CN106193493B - A kind of production method of soft decorative panel for building - Google Patents

A kind of production method of soft decorative panel for building Download PDF

Info

Publication number
CN106193493B
CN106193493B CN201610538410.0A CN201610538410A CN106193493B CN 106193493 B CN106193493 B CN 106193493B CN 201610538410 A CN201610538410 A CN 201610538410A CN 106193493 B CN106193493 B CN 106193493B
Authority
CN
China
Prior art keywords
parts
slurries
decorative panel
poured
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610538410.0A
Other languages
Chinese (zh)
Other versions
CN106193493A (en
Inventor
孙高雷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Tican Industry Co., Ltd.
Original Assignee
Ningbo Heng Jin Automation Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Heng Jin Automation Technology Co Ltd filed Critical Ningbo Heng Jin Automation Technology Co Ltd
Priority to CN201610538410.0A priority Critical patent/CN106193493B/en
Publication of CN106193493A publication Critical patent/CN106193493A/en
Application granted granted Critical
Publication of CN106193493B publication Critical patent/CN106193493B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of production methods of soft decorative panel for building, include the following steps：The preparation of base：Plaster, sodium trimetaphosphate, cornstarch, water are mixed and are divided into A, two parts of slurries of B；Glass fibre and antifoaming agent are added in A parts of slurries, is stirred evenly；Compressed air is passed through in B slurries；A parts of slurries are poured into template, B parts of slurries are poured into after striking off, basal plate is obtained after standing and drying；The making of bonding agent；EP rubbers powder part, polypropylene part, precipitated calcium carbonate part, antioxidant, colorant part are proportionally added into closed high speed mixer and carry out mixing high-speed stirred；The raw material handled well is imported blended mediate in extruder to squeeze out；Binding agent is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, and decorative panel is obtained after cooling.The decorative panel has many advantages, such as that intensity is big, service life is long, high temperature resistant, low temperature.

Description

A kind of production method of soft decorative panel for building
The present invention is application number：2015102184767, the applying date：2015-04-30, denomination of invention：A kind of soft building The divisional application of the production method of decorative panel.
Technical field
The present invention relates to a kind of production methods of decorative panel for building.
Background technology
Now widely used decorative plate of outer wall is aluminium-plastic panel or stone plate, both decorative panels belong to rigid decoration Plate in some special places, needs to set flexible material, such as kindergarten's exterior wall dado, in order to avoid the student of kindergarten Colliding in being at play needs to be set as flexible material cladding, and the prior art mainly adopts artificial leathers to coat sponge, this material It is non-watertight, after exposing to the sun and rain quickly can aging, service life is extremely short.And this covering material all encloses a face wall Firmly, appearance is plain.
Invention content
For problem and shortage in the prior art, the present invention provides a kind of production method of soft decorative panel for building, the life The soft decorative panel for building that production method is produced has many advantages, such as that appearance looks elegant, service life are long.
Technical scheme is as follows：
A kind of production method of soft decorative panel for building, which is characterized in that include the following steps：
1) preparation of base：By plaster, sodium trimetaphosphate, cornstarch according to 100:0.03:1 weight ratio mixing, The water of 1.1 times of said mixture weight is added, is stirred evenly after mixing, is then classified as A, two parts of slurries of B；
2) it is added in A parts of slurries and accounts for the glass fibre of entire A parts of weight 0.5% and account for entire A parts of weight 0.02% Antifoaming agent stirs evenly；
3) B parts of slurries are continued to stir, compressed air is passed through in B parts of slurries during stirring so that the material in B parts Slurry is full of bubble；
4) A parts of slurries are poured into template, B parts of slurries is poured into after striking off, then B parts of slurry surfaces are struck off, A parts in template The thickness ratio of slurry and B parts of slurries is 4：1；Basal plate is obtained after standing and drying；
5) making of bonding agent：By weight, 20 parts of pitch, 35 parts of activated rubber powder, 15 parts of calcium carbonate, Petropols 15 Part；Pitch is added in reaction kettle and is warming up to 200 DEG C of fusings completely, activated rubber powder is added under conditions of constant temperature is kept and is stirred 120min is mixed, then adds in Petropols, calcium carbonate is added in after being cooled to 150 DEG C, stirs heat preservation for standby use after 60min；
6) soft layer is prepared：By weight, by 20 parts of EP rubbers powder, 10 parts of polypropylene, 15 parts of precipitated calcium carbonate, antioxygen 0.1 part of agent, 2 parts of colorant are proportionally added into closed high speed mixer and are mixed, and mixing temperature is 90 DEG C, high-speed stirred 10min；The raw material handled well is imported in extruder and is mediated through 180 DEG C of blendings, 180~200 DEG C of extrusions, while by soft layer The laminating metallized film in bottom surface；
7) binding agent in step 5 is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, cooling After obtain decorative panel.
There is no the schemes same or similar with the present invention program in the prior art, unique by gypsum basal plate On the basis of coating soft resin material obtain, the characteristics of present invention is main, is：
1st, basal plate is divided into two layers up and down, is obtained respectively by A, B slurry, adds glass fibre in A slurries so that base The lower floor of plate has enough intensity as structure sheaf, and the effect for adding in antifoaming agent is to make lower floor fine and close, further improves intensity； Compressed gas is passed through in B slurries so that the upper surface of basal plate is full of hole, and bonding agent can be penetrated into these holes, be carried High bond strength.Comparison finds, is provided with adhesion strength between the basal plate and soft layer of B slurries far above not having B slurries Situation, it is at least high by 30%.
2nd, the addition of cornstarch and sodium trimetaphosphate is so that the intensity of base increases more than 20%.
3rd, soft layer has high temperature resistant waterproof, non-aging in the environment of exposing to the weather, and has been carried out in applicant 2 years experiment in find no aging phenomenon.
4th, soft layer is not hardened still at low temperature.
Specific embodiment
Embodiment 1
A kind of production method of soft decorative panel for building, includes the following steps：
1) preparation of base：By plaster, sodium trimetaphosphate, cornstarch according to 100:0.03:1 weight ratio mixing, The water of 1.1 times of said mixture weight is added, is stirred evenly after mixing, is then classified as A, two parts of slurries of B；
2) it is added in A parts of slurries and accounts for the glass fibre of entire A parts of weight 0.5% and account for entire A parts of weight 0.02% Antifoaming agent stirs evenly；
3) B parts of slurries are continued to stir, compressed air is passed through in B parts of slurries during stirring so that the material in B parts Slurry is full of bubble；
4) A parts of slurries are poured into template, B parts of slurries is poured into after striking off, then B parts of slurry surfaces are struck off, A parts in template The thickness ratio of slurry and B parts of slurries is 4：1；Basal plate is obtained after standing and drying；
5) making of bonding agent：By weight, 20 parts of pitch, 35 parts of activated rubber powder, 15 parts of calcium carbonate, Petropols 15 Part；Pitch is added in reaction kettle and is warming up to 200 DEG C of fusings completely, activated rubber powder is added under conditions of constant temperature is kept and is stirred 120min is mixed, then adds in Petropols, calcium carbonate is added in after being cooled to 150 DEG C, stirs heat preservation for standby use after 60min；
6) soft layer is prepared：By weight, by 20 parts of EP rubbers powder, 10 parts of polypropylene, 15 parts of precipitated calcium carbonate, antioxygen 0.1 part of agent, 2 parts of colorant are proportionally added into closed high speed mixer and are mixed, and mixing temperature is 90 DEG C, high-speed stirred 3- 10min；The raw material handled well is imported in extruder and is mediated through 110~180 DEG C of blendings, 180~200 DEG C of extrusions, while will be soft The laminating metallized film in bottom surface of property layer；
7) binding agent in step 5 is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, cooling After obtain decorative panel.
It is understood that the principle that embodiment of above is intended to be merely illustrative of the present and the exemplary implementation that uses Mode, however the present invention is not limited thereto.For those skilled in the art, in the essence for not departing from the present invention In the case of refreshing and essence, various changes and modifications can be made therein, these variations and modifications are also considered as protection scope of the present invention.

