CN106243755A - A kind of rape stalk Plant fiber's synthetic resin and preparation technology thereof - Google Patents
A kind of rape stalk Plant fiber's synthetic resin and preparation technology thereof Download PDFInfo
- Publication number
- CN106243755A CN106243755A CN201610618729.4A CN201610618729A CN106243755A CN 106243755 A CN106243755 A CN 106243755A CN 201610618729 A CN201610618729 A CN 201610618729A CN 106243755 A CN106243755 A CN 106243755A
- Authority
- CN
- China
- Prior art keywords
- rape
- parts
- rape stalk
- fiber
- synthetic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to chemical material field, particularly relate to a kind of rape stalk Plant fiber's synthetic resin and preparation technology thereof, including following raw material: rape straw, rice bran wax, agar, p-phthalic acid, tapioca, propylene glycol, balsamum powder, silicon dioxide, acid fiber by polylactic；Its preparation technology comprises the following steps: (1), prepared fine particle rape straw；(2), the most mixed material is prepared；(3), rape stalk fiber powder is prepared；(4), prepare mixing to add materials；(5) mixing is added materials and after acid fiber by polylactic stirs, blending extrusion, injection mo(u)lding, obtain rape stalk Plant fiber's synthetic resin.The present invention is the waste for avoiding the resources such as wastes of crops, it is sufficiently utilized, and reduces the pollution to environment；The production cost of invention is low, and application widely, can play rural resource advantage, and the Appropriate application for waste agronomic crop provides effective method and approach.
Description
Technical field
The present invention relates to chemical material field, particularly relate to a kind of rape stalk Plant fiber's synthetic resin and system thereof
Standby technique.
Background technology
China is as large agricultural country, and along with agricultural is scored consecutive bumper harvests, agricultural crop straw and other waste material yield the most significantly go up
Rising, wherein light straw yield is about 6.5 hundred million t/, and the process of wastes of crops straw etc. has become social problem, except few
Outside part is taken as feedstuff, fertilizer etc. to develop, major part is committed to the flames, not only wastes resource, and serious harm
Natural ecological environment, therefore, the comprehensive utilization of waste agronomic crop is significant.And the mankind are while creating modern civilization, also
It is negatively affected white pollution.Disposable tableware, Phthalates and agricultural mulching etc. are all difficult to recycling
Utilizing, its processing method is to burn and to bury.Burning can produce substantial amounts of harmful gas, pollutes environment；Bury wherein
The polymer short time in can not be decomposed by the microorganisms, also pollute environment.The residual plastic foil abandoned is present in soil, hinders farming
The growth of thing root system and to moisture, the absorption of nutrient, makes the gas permeability of soil reduce, causes crop production reduction；Action eats residual abandoning
Plastic foil after, intestinal obstruction can be caused and dead；The synthetic netting being lost in ocean or discard in ocean and fishline
Marine organisms are caused suitable harm, has therefore advocated green consumption imperative with reinforcement environmental conservation.In the face of day by day
Exhausted petroleum resources, popular biodegradation material is just becoming a research and development heat as high-tech product and environment-friendly products
Point.
Along with people are to resource, the raising of environmental consciousness, it has been recognized that resources conservation, environmental conservation are that the mankind can enter
The mandatory principle of row sustainable development, is the inevitable requirement of the Scientific Outlook on Development.Existing tableware on the market, furniture, kitchen tools
All use the products such as wood, bamboo, common plastics etc. the articles for daily use, this type of product cost is high, be unfavorable for degraded, not environmentally, Qi Zhongpu
Logical plastics not only can not be degraded, and is widely acknowledged as " white pollution ", destroys the water penetration of soil, and wood, Bamboo products to be cut down
Forest, has contaminated wastewater in manufacture process, be not good environment-friendly materials.It is subject to the filling-modified plastics of Plant fiber at present
The attention of countries in the world, this technology meets the theory of resources conservation, environmental conservation.Lignocellulosic fiber source is abundant, cheap, its
Density is less than all inorfils, and modulus and hot strength are close with inorfil, Plant fiber's potting resin materials processing
Time less energy consumption, the loss to process equipment is little, the beneficially saving of the energy in the course of processing, and can natural degradation, it is possible to subtract
That lacks plastics uses the pressure brought to environment, in a large number simultaneously for improving the production of people, life a kind of brand-new material of offer.
Summary of the invention
It is an object of the invention to solve the problems of the prior art, it is provided that a kind of technique is simple, steady quality, cost
Low, can rape stalk Plant fiber's synthetic resin of natural degradation and preparation technology thereof.
