CN106189266A - 一种疏水型复合碳酸钙及其制备方法 - Google Patents
一种疏水型复合碳酸钙及其制备方法 Download PDFInfo
- Publication number
- CN106189266A CN106189266A CN201610652142.5A CN201610652142A CN106189266A CN 106189266 A CN106189266 A CN 106189266A CN 201610652142 A CN201610652142 A CN 201610652142A CN 106189266 A CN106189266 A CN 106189266A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium carbonate
- modifying agent
- preparation
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种疏水型复合碳酸钙及其制备方法,包括以下原料:碳酸钙、聚乳酸树脂、羟基丙烯酸树脂、滑石粉、硫酸钡、聚酯改性硅氧烷、季戊四醇、丙二醇丁醚、甲基异丁基甲酮、改性剂、水适量;其制备方法包括以下步骤:(1)制得预混料待用;(2)制得混合液;(3)制得改性剂;(4)将预混料、混合液和改性剂混合,搅拌均匀,研磨、烘干、粉碎成超细粉末即得。本发明通过将碳酸钙与硫酸钡、聚乳酸树脂、羟基丙烯酸树脂、聚酯改性硅氧烷等综合性能较佳的材料进行组合,改进生产工艺,采用改性剂等有效地增加了组合物的疏水性能;其生产工艺简单,生产周期短,质量稳定,生产成本低,应用价值较高。
Description
技术领域
本发明涉及工业填料领域,尤其涉及一种疏水型复合碳酸钙及其制备方法。
背景技术
碳酸钙是一种无机化合物,CaCO3俗称:灰石、石灰石、石粉、大理石等,是由钙离子和碳酸根离子结合生成的,是一类重要的功能性无机填料,工业上用途甚广,具有价格低廉、储量丰富、性能稳定、易加工、无毒等优点,能够显著的改善材料的加工性能、物理性能以及降低生产成本等等,广泛应用于塑料、橡胶、涂料、造纸等领域。
在碳酸钙的应用领域中,大多产品属于聚合物的范畴,然而,碳酸钙粒子表面分布有强亲水性的羟基,表现为碱性,和有机高聚物基质材料的界面性质不同,相容性差,难以在基质材料中分散均匀以及和基质材料形成强的结合力,造成两材料之间的界面缺陷,使复合材料某些力学性能下降。因此需要改变传统碳酸钙产品的性能,改善其应用性能以满足新材料、新技术发展的需要,是碳酸钙工业急需解决的问题。
发明内容
本发明的目的在于,提供一种疏水型复合碳酸钙及其制备方法,通过将综合性能较佳的材料进行组合,改进生产工艺,采用改性剂等有效地增加了组合物的疏水性能。
为了实现上述目的,本发明采用的技术方案如下:
一种疏水型复合碳酸钙及其制备方法,包括以下重量份的原料:碳酸钙50~80份、聚乳酸树脂2~4份、羟基丙烯酸树脂1~3份、滑石粉1~3份、硫酸钡3~5份、聚酯改性硅氧烷4~6份、季戊四醇2~3份、丙二醇丁醚1~1.5份、甲基异丁基甲酮1~2份、改性剂5~8份、水适量;其中所述改性剂由以下重量份的原料制成:纳米二氧化硅30~50份、玻璃粉2~4份、琥珀酸酐3~5份、苯丙乳液2~5份、烷基季铵盐1~3份、碳酸钠3~5份、异佛尔酮2~4份;
其制备方法包括以下步骤:
(1)将碳酸钙、聚乳酸树脂、羟基丙烯酸树脂、滑石粉混合均匀加入砂磨机内,研磨至300~400目,得预混料待用;
(2)将硫酸钡、聚酯改性硅氧烷、季戊四醇放入混料机中,升温至75~85℃,混合搅拌半小时,然后加入丙二醇丁醚、甲基异丁基甲酮,继续升温至120~140℃,搅拌均匀,得混合液;
(3)将纳米二氧化硅、玻璃粉、琥珀酸酐、苯丙乳液加适量水搅拌,并升温至75~85℃,搅拌均匀后加入烷基季铵盐、碳酸钠、异佛尔酮,继续加热至120~140℃,混合搅拌均匀,得改性剂;
(4)将步骤(1)得到的预混料、步骤(2)得到的混合液和步骤(3)得到的改性剂混合,搅拌均匀,研磨、烘干、粉碎成超细粉末即得。
本发明的有益效果为:
