CN106494042A - 一种abs复合板材 - Google Patents

一种abs复合板材 Download PDF

Info

Publication number
CN106494042A
CN106494042A CN201611002567.8A CN201611002567A CN106494042A CN 106494042 A CN106494042 A CN 106494042A CN 201611002567 A CN201611002567 A CN 201611002567A CN 106494042 A CN106494042 A CN 106494042A
Authority
CN
China
Prior art keywords
abs
composite boards
absorbing layer
abs composite
sound absorbing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611002567.8A
Other languages
English (en)
Inventor
徐志明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Hengdaer Industrial Materials Co Ltd
Original Assignee
Suzhou Hengdaer Industrial Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Hengdaer Industrial Materials Co Ltd filed Critical Suzhou Hengdaer Industrial Materials Co Ltd
Priority to CN201611002567.8A priority Critical patent/CN106494042A/zh
Publication of CN106494042A publication Critical patent/CN106494042A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种ABS复合板材，其特征在于，包括ABS板层和吸音层，所述吸音层上、下两面均与ABS板层内表面相连接，所述ABS板层外表面均复合有ASA材料层；本发明所述一种ABS复合板材通过ASA材料层的设置，具有耐候、抗冲击特点，户外可以使用的优点，通过吸音层的设置，一方面可加强板材的刚性，另一方面又可提供良好的吸音性和隔音性；所述一种ABS复合板材通过抗菌母粒的设置，具有抗菌性，使该板材具有一定的杀菌能力，减少细菌的滋生，起到保护人体健康的目的，可应用于医院手术室，制药工程，食品加工等建筑内墙装饰达到卫生抗菌等级。

Description

一种ABS复合板材
技术领域
本发明涉及一种板材，具体是一种新型ABS抗菌复合板材。
背景技术
传统板材，尤其是地板，木质品种居多，因其木质工艺，胶贴现状，防潮、 防菌等品质无法满足人们的需求，现在比较常用的为ABS板材，因ABS板材具有突出的美学性，流动性，韧性，尺寸稳定性和高耐热性，成为当前热门板材材料，但纯粹的ABS板仍无法满足人们日益多样化的需求，比如其不具备抗菌能力，易滋生细菌，对人体健康带来潜在威胁。
发明内容
本发明要解决的技术问题是，克服以上现有技术的缺陷，提供一种可综合ABS复合板层，含抗菌、防静电和隔音多种功能的板材。
本发明的技术方案是：一种ABS复合板材，其特征在于，包括ABS板层和吸音层，所述吸音层上、下两面均与ABS板层内表面相连接，所述ABS板层外表面均复合有ASA材料层。
进一步的，所述ABS板层由ABS树脂掺混其质量1-3％的ABS抗菌母粒后加工而成，增强抗菌性。
进一步的，所述ABS板层的厚度为3～15mm。
进一步的，所述吸音层包括横板和纵板，所述横板和纵板交错排列形成网格，在网格中填充有隔音棉块，可达到良好的隔音作用。
进一步的，所述横板和纵板设置有加强筋。
进一步的，所述吸音层为由纤维和粉末构成的多孔结构。
进一步的，所述纤维为改性聚丙烯纤维 PP、改性聚酰胺纤维 PA、改性聚对苯二甲酸乙二醇纤维 PET 中的一种或几种聚合物纤维的混合物。
进一步的，所述粉末为玻璃纤维、二氧化硅、二氧化钛和滑石粉中的一种或几种的混合物，通过多孔结构可达到良好的吸音和隔音作用，同时，热塑性树脂纤维与增强填料可加强板材的刚性。
进一步的，所述ASA材料层的上表面设置有防静电镀膜。
本发明所达到的有益效果：本发明所述一种ABS复合板材通过ASA材料层的设置，具有耐候、抗冲击特点，户外可以使用的优点，通过吸音层的设置，一方面可加强板材的刚性，另一方面又可提供良好的吸音性和隔音性；所述一种ABS复合板材通过抗菌母粒的设置，具有抗菌性，使该板材具有一定的杀菌能力，减少细菌的滋生，起到保护人体健康的目的，可应用于医院手术室，制药工程，食品加工等建筑内墙装饰达到卫生抗菌等级；本发明所述一种ABS复合板材通过防静电镀膜的设置，不会产生静电，起到有效避免因静电作用吸尘而造成的灰尘及细菌积聚。
附图说明
图1是本发明的结构示意图。
具体实施方式
下面结合附图对本发明作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
如图1所示，一种ABS复合板材，其特征在于，包括ABS板层2和吸音层1，所述吸音层1上、下两面均与ABS板层2内表面相连接，所述ABS板层外表面均复合有ASA材料层3，所述ABS板层2由ABS树脂掺混其质量2％的ABS抗菌母粒后加工而成，增强抗菌性，所述ABS板层2的厚度为10mm，所述吸音层1包括横板和纵板，所述横板和纵板交错排列形成网格，在网格中填充有隔音棉块，可达到良好的吸音、隔音作用，所述横板和纵板设置有加强筋，所述ASA材料层3的上表面设置有防静电镀膜。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变形，这些改进和变形也应视为本发明的保护范围。

Claims (9)

1.一种ABS复合板材，其特征在于，包括ABS板层和吸音层，所述吸音层上、下两面均与ABS板层内表面相连接，所述ABS板层外表面均复合有ASA材料层。
2.根据权利要求1所述的一种ABS复合板材，其特征是，所述ABS板层由ABS树脂掺混其质量1～3％的ABS抗菌母粒后加工而成。
3.根据权利要求1所述的一种ABS复合板材，其特征是，所述ABS板层的厚度为3～15mm。
4.根据权利要求1所述的一种ABS复合板材，其特征是，所述吸音层包括横板和纵板，所述横板和纵板交错排列形成网格，在网格中填充有隔音棉块。
5.根据权利要求4所述的一种ABS复合板材，其特征是，所述横板和纵板设置有加强筋。
6.根据权利要求1所述的一种ABS复合板材，其特征是，所述吸音层为由纤维和粉末构成的多孔结构。
7.根据权利要求6所述的一种ABS复合板材，其特征是，所述纤维为改性聚丙烯纤维PP、改性聚酰胺纤维 PA、改性聚对苯二甲酸乙二醇纤维 PET 中的一种或几种聚合物纤维的混合物。
8.根据权利要求6所述的一种ABS复合板材，其特征是，所述粉末为玻璃纤维、二氧化硅、二氧化钛和滑石粉中的一种或几种的混合物。
9.根据权利要求1所述的一种ABS复合板材，其特征是，所述ASA材料层的上表面设置有防静电镀膜。
CN201611002567.8A 2016-11-15 2016-11-15 一种abs复合板材 Pending CN106494042A (zh)