CN106590512B - 一种紫外及湿气双重固化触摸屏粘胶剂 - Google Patents
一种紫外及湿气双重固化触摸屏粘胶剂 Download PDFInfo
- Publication number
- CN106590512B CN106590512B CN201510669571.9A CN201510669571A CN106590512B CN 106590512 B CN106590512 B CN 106590512B CN 201510669571 A CN201510669571 A CN 201510669571A CN 106590512 B CN106590512 B CN 106590512B
- Authority
- CN
- China
- Prior art keywords
- touch screen
- ultraviolet
- dual cure
- moisture
- moisture dual
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种紫外及湿气双重固化触摸屏粘胶剂,其由以下重量百分比的原料组成:聚氨酯丙烯酸酯:50~75%;丙烯酸活性稀释剂:15~40%;硅烷偶联剂:3~5%;光引发剂:1~5%;触变剂:1~5%;抗氧化剂:0.5~1%;催化剂:0.5~1%。本发明的紫外及湿气双重固化触摸屏粘胶剂采用可湿气固化的聚氨酯丙烯酸酯为主原料,不仅可通过UV光固化,对于UV光照射不到的部位,还可通过湿气固化,保证固化完全,提高了产品的质量。
Description
技术领域
本发明涉及一种紫外及湿气双重固化触摸屏粘胶剂。
背景技术
触摸屏在组装过程中一般采用的粘接材料为双面胶带,先利用模具将胶带裁剪成适合的形状,再进行粘接。由于其使用简便,无需后端的固化流程,深受触摸屏生产厂家的喜爱。然而,随着触摸屏产业的扩大和对品质的要求越来越高,双面胶带的缺陷逐渐突显出来。首先是透光率的问题,从微观的角度来看双面胶带由三个界面组成,光在遇到界面时会发生折射,故而大大影响了触摸屏的透光率,从而影响终端电子产品的清晰度。其次是返修困难,成品率不高。第三是无法实现高效率的机械操作。
触摸屏粘接胶水的出现有效的解决了上述问题。首先,胶水层在固化后只有一个界面,可以大大提升产品的透光率。其次,触摸屏粘接胶在生产过程中可以采用先点固化初步固定,检测性能后再完全固化,提升了成品率。再次,胶水可以和专门的机械配合,能够大幅提高生产效率。越来越多的厂家开始认识到触摸屏粘接胶水的优势,因此国内外对触摸屏粘接胶的需求也在日益增加。
目前市场上比较成熟的触摸屏粘胶剂多为单UV固化型的,在实际生产过程中,总会有一些区域无法照射到紫外光即所谓的阴影部分,在这些无法照射到UV光的区域,胶水会出现固化不良的现象,甚至于不能固化,这就为触摸屏的长期使用埋下了隐患。为解决此问题国内外有很多专业的粘胶剂生产厂家做了不少研究,但目前尚未取得比较完善的解决方案。因此,亟需开发一种新的触摸屏粘胶剂来解决阴影部分的固化问题。
发明内容
本发明的目的在于提供一种紫外及湿气双重固化触摸屏粘胶剂。
本发明所采取的技术方案是:
一种紫外及湿气双重固化触摸屏粘胶剂,由以下重量百分比的原料组成:
聚氨酯丙烯酸酯:50~75%;
丙烯酸活性稀释剂:15~40%;
硅烷偶联剂:3~5%;
光引发剂:1~5%;
触变剂:1~5%;
抗氧化剂:0.5~1%;
催化剂:0.5~1%。
所述聚氨酯丙烯酸酯为含异氰酸根的丙烯酸酯。
所述丙烯酸活性稀释剂为N,N二甲基丙烯酰胺、丙烯酸羟乙酯、丙烯酸羟丙酯、甲基丙烯酸羟乙酯、甲基丙烯酸羟丙酯、丙烯酸环已酯、丙烯酸异冰片酯、甲基丙烯酸异冰片酯、丙烯酸四氢呋喃酯、甲基丙烯酸四氢呋喃酯、三羟甲基丙烷二丙烯酸酯、苯氧乙基甲基丙烯酸酯中的至少一种。
所述硅烷偶联剂为KH550、KH560、KH570、KH792、DL602、DL171中的至少一种。
