CN106827261A - The preparation method of eolith ware and eolith ware obtained by this method - Google Patents
The preparation method of eolith ware and eolith ware obtained by this method Download PDFInfo
- Publication number
- CN106827261A CN106827261A CN201710168088.1A CN201710168088A CN106827261A CN 106827261 A CN106827261 A CN 106827261A CN 201710168088 A CN201710168088 A CN 201710168088A CN 106827261 A CN106827261 A CN 106827261A
- Authority
- CN
- China
- Prior art keywords
- eolith
- ware
- firing
- glaze spraying
- base substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides the preparation method and eolith ware obtained by this method of eolith ware.In the present invention, after by the cutting of former stone, rotary-cut and engraving polishing, it is fired again, the step operation such as glaze spraying and secondary firing prepares eolith ware, such that it is able to while the original form and feature of former stone is retained to greatest extent, the release property and health-care effect of obtained eolith ware can also further be improved, vessel infiltration can also be prevented effectively from, its practicality is improved.Meanwhile, eolith ware provided by the present invention has the advantages that good impermeable, release property, no dust pollution and good health care effect.
Description
Technical field
Field is made the present invention relates to stone matter utensil, preparation method in particular to eolith ware and by the method
Obtained eolith ware.
Background technology
With the increase of the fast-developing and survival pressure of society, more and more the referring to of people returns nature, the need of people
Will also increasingly " regress into nature ", the product of various natural materials is also increasingly subject to the concern of people.
Stone matter vessel are natural due to moulding nature, quality, and with preferable machinability and certain health care work(
Effect, thus more and more welcomed by the people, it is various it is made of stones be filled with water or take up the stone matter vessel of food also emerge in an endless stream.
Traditional stone matter vessel are substantially and are made up of the direct grinding and buffing of former stone or engraving, for example, in the market is sold
The manufacture craft of limonite cup be typically just:Quarrying-primary election stone-examination wet concentration stone-cutting-pre-profiling-corase grind-is fixed
Type-finishing impression-polishing-selection packaging-finished product, or further in finished surface shell mechanism is inlayed by pressure, and
To finished product.Stone matter vessel prepared by this use traditional handicraft have the shortcomings that it is certain, such as due to the chamber wall of vessel is relatively thin,
Thus it is easily damaged, while relatively thin chamber wall is also easily caused infiltration, and then causes practicality poor.And temperature in the winter time
When relatively low, vessel note boiling water easily caused burst phenomenon suddenly.
Meanwhile, there is also in the prior art and natural stone is milled, and through further firing the method for preparing, such as it is existing
Technology CN103910522A (publication date:On July 9th, 2014) disclose a kind of drinking vessel being made of medical stone raw material and
Its manufacturing process, is raw material from medical stone raw ore in the technique, and pug will be sieved into after its ball milling, then base, is dried in the air
Dry sizing, is obtained drinking vessel.Although can to a certain extent solve the problems, such as that stone matter vessel seep water in this way,
It is that not only workload is big by natural stone milling, and dust pollution can be caused, while the further behaviour such as base, mud refining and firing
Make also relatively complicated, and the obtained vessel also natural texture without lithotome, the process of milling also results in vessel
Healthcare function declines.
Therefore, on the basis of the original natural texture of stone matter vessel and healthcare function is kept, the problems such as solve its infiltration,
Its practical effect is improved, just into current technical problem urgently to be resolved hurrily.
In view of this, it is special to propose the present invention.
The content of the invention
The first object of the present invention is to provide a kind of preparation method of eolith ware, in methods described, by by former stone
After stone material cutting, rotary-cut and engraving polishing, then be fired, the step operation such as glaze spraying and secondary firing prepares eolith
Ware, such that it is able to while the original form and feature of former stone is retained to greatest extent, can also further improve made
Obtain the release property and health-care effect of eolith ware, additionally it is possible to be prevented effectively from vessel infiltration, improve its practical effect.
The second object of the present invention is to provide a kind of eolith ware as obtained by the inventive method, eolith of the present invention
Ware has the advantages that good impermeable, release property, no dust pollution and good health care effect.