The technical solution adopted in the present invention is such that
A kind of rape stalk Plant fiber's synthetic resin, including the raw material of following weight portion: rape straw 30～60 parts,
Rice bran wax 5～10 parts, agar 15～40 parts, p-phthalic acid 3～8 parts, tapioca 15～40 parts, propylene glycol 3～8 parts, perfume
Rubber powder 3～8 parts, silicon dioxide 5～10 parts, acid fiber by polylactic 10～20 parts；
Its preparation technology comprises the following steps:
(1), rape stalk is carried out super-refinement attrition process, obtain fine particle rape straw；
(2), propylene glycol, p-phthalic acid are put into high speed mixer, be simultaneously introduced rice bran wax and stir, obtain the most mixed
Material；
(3), the rape straw of step (1) is put into high speed mixer to mix, simultaneously with the first mixed material of step (2)
Add tapioca to stir, be then cooled to room temperature, pulverize after one-tenth bulk to be solidified, obtain rape stalk fiber powder；
(4), agar and balsamum powder are put into reaction vessel stir, at temperature is 100 DEG C～160 DEG C, reacts 60
Minute～120 minutes, be subsequently adding silicon dioxide and rape stalk fiber powder continue to stir, be 80 DEG C～120 in temperature
React 60 minutes～120 minutes at DEG C, pulverize after cooling, obtain mixing and add materials；
(5) mixing that step (4) obtains is added materials and acid fiber by polylactic is put into after high speed mixer stirs,
Blending extrusion in double screw extruder, then injection mo(u)lding, obtain rape stalk Plant fiber's synthetic resin, packaging storage after cooling
Deposit.
Preferably, in step (1), described rape stalk grinds to form the molecule rape straw of 50～200 mesh；
Preferably, in step (2), described high speed mixer high-speed stirred 2～after 5 minutes, then stirring at low speed 5～8
Minute to stirring fully, the temperature of high-speed stirred controls at 70 DEG C～90 DEG C, and the temperature of stirring at low speed controls at 20 DEG C～50 DEG C.
Preferably, the mix and blend temperature in described step (3) is 15 DEG C～40 DEG C.
By using preceding solution, the invention has the beneficial effects as follows:
The present invention is the waste for avoiding the resources such as wastes of crops, it is sufficiently utilized, with reach to turn waste into wealth
Purpose, and reduce the pollution to environment, the product of the present invention has resistance to freezing, high temperature resistant, high density, high intensity, smooth, nothing
The characteristics such as poison, length in service life, and there is superpower resistance to water, moreover it is possible in large nature, it is degraded into organic fertilizer voluntarily,
Back to nature, is the material of a kind of extremely environmental protection.Production low cost of the present invention, can be used for packing, tableware, bottle for cosmetics and
The fields such as drug bottle, disposable medical article, pesticide and slow-release fertilizer carrier matrix, biological medical polymer material, also have it
It relates to the various plastics of environmental conservation, and such as building greening net, film etc., application is widely.The present invention opens
New raw material sources, can play rural resource advantage, add farmers' income, alleviates the contradiction of shortage of resources, is discarded
The Appropriate application of crops provides effective method and approach.
Detailed description of the invention
Being specifically described the present invention with embodiment below, the scope of the present invention should not be limited by the examples.
Embodiment 1:
A kind of rape stalk Plant fiber's synthetic resin, including the raw material of following weight portion: rape straw 30 parts, Testa oryzae
5 parts of wax, 15 parts of agar, p-phthalic acid 3 parts, tapioca 15 parts, propylene glycol 3 parts, balsamum powder 3 parts, silicon dioxide 5 parts, poly-
Acid fiber 10 parts；
Its preparation technology comprises the following steps:
(1), rape stalk is carried out super-refinement attrition process, obtain fine particle rape straw；
(2), propylene glycol, p-phthalic acid are put into high speed mixer, be simultaneously introduced rice bran wax and stir, obtain the most mixed
Material；
(3), the rape straw of step (1) is put into high speed mixer to mix, simultaneously with the first mixed material of step (2)
Add tapioca to stir, be then cooled to room temperature, pulverize after one-tenth bulk to be solidified, obtain rape stalk fiber powder；
(4), agar and balsamum powder are put into reaction vessel stir, react at temperature is 100 DEG C～160 DEG C
120 minutes, it is subsequently adding silicon dioxide and rape stalk fiber powder continues to stir, anti-at temperature is 80 DEG C～120 DEG C
Answer 60 minutes, pulverize after cooling, obtain mixing and add materials；
(5) mixing that step (4) obtains is added materials and acid fiber by polylactic is put into after high speed mixer stirs,
Blending extrusion in double screw extruder, then injection mo(u)lding, obtain rape stalk Plant fiber's synthetic resin, packaging storage after cooling
Deposit.
In step (1), described rape stalk grinds to form the molecule rape straw of 50～200 mesh；
In step (2), described high speed mixer high-speed stirred is after 2 minutes, then stirring at low speed is filled for 8 minutes to stirring
Point, the temperature of high-speed stirred controls at 70 DEG C～90 DEG C, and the temperature of stirring at low speed controls at 20 DEG C～50 DEG C.
