3-5份，硫化钠2-5份，次亚磷酸钠1-3份，鞣花酸1-2份，松醇油12-15份，全氟辛烷磺酸钾12-15份，水20-25份。
2.根据权利要求1所述的银器发黑泡沫剂，其特征在于：所述各组分的重量份数为：二巯基丙醇3份，硫化钠3份，次亚磷酸钠2份，鞣花酸1份，松醇油15份，全氟辛烷磺酸钾15份，水25份。
3.权利要求1或2所述的银器发黑泡沫剂的制备方法，其特征在于：将所述二巯基丙醇和松醇油在容器中搅拌混合，再加入全氟辛烷磺酸钾和水，搅拌15-20min，最后加入所述硫化钠、次亚磷酸钠和鞣花酸，搅拌5-10min即可。
4.根据权利要求3所述的方法，其特征在于：所述搅拌的转速为150-200rpm。