CN106467361A - 一种无铅易洁日用瓷及其制法 - Google Patents

一种无铅易洁日用瓷及其制法 Download PDF

Info

Publication number
CN106467361A
CN106467361A CN201510592963.XA CN201510592963A CN106467361A CN 106467361 A CN106467361 A CN 106467361A CN 201510592963 A CN201510592963 A CN 201510592963A CN 106467361 A CN106467361 A CN 106467361A
Authority
CN
China
Prior art keywords
glaze
household china
oxide
china
base substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510592963.XA
Other languages
English (en)
Other versions
CN106467361B (zh
Inventor
刘云龙
刘安琪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZIBO LONGJIA INDUSTRY TRADE Co.,Ltd.
Original Assignee
Zibo Gongxiang Yangguang Ceramic Art Research Center
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zibo Gongxiang Yangguang Ceramic Art Research Center filed Critical Zibo Gongxiang Yangguang Ceramic Art Research Center
Priority to CN201510592963.XA priority Critical patent/CN106467361B/zh
Publication of CN106467361A publication Critical patent/CN106467361A/zh
Application granted granted Critical
Publication of CN106467361B publication Critical patent/CN106467361B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种无铅易洁日用瓷及其制法，属于日用瓷技术领域，包括坯体和覆盖在坯体上的釉面，其特征是，所述釉面是采用包括如下重量份的原料制成的熔块釉：长石20‑40，焦宝石10‑20，熟滑石10‑20，大同土5‑10，钟乳石1‑2，石英1‑3，钛酸钡1‑2，氧化铋1‑2，光泽剂0.1‑0.5，改进剂0.1‑0.5；所述光泽剂是氧化镧；所述改进剂是氧化钇、氧化铈、氧化钐按照重量比1:1:1组成的混合物；或者所述改进剂是氧化铈、氧化钐和钆按照重量比1:1:1组成的混合物；所述坯体为长石质瓷或滑石质瓷。本发明采用无铅陶瓷釉配方、优化制作工艺，得到了表面超光滑的日用瓷，该日用瓷具有优良的抗污性能和易洁性能，且铅镉等重金属含量为国家标准的十分之一。