Claims (1)

1. a kind of production method of soft decorative panel for building, which is characterized in that include the following steps：
1) preparation of base：By plaster, sodium trimetaphosphate, cornstarch according to 100:0.03:1 weight ratio mixing, then add Enter the water of 1.1 times of said mixture weight, stirred evenly after mixing, be then classified as A, two parts of slurries of B；
2) it is added in A parts of slurries and accounts for the glass fibre of entire A parts of weight 0.5% and account for the defoaming of entire A parts of weight 0.02% Agent stirs evenly；
3) B parts of slurries are continued to stir, compressed air is passed through in B parts of slurries during stirring so that the slurry in B parts fills Full bubble；
4) A parts of slurries are poured into template, B parts of slurries is poured into after striking off, then B parts of slurry surfaces are struck off, A parts of slurries in template Thickness ratio with B parts of slurries is 4：1；Basal plate is obtained after standing and drying；
5) making of bonding agent：By weight, 20 parts of pitch, 35 parts of activated rubber powder, 15 parts of calcium carbonate, 15 parts of Petropols；It will Pitch, which is added in reaction kettle, is warming up to 200 DEG C of fusings completely, and activated rubber powder stirring is added under conditions of constant temperature is kept Then 120min adds in Petropols, calcium carbonate is added in after being cooled to 150 DEG C, stirs heat preservation for standby use after 60min；
6) soft layer is prepared：By weight, by 20 parts of EP rubbers powder, 10 parts of polypropylene, 15 parts of precipitated calcium carbonate, antioxidant 0.1 part, 2 parts of colorant be proportionally added into closed high speed mixer and mixed, mixing temperature be 90 DEG C, high-speed stirred 10min；The raw material handled well is imported in extruder and is mediated through 180 DEG C of blendings, 180~200 DEG C of extrusions, while by soft layer The laminating metallized film in bottom surface；
7) binding agent in step 5 is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, after cooling To decorative panel.
CN201610538410.0A 2015-04-30 2015-04-30 A kind of production method of soft decorative panel for building Active CN106193493B (en)