CN106380182A - Sandy vessel for wine heating and manufacturing method thereof - Google Patents

Sandy vessel for wine heating and manufacturing method thereof Download PDF

Info

Publication number
CN106380182A
CN106380182A CN201610766657.8A CN201610766657A CN106380182A CN 106380182 A CN106380182 A CN 106380182A CN 201610766657 A CN201610766657 A CN 201610766657A CN 106380182 A CN106380182 A CN 106380182A
Authority
CN
China
Prior art keywords
base substrate
parts
mud
vessel
wine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610766657.8A
Other languages
Chinese (zh)
Inventor
古林子
刘先勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Original Assignee
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pingding County Hat Kiln Sand Device Pottery Art Co Ltd filed Critical Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority to CN201610766657.8A priority Critical patent/CN106380182A/en
Publication of CN106380182A publication Critical patent/CN106380182A/en
Pending legal-status Critical Current

Abstract

The invention belongs to a sandy container and a manufacturing method thereof and relates to a sandy vessel for wine heating and a manufacturing method thereof. A blank is prepared from 20-30 parts of bauxite, 10-30 parts of spodumene, 8-20 parts of bentonite, 10-20 parts of floating beads and 10-30 parts of green waste rock. Through blending, mud making, blank making, blank finishing, decoration, drying and sintering, the sandy vessel is obtained. The blending, blank making and sintering processes are key processes. The manufacturing method prevents seepage and cracks of the wine heating vessel after heating. The wine heating vessel does not produce water marks in 24h, has stable physical properties and heat insulation effects and has good air permeability.

Description

A kind of chiltern vessel for heat wine and preparation method thereof
Technical field
The invention belongs to sand container and preparation method thereof is and in particular to a kind of chiltern vessel for heat wine and its making Method.
Background technology
Boil wine opinion hero, heat wine is of long standing and well established as an arteries and veins of Characters of Chinese Alcoholic Drink Culture from ancient times.Either white wine or yellow rice wine, its In all contain the organic compounds such as methyl alcohol, formaldehyde, methyl ether, in order to reduce the residual quantity of these toxin, by drinks scald heat arrive 30-40 Degree is drunk again, because formaldehyde, methyl ether boiling point are relatively low, during boiling hot heat, formaldehyde, methyl ether thoroughly volatilize with the rising of temperature Fall.Although market is no lack of pottery or porcelain wine heater, the characteristic of pottery or porcelain is heated fast radiating also soon, can not be continued constant temperature； In addition, ceramic surface glazing, has directly prevented the gas permeability of wine heater, but removes not thorough limited by alcohol intoxication element residual natural.
Content of the invention
Present invention aim to address existing wine heater exists and being heated uneven, poor air permeability and removes alcohol intoxication element residual Halfway technical problem limited by nature, provides a kind of chiltern vessel for heat wine and preparation method thereof.
For solving above-mentioned technical problem, the technical solution used in the present invention is：
A kind of chiltern vessel for heat wine, it is to be prepared from the following raw materials in parts by weight blank：Bauxite 20-30 Part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10-30 part.
A kind of method making the described chiltern vessel for heat wine, comprises the following steps：
1) dispensing：Weigh bauxite 20-30 part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10-30 part, and mix；
2) mud processed：By step 1) dispensing put into grinding in ball grinder to the fine powder of 80 mesh, and by the fine powder after grinding and Water is with 1:The proportioning of 3-6 is placed in clear mud sump degenerates 2 months to 6 months, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body：By walk, on mud platform, throwing makes required base substrate；
5) repaired biscuit：Dried in the shade in the base substrate the having drawn placement cool place place of drying, treat that base substrate places it in rotation car after parching On place under repair, make outside light in base substrate flat, and part unnecessary for bottom pared off；
6) decorate：To step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry：The base substrate decorated is dried and is 50 DEG C to its surface temperature；
8) fire：By step 7) base substrate prepared is positioned in kiln, fires 12 little at a temperature of 1230-1270 DEG C When, naturally cool to normal temperature, kiln discharge.
The present invention adopts above technical scheme, makees raw material by bauxite, spodumene, bentonite, floating bead and blue or green cash, by joining Material, mud processed, base, repaired biscuit, decoration, drying, burning process flow process make, critical process in dispensing, base, the link such as fire, Ensure heat wine alms bowl heating after non-leakage flawless, 24 hour circle foot no washmarkings, the wine heater stable physical property produced, Effect of heat insulation is stable, good permeability.Sand utensil has " fast slow, the good permeability that radiates of heat transfer " special physical characteristic, therefore, uses sand Device heats wine heat wine vessel, both can temperature raising (30-40 degree) rapidly, again can be quickly by the methyl alcohol in white wine or yellow rice wine, formaldehyde, methyl ether The residual quantity of these organic toxin thoroughly vapors away；Both sustainable constant temperature kept hot gas in kettle, can make aroma more glycol again.And not Species by wine is limited, can multi-use.
Specific embodiment
Embodiment 1
One of the present embodiment is used for the chiltern vessel of heat wine, and it is to be prepared from the following raw materials in parts by weight blank： 20 parts of bauxite, 10 parts of spodumene, 8 parts of bentonite, 10 parts of floating bead and blue or green 10 parts of cash.
A kind of method making the chiltern vessel being used for heat wine described in the present embodiment, comprises the following steps：
1) dispensing：Weigh 20 parts of bauxite, 10 parts of spodumene, 8 parts of bentonite, 10 parts of floating bead and blue or green 10 parts of cash, and mix Uniformly.
2) mud processed：By step 1) dispensing put into grinding in ball grinder to the fine powder of 80 mesh, and by the fine powder after grinding and Water is with 1:3 proportioning is placed in clear mud sump degenerates 2 months, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body：By walk, on mud platform, throwing makes required base substrate；
5) repaired biscuit：Dried in the shade in the base substrate the having drawn placement cool place place of drying, treat that base substrate places it in rotation car after parching On place under repair, make outside light in base substrate flat, and part unnecessary for bottom pared off；
6) decorate：To step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry：The base substrate decorated is dried and is 50 DEG C to its surface temperature；
8) fire：By step 7) base substrate prepared is positioned in kiln, fires 12 hours at a temperature of 1230 DEG C, natural It is cooled to normal temperature, kiln discharge.
Embodiment 2
One of the present embodiment is used for the chiltern vessel of heat wine, and it is to be prepared from the following raw materials in parts by weight blank： 30 parts of bauxite, 30 parts of spodumene, 20 parts of bentonite, 20 parts of floating bead and blue or green 30 parts of cash.
A kind of method making the chiltern vessel being used for heat wine described in the present embodiment, comprises the following steps：
1) dispensing：Weigh 30 parts of bauxite, 30 parts of spodumene, 20 parts of bentonite, 20 parts of floating bead and blue or green 30 parts of cash, and mix Uniformly.
2) mud processed：By step 1) dispensing put into grinding in ball grinder to the fine powder of 80 mesh, and by the fine powder after grinding and Water is with 1:6 proportioning is placed in clear mud sump degenerates 6 months, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body：By walk, on mud platform, throwing makes required base substrate；
5) repaired biscuit：Dried in the shade in the base substrate the having drawn placement cool place place of drying, treat that base substrate places it in rotation car after parching On place under repair, make outside light in base substrate flat, and part unnecessary for bottom pared off；
6) decorate：To step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry：The base substrate decorated is dried and is 50 DEG C to its surface temperature；
8) fire：By step 7) base substrate prepared is positioned in kiln, fires 12 hours at a temperature of 1270 DEG C, natural It is cooled to normal temperature, kiln discharge.
Embodiment 3
One of the present embodiment is used for the chiltern vessel of heat wine, and it is to be prepared from the following raw materials in parts by weight blank： 25 parts of bauxite, 20 parts of spodumene, 12 parts of bentonite, 15 parts of floating bead and blue or green 20 parts of cash.
A kind of method making the chiltern vessel being used for heat wine described in the present embodiment, comprises the following steps：
1) dispensing：Weigh 25 parts of bauxite, 20 parts of spodumene, 12 parts of bentonite, 15 parts of floating bead and blue or green 20 parts of cash, and mix Uniformly.
2) mud processed：By step 1) dispensing put into grinding in ball grinder to the fine powder of 80 mesh, and by the fine powder after grinding and Water is with 1:5 proportioning is placed in clear mud sump degenerates 3 months, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body：By walk, on mud platform, throwing makes required base substrate；
5) repaired biscuit：Dried in the shade in the base substrate the having drawn placement cool place place of drying, treat that base substrate places it in rotation car after parching On place under repair, make outside light in base substrate flat, and part unnecessary for bottom pared off；
6) decorate：To step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry：The base substrate decorated is dried and is 50 DEG C to its surface temperature；
8) fire：By step 7) base substrate prepared is positioned in kiln, fires 12 hours at a temperature of 1250 DEG C, natural It is cooled to normal temperature, kiln discharge.

