CN104356691A - 一种具有疏水亲油防潮效果的改性碳酸钙及其制备方法 - Google Patents

一种具有疏水亲油防潮效果的改性碳酸钙及其制备方法 Download PDF

Info

Publication number
CN104356691A
CN104356691A CN201410507929.3A CN201410507929A CN104356691A CN 104356691 A CN104356691 A CN 104356691A CN 201410507929 A CN201410507929 A CN 201410507929A CN 104356691 A CN104356691 A CN 104356691A
Authority
CN
China
Prior art keywords
calcium carbonate
parts
modified calcium
titanium dioxide
dry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410507929.3A
Other languages
English (en)
Inventor
王明竹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd
Original Assignee
ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd filed Critical ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd
Priority to CN201410507929.3A priority Critical patent/CN104356691A/zh
Publication of CN104356691A publication Critical patent/CN104356691A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种具有疏水亲油防潮效果的改性碳酸钙，其特征在于，由下列重量份的原料制备制成：碳酸钙85-90、锂皂石2-3、干燥落叶粉3-4、二甲基硅油2-2.5、烷基烯酮二聚体4-6、大豆油2-3、司盘801-2、烟片胶4-5、油酸钾2-2.5、三聚异氰酸三甲酯5-7、改性二氧化钛3-4；本发明添加多种油性物质，以及油包水表面活性剂进行包覆，具有良好的表面性能，疏水亲油，添加改性二氧化钛，分散性良好，本发明防水防潮，适用于涂料、颜料、造纸助剂等，生产工艺简单，成本低。

Description

一种具有疏水亲油防潮效果的改性碳酸钙及其制备方法
技术领域
本发明涉及工业填料领域，特别是一种具有疏水亲油防潮效果的改性碳酸钙及其制备方法。
背景技术
碳酸钙由于稳定性好、色泽单纯、低磨耗、易加工、无毒、来源广泛、价格低廉等诸多优点常用来填充塑料、橡胶等材料，起到增容、增量、降低生产成本的作用。但由于其表面亲水疏油且易团聚，与有机高聚物的界面性质不同，相容性差，直接或过多地填充易导致材料力学性能下降。通过改性可改善其表面性质，提高分散性、与聚合物界面相容性和材料的机械强度等综合性能。
发明内容
本发明的目的是提供一种具有疏水亲油防潮效果的改性碳酸钙及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种具有疏水亲油防潮效果的改性碳酸钙，由下列重量份的原料制备制成：碳酸钙85-90、锂皂石2-3、干燥落叶粉3-4、二甲基硅油2-2.5、烷基烯酮二聚体4-6、大豆油2-3、司盘80 1-2、烟片胶4-5、油酸钾2-2.5、三聚异氰酸三甲酯5-7、改性二氧化钛3-4；
所述改性二氧化钛由以下重量份的原料制成：纳米二氧化钛50-60、氢氧化镁2-4、乙基纤维素4-6、丙烯酸正丁酯5-7、石英粉3-4、聚异丁烯3-4、醇酸树脂3-5、松油醇2-4、水50-60；制备方法是首先加入丙烯酸正丁酯、纳米二氧化钛、氢氧化镁、乙基纤维素、水搅拌均匀，形成悬浮液，在45-50℃下烘干至含水量2-3%，然后立即加入聚异丁烯、醇酸树脂混合搅拌25-35分钟，然后加入其余剩余成分，在1200-1500转/分条件下搅拌，在50-60℃下烘干，粉碎成超细粉末即得。
本发明所述一种具有疏水亲油防潮效果的改性碳酸钙，由以下具体步骤制成：
（1）将碳酸钙、锂皂石、二甲基硅油、烷基烯酮二聚体、烟片胶、油酸钾加入高速捏合机中，升温至70-80℃之间，保温搅拌半小时，继续添加三聚异氰酸三甲酯，继续升温至110-130℃，保温15-20分钟后倒出；
（2）将趁热将倒出物料加入适量的去离子水以及除改性二氧化钛之外的其余剩余成分，搅拌并研磨2-3小时，形成混悬液待用；
（3）将混悬液与改性二氧化钛混合，800-1000转/分下搅拌10-15分钟，烘干、粉碎成超细粉末即得。
本发明的有益效果是：本发明添加多种油性物质，以及油包水表面活性剂进行包覆，具有良好的表面性能，疏水亲油，添加改性二氧化钛，分散性良好，本发明防水防潮，适用于涂料、颜料、造纸助剂等，生产工艺简单，成本低。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种具有疏水亲油防潮效果的改性碳酸钙，由下列重量份（公斤）的原料制备制成：碳酸钙85、锂皂石2、干燥落叶粉3、二甲基硅油2、烷基烯酮二聚体4、大豆油2、司盘80 1、烟片胶4、油酸钾2、三聚异氰酸三甲酯5、改性二氧化钛3；
所述改性二氧化钛由以下重量份（公斤）的原料制成：纳米二氧化钛50、氢氧化镁2、乙基纤维素4、丙烯酸正丁酯5、石英粉3、聚异丁烯3、醇酸树脂3、松油醇2、水50；制备方法是首先加入丙烯酸正丁酯、纳米二氧化钛、氢氧化镁、乙基纤维素、水搅拌均匀，形成悬浮液，在45-50℃下烘干至含水量2-3%，然后立即加入聚异丁烯、醇酸树脂混合搅拌25-35分钟，然后加入其余剩余成分，在1200-1500转/分条件下搅拌，在50-60℃下烘干，粉碎成超细粉末即得。
本发明所述一种具有疏水亲油防潮效果的改性碳酸钙，由以下具体步骤制成：
（1）将碳酸钙、锂皂石、二甲基硅油、烷基烯酮二聚体、烟片胶、油酸钾加入高速捏合机中，升温至70-80℃之间，保温搅拌半小时，继续添加三聚异氰酸三甲酯，继续升温至110-130℃，保温15-20分钟后倒出；
（2）将趁热将倒出物料加入适量的去离子水以及除改性二氧化钛之外的其余剩余成分，搅拌并研磨2-3小时，形成混悬液待用；
（3）将混悬液与改性二氧化钛混合，800-1000转/分下搅拌10-15分钟，烘干、粉碎成超细粉末即得。
对本发明的改性碳酸钙和普通碳酸钙的性能检测比较如下 ：
首先测量改性前、后碳酸钙的堆积密度，然后将改性好的碳酸钙和未改性的重质碳酸钙分别按 15％的比例加入到PVC树脂中，制成样品，分别测试两者的力学性能，对比结果见下表 ：
由上表可以看出，改性后的碳酸钙的松散堆积密度变小，说明碳酸钙分体充分分散，还可以看出改性后碳酸钙的各项力学性能都得到提高。