本发明通过将碳酸钙与硫酸钡、聚乳酸树脂、羟基丙烯酸树脂、聚酯改性硅氧烷等综合性能较佳的材料进行组合,改进生产工艺,采用改性剂等有效地增加了组合物的疏水性能;本发明生产工艺简单,生产过程环保无污染,实现了资源和能源的充分利用,生产周期短,质量稳定,生产成本低,应用价值较高。
具体实施方式:
以下以具体实施例来说明本发明的技术方案,但本发明的保护范围不限于此:
实施例1:
一种疏水型复合碳酸钙及其制备方法,包括以下重量份的原料:碳酸钙50份、聚乳酸树脂2份、羟基丙烯酸树脂1份、滑石粉1份、硫酸钡3份、聚酯改性硅氧烷4份、季戊四醇2份、丙二醇丁醚1份、甲基异丁基甲酮1份、改性剂5份、水适量;其中所述改性剂由以下重量份的原料制成:纳米二氧化硅30份、玻璃粉2份、琥珀酸酐3份、苯丙乳液2份、烷基季铵盐1份、碳酸钠3份、异佛尔酮2份;
其制备方法包括以下步骤:
(1)将碳酸钙、聚乳酸树脂、羟基丙烯酸树脂、滑石粉混合均匀加入砂磨机内,研磨至300~400目,得预混料待用;
(2)将硫酸钡、聚酯改性硅氧烷、季戊四醇放入混料机中,升温至75℃,混合搅拌半小时,然后加入丙二醇丁醚、甲基异丁基甲酮,继续升温至140℃,搅拌均匀,得混合液;
(3)将纳米二氧化硅、玻璃粉、琥珀酸酐、苯丙乳液加适量水搅拌,并升温至85℃,搅拌均匀后加入烷基季铵盐、碳酸钠、异佛尔酮,继续加热至120℃,混合搅拌均匀,得改性剂;
(4)将步骤(1)得到的预混料、步骤(2)得到的混合液和步骤(3)得到的改性剂混合,搅拌均匀,研磨、烘干、粉碎成超细粉末即得。
实施例2:
一种疏水型复合碳酸钙及其制备方法,包括以下重量份的原料:碳酸钙80份、聚乳酸树脂4份、羟基丙烯酸树脂3份、滑石粉3份、硫酸钡5份、聚酯改性硅氧烷6份、季戊四醇3份、丙二醇丁醚1.5份、甲基异丁基甲酮2份、改性剂8份、水适量;其中所述改性剂由以下重量份的原料制成:纳米二氧化硅50份、玻璃粉4份、琥珀酸酐5份、苯丙乳液5份、烷基季铵盐3份、碳酸钠5份、异佛尔酮4份;
其制备方法包括以下步骤:
(1)将碳酸钙、聚乳酸树脂、羟基丙烯酸树脂、滑石粉混合均匀加入砂磨机内,研磨至300~400目,得预混料待用;
(2)将硫酸钡、聚酯改性硅氧烷、季戊四醇放入混料机中,升温至85℃,混合搅拌半小时,然后加入丙二醇丁醚、甲基异丁基甲酮,继续升温至120℃,搅拌均匀,得混合液;
(3)将纳米二氧化硅、玻璃粉、琥珀酸酐、苯丙乳液加适量水搅拌,并升温至75℃,搅拌均匀后加入烷基季铵盐、碳酸钠、异佛尔酮,继续加热至140℃,混合搅拌均匀,得改性剂;
(4)将步骤(1)得到的预混料、步骤(2)得到的混合液和步骤(3)得到的改性剂混合,搅拌均匀,研磨、烘干、粉碎成超细粉末即得。
以上实施例仅用以说明本发明的技术方案,而非对本发明保护范围的限制,尽管参照较佳实施例对本发明作了详细地说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的实质和范围。
Claims (1)
1.一种疏水型复合碳酸钙及其制备方法,其特征在于,包括以下重量份的原料:碳酸钙50~80份、聚乳酸树脂2~4份、羟基丙烯酸树脂1~3份、滑石粉1~3份、硫酸钡3~5份、聚酯改性硅氧烷4~6份、季戊四醇2~3份、丙二醇丁醚1~1.5份、甲基异丁基甲酮1~2份、改性剂5~8份、水适量;其中所述改性剂由以下重量份的原料制成:纳米二氧化硅30~50份、玻璃粉2~4份、琥珀酸酐3~5份、苯丙乳液2~5份、烷基季铵盐1~3份、碳酸钠3~5份、异佛尔酮2~4份;
其制备方法包括以下步骤:
(1)将碳酸钙、聚乳酸树脂、羟基丙烯酸树脂、滑石粉混合均匀加入砂磨机内,研磨至300~400目,得预混料待用;
(2)将硫酸钡、聚酯改性硅氧烷、季戊四醇放入混料机中,升温至75~85℃,混合搅拌半小时,然后加入丙二醇丁醚、甲基异丁基甲酮,继续升温至120~140℃,搅拌均匀,得混合液;
(3)将纳米二氧化硅、玻璃粉、琥珀酸酐、苯丙乳液加适量水搅拌,并升温至75~85℃,搅拌均匀后加入烷基季铵盐、碳酸钠、异佛尔酮,继续加热至120~140℃,混合搅拌均匀,得改性剂;
(4)将步骤(1)得到的预混料、步骤(2)得到的混合液和步骤(3)得到的改性剂混合,搅拌均匀,研磨、烘干、粉碎成超细粉末即得。