CN106366666A - 一种混凝胶的制备方法 - Google Patents
一种混凝胶的制备方法 Download PDFInfo
- Publication number
- CN106366666A CN106366666A CN201610492800.9A CN201610492800A CN106366666A CN 106366666 A CN106366666 A CN 106366666A CN 201610492800 A CN201610492800 A CN 201610492800A CN 106366666 A CN106366666 A CN 106366666A
- Authority
- CN
- China
- Prior art keywords
- preparation
- silicone oil
- solid fraction
- viscose
- blob
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种混凝胶的制备方法，所述混凝胶包括下述重量份的原料：甲基乙烯基硅橡胶30‑70份、二氧化硅2‑5份、硅油2‑5份、硬脂酸锌0.8‑1份。本发明制备的混凝胶符合测试标准，环保无害，抗高温抗老化，绝缘性能好，可广泛用于医疗设备输液、整形美容用硅胶、电力电线电缆及婴幼儿制品等领域。
Description
技术领域
本发明涉及一种混凝胶的技术领域，尤其涉及一种混凝胶的制备方法。
背景技术
一般的电力行业中大多使用陶瓷材料作为一些成品，但是其绝缘性能不是太好，在一些高温情况下，普通的电线电缆的外层的绝缘胶层容易老化，抗高温性不强，使用寿命短。
发明内容
本发明针对现有技术的不足，提供了一种混凝胶的制备方法。其解决技术问题所采用的技术方案是：一种混凝胶的制备方法，所述混凝胶包括下述重量份的原料：甲基乙烯基硅橡胶30-70份、二氧化硅2-5份、硅油2-5份、硬脂酸锌0.8-1份；
其制备方法按如下步骤：
一、将所述甲基乙烯基硅橡胶经高温170-180℃进行硫化；
二、将所述甲基乙烯基硅橡胶、所述二氧化硅、所述硅油和所述硬脂酸锌经高温150-175℃相对搅拌混合，相对搅拌转速100-120转/min，搅拌时间为200-220分钟，经抽真空高温170-180℃混炼30分钟后，冷却成固状胶块；
三、经过滤设备过滤掉所述固状胶块中的杂质后，制成半成品固状或者块状胶块结构；
四、将促进剂或者硫化机加入到所述半成品固状或者块状胶块结构，压制成形。
较佳的，所述硅油为甲基硅油或者羟基硅油或者含氢硅油。
较佳的，所述促进剂为至少一种颜色的色模。
本发明的有益效果是，本发明制备的混凝胶符合测试标准，环保无害，抗高温抗老化，使用寿命长，绝缘性能好，可广泛用于医疗设备输液、整形美容用硅胶、电力电线电缆及婴幼儿制品等领域。
具体实施方式
以下具体实施方式对本发明做进一步详细说明。
一种混凝胶的制备方法，所述混凝胶包括下述重量份的原料：甲基乙烯基硅橡胶30-70份、二氧化硅2-5份、硅油2-5份、硬脂酸锌0.8-1份；
其制备方法按如下步骤：
一、将所述甲基乙烯基硅橡胶经高温170-180℃进行硫化；
二、将所述甲基乙烯基硅橡胶、所述二氧化硅、所述硅油和所述硬脂酸锌经高温150-175℃相对搅拌混合，相对搅拌转速100-120转/min，搅拌时间为200-220分钟，经抽真空高温170-180℃混炼30分钟后，冷却成固状胶块；
三、经过滤设备过滤掉所述固状胶块中的杂质后，制成半成品固状或者块状胶块结构；
四、将促进剂或者硫化机加入到所述半成品固状或者块状胶块结构，压制成形。
所述硅油为甲基硅油或者羟基硅油或者含氢硅油。所述促进剂为至少一种颜色的色模。
以上仅为本发明较佳的实施例，故不能依此限定本发明实施的范围，即依本发明说明书内容所作的等效变化与装饰，皆应属于本发明覆盖的范围内。
Claims (3)
1.一种混凝胶的制备方法，其特征在于：所述混凝胶包括下述重量份的原料：甲基乙烯基硅橡胶30-70份、二氧化硅2-5份、硅油2-5份、硬脂酸锌0.8-1份；
其制备方法按如下步骤：
一、将所述甲基乙烯基硅橡胶经高温170-180℃进行硫化；
二、将所述甲基乙烯基硅橡胶、所述二氧化硅、所述硅油和所述硬脂酸锌经高温150-175℃相对搅拌混合，相对搅拌转速100-120转/min，搅拌时间为200-220分钟，经抽真空高温170-180℃混炼30分钟后，冷却成固状胶块；
三、经过滤设备过滤掉所述固状胶块中的杂质后，制成半成品固状或者块状胶块结构；
四、将促进剂或者硫化机加入到所述半成品固状或者块状胶块结构，压制成形。
2.根据权利要求1所述的一种混凝胶的制备方法，其特征在于：所述硅油为甲基硅油或者羟基硅油或者含氢硅油。
3.根据权利要求1所述的一种混凝胶的制备方法，其特征在于：所述促进剂为至少一种颜色的色模。