CN106430945B - 玻璃的制备方法 - Google Patents

玻璃的制备方法 Download PDF

Info

Publication number
CN106430945B
CN106430945B CN201610787003.3A CN201610787003A CN106430945B CN 106430945 B CN106430945 B CN 106430945B CN 201610787003 A CN201610787003 A CN 201610787003A CN 106430945 B CN106430945 B CN 106430945B
Authority
CN
China
Prior art keywords
glass
parts
cooled
preparation
later
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610787003.3A
Other languages
English (en)
Other versions
CN106430945A (zh
Inventor
黄福萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Blue Dish Feather Crystal Jewelry Co., Ltd.
Original Assignee
Foshan Nanhai Blue Feather Feather Hardware Product Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Nanhai Blue Feather Feather Hardware Product Co Ltd filed Critical Foshan Nanhai Blue Feather Feather Hardware Product Co Ltd
Priority to CN201610787003.3A priority Critical patent/CN106430945B/zh
Publication of CN106430945A publication Critical patent/CN106430945A/zh
Application granted granted Critical
Publication of CN106430945B publication Critical patent/CN106430945B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种玻璃的制备方法，包括：步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行混合，得到混合料，将混合料升温至1755～1765℃下熔融，再降温至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸盐3～4份，氧化锡0.4～0.6份；步骤(2)玻璃液成型，成型之后降温至室温，之后再升温至300～310℃，再置于400～415℃的硝酸钠熔融液中处理30min。本发明所述的玻璃的制备方法可以有效减少玻璃内的气泡含量。

Description

玻璃的制备方法
技术领域
本发明涉及一种玻璃的制备方法。
背景技术
制备玻璃的熔融阶段中会产生大量的气体。因此，气泡是一种最常见的玻璃缺陷，会影响玻璃制品的外观、透明度、机械强度、光学均匀性等，全世界每年由此导致的损失在数亿美元以上。随着越来越严峻的市场竞争，客户对品质的要求也越来越高，使得所有玻璃生产厂家竭尽所能采取措施降低气泡缺陷，最常见消除气泡的措施就是升高熔化温度和澄清温度。浮法工艺制造的铝硅酸盐玻璃(Al2O3＞12％)时，存在熔化、澄清均化较为困难、玻筋重、气泡缺陷多的缺点，在不添加澄清剂的状态下，一般玻璃正常熔化温度高于1540℃，澄清温度高于1640℃，才能满足熔化和澄清的需要，不仅能耗高，还会降低窑炉耐材的寿命。
因此，在玻璃生产过程中，有必要加入澄清剂，以消除玻璃中的可见气泡。As2O3、Sb2O3、Cl2、F2等是目前常用的优良的澄清剂，对于玻璃具有优良的澄清效果。但是它们是非环境友好型物质，国外已禁止使用。因此研制出一种无毒无害、且澄清效果较好的玻璃澄清剂，已成为必然趋势。
发明内容
本发明设计开发了一种澄清效果好的玻璃的制备方法。
本发明提供的技术方案为：
一种玻璃的制备方法，包括：
步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行混合，得到混合料，将混合料升温至1755～1765℃下熔融，再降温至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸盐3～4份，氧化锡0.4～0.6份；
步骤(2)玻璃液成型，成型之后降温至室温，之后再升温至300～310℃，再置于400～415℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入400～415℃的硝酸钠熔融液中处理60～90min。
优选的是，所述的玻璃的制备方法中，所述步骤(1)中，将88份的原料与6份的玻璃澄清剂混合。
优选的是，所述的玻璃的制备方法中，所述步骤(1)中，将混合料升温至1755～1765℃下熔融，并维持10～15min，之后再降温。
优选的是，所述的玻璃的制备方法中，玻璃澄清剂中的各成分的质量份数为硝酸钠3.6份，氧化锡0.4份。
优选的是，所述的玻璃的制备方法中，所述步骤(2)中，玻璃液成型，成型之后降温至室温，之后再升温至300℃，再置于405℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入405℃的硝酸钠熔融液中处理60～90min。
本发明所述的玻璃的制备方法可以有效减少玻璃内的气泡含量。
具体实施方式
下面对本发明做进一步的详细说明，以令本领域技术人员参照说明书文字能够据以实施。
本发明提供一种玻璃的制备方法，包括：
步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行混合，得到混合料，将混合料升温至1755～1765℃下熔融，再降温至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸盐3～4份，氧化锡0.4～0.6份。本发明先将混合料升温至相对高的温度下熔融，之后再降温至玻璃澄清剂适宜作用的温度，可以有效促使溶解在玻璃液中的气体释放出去。
步骤(2)玻璃液成型，成型之后降温至室温，之后再升温至300～310℃，再置于400～415℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入400～415℃的硝酸钠熔融液中处理60～90min。成型之后再对玻璃液进行处理，得到的玻璃的强度高。
本发明制备得到的玻璃的澄清效果好，每平方米气泡数量仅1个。且玻璃的强度高。
本发明优选采用石英砂、碳酸钠、碳酸钙、硝酸钾以及氧化镁为原料。
优选的是，所述的玻璃的制备方法中，所述步骤(1)中，将88份的原料与6份的玻璃澄清剂混合。
优选的是，所述的玻璃的制备方法中，所述步骤(1)中，将混合料升温至1755～1765℃下熔融，并维持10～15min，之后再降温。
优选的是，所述的玻璃的制备方法中，玻璃澄清剂中的各成分的质量份数为硝酸钠3.6份，氧化锡0.4份。
优选的是，所述的玻璃的制备方法中，所述步骤(2)中，玻璃液成型，成型之后降温至室温，之后再升温至300℃，再置于405℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入405℃的硝酸钠熔融液中处理60～90min。
尽管本发明的实施方案已公开如上，但其并不仅仅限于说明书和实施方式中所列运用，它完全可以被适用于各种适合本发明的领域，对于熟悉本领域的人员而言，可容易地实现另外的修改，因此在不背离权利要求及等同范围所限定的一般概念下，本发明并不限于特定的细节。

Claims (4)

1.一种玻璃的制备方法，其特征在于，包括：
步骤(1)将按重量份数计的87～97份的原料与3～6份的玻璃澄清剂进行混合，得到混合料，将混合料升温至1755～1765℃下熔融，并维持10～15min，再降温至1520～1530℃，得到玻璃液，玻璃澄清剂中的各成分的质量份数为：硝酸盐3～4份，氧化锡0.4～0.6份；
步骤(2)玻璃液成型，成型之后降温至室温，之后再升温至300～310℃，再置于400～415℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入400～415℃的硝酸钠熔融液中处理60～90min。
2.如权利要求1所述的玻璃的制备方法，其特征在于，所述步骤(1)中，将88份的原料与6份的玻璃澄清剂混合。
3.如权利要求1所述的玻璃的制备方法，其特征在于，玻璃澄清剂中的各成分的质量份数为硝酸钠3.6份，氧化锡0.4份。
4.如权利要求1所述的玻璃的制备方法，其特征在于，所述步骤(2)中，玻璃液成型，成型之后降温至室温，之后再升温至300℃，再置于405℃的硝酸钠熔融液中处理30min，之后取出降温至100℃，之后再放入405℃的硝酸钠熔融液中处理60～90min。
CN201610787003.3A 2016-08-31 2016-08-31 玻璃的制备方法 Active CN106430945B (zh)