CN106193494B - A kind of production method of soft decorative panel for building - Google Patents

A kind of production method of soft decorative panel for building Download PDF

Info

Publication number
CN106193494B
CN106193494B CN201610542032.3A CN201610542032A CN106193494B CN 106193494 B CN106193494 B CN 106193494B CN 201610542032 A CN201610542032 A CN 201610542032A CN 106193494 B CN106193494 B CN 106193494B
Authority
CN
China
Prior art keywords
parts
slurries
added
decorative panel
poured
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201610542032.3A
Other languages
Chinese (zh)
Other versions
CN106193494A (en
Inventor
孙高雷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
The Xie Run of Shunde District, Foshan City decorative building material Co., Ltd
Original Assignee
Ningbo Hi-Tech Zone Rising And Electrical Machinery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Hi-Tech Zone Rising And Electrical Machinery Co Ltd filed Critical Ningbo Hi-Tech Zone Rising And Electrical Machinery Co Ltd
Priority to CN201610542032.3A priority Critical patent/CN106193494B/en
Publication of CN106193494A publication Critical patent/CN106193494A/en
Application granted granted Critical
Publication of CN106193494B publication Critical patent/CN106193494B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of production methods of soft decorative panel for building, include the following steps:The preparation of base:Plaster, sodium trimetaphosphate, cornstarch, water are mixed and are divided into A, two parts of slurries of B;Glass fibre and antifoaming agent are added in A parts of slurries, stirs evenly;It is passed through compressed air in B slurries;A parts of slurries are poured into template, B parts of slurries are poured into after striking off, basal plate is obtained after standing and drying;The making of bonding agent;EP rubbers powder part, polypropylene part, precipitated calcium carbonate part, antioxidant, colorant part are proportionally added into closed high speed mixer and carry out mixing high-speed stirred;The raw material handled well is imported blended kneading in extruder to squeeze out;Binder is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, and decorative panel is obtained after cooling.The decorative panel has many advantages, such as that intensity is big, service life is long, high temperature resistant, low temperature.

Description

A kind of production method of soft decorative panel for building
The present invention is application number:2015102184767, the applying date:2015-04-30, denomination of invention:A kind of soft building The divisional application of the production method of decorative panel.
Technical field
The present invention relates to a kind of production methods of decorative panel for building.
Background technology
Now widely used decorative plate of outer wall is aluminium-plastic panel or stone plate, both decorative panels belong to rigid decoration Plate needs that flexible material, such as kindergarten's exterior wall dado is arranged, in order to avoid the student of kindergarten in some special places Colliding in being at play needs to be set as flexible material cladding, and the prior art mainly adopts artificial leathers to coat sponge, this material It is non-watertight, after exposing to the sun and rain quickly can aging, service life is extremely short.And this covering material all encloses a face wall Firmly, appearance is plain.
Invention content
For problem and shortage in the prior art, the present invention provides a kind of production method of soft decorative panel for building, the life The soft decorative panel for building that production method is produced has many advantages, such as that appearance looks elegant, service life are long.
Technical scheme is as follows:
A kind of production method of soft decorative panel for building, which is characterized in that include the following steps:
1) preparation of base:By plaster, sodium trimetaphosphate, cornstarch according to 100:0.03:1 weight ratio mixing, The water for adding 1.1 times of said mixture weight, stirs evenly after mixing, is then classified as A, two parts of slurries of B;
2) it is added in A parts of slurries and accounts for the glass fibre of entire A parts of weight 0.5% and account for entire A parts of weight 0.02% Antifoaming agent stirs evenly;
3) B parts of slurries are continued to stir, compressed air is passed through in B parts of slurries during stirring so that the material in B parts Slurry is full of bubble;
4) A parts of slurries are poured into template, B parts of slurries is poured into after striking off, then B parts of slurry surfaces are struck off, A parts in template The thickness of slurry and B parts of slurries ratio is 4:1;Basal plate is obtained after standing and drying;
5) making of bonding agent:By weight, 20 parts of pitch, 35 parts of activated rubber powder, 15 parts of calcium carbonate, Petropols 15 Part;Pitch is added in reaction kettle and is warming up to 200 DEG C of fusings completely, activated rubber powder is added under conditions of keeping temperature constant and stirs 120min is mixed, Petropols are then added, calcium carbonate is added after being cooled to 150 DEG C, stirs heat preservation for standby use after 60min;
6) soft layer is prepared:By weight, by 20 parts of EP rubbers powder, 10 parts of polypropylene, 15 parts of precipitated calcium carbonate, antioxygen 0.1 part of agent, 2 parts of colorant are proportionally added into closed high speed mixer and are mixed, and mixing temperature is 90 DEG C, high-speed stirred 10min;The raw material handled well is imported to be blended through 180 DEG C in extruder and is mediated, 200 DEG C of extrusions, while by the bottom surface of soft layer Laminating metallized film;
7) binder in step 5 is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, cooling After obtain decorative panel.
There is no the schemes same or similar with the present invention program in the prior art, unique by gypsum basal plate On the basis of coating soft resin material obtain, the main feature of the present invention is:
1, basal plate is divided into upper layer and lower layer, is obtained respectively by A, B slurry, adds glass fibre in A slurries so that base It is to keep lower layer fine and close that the lower layer of plate has enough intensity, the effect that antifoaming agent is added as structure sheaf, further increases intensity; It is passed through compressed gas in B slurries so that the upper surface of basal plate is full of hole, and bonding agent can be penetrated into these holes, be carried High bond strength.Comparison finds, is provided with adhesion strength between the basal plate and soft layer of B slurries far above not having B slurries The case where, it is at least high by 30%.
2, the addition of cornstarch and sodium trimetaphosphate is so that the intensity of base increases 20% or more.
3, soft layer has high temperature resistant waterproof, non-aging in the environment of exposing to the weather, and has been carried out in applicant 2 years experiment in find no aging phenomenon.
4, soft layer is not hardened still at low temperature.
Specific implementation mode
Embodiment 1
A kind of production method of soft decorative panel for building, includes the following steps:
1) preparation of base:By plaster, sodium trimetaphosphate, cornstarch according to 100:0.03:1 weight ratio mixing, The water for adding 1.1 times of said mixture weight, stirs evenly after mixing, is then classified as A, two parts of slurries of B;
2) it is added in A parts of slurries and accounts for the glass fibre of entire A parts of weight 0.5% and account for entire A parts of weight 0.02% Antifoaming agent stirs evenly;
3) B parts of slurries are continued to stir, compressed air is passed through in B parts of slurries during stirring so that the material in B parts Slurry is full of bubble;
4) A parts of slurries are poured into template, B parts of slurries is poured into after striking off, then B parts of slurry surfaces are struck off, A parts in template The thickness of slurry and B parts of slurries ratio is 4:1;Basal plate is obtained after standing and drying;
5) making of bonding agent:By weight, 20 parts of pitch, 35 parts of activated rubber powder, 15 parts of calcium carbonate, Petropols 15 Part;Pitch is added in reaction kettle and is warming up to 200 DEG C of fusings completely, activated rubber powder is added under conditions of keeping temperature constant and stirs 120min is mixed, Petropols are then added, calcium carbonate is added after being cooled to 150 DEG C, stirs heat preservation for standby use after 60min;
6) soft layer is prepared:By weight, by 20 parts of EP rubbers powder, 10 parts of polypropylene, 15 parts of precipitated calcium carbonate, antioxygen 0.1 part of agent, 2 parts of colorant are proportionally added into closed high speed mixer and are mixed, and mixing temperature is 90 DEG C, high-speed stirred 3- 10min;The raw material handled well is imported to be blended through 110~180 DEG C in extruder and is mediated, 180~200 DEG C of extrusions, while will be soft The laminating metallized film in bottom surface of property layer;
7) binder in step 5 is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, cooling After obtain decorative panel.
It is understood that the principle that embodiment of above is intended to be merely illustrative of the present and the exemplary implementation that uses Mode, however the present invention is not limited thereto.For those skilled in the art, in the essence for not departing from the present invention In the case of refreshing and essence, various changes and modifications can be made therein, these variations and modifications are also considered as protection scope of the present invention.

