CN106244836B - 一种锑合金的除镉方法 - Google Patents

一种锑合金的除镉方法 Download PDF

Info

Publication number
CN106244836B
CN106244836B CN201610736969.4A CN201610736969A CN106244836B CN 106244836 B CN106244836 B CN 106244836B CN 201610736969 A CN201610736969 A CN 201610736969A CN 106244836 B CN106244836 B CN 106244836B
Authority
CN
China
Prior art keywords
cadmium
antimony alloy
air blast
agent
compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610736969.4A
Other languages
English (en)
Other versions
CN106244836A (zh
Inventor
唐好
范凌
张洋
田智
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shiny Materials Science And Technology Inc
Original Assignee
Shiny Materials Science And Technology Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shiny Materials Science And Technology Inc filed Critical Shiny Materials Science And Technology Inc
Priority to CN201610736969.4A priority Critical patent/CN106244836B/zh
Publication of CN106244836A publication Critical patent/CN106244836A/zh
Application granted granted Critical
Publication of CN106244836B publication Critical patent/CN106244836B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种锑合金的除镉方法，包括以下步骤：(1)以锑合金中镉的含量来计算，按1kg镉加入60kg±1kg复合型除镉剂的比例，向锑合金中加入复合型除镉剂；所述的复合型除镉剂中：碳酸胺盐5wt％±0.5wt％，氯化钠5wt％±0.5wt％，磷酸钠‑胺盐90wt％±0.5wt％；(2)控制熔化炉的温度在1100℃±50℃，保温，鼓风，使金属镉氧化进胺盐渣；(3)移动鼓风点，让锑合金中镉与复合型除镉剂充分反应；(4)扒出浮渣，提高锑合金品质。本发明具有操作简单、方便，一次除镉效率高，安全无污染，能实现精锑提纯等优点。

Description

一种锑合金的除镉方法
技术领域
本发明涉及锑金属冶炼时除杂方法，具体涉及一种锑合金的除镉方法。
背景技术
按照传统冶炼工艺，所生产的锑合金中含少量镉金属(约0.1％)，不仅影响下一步的氧化锑生产，使得氧化锑产品白度不能提高，也为氧化锑产品的应用埋下了安全隐患。在市场竞争日益激烈的今天，氧化锑产品需要除去杂质镉元素，确保产品质量。
目前，有色金属冶炼大多采用碱性熔剂，除去杂质元素，如重金属砷(As)就是利用碱金属钠(Na)离子的引入生成砷酸钠入渣从而达到除砷的目的。但镉与砷不同，这种金属经冶金炉熔炼，很难有效除掉。因此，目前亟需一种有效的锑合金的除镉方法。
发明内容
本发明所要解决的技术问题是，提供一种有效的锑合金的除镉方法。
根据镉金属特性，熔点320.9℃，沸点765℃，密度8650kg/m3，镉在潮湿空气缓慢氧化，加热时表面形成棕色的氧化物层。高温下镉与卤素反应激烈，形成卤化镉。也可与硫直接化合，生成硫化镉。镉的氧化态为+1、+2。氧化镉和氢氧化镉的溶解度都很小，可溶于酸、胺盐，但不溶于碱。镉可形成多种配离子，如Cd(NH3)、Cd(CN)、CdCl等。
本发明在熔化炉内，1100±50℃下鼓风，使熔体中金属镉氧化，在胺盐作用下，Cd(NH3)、CdCL入渣，是锑冶炼技术上的突破，在国内外还没有先例。
本发明解决其技术问题所采用的技术方案是：锑合金的除镉方法，包括以下步骤：
(1)以锑合金中镉的含量来计算，按1kg镉加入60kg±1kg复合型除镉剂的比例，向锑合金中加入复合型除镉剂；
所述的复合型除镉剂中：碳酸胺盐5wt％±0.5wt％，氯化钠5wt％±0.5wt％，磷酸钠-胺盐90wt％±0.5wt％；
(2)控制熔化炉的温度在1100℃±50℃，保温，鼓风，使金属镉氧化进胺盐渣；
(3)移动鼓风点，让锑合金中镉与复合型除镉剂充分反应；
(4)扒出浮渣，提高锑合金品质。
进一步，步骤(2)中，鼓风的压力为0.05-0.1MPa。
进一步，步骤(2)中，鼓风的时间为1.5-2.5h(优选2h)。
进一步，步骤(3)中，每隔12-20分钟(优选15分钟)移动鼓风点。
进一步，步骤(3)中，反应的时间为25-40分钟(优选30分钟)。
本发明在高温下使金属镉氧化进渣，研究表明，利用本发明进行锑合金的除镉，可提高冶炼金属锑的品质，其镉含量从0.1wt％下降到0.005wt％。
与现有技术相比，本发明具有操作简单、方便，一次除镉效率高，安全无污染，能实现精锑提纯等优点。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例
本实施例之锑合金的除镉方法，包括以下步骤：
(1)以锑合金中镉的含量来计算，按1kg镉加入60kg复合型除镉剂的比例，向锑合金中加入复合型除镉剂，例：10m2熔化炉含锑合金30吨，其中含镉0.05wt％，即15kg，所加复合型除镉剂为900kg；
所述的复合型除镉剂中：碳酸胺盐5wt％，氯化钠5wt％，磷酸钠-胺盐90wt％；
(2)控制熔化炉的温度在1100℃±50℃，保温，鼓风，使金属镉氧化进胺盐渣；
(3)移动鼓风点，让锑合金中镉与复合型除镉剂充分反应；
(4)扒出浮渣，提高锑合金品质。
本实施例中，步骤(2)中，鼓风的压力为0.08MPa。
本实施例中，步骤(2)中，鼓风的时间为2h。
本实施例中，步骤(3)中，每隔15分钟移动鼓风点。
本实施例中，步骤(3)中，反应的时间为30分钟。
试验表明，利用本发明进行锑合金的除镉，可提高冶炼金属锑的品质，其镉含量从0.1wt％下降到0.005wt％。
本发明操作简单、方便，一次除镉效率高，安全无污染，能实现精锑提纯。

Claims (3)

1.一种锑合金的除镉方法，其特征在于，包括以下步骤：
（1）以锑合金中镉的含量来计算，按1kg镉加入60kg±1kg复合型除镉剂的比例，向锑合金中加入复合型除镉剂；
所述的复合型除镉剂中：碳酸铵5wt%±0.5wt%，氯化钠5wt%±0.5wt%，磷酸钠铵90wt%±0.5wt%；
（2）控制熔化炉的温度在1100℃±50℃，保温，鼓风，使金属镉氧化进铵盐渣；
（3）移动鼓风点，让锑合金中镉与复合型除镉剂充分反应；
（4）扒出浮渣，提高锑合金品质；
步骤（2）中，鼓风的压力为0.05-0.1MPa；
步骤（2）中，鼓风的时间为1.5-2.5h；
步骤（3）中，每隔12-20分钟移动鼓风点；
步骤（3）中，反应的时间为25-40分钟。
2.根据权利要求1所述的锑合金的除镉方法，其特征在于，步骤（3）中，每隔15分钟移动鼓风点。
3.根据权利要求1或2所述的锑合金的除镉方法，其特征在于，步骤（3）中，反应的时间为30分钟。
CN201610736969.4A 2016-08-26 2016-08-26 一种锑合金的除镉方法 Active CN106244836B (zh)