In order to realize above-mentioned purpose of the invention, spy uses following technical scheme:
A kind of preparation method of eolith ware, methods described comprises the following steps:Former stone is cut into base, Ran Houxuan
Cut, carve, and polish, obtain eolith ware base substrate;Then, eolith ware base substrate is fired;Then, outer surface glaze spraying is carried out simultaneously
Form by a firing, or electroplated or baking vanish, obtain final product eolith ware.
Optionally, in the present invention, the engraving includes engraving shaping and finishing impression.
Optionally, in the present invention, the firing temperature that eolith ware base substrate is fired is 400~900 DEG C.
Optionally, in the present invention, the glaze spraying is that the outer surface of eolith ware base substrate after firing carries out glaze spraying.
Optionally, in the present invention, the glaze spraying is one or many glaze spraying;
Wherein, when the glaze spraying is multiple glaze spraying, after eolith ware billet surface drying that need to be after previous glaze spraying, then
Glaze spraying after carrying out once, and formed by a firing after last time glaze spraying.
Optionally, in the present invention, described forming by a firing is to fire the eolith ware base substrate feeding stove high temperature after glaze spraying
Shaping;
Furnace temperature is uniformly warmed up to 400~900 DEG C from indoor temperature, the heating-up time is controlled in 12h~24h, is then lowered the temperature
Come out of the stove;And the vessel after firing are detected, if detection is qualified, the vessel after firing are finished product eolith ware, if
Detection is unqualified, then repeat repeatedly firing, until it is qualified to fire products obtained therefrom detection.
Optionally, in the present invention, the cooling is come out of the stove specially:Under the conditions of 400~900 DEG C of furnace temperature Temperature fall 12~
24h comes out of the stove for 120 DEG C or so to in-furnace temperature.
Meanwhile, present invention also offers a kind of eolith ware, the eolith ware is made to by the method for the invention
Arrive.
Optionally, in the present invention, the vessel are aquamanile.
Compared with prior art, beneficial effects of the present invention are:
(1) in the present invention, it is fired by eolith ware base substrate, such that it is able to effectively improve the suction of obtained vessel
Attached ability, can adsorb, decompose, removing various harmful substances;The water for wherein preserving is set to undergo no deterioration, it is spoiled.Meanwhile, by burning
System also can effectively discharge contained mineral matter in former stone, mineral element is enriched in surface, and then improve eolith ware of the present invention
Health-care effect;
(2) in the present invention, by carrying out glaze spraying and firing on face outside eolith ware, such that it is able to avoid eolith ware
There is infiltration phenomenon, improve the actually used value and performance of vessel;Water body and stone material directly contact can be made again, make ore deposit
Thing ion enters in water.
(3) integral production method of the present invention does not interfere with the natural texture of former stone, and causes obtained vessel sense organ more
Plus create an aesthetic feeling naturally, good practical effect and more resistant to pollution.
(4) glaze spraying and firing are carried out by eolith ware in the present invention, such that it is able to avoid eolith ware in daily life
Be not in burst in the case of in use living eolith ware being made to be heated to 95~100 DEG C suddenly under 0~10 DEG C of low temperature
Phenomenon.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the present invention.It is unreceipted specific in embodiment
Condition person, the condition advised according to normal condition or manufacturer is carried out.Agents useful for same or the unreceipted production firm person of instrument, are
The conventional products that can be obtained by commercially available purchase.
Preparation method provided by the present invention, raw material original stone can be the lithotomes such as medical stone, limonite, using natural
On the one hand stone material can cause the characteristics of product container is textured natural as raw material, on the other hand can also be using natural
The characteristics of stone material has health-care effect so that prepared vessel have health-care effect;
After selected former stone is cut into base, rotary-cut, engraving shaping and finishing impression are carried out, and polish and polish,
Obtain eolith ware base substrate;
Then, eolith ware base substrate is fired, by firing, can causes that stone material adsorption capacity strengthens, can adsorbed, divide
Solve, remove various harmful substances, suppress bacterium, viral activity, so that the water for wherein preserving will not be sent out rotten, will not also become
Taste, meanwhile, fire it is also possible that contained mineral element is enriched in surface in natural stone, the effect of health care can be played;Together
When, by firing, it is also possible to so that the micropore increase of stone material, so as to improve the rate of release of mineral matter included in stone material, enters
And improve the health-care effect of mineral concentration that it takes up water body and eolith ware of the present invention;
Meanwhile, the temperature of firing should be controlled at 400~900 DEG C, it is furthermore preferred that the temperature fired can be controlled 600
~750 DEG C, such as 620,650 or 700 DEG C etc.;
If firing temperature is too low, the effect for causing stone material by firing enhancing release is unable to reach;And if fired
Temperature is too high, then can destroy stone structure, and stone material is burnt what is more.
