CN106192377A - 一种防霉防蛀帆布帐篷面料及其制备方法 - Google Patents

一种防霉防蛀帆布帐篷面料及其制备方法 Download PDF

Info

Publication number
CN106192377A
CN106192377A CN201610680575.1A CN201610680575A CN106192377A CN 106192377 A CN106192377 A CN 106192377A CN 201610680575 A CN201610680575 A CN 201610680575A CN 106192377 A CN106192377 A CN 106192377A
Authority
CN
China
Prior art keywords
mould
moth
canvas
colloidal sol
tent fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610680575.1A
Other languages
English (en)
Inventor
龙小伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yingshang County Yida Tent Co Ltd
Original Assignee
Yingshang County Yida Tent Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yingshang County Yida Tent Co Ltd filed Critical Yingshang County Yida Tent Co Ltd
Priority to CN201610680575.1A priority Critical patent/CN106192377A/zh
Publication of CN106192377A publication Critical patent/CN106192377A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防霉防蛀帆布帐篷面料，其是由下述重量份的原料制得：涤纶纤维30‑40，竹炭纤维10‑15，大麻纤维10‑15，硅藻土3‑5，苯丙乳液5‑10，十二烷基三甲基氯化铵0.2‑0.4，月桂酸单甘油酯1‑2，苯甲酸钠0.1‑0.2，联苯菊酯0.1‑0.2，双乙酸钠2‑4，改性淀粉溶胶5‑10。本发明的帆布帐篷面料既符合基本的使用要求，又具有良好的透湿透气性，涂层稳定性和均匀度高，不易脱落、开裂，防水效果和外观品质好，并且具有防霉防蛀性能，附加价值高。

Description

一种防霉防蛀帆布帐篷面料及其制备方法
技术领域
本发明涉及帐篷面料技术领域，尤其涉及一种防霉防蛀帆布帐篷面料及其制备方法。
背景技术
帐篷是一种具有建筑材料功能的纺织品，用于在野外环境中隔离出一个独立安全的空间。帐篷具有简便、轻巧的特点，需要具有防风、防雨、防雪、防寒、防蚊虫的基本功能。近年来随着旅游业的发展，帐篷的销量得到大幅度增长，市场进一步扩大，人们对帐篷外观、性能的需求也进一步提高。帐篷面料由基布经表面整理制成，它的性能很大程度上影响了帐篷的使用性能。目前应用最广泛的帐篷面料是涤纶帆布，其透气透湿性能差，使用性能和附加价值不高，无法满足市场对中高档产品的潜在需求。帐篷面料在使用、存放过程中容易发生霉变、虫蛀，改善其防霉防蛀效果有利于提升其使用性能和清洁性。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种防霉防蛀帆布帐篷面料及其制备方法。
本发明是通过以下技术方案实现的：
一种防霉防蛀帆布帐篷面料，其是由下述重量份的原料制得：
涤纶纤维30-40，竹炭纤维10-15，大麻纤维10-15，硅藻土3-5，苯丙乳液5-10，十二烷基三甲基氯化铵0.2-0.4，月桂酸单甘油酯1-2，苯甲酸钠0.1-0.2，联苯菊酯0.1-0.2，双乙酸钠2-4，改性淀粉溶胶5-10；
其中改性淀粉溶胶由下列重量份的原料制成：玉米淀粉30-40，石墨粉10-15，硝酸钠1-2，高锰酸钾2-4，丙烯酸3-5，甲基丙烯酸甲酯6-8，15-20%浓度双氧水水溶液10-15，过硫酸铵0.5-1，十二烷基硫酸钠0.5-1，水200-300；改性淀粉溶胶的制备方法是将石墨粉按固液重量比1：1.5-1：2与质量分数为98%的浓硫酸混合后加入硝酸钠、高锰酸钾，40-50℃反应0.5-1h后依次加入水、玉米淀粉和15-20%浓度双氧水水溶液60-80℃搅拌3-4h，将pH调至中性后加入其余原料70-80℃反应1-2h，冷却后即得。
一种防霉防蛀帆布帐篷面料的制备方法，包括以下步骤：
（1）将涤纶纤维、竹炭纤维和大麻纤维按比例混纺编织，得帆布基布；
（2）将苯丙乳液、改性淀粉溶胶、月桂酸单甘油酯与十二烷基三甲基氯化铵混合后40-50℃搅拌1-2h，冷却后加入其余原料共同研磨至细度≤50μm，得涂覆剂；
（3）将（2）中的涂覆剂均匀涂覆于（1）中的帆布基布表面，先于80-90℃干燥4-6h，再于120-140℃热处理10-20min，冷却后即得防霉防蛀帆布帐篷面料。
本发明的优点是：
本发明通过改性淀粉溶胶与苯丙乳液等原料复配，合成的涂覆剂与帐篷帆布基布具有良好的结合性，在基布上生成具有良好粘着牢度、透湿透气性和力学性能的涂膜，使最终得到的帆布帐篷面料既符合基本的使用要求，又具有良好的透湿透气性，涂层稳定性和均匀度高，不易脱落、开裂，防水效果和外观品质好，并且具有防霉防蛀性能，附加价值高。
具体实施方式
一种防霉防蛀帆布帐篷面料，其是由下述重量份的原料制得：
涤纶纤维30，竹炭纤维10，大麻纤维10，硅藻土3，苯丙乳液5，十二烷基三甲基氯化铵0.2，月桂酸单甘油酯1，苯甲酸钠0.1，联苯菊酯0.1，双乙酸钠2，改性淀粉溶胶5；
其中改性淀粉溶胶由下列重量份的原料制成：玉米淀粉30，石墨粉10，硝酸钠1，高锰酸钾2，丙烯酸3，甲基丙烯酸甲酯6，15%浓度双氧水水溶液10，过硫酸铵0.5，十二烷基硫酸钠0.5，水200；改性淀粉溶胶的制备方法是将石墨粉按固液重量比1：1.5与质量分数为98%的浓硫酸混合后加入硝酸钠、高锰酸钾，40℃反应0.5h后依次加入水、玉米淀粉和15%浓度双氧水水溶液60℃搅拌3h，将pH调至中性后加入其余原料70℃反应1h，冷却后即得。
一种防霉防蛀帆布帐篷面料的制备方法，包括以下步骤：
（1）将涤纶纤维、竹炭纤维和大麻纤维按比例混纺编织，得帆布基布；
（2）将苯丙乳液、改性淀粉溶胶、月桂酸单甘油酯与十二烷基三甲基氯化铵混合后40℃搅拌1h，冷却后加入其余原料共同研磨至细度≤50μm，得涂覆剂；
（3）将（2）中的涂覆剂均匀涂覆于（1）中的帆布基布表面，先于80℃干燥4h，再于120℃热处理10min，冷却后即得防霉防蛀帆布帐篷面料。
上述制得的帆布帐篷面料性能指标测试结果如下：
项目 单位 指标
断裂强力（经向） N 2090
断裂强力（纬向） N 1870
透湿量 g/m2d 1642

