CN107879717A - A kind of boccaro rock mud health water storage bottle and preparation method thereof - Google Patents
A kind of boccaro rock mud health water storage bottle and preparation method thereof Download PDFInfo
- Publication number
- CN107879717A CN107879717A CN201711211882.6A CN201711211882A CN107879717A CN 107879717 A CN107879717 A CN 107879717A CN 201711211882 A CN201711211882 A CN 201711211882A CN 107879717 A CN107879717 A CN 107879717A
- Authority
- CN
- China
- Prior art keywords
- parts
- mud
- boccaro
- water storage
- health
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of boccaro rock mud health water storage bottle, including, each raw material of following parts by weight：85 99.5 parts of mixing raw ore base-material and 0.5 15 parts of health additive；The mixing raw ore base-material includes：Calm down volcanic rock mud and boccaro group mud of calming down, the health additive includes blue or green spoil, white spoil, orpiment stone, astroies, tourmaline, opal, serpentine, medical stone, Strange ice stone, hokutolite, Doctor king stone and shell.The present invention also provides a kind of preparation method of boccaro rock mud health water storage bottle.The mixing raw ore of the present invention, which originates from, calms down pure natural mineral aggregate, and volcanic rock mud density is relatively low, containing human body several mineral materials, has the function that demineralized water, meanwhile, the also sustainable multiple beneficial element that discharges greatly promotes the effect of health into water；In addition, volcanic rock mud with honeycomb air hole structure not only wall is with more preferable gas permeability, and device body particle is plentiful, glossiness is uniform, and feel exquisiteness is gentle.
Description
Technical field
The invention belongs to boccaro production field, and in particular to a kind of to utilize the boccaro rock mud health water storage for mixing raw ore preparation
Kettle and preparation method thereof.
Background technology
During purple sand process product are made, pug is most important factor, is to determine a purple sand process product taste
Important scale.The pug of purple sand process product is made, species there are many kinds, is broadly divided into three major types：Purple mud, red soil, green mud.
At present, the pug that in the market makes purple-clay product is typically all to be formed using proportionings such as purple mud, section mud, red soil.Have
When, the original color and luster of pigment alteration sand can be also added in the formula of pug, produces the dark-red enameled pottery and tea set of various color and lusters.But
At present, the purple-clay product generally existing pug made using above-mentioned pug is not coarse, exquisite, is typically made compared with adaptive model, together
When the pug also bring the inconvenience made by hand, be mainly shown as that the thickness of slice cannot be guaranteed uniformly, to easily cause change
Shape, and easily being ftractureed when burning till, brings the decline of yield rate, and the waste of pug is larger.Made in addition using such a pug
Purple-clay product can also influence the gas permeability and quality of purple-clay product.The technique for exquisiteness of being done manual work especially for some requirements, by
The value of purple-clay product is influenceed in the reason for the pug itself, while has also had a strong impact on the popularization of purple sand process culture.
The content of the invention
In consideration of it, it is an object of the present invention to provide it is a kind of using mix raw ore preparation boccaro rock mud health water storage bottle,
It is intended to overcome existing purple-clay product pug is unfavorable in manufacturing process to be molded and be easily deformed by hand, causes the boccaro being fired into
The defects of product generally existing pug is coarse, not exquisite and then influence purple-clay product gas permeability.
Another object of the present invention is to, there is provided a kind of utilize mixes the making that raw ore prepares boccaro rock mud health water storage bottle
Method, it is intended to solve the problems, such as using easy cracking during existing pug fired purple-clay product.
In order to reach foregoing invention purpose, the technical scheme taken is as follows：
A kind of boccaro rock mud health water storage bottle, including, each raw material of following parts by weight：
The mixing raw ore base-material of 85-99.5 parts and the health additive of 0.5-15 parts；
The mixing raw ore base-material includes：Calm down volcanic rock mud and calm down boccaro group mud, wherein, the volcanic rock mud of calming down
With calm down boccaro group mud weight proportion be 80:20；
The health additive includes following ingredients in parts by weight：Blue or green 45~60 parts of spoil；White spoil 35~50
Part；7~15 parts of orpiment stone；10~15 parts of astroies；30~50 parts of tourmaline；10~20 parts of opal；Serpentine 15~20
Part；5~10 parts of medical stone；10~15 parts of Strange ice stone；2~4 parts of hokutolite；2~4 parts of Doctor king stone；10~15 parts of shell.