Then, the step of being exactly surface-treated, base substrate outer surface that for example can be after firing carries out glaze spraying and is fired into
Type, or electroplated or baking vanish in base substrate outer surface;Preferably, it is after carrying out glaze spraying to the base substrate after firing in the present invention
Form by a firing;
The step of glaze spraying, it is preferred that glaze spraying is to carry out glaze spraying in the outer surface of eolith ware base substrate, thus both be can guarantee that
Will not seepage, and water body can be allowd with stone material directly contact so that mineral ion can enter in water body;
Meanwhile, glaze spraying can be once glaze spraying, or repeatedly glaze spraying, the integral thickness of glaze can control 0.2~
0.4mm, such as 0.3 or 0.4mm etc.;When the glaze spraying is multiple glaze spraying, eolith ware base substrate that need to be after previous glaze spraying
After dry tack free (i.e. previous glaze dry after), then the glaze spraying after carrying out once;Drying can be used dries, dries or low temperature
The method of firing is carried out;
Then, it is exactly that the step of eolith ware base substrate after glaze spraying is sent into the firing of stove high temperature, high-temperature firing can join
Examine as follows:In-furnace temperature is uniformly warmed up to 400~900 DEG C from room temperature, the heating-up time is controlled in 12~24h, then lowers the temperature
Stove, obtains eolith ware.
Further, the firing can for once or repeatedly, specifically will test stone vessel according to the observation firing feelings
Condition (having bubble-free, crackle) determines that vessel once or repeatedly fire, lower the temperature by decision, finally obtain flawless falling into
Eolith ware finished product.
Using the method for the firing that progressively heats up, it is possible to increase yield rate, it is to avoid the appearance caused by too fast intensification is split
The defect of the finished product structures such as line;
Finally, it is that cooling is come out of the stove, obtains eolith ware finished product;Preferably, cooling step is also adopted by following progressively cooling
Method, i.e.,:Come out of the stove when 12~24h of Temperature fall under the conditions of 400~900 DEG C of furnace temperature is to 120 DEG C or so of in-furnace temperature;
Progressively lower the temperature, and be incubated in temperature-fall period, it is also possible to further improve yield rate, too fast cooling rate
It is equally possible to cause the appearance of defect ware or shoddy goods.
Eolith ware provided by the present invention, can be aquamanile, or take up food or as ornament
Vessel;Because the eolith ware as made by the present invention has good adsorption capacity, can adsorb, decompose, remove it is various
Harmful substance, suppresses bacterium, viral activity, it is possible to so that the water body for being taken up never degenerates for a long time, simultaneously as former stone
Vessel surface is enriched mineral matter element, it is also possible to so that water body is rich in mineral matter, with good health-care effect.
Embodiment 1
Natural limonite is taken for raw material, and limonite teacup is prepared according to methods described below:
Wooden fish stone is cut into base, then rotary-cut, hand engraving shaping, manual finishing impression, and polish, respectively obtain wood
Fish stone teacup cup body base substrate and cup lid base substrate;
Gained base substrate is incubated under the conditions of 400~900 DEG C 12~24h of firing, and by the base substrate natural cooling after firing
To room temperature;
Base substrate after cooling is carried out into first time glaze spraying in outer surface, the thickness control of glaze treats base in 0.1~0.2mm
After body surface face is dried, second glaze spraying is carried out, the thickness control of glaze is dried in 0.15~0.2mm;
Base substrate after glaze spraying is fired, step is fired specific as follows:
Eolith ware base substrate feeding stove high temperature after glaze spraying is fired, furnace temperature is uniformly heating to 400~900 from room temperature
DEG C, 12~24h of heating-up time.Then cooling is come out of the stove.And repeat this step and burn repeatedly to obtaining zero defect eolith ware.
