CN106396367B - 玻璃的澄清工艺 - Google Patents

玻璃的澄清工艺 Download PDF

Info

Publication number
CN106396367B
CN106396367B CN201610787192.4A CN201610787192A CN106396367B CN 106396367 B CN106396367 B CN 106396367B CN 201610787192 A CN201610787192 A CN 201610787192A CN 106396367 B CN106396367 B CN 106396367B
Authority
CN
China
Prior art keywords
glass
nitrate
parts
cooled
later
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610787192.4A
Other languages
English (en)
Other versions
CN106396367A (zh
Inventor
黄福萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi tiger glass (Group) Co., Ltd.
Original Assignee
Shanxi Tiger Glass (group) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Tiger Glass (group) Co Ltd filed Critical Shanxi Tiger Glass (group) Co Ltd
Priority to CN201610787192.4A priority Critical patent/CN106396367B/zh
Publication of CN106396367A publication Critical patent/CN106396367A/zh
Application granted granted Critical
Publication of CN106396367B publication Critical patent/CN106396367B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种玻璃的澄清工艺，包括：步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行混合，得到混合料，将混合料升温至1755～1765℃下熔融，之后再降温至1520～1530℃进行澄清，澄清20～25min，之后再升温至1620～1630℃，再降温至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸盐3～4份，氧化锡0.4～0.6份，其中，硝酸盐为由以下重量百分比计的组分组成：硝酸钠5～8％、硝酸钾5～8％、硝酸镁5～8％、硝酸铝5～8％和硝酸铵68～80％；步骤(2)玻璃液成型。本发明所述的玻璃的澄清工艺可以有效减少玻璃内的气泡含量。

