CN106242541A - A kind of chiltern vessel for tea frying and preparation method thereof - Google Patents

A kind of chiltern vessel for tea frying and preparation method thereof Download PDF

Info

Publication number
CN106242541A
CN106242541A CN201610778524.2A CN201610778524A CN106242541A CN 106242541 A CN106242541 A CN 106242541A CN 201610778524 A CN201610778524 A CN 201610778524A CN 106242541 A CN106242541 A CN 106242541A
Authority
CN
China
Prior art keywords
base substrate
parts
mud
base
chiltern
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610778524.2A
Other languages
Chinese (zh)
Other versions
CN106242541B (en
Inventor
张宏亮
古林子
刘先勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Original Assignee
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pingding County Hat Kiln Sand Device Pottery Art Co Ltd filed Critical Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority to CN201610778524.2A priority Critical patent/CN106242541B/en
Publication of CN106242541A publication Critical patent/CN106242541A/en
Application granted granted Critical
Publication of CN106242541B publication Critical patent/CN106242541B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention belongs to sand container and preparation method thereof, be specifically related to a kind of chiltern vessel for tea frying and preparation method thereof.Blank is made by Pulvis Talci 10 parts, spodumene 10 parts, bentonite 8 parts, floating bead 10 parts and blue or green cash 10 parts, by dispensing, mud processed, base, repaired biscuit, decorate, dry, fire fabrication processing, critical process at dispensing, base, the link such as fire, can ensure that long-time anti-dry combustion method does not bursts, producing heat stability, adsorptivity is preferably and the sand device of other stable physical property.