Claims (2)

1. a kind of chiltern vessel for heat wine it is characterised in that：It is to be prepared from the following raw materials in parts by weight blank：Aluminium alum Native 20-30 part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10-30 part.
2. a kind of make described in claim 1 be used for heat wine chiltern vessel method it is characterised in that：Comprise the following steps：
1) dispensing：Weigh bauxite 20-30 part, spodumene 10-30 part, bentonite 8-20 part, floating bead 10-20 part and blue or green cash 10- 30 parts, and mix；
2) mud processed：By step 1) dispensing put into grinding in ball grinder to the fine powder of 80 mesh, and by the fine powder after grinding and water with 1:The proportioning of 3-6 is placed in clear mud sump degenerates 2 months to 6 months, makes base mud；
3) by step 2) the base mud prepared is kneaded into walk repeatedly, and walk requires pore-free, free from admixture, and uniformly；
4) base body：By walk, on mud platform, throwing makes required base substrate；
5) repaired biscuit：Dried in the shade in the base substrate the having drawn placement cool place place of drying, treat that base substrate places it in rotation car after parching enterprising Row is repaired, and makes flat outside light in base substrate, and part unnecessary for bottom is pared off；
6) decorate：To step 5) base substrate made carries out the decoration of shape, moulding and color；
7) dry：The base substrate decorated is dried and is 50 DEG C to its surface temperature；
8) fire：By step 7) base substrate prepared is positioned in kiln, fires 12 hours at a temperature of 1230-1270 DEG C, from So it is cooled to normal temperature, kiln discharge.
CN201610766657.8A 2016-08-30 2016-08-30 Sandy vessel for wine heating and manufacturing method thereof Pending CN106380182A (en)