Further, the boccaro of calming down rolls into a ball each component that mud drum includes following parts by weight:Purple mud, green mud and white clay, wherein
The ratio of purple mud, green mud and white clay is 70-80:5-10:10-25.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water storage bottle, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 75 mesh, it is standby；
S2：System material, calm down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 80 by ground:20 ratio
Mixing raw ore base-material is mixed to form, it is standby；
S3：Pugging, choose mixing raw ore base-material 85-99.5 parts in parts by weight and the mixing of health additive 0.5-15 parts
Mixing pug is formed, and is placed in pugging and mixes after mountain spring water is added in mixing pug；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 100:30, the health additive is included with weight
Measure the following ingredients of part meter：Blue or green 45~60 parts of spoil；White 35~50 parts of spoil；7~15 parts of orpiment stone；Astroies 10~15
Part；30~50 parts of tourmaline；10~20 parts of opal；15~20 parts of serpentine；5~10 parts of medical stone；10~15 parts of Strange ice stone；
2~4 parts of hokutolite；2~4 parts of Doctor king stone；10~15 parts of shell；
S4：Mixing pug equal portions that are old, will having refined, cylinder interior sealing is placed in oilpaper encapsulation, cylinder is placed in closed
1-5 is stood in environment；
S5：Embryo processed, will be old after mixing pug, pat be moulded into type into being labelled to mould left-hand seat after 3-5mm slice by hand
Form mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 24-36h, forged
It is 1230-1370 DEG C to burn temperature, kiln discharge after calcining terminates insulation 12-24 hours, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water storage bottle burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 24-36h,
Calcining heat is 1230-1370 DEG C, kiln discharge after calcining terminates insulation 12-24 hours, automatic cooling；
S9：Third firing, the water storage bottle after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 45-60mi n, calcining heat is 1350-1450 DEG C, and its water storage bottle is immediately placed on closed reduction kiln by calcining after terminating
Kiln discharge forms boccaro rock mud health water storage bottle after interior automatic cooling.
Further, the boccaro of calming down rolls into a ball each component that mud drum includes following parts by weight:Purple mud, green mud and white clay, wherein
The ratio of purple mud, green mud and white clay is 70-80:5-10:10-25.
Beneficial effects of the present invention：The boccaro rock mud health water storage bottle of the present invention is prepared using raw ore is mixed, and it is mixed
Raw ore originates from the pollution-free pure natural mineral aggregate calmed down and produced, and the volcanic rock mud density of one of them is relatively low, containing pole beneficial to people
The several mineral materials of body, demineralized water can be played a part of, and the pH value of adjustable water quality enters millet paste between 7.1-8.2
Mouth is natural, returns sweet long, larynx rhythm multiplication, meanwhile, also sustainable release multiple beneficial element greatly promotes the effect of health into water
Fruit；In addition, the honeycomb air hole structure that volcanic rock mud has itself makes the gas permeability of the boccaro rock mud health water storage bottle of preparation remote
Better than other tanks, not only wall has more preferable gas permeability, and device body particle is plentiful, glossiness is uniform, and feel is thin
It is greasy gentle；In addition, nuisance can be kept at a high temperature of 1200 degree using the boccaro rock mud health water storage bottle for mixing raw ore preparation
Zero separates out so that diet is safer, while will not make pottery porcelain under hot environment, can also allow its gas permeability and saturating fragrance more
It is excellent；Finally, the present invention uses the combination of mixing raw ore base-material and health additive, and optimizes composition proportion so that air hole structure
Maximize, while also overcome the defects of slow seepage is understood in not glazing in traditional technique.
Embodiment
In order that those skilled in the art more fully understand application scheme, below in conjunction with the implementation in the application
Example, the technical scheme of the application is clearly and completely described, it is clear that described embodiment is only the application one
The embodiment divided, rather than whole embodiments.Based on the embodiment in the application, those of ordinary skill in the art are not doing
Go out under the premise of creative work the every other embodiment obtained, should all belong to the scope of the application protection.