Then, after last time is fired, by furnace temperature by 400~900 DEG C of 12~24h of Temperature fall to in-furnace temperature 120
DEG C come out of the stove, that is, obtain the limonite teacup of embodiment 1.
Observed through surface, the limonite teacup inwall obtained by embodiment 1 still keeps the natural form of natural limonite, whole
Figure modelling nature, close to original stone form.
Embodiment 2
Natural medical stone is taken for raw material, and medical stone teapot is prepared according to methods described below:
Medical stone stone material is cut into base, then rotary-cut, hand engraving shaping, manual finishing impression, and polish, respectively obtain wheat
Meal stone tea kettle bottle body base substrate and pot lid base substrate;
Gained base substrate is incubated under the conditions of 400~900 DEG C 12~24h of firing, and by the base substrate natural cooling after firing
To room temperature;
Base substrate after cooling is carried out into first time glaze spraying in outer surface, the thickness control of glaze treats base in 0.1~0.2mm
After body surface face is dried, second glaze spraying is carried out, the thickness control of glaze is dried in 0.15~0.2mm;
Base substrate after glaze spraying is fired, step is fired specific as follows:
Eolith ware base substrate feeding stove high temperature after glaze spraying is fired;By in the eolith ware base substrate feeding stove after glaze spraying
High-temperature firing, 400~900 DEG C are uniformly heating to by furnace temperature from room temperature, and 12~24h of heating-up time, then cooling is come out of the stove;And repeat
This step is fired repeatedly, until obtaining flawless eolith ware.
After last time is fired, furnace temperature is come out of the stove for 120 DEG C by 400~900 DEG C of 12~24h of Temperature fall to in-furnace temperature
Obtain the medical stone teapot of embodiment 2.
Observed through surface, the medical stone teapot inwall obtained by embodiment 2 still keeps the natural form of natural medical stone, whole
Figure modelling nature.
Comparative example 1
Limonite teacup is prepared according to the methods described of embodiment 1, wherein, burnt not comprising glaze spraying and further in comparative example 1
Processed the step of.
Comparative example 2
Prepare limonite teacup according to the methods described of embodiment 1, wherein, in comparative example 2 not to limonite teacup cup body and
Cup lid base substrate is fired, but directly carries out glaze spraying and firing to gained base substrate.Comparative example 3
Limonite teacup is prepared according to the methods described of embodiment 2, wherein, burnt not comprising glaze spraying and further in comparative example 3
Processed the step of.
Comparative example 4
Limonite teacup is prepared according to the methods described of embodiment 2, wherein, not to medical stone teapot bottle body base in comparative example 4
Body and pot lid base substrate are fired, but directly carry out glaze spraying and firing to gained base substrate.