Description

A kind of chiltern vessel for tea frying and preparation method thereof
Technical field
The invention belongs to sand container and preparation method thereof, be specifically related to a kind of chiltern vessel for tea frying and making thereof Method.
Background technology
Tea frying is that the vessel that through program, must be currently used for tea frying producing tea product mostly are irony or rustless steel container, ferrum Matter container is except the free son of Iron Release, and iron pan face coat usually contains carbon tetrafluoride, and this chemical substance at high temperature can become Become gaseous volatilization out, and along with the process of stirring of Folium Camelliae sinensis is absorbed by Folium Camelliae sinensis, drunk in belly by people the most after infusion, no Safety.Stainless steel machinery tea making, efficiency does height, but the free son of ferrum that itself discharges, and not only can allow Folium Camelliae sinensis variable color, and meeting Organic component in reduction or loss Folium Camelliae sinensis.
Summary of the invention
Present invention aim to address that existing irony or rustless steel tea frying container exist technical problem not environmentally, it is provided that one Kind is used for chiltern vessel of tea frying and preparation method thereof.
For solving above-mentioned technical problem, the technical solution used in the present invention is:
A kind of chiltern vessel for tea frying, it is to be prepared from the following raw materials in parts by weight blank: Pulvis Talci 10-20 Part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10-30 part.
A kind of method making the described chiltern vessel for tea frying, comprises the following steps:
1) dispensing: weigh Pulvis Talci 10-20 part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10-30 part, and mix homogeneously；
2) mud processed: by step 1) dispensing put into grinding in ball grinder to the fine powder of 30 mesh, and fine powder after grinding and Water is placed in clear mud sump corruption 2 months to 6 months with the proportioning of 1:3-6, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body: walk throwing on mud platform is made required base substrate；
5) repaired biscuit: the base substrate drawn is placed dry place, cool place and dries in the shade, treat base substrate to parch afterwards and place it in rotation car On place under repair, make in base substrate outside light flat, and part unnecessary for bottom pared off；
6) decoration: to step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry: by the base substrate decorate drying to its surface temperature be 50 DEG C；
8) fire: by step 7) base substrate prepared is positioned in kiln, fires 24 little at a temperature of 1230-1270 DEG C Time, naturally cool to room temperature, kiln discharge.
The present invention uses above technical scheme, Pulvis Talci, spodumene, bentonite, floating bead and blue or green cash make blank, pass through Dispensing, mud processed, base, repaired biscuit, decorate, dry, fire fabrication processing, critical process at dispensing, base, the ring such as fire Joint, can ensure that long-time anti-dry combustion method does not bursts, produce heat stability, and adsorptivity is preferable and the sand of other stable physical property Device.Marmite tea frying, by the most traditional manual tea frying technique and method, utilizes the preferable cold and hot expansion physical property of sand device, suppression Enzymatic oxidation, forms the sand distinctive quality of device tea frying.The free son of the lead and cadmium free of sand device own, non-iron content, during by marmite tea frying, in warm Under change effect, the adsorptivity of marmite itself and heat stability preferably remain organic principle and the nutritional labeling of tea, can inhibitory enzyme Property oxidation, eliminate bitter taste further；And along with in process of the stirring sand device of Folium Camelliae sinensis rich in trace element can become gas and wave Issue to be sucked by the volatilization of Folium Camelliae sinensis grass gas own and organically combine, promote that flavour is mellow, form strong fragrant tea fragrant.
Detailed description of the invention
Embodiment 1
A kind of chiltern vessel for tea frying, it is to be prepared from the following raw materials in parts by weight blank: Pulvis Talci 10 parts, lithium 10 parts of pyroxene, bentonite 8 parts, floating bead 10 parts and blue or green cash 10 parts.
A kind of method of chiltern vessel made described in the present embodiment for tea frying, comprises the following steps:
1) dispensing: weigh Pulvis Talci 10 parts, spodumene 10 parts, bentonite 8 parts, floating bead 10 parts and blue or green cash 10 parts, and mix Uniformly.
2) mud processed: by step 1) dispensing put into grinding in ball grinder to the fine powder of 30 mesh, and fine powder after grinding and Water is placed in clear mud sump corruption 2 months with the proportioning of 1:3, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body: walk throwing on mud platform is made required base substrate；
5) repaired biscuit: the base substrate drawn is placed dry place, cool place and dries in the shade, treat base substrate to parch afterwards and place it in rotation car On place under repair, make in base substrate outside light flat, and part unnecessary for bottom pared off；
6) decoration: to step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry: by the base substrate decorate drying to its surface temperature be 50 DEG C；
8) fire: by step 7) base substrate prepared is positioned in kiln, fires 24 hours at a temperature of 1230 DEG C, natural It is cooled to room temperature, kiln discharge.
Embodiment 2
A kind of chiltern vessel for tea frying in the present embodiment, it is to be prepared from the following raw materials in parts by weight blank: Pulvis Talci 20 parts, spodumene 30 parts, bentonite 20 parts, floating bead 20 parts and blue or green cash 30 parts.
A kind of method of chiltern vessel made described in the present embodiment for tea frying, comprises the following steps:
1) dispensing: weigh Pulvis Talci 20 parts, spodumene 30 parts, bentonite 20 parts, floating bead 20 parts and blue or green cash 30 parts, and mix Uniformly.
2) mud processed: by step 1) dispensing put into grinding in ball grinder to the fine powder of 30 mesh, and fine powder after grinding and Water is placed in clear mud sump corruption 6 months with the proportioning of 1:6, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body: walk throwing on mud platform is made required base substrate；
5) repaired biscuit: the base substrate drawn is placed dry place, cool place and dries in the shade, treat base substrate to parch afterwards and place it in rotation car On place under repair, make in base substrate outside light flat, and part unnecessary for bottom pared off；
6) decoration: to step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry: by the base substrate decorate drying to its surface temperature be 50 DEG C；
8) fire: by step 7) base substrate prepared is positioned in kiln, fires 24 hours at a temperature of 1270 DEG C, natural It is cooled to room temperature, kiln discharge.
Embodiment 3
A kind of chiltern vessel for tea frying, it is to be prepared from the following raw materials in parts by weight blank: Pulvis Talci 15 parts, lithium 20 parts of pyroxene, bentonite 14 parts, floating bead 15 parts and blue or green cash 20 parts.
A kind of method of chiltern vessel made described in the present embodiment for tea frying, comprises the following steps:
1) dispensing: weigh Pulvis Talci 15 parts, spodumene 20 parts, bentonite 14 parts, floating bead 15 parts and blue or green cash 20 parts, and mix Uniformly.
2) mud processed: by step 1) dispensing put into grinding in ball grinder to the fine powder of 30 mesh, and fine powder after grinding and Water is placed in clear mud sump corruption 4 months with the proportioning of 1:5, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body: walk throwing on mud platform is made required base substrate；
5) repaired biscuit: the base substrate drawn is placed dry place, cool place and dries in the shade, treat base substrate to parch afterwards and place it in rotation car On place under repair, make in base substrate outside light flat, and part unnecessary for bottom pared off；
6) decoration: to step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry: by the base substrate decorate drying to its surface temperature be 50 DEG C；
8) fire: by step 7) base substrate prepared is positioned in kiln, fires 24 hours at a temperature of 1260 DEG C, natural It is cooled to room temperature, kiln discharge.

Claims (2)

1. the chiltern vessel for tea frying, it is characterised in that: it is to be prepared from the following raw materials in parts by weight blank: Talcum Powder 10-20 part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10-30 part.
2. the method for chiltern vessel made described in claim 1 for tea frying, it is characterised in that: comprise the following steps:
1) dispensing: weigh Pulvis Talci 10-20 part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10- 30 parts, and mix homogeneously；
2) mud processed: by step 1) dispensing put into grinding in ball grinder to the fine powder of 30 mesh, and fine powder after grinding and water with The proportioning of 1:3-6 is placed in clear mud sump corruption 2 months to 6 months, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body: walk throwing on mud platform is made required base substrate；
5) repaired biscuit: the base substrate drawn is placed cool place and is dried place and dries in the shade, treat base substrate to parch afterwards to place it in that rotation car is enterprising Row is repaired, and makes in base substrate flat outside light, and part unnecessary for bottom is pared off；
6) decoration: to step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry: by the base substrate decorate drying to its surface temperature be 50 DEG C；
8) fire: by step 7) base substrate prepared is positioned in kiln, fires 24 hours at a temperature of 1230-1270 DEG C, from So it is cooled to room temperature, kiln discharge.
CN201610778524.2A 2016-08-30 2016-08-30 A kind of production method of the chiltern vessel for fried tea Active CN106242541B (en)