Claims (2)

1.一种防霉防蛀帆布帐篷面料，其特征在于，其是由下述重量份的原料制得：
涤纶纤维30-40，竹炭纤维10-15，大麻纤维10-15，硅藻土3-5，苯丙乳液5-10，十二烷基三甲基氯化铵0.2-0.4，月桂酸单甘油酯1-2，苯甲酸钠0.1-0.2，联苯菊酯0.1-0.2，双乙酸钠2-4，改性淀粉溶胶5-10；
所述的改性淀粉溶胶由下列重量份的原料制成：玉米淀粉30-40，石墨粉10-15，硝酸钠1-2，高锰酸钾2-4，丙烯酸3-5，甲基丙烯酸甲酯6-8，15-20%浓度双氧水水溶液10-15，过硫酸铵0.5-1，十二烷基硫酸钠0.5-1，水200-300；改性淀粉溶胶的制备方法是将石墨粉按固液重量比1：1.5-1：2与质量分数为98%的浓硫酸混合后加入硝酸钠、高锰酸钾，40-50℃反应0.5-1h后依次加入水、玉米淀粉和15-20%浓度双氧水水溶液60-80℃搅拌3-4h，将pH调至中性后加入其余原料70-80℃反应1-2h，冷却后即得。
2.根据权利要求1所述的一种防霉防蛀帆布帐篷面料的制备方法，其特征在于，包括以下步骤：
（1）将涤纶纤维、竹炭纤维和大麻纤维按比例混纺编织，得帆布基布；
（2）将苯丙乳液、改性淀粉溶胶、月桂酸单甘油酯与十二烷基三甲基氯化铵混合后40-50℃搅拌1-2h，冷却后加入其余原料共同研磨至细度≤50μm，得涂覆剂；
（3）将（2）中的涂覆剂均匀涂覆于（1）中的帆布基布表面，先于80-90℃干燥4-6h，再于120-140℃热处理10-20min，冷却后即得防霉防蛀帆布帐篷面料。
CN201610680575.1A 2016-08-17 2016-08-17 一种防霉防蛀帆布帐篷面料及其制备方法 Pending CN106192377A (zh)