Experimental example 1
Take the limonite teacup obtained by 10 sets of embodiments 1, comparative example 1 and comparative example 2 at random respectively, meanwhile, in market
Upper 10 sets of with cover ceramic teacups close with the shapes and sizes of embodiment 1 of buying at random;
Then, respectively to the water that equivalent is poured into embodiment 1, comparative example 1, comparative example 2 and commercially available teacup, amount of water control
The 3/4~4/5 of teacup volume;Then, the teacup lid of each group teacup correspondence is covered, be placed in cool place under room temperature condition,
In ventilative environment;
After 3h is placed, each group teacup is observed, as a result found:10 sets of teacup surfaces of comparative example 1 substantially go out
The different infiltration phenomenon of existing degree, and other experimental group teacups do not occur infiltration;
After 1d is placed, each group teacup is observed again, as a result found:10 sets of teacup surfaces of comparative example 1 are still
The different infiltration phenomenon of presentation degree, and other experimental group teacups do not occur infiltration;Then, taken out from each group teacup respectively
The water of appropriate storage, and trial test evaluation and test is carried out, as a result finding, in embodiment 1 and comparative example 1, the water deposited in each teacup is simultaneously
There is not discoloration or peculiar smell, and the water deposited in comparative example 2 and commercially available each teacup slightly has fishy smell;
After 3d is placed, each group teacup is observed again, as a result found:10 sets of teacups of comparative example 1 still have seepage
Phenomenon, the water deposited in cup remains little, and other experimental group teacups do not occur infiltration;Then, respectively from each group teacup
The water of appropriate storage is taken out, and carries out trial test evaluation and test, as a result found, the water deposited in embodiment 1 and each teacup of comparative example 1 is simultaneously
There is not discoloration or peculiar smell, and the water fishy smell deposited in comparative example 2 is more obvious, the water fishy smell deposited in commercially available teacup
It is larger, it is more difficult to swallow;
After 7d is placed, each group teacup is observed again, as a result found:10 sets of teacup reclaimed waters of comparative example 1 have been leaked
Light, and other experimental group teacups do not occur infiltration;Then, the water of appropriate storage is taken out from each group teacup respectively, and is carried out
Evaluation and test is tasted, is as a result found, peculiar smell does not occur changing colour or occur in the water deposited in embodiment 1, and comparative example 2 and commercially available
Each teacup in the water fishy smell deposited clearly and slightly stink, it is impossible to drink.
As can be seen here, the limonite teacup as obtained by the inventive method can not only be prevented effectively from the seepage of water, together
When food materials functional fibre on containing the trace element such as substantial amounts of silicon, aluminium, all there is very strong suction-operated, energy to bacterium and virus
Enough activities for effectively suppressing bacterium and virus, it is also possible to effectively improve the shelf-life of water.
Meanwhile, found through ion detection, after being deposited through embodiment 1 and the teacup of comparative example 1, the content of mineral substances in water body is bright
It is aobvious to increase;And after using the teacup of embodiment 2 storage water body, the content of mineral substances of water body also increased, but content of mineral substances
Significantly lower than embodiment 1 and comparative example 1;In water body after being deposited using commercially available ceramic teacup, content of mineral substances is increased slightly, but
It is unobvious.
Experimental example 2
Take the medical stone teapot obtained by 10 sets of embodiments 2, comparative example 3 and comparative example 4 at random respectively, meanwhile, in market
Upper 10 sets of with cover ceramic teapots close with the shapes and sizes of embodiment 1 of buying at random;
Then, identical experiment is carried out with reference to the method for experimental example 1, is as a result found, it is embodiment 2, right in process of the test
Not there is seepage in ratio 4 and commercially available teapot, and the seepage of each set teapot is more obvious in comparative example 3, and after 5d, water is complete
Full light leak;
Meanwhile, the water in the teapot of embodiment 2 does not go bad after 7d is deposited, and its flavor taste has no with fresh water body
Difference;And the water deposited in comparative example 4 just substantially has fishy smell after 2d, bad smell is obvious after storage 5d;Meanwhile, it is commercially available
The water deposited in teapot just substantially has peculiar smell after 1d, and fishy smell is particularly evident after storage 3d, is smelt as of rotten fish after 5d unpleasant, it is impossible to drink
With.
Experimental example 3
(1) experimental group 1:
Natural limonite is taken for raw material, and limonite teacup is prepared according to the methods described of embodiment 1, wherein, in experimental group 1
Step is fired after glaze spraying specific as follows:
Eolith ware base substrate feeding stove high temperature after glaze spraying is fired, wherein firing temperature is directly warming up to by room temperature
400~900 DEG C, and it is 2~4h to control the heating-up time;Then, in 2-3h, furnace temperature is down to 120 DEG C or so to coming out of the stove, i.e.,
Obtain the limonite teacup of experimental group 1.
Then, 100 limonite teacups as obtained by experimental group 1 are randomly selected, is as a result found, obtained by experimental group 1
Limonite teacup in:There are 3 cups of teacup obvious crackle occur, and after water is filled, cracks occur and occur oozing a little
Leakage;There is crackle in the cup or cup lid for having 8 teacups, after there is the cup dress water of crackle, it may appear that slight seepage;
Meanwhile, 100 limonite teacups as obtained by embodiment 1 are randomly selected, as a result find, only 2 teacups
There is crackle in cup, and can slightly have seepage after water is filled.