Description

一种无铅易洁日用瓷及其制法
技术领域
本发明涉及日用瓷技术领域，具体是一种无铅易洁日用瓷及其制法。
背景技术
日用陶瓷在人们日常生活中使用频繁，尤其是涉及人们餐饮过程中。日用瓷的基本形式是：陶瓷坯体，其外表面覆盖有釉面。
釉面中铅镉等重金属容易超标，对人体健康危害较大。随着人们对健康越来越关注，人们对陶瓷釉面中铅、镉溶出量越来越关注。现有技术的无铅陶瓷釉Zn含量过高，且其含Bi2O3，该物质有一定毒性且价格高。
另外，日用瓷作为日常用具还存在清洁困难问题，在餐饮行业，清洗劳动强度很大，在日常使用中，一些特殊器型，例如：茶壶，清洁比较困难。
陶瓷表面沾染污垢的原因是：微观结构上，陶瓷表面存在凹凸不平以及微小的针孔或气孔，在陶瓷的使用过程中很容易接触到环境中的污染物，这些污染物在范德华力、毛细管力、氢键等多种物理或化学力的作用下，很容易积聚在表面的凹凸处或进入微孔中，对陶瓷的表面造成污染。
为提高陶瓷表面的抗污性能以及使陶瓷易于清洁，现有技术常采用以下技术手段：
1)通过在陶瓷表面覆盖一层具有憎水性质的有机硅氧烷薄膜，使污染物在陶瓷表面无法停留；
2)陶瓷表面超级光滑技术，即：通过改变陶瓷表面成分、烧结工艺等方 法，使陶瓷形成致密的表面，减少陶瓷表面微观缺陷。
3)采用陶瓷表面涂膜技术，在陶瓷表面涂敷具有光催化作用的薄膜，利用薄膜在紫外光的照射下可以通过光催化反应来分解陶瓷表面的有机污染物，以及光催化薄膜可以在陶瓷表面形成连续的亲水区，使陶瓷表面覆盖上一层水膜，自动清洗掉降解产物，从而达到陶瓷表面的易清洁效果。
4)在提高釉浆细度、降低表面粗糙度的同时，在坯体和釉层之间增加一层金属离子层，当污物接触到壁的瞬间，离子力层即时发生作用，将其弹出，不让污染物附上。
发明内容
本发明提供一种无铅易洁日用瓷及其制法，其采用无铅陶瓷釉配方、优化制作工艺，得到了表面超光滑的日用瓷，该日用瓷具有优良的抗污性能和易洁性能，且铅镉等重金属含量为国家标准的十分之一。
本发明具体采用的技术方案是：
一种无铅易洁日用瓷，包括坯体和覆盖在坯体上的釉面，其特征是，所述釉面是采用包括如下重量份的原料制成的熔块釉：
长石20-40，焦宝石10-20，熟滑石10-20，大同土5-10，钟乳石1-2，石英1-3，钛酸钡1-2，氧化铋1-2，光泽剂0.1-0.5，改进剂0.1-0.5；
所述光泽剂是氧化镧；
所述改进剂是氧化钇、氧化铈、氧化钐按照重量比1:1:1组成的混合物；或者所述改进剂是氧化铈、氧化钐和钆按照重量比1:1:1组成的混合物；
所述坯体为长石质瓷或滑石质瓷。
本发明中，所述坯体材质可为现有技术的长石质瓷或滑石质瓷，
其中，长石质瓷是以长石为熔剂，原料采用长石、石英和高岭土为主，其材质化学组成以氧化物质量百分比计为：SiO265-75％，Al2O320～28％，K2O+Na2O不低于2.5％，其他为不可避免杂质。
其中，滑石质瓷的坯料配方是以滑石、粘土和长石为主要原料，其材质化学组成以氧化物质量百分比计为：SiO263-66％，Al2O37～14％，MgO 15～24％，其他为不可避免杂质。
为得到阳黄色的釉面，所述釉面原料中还添加有氧化镨；
为得到绿色的釉面，所述釉面原料中还添加有氧化镨和五氧化二钒，二者添加重量比可根据实际颜色需要调整，一般是1：3～10。
为得到紫色的釉面，所述釉面原料中还添加有氧化镨和硒化锌，二者添加重量比可根据实际颜色需要调整，一般是1：3～10。
根据需要，本发明还可以添加其他的无机颜料，以使釉面着色，所加无机颜料需耐受烧成最高温。
申请人特别指出，釉料中的着色剂添加量本领域技术人员可通过颜色的具体要求进行调整。
一种无铅易洁日用瓷的制法，其特征是，包括如下步骤：
1)坯料的制备；
2)釉料的制备：按照现有技术制成釉料，其中，釉料的平均细度为200-400目。
3)等静压成型：在真空度为0.07～0.09MPa的条件下等静压成型；
4)干燥、修坯；
5)坯体内外施釉；
6)高温釉烧：烧成制度是：
常温至300℃ 升温速率为50℃/h；
300℃至900℃ 升温速率为60℃/h；
900℃至1300℃ 升温速率为100℃/h；
在最高温1300℃保持0.5～1h；
7)自然降至常温，得制品
与现有技术相比，本发明的优点是：
1)本发明通过优化了无铅陶瓷釉配方和工艺，得到了表面超光滑的日用瓷，该日用瓷具有优良的抗污性能和易洁性能，且铅镉等重金属含量为国家标准的十分之一。
2)本发明釉料中的光泽剂，可提高釉面的光滑度和光亮度，降低污物的附着力；改进剂可使釉面在烧成过程中形成更多致密晶相，且能提高釉面的耐酸碱性能。
3)本发明等静压成型可最大程度降低坯体中残留空气，降低产生气泡、爆裂或开裂的可能性；
4)与现有日用瓷烧成相比，本发明烧成速率慢，保证在烧成蒸发期、晶型转变期、成瓷期气体缓慢排出，制得产品表面光滑度远远高于现有技术。
具体实施方式
实施例
一种无铅易洁日用瓷的制法，包括如下步骤：
1)坯料的制备；
采用市售的长石质瓷原料，或者按照现有技术配方，例如：粘土、石英、长石以2∶1∶1的比例准备坯体原料，其材质化学组成以氧化物质量百分比计为：SiO265-75％，Al2O320～28％，K2O+Na2O不低于2.5％，其他为不可避免杂质。
2)釉料的制备：按照现有技术制成釉料，其中，釉料的平均细度为200-400目
釉料配方：长石20-40，焦宝石10-20，熟滑石10-20，大同土5-10，钟乳石1-2，石英1-3，钛酸钡1-2，氧化铋1-2，氧化镧0.1-0.5，改进剂0.1-0.5，0.1-0.5份着色剂；所述改进剂是氧化钇、氧化铈、氧化钐按照重量比1:1:1组成的混合物；为得到紫色的釉面，所述着色剂是氧化镨和硒化锌，按照重量比1：3～10的混合物。
3)等静压成型：在真空度为0.07～0.09MPa的条件下等静压成型；
4)干燥、修坯；
5)坯体内外施釉；
6)高温釉烧：烧成制度是：
常温至300℃ 升温速率为50℃/h；
300℃至900℃ 升温速率为60℃/h；
900℃至1300℃ 升温速率为100℃/h；
在最高温1300℃保持0.5～1h；
7)自然降至常温，得制品。