所述光引发剂为2-羟基-甲基苯基丙烷-1-酮、1-羟基环已基苯基甲酮、安息香双甲醚、二苯甲酮、2,4,6-三甲基苯甲酰基-二苯基氧化膦、2-甲基-1-(4-甲硫基苯基 )-2-吗啉基-1-丙酮中的至少一种。
所述触变剂为白炭黑、有机膨润土、氢化蓖麻油、聚酰胺蜡中的至少一种。
所述抗氧化剂为受阻酚类抗氧剂、亚磷酸酯类抗氧剂中的至少一种。
所述催化剂为二月桂酸二丁基锡、正硅酸甲酯、正硅酸乙酯中的至少一种。
本发明的有益效果是:本发明的紫外及湿气双重固化触摸屏粘胶剂采用可湿气固化的聚氨酯丙烯酸酯为主原料,不仅可通过UV光固化,对于UV光照射不到的部位,还可通过湿气固化,保证固化完全,提高了产品的质量。
具体实施方式
一种紫外及湿气双重固化触摸屏粘胶剂,由以下重量百分比的原料组成:
聚氨酯丙烯酸酯:50~75%;
丙烯酸活性稀释剂:15~40%;
硅烷偶联剂:3~5%;
光引发剂:1~5%;
触变剂:1~5%;
抗氧化剂:0.5~1%;
催化剂:0.5~1%。
优选的,所述聚氨酯丙烯酸酯为含异氰酸根的丙烯酸酯。
优选的,所述丙烯酸活性稀释剂为N,N二甲基丙烯酰胺、丙烯酸羟乙酯、丙烯酸羟丙酯、甲基丙烯酸羟乙酯、甲基丙烯酸羟丙酯、丙烯酸环已酯、丙烯酸异冰片酯、甲基丙烯酸异冰片酯、丙烯酸四氢呋喃酯、甲基丙烯酸四氢呋喃酯、三羟甲基丙烷二丙烯酸酯、苯氧乙基甲基丙烯酸酯中的至少一种。
优选的,所述硅烷偶联剂为KH550、KH560、KH570、KH792、DL602、DL171中的至少一种。
优选的,所述光引发剂为2-羟基-甲基苯基丙烷-1-酮、1-羟基环已基苯基甲酮、安息香双甲醚、二苯甲酮、2,4,6-三甲基苯甲酰基-二苯基氧化膦、2-甲基-1-(4-甲硫基苯基 )-2-吗啉基-1-丙酮中的至少一种。
优选的,所述触变剂为白炭黑、有机膨润土、氢化蓖麻油、聚酰胺蜡中的至少一种。
进一步优选的,所述触变剂为白炭黑。
优选的,所述抗氧化剂为受阻酚类抗氧剂、亚磷酸酯类抗氧剂中的至少一种。
进一步优选的,所述抗氧化剂为抗氧化剂264、抗氧化剂1076、抗氧化剂1010、抗氧化剂1098、抗氧化剂2246-S、抗氧化剂300、抗氧化剂KY-586、抗氧化剂Irganox1010、抗氧化剂Irganox1076、抗氧化剂Irganox1330、抗氧化剂Irganox168中的至少一种。
优选的,所述催化剂为二月桂酸二丁基锡、正硅酸甲酯、正硅酸乙酯中的至少一种。
下面结合具体实施例对本发明作进一步的解释和说明。
实施例1:
一种紫外及湿气双重固化触摸屏粘胶剂,其原料的配方组成如下表1:
表1 紫外及湿气双重固化触摸屏粘胶剂的原料配方组成:
本发明中,所述紫外及湿气双重固化触摸屏粘胶剂的制备方法为:将各原料混合分散均匀,再分装到专用的容器中,即为成品。
实施例2:
一种紫外及湿气双重固化触摸屏粘胶剂,其原料的配方组成如下表2:
表2 紫外及湿气双重固化触摸屏粘胶剂的原料配方组成:
本发明中,所述紫外及湿气双重固化触摸屏粘胶剂的制备方法为:将各原料混合分散均匀,再分装到专用的容器中,即为成品。
实施例3:
一种紫外及湿气双重固化触摸屏粘胶剂,其原料的配方组成如下表3:
表3 紫外及湿气双重固化触摸屏粘胶剂的原料配方组成:
本发明中,所述紫外及湿气双重固化触摸屏粘胶剂的制备方法为:将各原料混合分散均匀,再分装到专用的容器中,即为成品。
本发明实施例3的产品性能测试数据如表4所示。
表4 紫外及湿气双重固化触摸屏粘胶剂的性能测试数据:
上述实施例为本发明较佳的实施方式,但本发明的实施方式并不受上述实施例的限制,其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化,均应为等效的置换方式,都包含在本发明的保护范围之内。
Claims (1)
1.一种紫外及湿气双重固化触摸屏粘胶剂,其特征在于:由以下重量百分比的原料组成:聚氨酯丙烯酸酯:64.5%;N,N二甲基丙烯酰胺:18%;丙烯酸异冰片酯:5%;硅烷偶联剂KH560:5%;1-羟基环已基苯基甲酮:1%;白炭黑:5%;抗氧化剂1010:1%;二月桂酸二丁基锡:0.5%;所述聚氨酯丙烯酸酯为含异氰酸根的丙烯酸酯。