Embodiment 1
A kind of boccaro rock mud health water storage bottle, including, each raw material of following parts by weight：
85 parts of mixing raw ore base-material and 15 parts of health additive；The mixing raw ore base-material includes：Calm down volcanic rock
Mud and calm down boccaro group mud, wherein, it is described calm down volcanic rock mud and calm down boccaro group mud weight proportion be 80:20；It is described flat
Determine each component that boccaro group mud drum includes following parts by weight:Purple mud, green mud and white clay, wherein comparing purple mud, green mud and matching somebody with somebody for white clay
Example is 70:5:25；The health additive includes following ingredients in parts by weight：Blue or green 45 parts of spoil；White 35 parts of spoil；Stone
7 parts of Huangshi；10 parts of astroies；30 parts of tourmaline；10~20 parts of opal；15 parts of serpentine；5 parts of medical stone；Strange ice stone 10
Part；2 parts of hokutolite；2 parts of Doctor king stone；10 parts of shell.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water storage bottle, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 75 mesh, it is standby；
S2：System material, calm down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 80 by ground:20 ratio
Mixing raw ore base-material is mixed to form, it is standby；
S3：Pugging, 85 parts of the mixing raw ore base-material chosen in parts by weight are mixed to form mixing with 15 parts of health additive
Pug, and be placed in pugging and mix after mountain spring water is added in mixing pug；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 100:30, the health additive is included with weight
Measure the following ingredients of part meter：Blue or green 45 parts of spoil；White 35 parts of spoil；7 parts of orpiment stone；10 parts of astroies；30 parts of tourmaline；Egg
White 10~20 parts of stone；15 parts of serpentine；5 parts of medical stone；10 parts of Strange ice stone；2 parts of hokutolite；2 parts of Doctor king stone；10 parts of shell；
S4：Mixing pug equal portions that are old, will having refined, cylinder interior sealing is placed in oilpaper encapsulation, cylinder is placed in closed
1 year is stood in environment；
S5：Embryo processed, will be old after mixing pug, pat be moulded into type shape into being labelled to mould left-hand seat after 3mm slice by hand
Into mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 24h, calcining temperature
Spend for 1230 DEG C, calcining terminates kiln discharge after being incubated 12 hours, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water storage bottle burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 24h, calcining
Temperature is 1230 DEG C, and calcining terminates kiln discharge after being incubated 12 hours, after automatic cooling；
S9：Third firing, the water storage bottle after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 45mi n, calcining heat is 1350 DEG C, and its water storage bottle is immediately placed in closed reduction kiln by calcining after terminating to drop automatically
Kiln discharge forms boccaro rock mud health water storage bottle after temperature.
Embodiment 2
A kind of boccaro rock mud health water storage bottle, including, each raw material of following parts by weight：99.5 parts of mixing raw ore base-material and
0.5 part of health additive；The mixing raw ore base-material includes：Calm down volcanic rock mud and boccaro group mud of calming down, wherein, it is described flat
Determine volcanic rock mud and calm down boccaro group mud weight proportion be 80:20；The boccaro group mud drum of calming down includes each of following parts by weight
Component:Purple mud, green mud and white clay, wherein the ratio of purple mud, green mud and white clay is 80:10:10；The health additive bag
Include following ingredients in parts by weight：Blue or green 60 parts of spoil；White 50 parts of spoil；15 parts of orpiment stone；15 parts of astroies；Tourmaline
50 parts；20 parts of opal；20 parts of serpentine；10 parts of medical stone；15 parts of Strange ice stone；4 parts of hokutolite；4 parts of Doctor king stone；Shell 15
Part.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water storage bottle, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 75 mesh, it is standby；
S2：System material, calm down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 80 by ground:20 ratio
Mixing raw ore base-material is mixed to form, it is standby；
S3：Pugging, 99.5 parts of the mixing raw ore base-material chosen in parts by weight are mixed to form mixed with 0.5 part of health additive
Pug is closed, and is placed in pugging and mixes after mountain spring water is added in mixing pug；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 100:30, the health additive is included with weight
Measure the following ingredients of part meter：Blue or green 60 parts of spoil；White 50 parts of spoil；15 parts of orpiment stone；15 parts of astroies；50 parts of tourmaline；
20 parts of opal；20 parts of serpentine；10 parts of medical stone；15 parts of Strange ice stone；4 parts of hokutolite；4 parts of Doctor king stone；15 parts of shell；
S4：Mixing pug equal portions that are old, will having refined, cylinder interior sealing is placed in oilpaper encapsulation, cylinder is placed in closed
5 years are stood in environment；
S5：Embryo processed, will be old after mixing pug, pat be moulded into type shape into being labelled to mould left-hand seat after 5mm slice by hand
Into mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 36h, calcining temperature
Spend for 1370 DEG C, calcining terminates kiln discharge after being incubated 24 hours, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water storage bottle burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 36h, calcining
Temperature is 1370 DEG C, and calcining terminates kiln discharge after being incubated 24 hours, after automatic cooling；
S9：Third firing, the water storage bottle after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 60mi n, calcining heat is 1450 DEG C, and its water storage bottle is immediately placed in closed reduction kiln by calcining after terminating to drop automatically
Kiln discharge forms boccaro rock mud health water storage bottle after temperature.