Claims (1)

1. a kind of production method of soft decorative panel for building, which is characterized in that include the following steps:
1) preparation of base:By plaster, sodium trimetaphosphate, cornstarch according to 100:0.03:1 weight ratio mixing, then add The water for entering 1.1 times of said mixture weight, stirs evenly after mixing, is then classified as A, two parts of slurries of B;
2) it is added in A parts of slurries and accounts for the glass fibre of entire A parts of weight 0.5% and account for the defoaming of entire A parts of weight 0.02% Agent stirs evenly;
3) B parts of slurries are continued to stir, compressed air is passed through in B parts of slurries during stirring so that the slurry in B parts fills Full bubble;
4) A parts of slurries are poured into template, B parts of slurries is poured into after striking off, then B parts of slurry surfaces are struck off, A parts of slurries in template Thickness ratio with B parts of slurries is 4:1;Basal plate is obtained after standing and drying;
5) making of bonding agent:By weight, 20 parts of pitch, 35 parts of activated rubber powder, 15 parts of calcium carbonate, 15 parts of Petropols;It will Pitch, which is added in reaction kettle, is warming up to 200 DEG C of fusings completely, and activated rubber powder stirring is added under conditions of keeping temperature constant Then Petropols are added in 120min, calcium carbonate is added after being cooled to 150 DEG C, stir heat preservation for standby use after 60min;
6) soft layer is prepared:By weight, by 20 parts of EP rubbers powder, 10 parts of polypropylene, 15 parts of precipitated calcium carbonate, antioxidant 0.1 part, 2 parts of colorant be proportionally added into closed high speed mixer and mixed, mixing temperature be 90 DEG C, high-speed stirred 10min;The raw material handled well is imported to be blended through 180 DEG C in extruder and is mediated, 200 DEG C of extrusions, while by the bottom surface of soft layer Laminating metallized film;
7) binder in step 5 is poured into base's plate surface, after striking off, metallized film spreads soft layer downward, is obtained after cooling To decorative panel.
CN201610542032.3A 2015-04-30 2015-04-30 A kind of production method of soft decorative panel for building Expired - Fee Related CN106193494B (en)