Claims (7)

1.一种无铅易洁日用瓷，包括坯体和覆盖在坯体上的釉面，其特征是，所述釉面是采用包括如下重量份的原料制成的熔块釉：
长石20-40，焦宝石10-20，熟滑石10-20，大同土5-10，钟乳石1-2，石英1-3，钛酸钡1-2，氧化铋1-2，光泽剂0.1-0.5，改进剂0.1-0.5；
所述光泽剂是氧化镧；
所述改进剂是氧化钇、氧化铈、氧化钐按照重量比1:1:1组成的混合物；或者所述改进剂是氧化铈、氧化钐和钆按照重量比1:1:1组成的混合物；
所述坯体为长石质瓷或滑石质瓷。
2.根据权利要求1所述的无铅易洁日用瓷，其特征是，所述长石质瓷，其材质化学组成以氧化物质量百分比计为：SiO2 65-75％，Al2O3 20～28％，K2O+Na2O不低于2.5％，其他为不可避免杂质。
3.根据权利要求1所述的无铅易洁日用瓷，其特征是，所述滑石质瓷，其材质化学组成以氧化物质量百分比计为：SiO2 63-66％，Al2O3 7～14％，MgO15～24％，其他为不可避免杂质。
4.根据权利要求1所述的无铅易洁日用瓷，其特征是，所述釉面原料中还添加有氧化镨。
5.根据权利要求1所述的无铅易洁日用瓷，其特征是，所述釉面原料中还添加有氧化镨和五氧化二钒，其重量比是1：3～10。
6.根据权利要求1所述的无铅易洁日用瓷，其特征是，所述釉面原料中还添加有氧化镨和硒化锌，二者添加重量比是1：3～10。
7.一种无铅易洁日用瓷的制法，其特征是，包括如下步骤：
1)坯料的制备；
2)釉料的制备：釉料的平均细度为200-400目；
3)等静压成型：在真空度为0.07～0.09MPa的条件下等静压成型；
4)干燥、修坯；
5)坯体内外施釉；
6)高温釉烧：烧成制度是：
常温至300℃ 升温速率为50℃/h；
300℃至900℃ 升温速率为60℃/h；
900℃至1300℃ 升温速率为100℃/h；
在最高温1300℃保持0.5～1h；
7)自然降至常温，得制品。
CN201510592963.XA 2015-09-17 2015-09-17 一种无铅易洁日用瓷及其制法 Active CN106467361B (zh)