Mix and blend temperature in described step (3) is 15 DEG C～40 DEG C.
Embodiment 2:
A kind of rape stalk Plant fiber's synthetic resin, including the raw material of following weight portion: rape straw 60 parts, Testa oryzae
10 parts of wax, 40 parts of agar, p-phthalic acid 8 parts, tapioca 40 parts, propylene glycol 8 parts, balsamum powder 8 parts, silica 10 part,
Acid fiber by polylactic 20 parts；
Its preparation technology comprises the following steps:
(1), rape stalk is carried out super-refinement attrition process, obtain fine particle rape straw；
(2), propylene glycol, p-phthalic acid are put into high speed mixer, be simultaneously introduced rice bran wax and stir, obtain the most mixed
Material；
(3), the rape straw of step (1) is put into high speed mixer to mix, simultaneously with the first mixed material of step (2)
Add tapioca to stir, be then cooled to room temperature, pulverize after one-tenth bulk to be solidified, obtain rape stalk fiber powder；
(4), agar and balsamum powder are put into reaction vessel stir, at temperature is 100 DEG C～160 DEG C, reacts 60
Minute, it is subsequently adding silicon dioxide and rape stalk fiber powder continues to stir, react at temperature is 80 DEG C～120 DEG C
120 minutes, pulverize after cooling, obtain mixing and add materials；
(5) mixing that step (4) obtains is added materials and acid fiber by polylactic is put into after high speed mixer stirs,
Blending extrusion in double screw extruder, then injection mo(u)lding, obtain rape stalk Plant fiber's synthetic resin, packaging storage after cooling
Deposit.
In step (1), described rape stalk grinds to form the molecule rape straw of 50～200 mesh；
In step (2), described high speed mixer high-speed stirred is after 5 minutes, then stirring at low speed is filled for 5 minutes to stirring
Point, the temperature of high-speed stirred controls at 70 DEG C～90 DEG C, and the temperature of stirring at low speed controls at 20 DEG C～50 DEG C.
Mix and blend temperature in described step (3) is 15 DEG C～40 DEG C.
Above example is only in order to illustrate technical scheme, rather than limiting the scope of the invention, although
Make to explain to the present invention with reference to preferred embodiment, it will be understood by those within the art that, can be to this
Bright technical scheme is modified or equivalent, without deviating from the spirit and scope of technical solution of the present invention.
Claims (4)
1. rape stalk Plant fiber's synthetic resin, it is characterised in that include the raw material of following weight portion: rape straw
30～60 parts, rice bran wax 5～10 parts, agar 15～40 parts, p-phthalic acid 3～8 parts, tapioca 15～40 parts, propylene glycol 3
～8 parts, balsamum powder 3～8 parts, silicon dioxide 5～10 parts, acid fiber by polylactic 10～20 parts；
Its preparation technology comprises the following steps:
(1), rape stalk is carried out super-refinement attrition process, obtain fine particle rape straw；
(2), propylene glycol, p-phthalic acid are put into high speed mixer, be simultaneously introduced rice bran wax and stir, obtain the most mixed thing
Material；
(3), by the rape straw of step (1) put into high speed mixer to mix with the first mixed material of step (2), be simultaneously introduced
Tapioca stirs, and is then cooled to room temperature, and pulverizes, obtain rape stalk fiber powder after one-tenth bulk to be solidified；
(4), agar and balsamum powder are put into reaction vessel stir, react 60 minutes at temperature is 100 DEG C～160 DEG C
～120 minutes, it is subsequently adding silicon dioxide and rape stalk fiber powder continues to stir, at temperature is 80 DEG C～120 DEG C
React 60 minutes～120 minutes, pulverize after cooling, obtain mixing and add materials；
(5) mixing that step (4) obtains is added materials and acid fiber by polylactic is put into after high speed mixer stirs, at double spiral shells
Blending extrusion in bar extruder, then injection mo(u)lding, obtain rape stalk Plant fiber's synthetic resin, packing and storing after cooling.
The preparation technology of a kind of rape stalk Plant fiber's synthetic resin the most according to claim 1, it is characterised in that:
In step (1), described rape stalk grinds to form the molecule rape straw of 50～200 mesh.
The preparation technology of a kind of rape stalk Plant fiber's synthetic resin the most according to claim 1, it is characterised in that:
In step (2), described high speed mixer high-speed stirred 2～after 5 minutes, then stirring at low speed 5～8 minutes are to stirring fully, high
The temperature of speed stirring controls at 70 DEG C～90 DEG C, and the temperature of stirring at low speed controls at 20 DEG C～50 DEG C.
The preparation technology of a kind of rape stalk Plant fiber's synthetic resin the most according to claim 1, it is characterised in that: institute
Stating the mix and blend temperature in step (3) is 15 DEG C～40 DEG C.