Embodiment 3
A kind of boccaro rock mud health water storage bottle, including, each raw material of following parts by weight：90 parts of mixing raw ore base-material and 10
The health additive of part；The mixing raw ore base-material includes：Calm down volcanic rock mud and calm down boccaro group mud, wherein, it is described to calm down
The weight proportion that volcanic rock mud and boccaro of calming down roll into a ball mud is 80:20；The boccaro of calming down rolls into a ball each group that mud drum includes following parts by weight
Point:Purple mud, green mud and white clay, wherein the ratio of purple mud, green mud and white clay is 75:8:17；The health additive includes
Following ingredients in parts by weight：Blue or green 52 parts of spoil；White 42 parts of spoil；8 parts of orpiment stone；13 parts of astroies；Tourmaline 42
Part；17 parts of opal；16 parts of serpentine；9 parts of medical stone；11 parts of Strange ice stone；3 parts of hokutolite；2.8 parts of Doctor king stone；14 parts of shell.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water storage bottle, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 75 mesh, it is standby；
S2：System material, calm down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 80 by ground:20 ratio
Mixing raw ore base-material is mixed to form, it is standby；
S3：Pugging, 90 parts of the mixing raw ore base-material chosen in parts by weight are mixed to form mixing with 10 parts of health additive
Pug, and be placed in pugging and mix after mountain spring water is added in mixing pug；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 100:30, the health additive is included with weight
Measure the following ingredients of part meter：Blue or green 52 parts of spoil；White 42 parts of spoil；8 parts of orpiment stone；13 parts of astroies；42 parts of tourmaline；Egg
White 17 parts of stone；16 parts of serpentine；9 parts of medical stone；11 parts of Strange ice stone；3 parts of hokutolite；2.8 parts of Doctor king stone；14 parts of shell.
S4：Mixing pug equal portions that are old, will having refined, cylinder interior sealing is placed in oilpaper encapsulation, cylinder is placed in closed
3.5 years are stood in environment；
S5：Embryo processed, will be old after mixing pug, pat be moulded into type shape into being labelled to mould left-hand seat after 4mm slice by hand
Into mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 30h, calcining temperature
Spend for 1300 DEG C, calcining terminates kiln discharge after being incubated 20 hours, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water storage bottle burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 28h, calcining
Temperature is 1350 DEG C, and calcining terminates kiln discharge after being incubated 22 hours, after automatic cooling；
S9：Third firing, the water storage bottle after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 50mi n, calcining heat is 1400 DEG C, and its water storage bottle is immediately placed in closed reduction kiln by calcining after terminating to drop automatically
Kiln discharge forms boccaro rock mud health water storage bottle after temperature.
