CN106242541B - A kind of production method of the chiltern vessel for fried tea - Google Patents

A kind of production method of the chiltern vessel for fried tea Download PDF

Info

Publication number
CN106242541B
CN106242541B CN201610778524.2A CN201610778524A CN106242541B CN 106242541 B CN106242541 B CN 106242541B CN 201610778524 A CN201610778524 A CN 201610778524A CN 106242541 B CN106242541 B CN 106242541B
Authority
CN
China
Prior art keywords
parts
green body
mud
ingredient
base
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610778524.2A
Other languages
Chinese (zh)
Other versions
CN106242541A (en
Inventor
张宏亮
古林子
刘先勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Original Assignee
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pingding County Hat Kiln Sand Device Pottery Art Co Ltd filed Critical Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority to CN201610778524.2A priority Critical patent/CN106242541B/en
Publication of CN106242541A publication Critical patent/CN106242541A/en
Application granted granted Critical
Publication of CN106242541B publication Critical patent/CN106242541B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention belongs to the production methods of sand container, and in particular to a kind of production method of the chiltern vessel for fried tea.The present invention, which mainly solves existing irony or stainless steel fried tea container, there is technical issues that.A kind of the technical solution adopted by the present invention are as follows: production method of the chiltern vessel for fried tea, comprising the following steps: 1) ingredient；2) mud processed: the ingredient of step 1) being put into ball mill and is ground to 30 targeted fine powders, and by after grinding fine powder and water be placed in clear mud sump and degenerated 2 months to 6 months with the proportion of 1:3-6, base mud is made；3) base mud prepared by step 2) is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and uniformly；4) base body；5) repaired biscuit；6) it decorates；7) it dries；8) it fires.Critical process can ensure that anti-dry combustion method is not burst for a long time in links such as ingredient, base, firings, produce thermal stability, and adsorptivity is preferably and the sand device of other stable physical properties.