Claims (2)

1.一种具有疏水亲油防潮效果的改性碳酸钙，其特征在于，由下列重量份的原料制备制成：碳酸钙85-90、锂皂石2-3、干燥落叶粉3-4、二甲基硅油2-2.5、烷基烯酮二聚体4-6、大豆油2-3、司盘80 1-2、烟片胶4-5、油酸钾2-2.5、三聚异氰酸三甲酯5-7、改性二氧化钛3-4；
所述改性二氧化钛由以下重量份的原料制成：纳米二氧化钛50-60、氢氧化镁2-4、乙基纤维素4-6、丙烯酸正丁酯5-7、石英粉3-4、聚异丁烯3-4、醇酸树脂3-5、松油醇2-4、水50-60；制备方法是首先加入丙烯酸正丁酯、纳米二氧化钛、氢氧化镁、乙基纤维素、水搅拌均匀，形成悬浮液，在45-50℃下烘干至含水量2-3%，然后立即加入聚异丁烯、醇酸树脂混合搅拌25-35分钟，然后加入其余剩余成分，在1200-1500转/分条件下搅拌，在50-60℃下烘干，粉碎成超细粉末即得。
2.根据权利要求1所述一种具有疏水亲油防潮效果的改性碳酸钙，其特征在于，由以下具体步骤制成：
（1）将碳酸钙、锂皂石、二甲基硅油、烷基烯酮二聚体、烟片胶、油酸钾加入高速捏合机中，升温至70-80℃之间，保温搅拌半小时，继续添加三聚异氰酸三甲酯，继续升温至110-130℃，保温15-20分钟后倒出；
（2）将趁热将倒出物料加入适量的去离子水以及除改性二氧化钛之外的其余剩余成分，搅拌并研磨2-3小时，形成混悬液待用；
（3）将混悬液与改性二氧化钛混合，800-1000转/分下搅拌10-15分钟，烘干、粉碎成超细粉末即得。
CN201410507929.3A 2014-09-28 2014-09-28 一种具有疏水亲油防潮效果的改性碳酸钙及其制备方法 Pending CN104356691A (zh)