As can be seen here, by the way of progressively liter is gently progressively lowered the temperature, the yield rate of vessel can be effectively improved.
(2) experimental group 2
Natural medical stone is taken for raw material, and medical stone teapot is made according to the methods described of embodiment 2, wherein, experimental group 2
In, medical stone teapot bottle body base substrate and pot lid base substrate are to be incubated to fire 1~2h under the conditions of 1100~1200 DEG C, and by after firing
Base substrate naturally cool to room temperature;Then glaze spraying and firing are carried out according still further to method described in embodiment 2.
Then, 100 medical stone teapots as obtained by experimental group 2 are randomly selected, is as a result found, obtained by experimental group 1
Medical stone teapot in:The kettle body inwall for having 5 teapots substantially blacks, and has obvious crackle, and kettle body inwall is gently scraped with file
Afterwards, there is a small amount of disintegrating slag for coming off, meanwhile, after water is filled, there is Crack handling and a little seepage occur;There are 6 kettle bodies of teapot
Or crackle occurs in pot lid, after there is the cup dress water of crackle, it may appear that slight seepage;
Meanwhile, 100 medical stone teapots as obtained by embodiment 2 are randomly selected, as a result find, only 2 teapots
There is crackle in kettle body inwall, and can slightly have seepage after water is filled;Meanwhile, the kettle body inwall of only 1 teapot slightly has nigrescence.
As can be seen here, former stone firing temperature has also influenceed for yield rate, and firing temperature is too high substantially to cause finished product
Rate declines.
Although illustrate and describing the present invention with specific embodiment, but will be appreciated that without departing substantially from of the invention
Many other changes and modification can be made in the case of spirit and scope.It is, therefore, intended that in the following claims
Including belonging to all such changes and modifications in the scope of the invention.
Claims (9)
1. a kind of preparation method of eolith ware, it is characterised in that methods described comprises the following steps:Former stone is cut into
Base, then rotary-cut, engraving, and polish, and obtain eolith ware base substrate;Then, eolith ware base substrate is fired;Then, sprayed
Glaze is simultaneously formed by a firing, or is electroplated or baking vanish, obtains final product eolith ware.
2. preparation method according to claim 1, it is characterised in that the engraving includes engraving shaping and finishing impression, beats
Mill, finishing polish.
3. preparation method according to claim 1, it is characterised in that according to different former stone materials by eolith ware base substrate
The firing temperature of firing is 400~900 DEG C.
4. preparation method according to claim 1, it is characterised in that the glaze spraying is eolith ware base substrate after firing
Outer surface carry out glaze spraying.
5. preparation method according to claim 4, it is characterised in that the glaze spraying is one or many glaze spraying;
Wherein, when the glaze spraying is multiple glaze spraying, after eolith ware billet surface drying that need to be after previous glaze spraying, then carry out
Glaze spraying once afterwards, and formed by a firing after last time glaze spraying.
6. preparation method according to claim 1, it is characterised in that described forming by a firing is eolith ware by after glaze spraying
Base substrate feeding stove high temperature is formed by a firing;
Furnace temperature is uniformly heating to 400~900 DEG C from indoor temperature, heating-up time control is come out of the stove in 12h~24h, then cooling;
And the vessel after firing are detected, if detection is qualified, the vessel after firing are finished product eolith ware, if detection is not
It is qualified, then repeat repeatedly firing, until it is qualified to fire products obtained therefrom detection.
7. preparation method according to claim 6, it is characterised in that the cooling is come out of the stove specially:By furnace temperature by 400~
Temperature fall 6h~12h under the conditions of 900 DEG C, comes out of the stove for 120 DEG C or so to in-furnace temperature.
8. a kind of eolith ware, it is characterised in that the eolith ware is the method system as any one of claim 1-7
.
9. eolith ware according to claim 8, it is characterised in that the eolith ware is aquamanile.