Description

玻璃的澄清工艺
技术领域
本发明涉及一种玻璃的澄清工艺。
背景技术
制备玻璃的熔融阶段中会产生大量的气体。因此，气泡是一种最常见的 玻璃缺陷，会影响玻璃制品的外观、透明度、机械强度、光学均匀性等，全 世界每年由此导致的损失在数亿美元以上。随着越来越严峻的市场竞争，客 户对品质的要求也越来越高，使得所有玻璃生产厂家竭尽所能采取措施降低 气泡缺陷，最常见消除气泡的措施就是升高熔化温度和澄清温度。浮法工艺 制造的铝硅酸盐玻璃(Al2O3＞12％)时，存在熔化、澄清均化较为困难、玻筋 重、气泡缺陷多的缺点，在不添加澄清剂的状态下，一般玻璃正常熔化温度高于1540℃，澄清温度高于1640℃，才能满足熔化和澄清的需要，不仅能耗 高，还会降低窑炉耐材的寿命。
因此，在玻璃生产过程中，有必要加入澄清剂，以消除玻璃中的可见气 泡。As2O3、Sb2O3、Cl2、F2等是目前常用的优良的澄清剂，对于玻璃具有 优良的澄清效果。但是它们是非环境友好型物质，国外已禁止使用。因此研 制出一种无毒无害、且澄清效果较好的玻璃澄清剂，已成为必然趋势。
发明内容
本发明设计开发了一种澄清效果好的玻璃的澄清工艺。
本发明提供的技术方案为：
一种玻璃的澄清工艺，包括：
步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行 混合，得到混合料，将混合料升温至1755～1765℃下熔融，之后再降温至 1520～1530℃进行澄清，澄清20～25min，之后再升温至1620～1630℃，再降温 至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸 盐3～4份，氧化锡0.4～0.6份，其中，硝酸盐为由以下重量百分比计的组分 组成：硝酸钠5～8％、硝酸钾5～8％、硝酸镁5～8％、硝酸铝5～8％和硝酸铵 68～80％；
步骤(2)玻璃液成型，成型之后降温至室温，之后再升温至300～310℃， 再置于400～415℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之 后再放入400～415℃的硝酸钠熔融液中处理60～90min。
优选的是，所述的玻璃的澄清工艺中，所述步骤(1)中，将88份的原 料与6份的玻璃澄清剂混合。
优选的是，所述的玻璃的澄清工艺中，所述步骤(1)中，将混合料升温至1755～1765℃下 熔融，并维持10～15min，之后再降温。
优选的是，所述的玻璃的澄清工艺中，所述步骤(2)中，玻璃液成型， 成型之后降温至室温，之后再升温至300℃，再置于405℃的硝酸钠熔融液中 处理30min，之后取出降温至100℃，之后再放入405℃的硝酸钠熔融液中处 理60～90min。
本发明所述的玻璃的澄清工艺可以有效减少玻璃内的气泡含量。
具体实施方式
下面对本发明做进一步的详细说明，以令本领域技术人员参照说明书文 字能够据以实施。
本发明提供一种玻璃的澄清工艺，包括：
步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行 混合，得到混合料，将混合料升温至1755～1765℃下熔融，之后再降温至 1520～1530℃进行澄清，澄清20～25min，之后再升温至1620～1630℃，再降温 至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸 盐3～4份，氧化锡0.4～0.6份，其中，硝酸盐为由以下重量百分比计的组分 组成：硝酸钠5～8％、硝酸钾5～8％、硝酸镁5～8％、硝酸铝5～8％和硝酸铵 68～80％。本发明先将混合料升温至相对高的温度下熔融，之后再降温至玻璃澄清剂适宜作用的温度，可以有效促使溶解在玻璃液中的气体释放出去。而 且在澄清阶段进行至20～25min时，再将温度上升大概100℃，有助于促使小 气泡上升，并使气泡最终能够释放出去。硝酸盐可以阻止氧化锡过早的释放 出氧气。基于上述的配比，硝酸盐可以表现出良好的强氧化作用，使氧化锡 在特定的温度条件下才释放氧气，进而保证澄清的效果。
步骤(2)玻璃液成型，成型之后降温至室温，之后再升温至300～310℃， 再置于400～415℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之 后再放入400～415℃的硝酸钠熔融液中处理60～90min。成型之后再对玻璃液 进行处理，得到的玻璃的强度高。
本发明制备得到的玻璃的澄清效果好，每平方米气泡数量仅1个。且玻 璃的强度高。
本发明优选采用石英砂、碳酸钠、碳酸钙、硝酸钾以及氧化镁为原料。
优选的是，所述的玻璃的澄清工艺中，所述步骤(1)中，将88份的原 料与6份的玻璃澄清剂混合。
优选的是，所述的玻璃的澄清工艺中，所述步骤(1)中，将混合料升温至1755～1765℃下 熔融，并维持10～15min，之后再降温。
优选的是，所述的玻璃的澄清工艺中，所述步骤(2)中，玻璃液成型， 成型之后降温至室温，之后再升温至300℃，再置于405℃的硝酸钠熔融液中 处理30min，之后取出降温至100℃，之后再放入405℃的硝酸钠熔融液中处 理60～90min。
尽管本发明的实施方案已公开如上，但其并不仅仅限于说明书和实施方 式中所列运用，它完全可以被适用于各种适合本发明的领域，对于熟悉本领 域的人员而言，可容易地实现另外的修改，因此在不背离权利要求及等同范 围所限定的一般概念下，本发明并不限于特定的细节。

Claims (3)

1.一种玻璃的澄清工艺，其特征在于，包括：
步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行混合，得到混合料，将混合料升温至1755～1765℃下熔融，并维持10～15min，之后再降温至1520～1530℃进行澄清，澄清20～25min，之后再升温至1620～1630℃，再降温至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸盐3～4份，氧化锡0.4～0.6份，其中，硝酸盐为由以下重量百分比计的组分组成：硝酸钠5～8％、硝酸钾5～8％、硝酸镁5～8％、硝酸铝5～8％和硝酸铵68～80％；
步骤(2)玻璃液成型，成型之后降温至室温，之后再升温至300～310℃，再置于400～415℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入400～415℃的硝酸钠熔融液中处理60～90min。
2.如权利要求1所述的玻璃的澄清工艺，其特征在于，所述步骤(1)中，将88份的原料与6份的玻璃澄清剂混合。
3.如权利要求1所述的玻璃的澄清工艺，其特征在于，所述步骤(2)中，玻璃液成型，成型之后降温至室温，之后再升温至300℃，再置于405℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入405℃的硝酸钠熔融液中处理60～90min。
CN201610787192.4A 2016-08-31 2016-08-31 玻璃的澄清工艺 Active CN106396367B (zh)