Description

A kind of production method of the chiltern vessel for fried tea
Technical field
The invention belongs to the production methods of sand container, and in particular to a kind of production side of the chiltern vessel for fried tea Method.
Background technique
Fried tea is the necessary procedure for producing tea product, and the vessel for being currently used for fried tea are mostly irony or rustless steel container, iron Matter container usually contains carbon tetrafluoride in addition to the free son of release iron, iron pan surface coating, and this chemical substance can become at high temperature It comes out at gaseous volatilization, and as the process of stirring of tealeaves is absorbed by tealeaves, is eventually drunk after infusion by people into belly, no Safety.Stainless steel machinery tea making, efficiency do height, but the free son of iron that itself releases, can not only tealeaves be allowed to change colour, and meeting The organic component for reducing or being lost in tealeaves.
Summary of the invention
Present invention aim to address existing ironys or stainless steel fried tea container there is technical issues that, provides one Production method of the kind for the chiltern vessel of fried tea.
In order to solve the above technical problems, the technical solution adopted by the present invention are as follows:
A kind of production method of the chiltern vessel for fried tea, comprising the following steps:
1) 10-20 parts of talcum powder, 10-30 parts of spodumene, 8-20 parts of bentonite, 10-20 parts of floating bead and blueness ingredient: are weighed 10-30 parts of cash, and be uniformly mixed；
2) mud processed: the ingredient of step 1) being put into ball mill and is ground to 30 targeted fine powders, and by after grinding fine powder and Water is placed in clear mud sump with the proportion of 1:3-6 degenerates 2 months to 6 months, and base mud is made；
3) base mud prepared by step 2) is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and uniformly；
4) base body: by walk, required green body is made in throwing on mud platform；
5) repaired biscuit: the green body drawn is placed and is dried in the shade at shady and cool drying, rotation vehicle is placed it in after parching to green body On place under repair, make in green body flat outside light, and the extra part in bottom pared off；
6) it decorates: carrying out the decoration of shape, moulding and color to green body made of step 5)；
7) dry: it is 50 DEG C that the green body decorated, which is dried to its surface temperature,；
8) it fires: green body prepared by step 7) is placed in kiln, it is small that 24 are fired at a temperature of 1230-1270 DEG C When, naturally cool to room temperature, kiln discharge.
The invention adopts the above technical scheme, and blank is made by talcum powder, spodumene, bentonite, floating bead and green cash, passes through Ingredient, base, repaired biscuit, decoration, drying, fires fabrication processing at mud processed, and critical process is in rings such as ingredient, base, firings Section can ensure that the anti-dry combustion method of long-time is not burst, and produce thermal stability, and adsorptivity is preferable and the sand of other stable physical properties Device.Casserole fried tea, use most traditional manual fried tea technique and method are inhibited using the preferably cold and hot expansion physical property of sand device Enzymatic oxidation forms the distinctive quality of sand device fried tea.The free son of sand device lead and cadmium free itself, non-iron content, when with casserole fried tea, in heat The adsorptivity of casserole itself and thermal stability preferably remain the organic principle and nutritional ingredient of tea under change acts on, and can inhibit enzyme Property oxidation, further eliminate bitter taste；And as the microelement being rich in process sand device that stirs of tealeaves will become gas and wave It issues to be volatilized to suck by tealeaves green grass gas itself and organically combine, promote flavour mellow, form strong fragrant tea perfume.
Specific embodiment
Embodiment 1
A kind of chiltern vessel for fried tea, it is to be prepared from the following raw materials in parts by weight blank: 10 parts of talcum powder, 10 parts of spodumene, 8 parts of bentonite, 10 parts of floating bead and green 10 parts of cash.
A method of making the chiltern vessel that fried tea is used for described in the present embodiment, comprising the following steps:
1) ingredient: 10 parts of talcum powder, 10 parts of spodumene, 8 parts of bentonite, 10 parts of floating bead and green 10 parts of cash are weighed, and is mixed Uniformly.
2) mud processed: the ingredient of step 1) being put into ball mill and is ground to 30 targeted fine powders, and by after grinding fine powder and Water is placed in clear mud sump with the proportion of 1:3 degenerates 2 months, and base mud is made；
3) base mud prepared by step 2) is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and uniformly；
4) base body: by walk, required green body is made in throwing on mud platform；
5) repaired biscuit: the green body drawn is placed and is dried in the shade at shady and cool drying, rotation vehicle is placed it in after parching to green body On place under repair, make in green body flat outside light, and the extra part in bottom pared off；
6) it decorates: carrying out the decoration of shape, moulding and color to green body made of step 5)；
7) dry: it is 50 DEG C that the green body decorated, which is dried to its surface temperature,；
8) it fires: green body prepared by step 7) being placed in kiln, is fired 24 hours at a temperature of 1230 DEG C, from It is so cooled to room temperature, kiln discharge.
Embodiment 2
One of the present embodiment is used for the chiltern vessel of fried tea, it is to be prepared from the following raw materials in parts by weight blank: 20 parts of talcum powder, 30 parts of spodumene, 20 parts of bentonite, 20 parts of floating bead and green 30 parts of cash.
A method of making the chiltern vessel that fried tea is used for described in the present embodiment, comprising the following steps:
1) ingredient: 20 parts of talcum powder, 30 parts of spodumene, 20 parts of bentonite, 20 parts of floating bead and green 30 parts of cash are weighed, and is mixed Uniformly.
2) mud processed: the ingredient of step 1) being put into ball mill and is ground to 30 targeted fine powders, and by after grinding fine powder and Water is placed in clear mud sump with the proportion of 1:6 degenerates 6 months, and base mud is made；
3) base mud prepared by step 2) is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and uniformly；
4) base body: by walk, required green body is made in throwing on mud platform；
5) repaired biscuit: the green body drawn is placed and is dried in the shade at shady and cool drying, rotation vehicle is placed it in after parching to green body On place under repair, make in green body flat outside light, and the extra part in bottom pared off；
6) it decorates: carrying out the decoration of shape, moulding and color to green body made of step 5)；
7) dry: it is 50 DEG C that the green body decorated, which is dried to its surface temperature,；
8) it fires: green body prepared by step 7) being placed in kiln, is fired 24 hours at a temperature of 1270 DEG C, from It is so cooled to room temperature, kiln discharge.
Embodiment 3
A kind of chiltern vessel for fried tea, it is to be prepared from the following raw materials in parts by weight blank: 15 parts of talcum powder, 20 parts of spodumene, 14 parts of bentonite, 15 parts of floating bead and green 20 parts of cash.
A method of making the chiltern vessel that fried tea is used for described in the present embodiment, comprising the following steps:
1) ingredient: 15 parts of talcum powder, 20 parts of spodumene, 14 parts of bentonite, 15 parts of floating bead and green 20 parts of cash are weighed, and is mixed Uniformly.
2) mud processed: the ingredient of step 1) being put into ball mill and is ground to 30 targeted fine powders, and by after grinding fine powder and Water is placed in clear mud sump with the proportion of 1:5 degenerates 4 months, and base mud is made；
3) base mud prepared by step 2) is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and uniformly；
4) base body: by walk, required green body is made in throwing on mud platform；
5) repaired biscuit: the green body drawn is placed and is dried in the shade at shady and cool drying, rotation vehicle is placed it in after parching to green body On place under repair, make in green body flat outside light, and the extra part in bottom pared off；
6) it decorates: carrying out the decoration of shape, moulding and color to green body made of step 5)；
7) dry: it is 50 DEG C that the green body decorated, which is dried to its surface temperature,；
8) it fires: green body prepared by step 7) being placed in kiln, is fired 24 hours at a temperature of 1260 DEG C, from It is so cooled to room temperature, kiln discharge.

Claims (1)

1. a kind of production method of the chiltern vessel for fried tea, it is characterised in that: the following steps are included:
1) 10-20 parts of talcum powder, 10-30 parts of spodumene, 8-20 parts of bentonite, 10-20 parts of floating bead and green cash 10- ingredient: are weighed 30 parts, and be uniformly mixed；
2) mud processed: the ingredient of step 1) being put into ball mill and is ground to 30 targeted fine powders, and by after grinding fine powder and water with The proportion of 1:3-6, which is placed in clear mud sump, degenerates 2 months to 6 months, and base mud is made；
3) base mud prepared by step 2) is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and uniformly；
4) base body: by walk, required green body is made in throwing on mud platform；
5) repaired biscuit: the green body drawn is placed and is dried in the shade at shady and cool drying, rotation Che Shangjin is placed it in after parching to green body Row is repaired, and makes to put down outside light in green body, and pare off the extra part in bottom；
6) it decorates: carrying out the decoration of shape, moulding and color to green body made of step 5)；
7) dry: it is 50 DEG C that the green body decorated, which is dried to its surface temperature,；
8) it fires: green body prepared by step 7) being placed in kiln, is fired 24 hours at a temperature of 1230-1270 DEG C, from It is so cooled to room temperature, kiln discharge.
CN201610778524.2A 2016-08-30 2016-08-30 A kind of production method of the chiltern vessel for fried tea Active CN106242541B (en)