The boccaro rock mud health water storage bottle of the present invention is prepared using raw ore is mixed, and its mixing raw ore, which originates to calm down, to be produced
Pollution-free pure natural mineral aggregate, the volcanic rock mud density of one of them is relatively low, the several mineral materials containing pole beneficial to human body, can rise
To the effect of demineralized water, and millet paste entrance is natural, returns sweet long, larynx rhythm between 7.1-8.2, making for the pH value of adjustable water quality
Multiplication, meanwhile, also sustainable release multiple beneficial element greatly promotes the effect of health into water；In addition, volcanic rock mud itself
The honeycomb air hole structure having makes the gas permeability of the boccaro rock mud health water storage bottle of preparation be much better than other tanks, not only
Wall has more preferable gas permeability, and device body particle is plentiful, glossiness is uniform, and feel exquisiteness is gentle；It is in addition, former using mixing
Boccaro rock mud health water storage bottle prepared by ore deposit can keep nuisance zero to separate out at a high temperature of 1200 degree so that diet is more pacified
Entirely, while under hot environment it will not make pottery porcelain, can also allow its gas permeability and saturating fragrance more excellent；Finally, the present invention is using mixed
The combination of raw ore base-material and health additive is closed, and optimizes composition proportion so that air hole structure maximizes, while also overcomes biography
The defects of not glazing is meeting slow seepage in skill and technique of uniting.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (4)
1. a kind of boccaro rock mud health water storage bottle, it is characterised in that including each raw material of following parts by weight：
The mixing raw ore base-material of 85-99.5 parts and the health additive of 0.5-15 parts；
The mixing raw ore base-material includes：Calm down volcanic rock mud and calm down boccaro group mud, wherein, it is described calm down volcanic rock mud peace
The weight proportion for determining boccaro group mud is 80:20；
The health additive includes following ingredients in parts by weight：Blue or green 45~60 parts of spoil；White 35~50 parts of spoil；Stone
7~15 parts of Huangshi；10~15 parts of astroies；30~50 parts of tourmaline；10~20 parts of opal；15~20 parts of serpentine；Wheat
5~10 parts of meal stone；10~15 parts of Strange ice stone；2~4 parts of hokutolite；2~4 parts of Doctor king stone；10~15 parts of shell.
A kind of 2. boccaro rock mud health water storage bottle according to claim 1, it is characterised in that the boccaro group mud drum of calming down
Include each component of following parts by weight:Purple mud, green mud and white clay, wherein the ratio of purple mud, green mud and white clay is 70-80:5-
10:10-25。
3. a kind of utilize mixes the method that raw ore prepares boccaro rock mud health water storage bottle, it is characterised in that comprises the following steps：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and boccaro group cement mineral material of calming down spread harvested grain on a threshing floor weathering, dry after grind
Grinds, 75 mesh are screened to, it is standby；
S2：System material, calm down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 80 by ground:20 ratio mixing
Mixing raw ore base-material is formed, it is standby；
S3：Pugging, chooses mixing raw ore base-material 85-99.5 parts in parts by weight and health additive 0.5-15 parts are mixed to form
Pug is mixed, and is placed in pugging and mixes after mountain spring water is added in mixing pug；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 100:30, the health additive is included with parts by weight
The following ingredients of meter：Blue or green 45~60 parts of spoil；White 35~50 parts of spoil；7~15 parts of orpiment stone；10~15 parts of astroies；
30~50 parts of tourmaline；10~20 parts of opal；15~20 parts of serpentine；5~10 parts of medical stone；10~15 parts of Strange ice stone；North
2~4 parts of lapidation；2~4 parts of Doctor king stone；10~15 parts of shell；
S4：Mixing pug equal portions that are old, will having refined, cylinder interior sealing is placed in oilpaper encapsulation, cylinder is placed in closed environment
Middle standing 1-5；
S5：Embryo processed, will be old after mixing pug, pat formed into being labelled to mould left-hand seat after 3-5mm slice and be moulded into type by hand
Mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 24-36h, calcining temperature
Spend for 1230-1370 DEG C, kiln discharge after calcining terminates insulation 12-24 hours, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water storage bottle burnt till, is repaired, used using trimming device
Physical method reaches geometrically regular；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 24-36h, calcining
Temperature is 1230-1370 DEG C, kiln discharge after calcining terminates insulation 12-24 hours, automatic cooling；
S9：Third firing, the water storage bottle after second is calcined are put into smokeless coal pit and carry out third firing, and calcination time is
45-60min, calcining heat are 1350-1450 DEG C, and its water storage bottle is immediately placed in closed reduction kiln automatic by calcining after terminating
Kiln discharge forms boccaro rock mud health water storage bottle after cooling.
4. a kind of utilize according to claim 3 mixes the method that raw ore prepares boccaro rock mud health water storage bottle, its feature
It is, the boccaro of calming down rolls into a ball each component that mud drum includes following parts by weight:Purple mud, green mud and white clay, wherein purple mud, green mud with it is white
The ratio of mud is 70-80:5-10:10-25.