CN104031418A - 一种分散度高的改性碳酸钙及其制备方法 - Google Patents

一种分散度高的改性碳酸钙及其制备方法 Download PDF

Info

Publication number
CN104031418A
CN104031418A CN201410214666.7A CN201410214666A CN104031418A CN 104031418 A CN104031418 A CN 104031418A CN 201410214666 A CN201410214666 A CN 201410214666A CN 104031418 A CN104031418 A CN 104031418A
Authority
CN
China
Prior art keywords
calcium carbonate
parts
modified
titanium dioxide
dispersity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410214666.7A
Other languages
English (en)
Other versions
CN104031418B (zh
Inventor
王俊华
朱传路
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Qixin Building Materials Co ltd
Original Assignee
FENGTAI JINGHUA AUXILIARY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FENGTAI JINGHUA AUXILIARY Co Ltd filed Critical FENGTAI JINGHUA AUXILIARY Co Ltd
Priority to CN201410214666.7A priority Critical patent/CN104031418B/zh
Publication of CN104031418A publication Critical patent/CN104031418A/zh
Application granted granted Critical
Publication of CN104031418B publication Critical patent/CN104031418B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种分散度高的改性碳酸钙，其特征在于，由下列重量份的原料制备制成：碳酸钙85-90、扩散剂NNO1-2、衣康酸4-6、双丙酮丙烯酰胺5-6、马来酸二丁基锡1-2、聚丁二酸丁二醇酯4-6、聚合氯化铝2-3、云母粉2-4、易分散纤维2-4、秸秆灰烬2-3、改性二氧化钛3-4；本发明配方合理，生产工艺简单，添加了分散性能优异的易分散纤维以及改性二氧化钛，而且使用高分子聚合物对其表面进行改性，含有的不饱和双键可以与橡胶、塑料、涂料中的成膜物质发生交联反应，产生很强的结合力，大量添加也不会降低产品的性能，用于用于塑料添加剂、颜料、涂料助剂等产品。

Description

一种分散度高的改性碳酸钙及其制备方法
技术领域
本发明涉及工业填料领域，特别是一种分散度高的改性碳酸钙及其制备方法。
背景技术
改性剂对纳米碳酸钙的性能和应用起到了重要作用。例如，分散剂的加入可减少纳米颗粒的团聚，提高分散性；表面改性剂的加入可以提高纳米碳酸钙在聚合物体系中的相容性。由此可见，分散剂和表面改性剂对于纳米碳酸钙的应用是至关重要的。然而，分散剂和表面改性剂的加入，使得纳米碳酸钙温度使用窗口大大变小，原因是常用的分散剂和偶联剂在高温下易于分解，造成气泡、开裂、缺陷、变形等，从而影响材料的外观、耐热性能和力学性能。
发明内容
本发明的目的是提供一种分散度高的改性碳酸钙及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种分散度高的改性碳酸钙，由下列重量份的原料制备制成：碳酸钙85-90、扩散剂NNO1-2、衣康酸4-6、双丙酮丙烯酰胺5-6、马来酸二丁基锡1-2、聚丁二酸丁二醇酯4-6、聚合氯化铝2-3、云母粉2-4、易分散纤维2-4、秸秆灰烬2-3、改性二氧化钛3-4；
所述改性二氧化钛由以下重量份的原料制成：氢氧化铝2-4、纳米二氧化钛50-60、碳化硅4-6、甲基丙烯酸甲酯5-7、三氧化二锑3-4、对苯二甲酸3-4、马来酸二辛酯3-5、乙二醇5-6、水50-60；制备方法是首先加入甲基丙烯酸甲酯、纳米二氧化钛、氢氧化铝、乙二醇、水搅拌均匀，形成悬浮液，在45-50℃下烘干至含水量2-3％，然后立即加入对苯二甲酸、马来酸二辛酯混合搅拌25-35分钟，然后加入其余剩余成分，在1200-1500转/分条件下搅拌，在50-60℃下烘干，粉碎成超细粉末即得。
本发明所述一种分散度高的改性碳酸钙，由以下具体步骤制成：
(1)将碳酸钙、碳酸钙、扩散剂NNO、衣康酸、双丙酮丙烯酰胺、马来酸二丁基锡、云母粉加入高速捏合机中，升温至70-80℃之间，保温搅拌半小时，继续添加除改性二氧化钛、聚合氯化铝、易分散纤维之外的其余剩余成分，继续升温至110-130℃，保温15-20分钟后倒出；
(2)将趁热将倒出物料加入适量的去离子水以及聚合氯化铝、易分散纤维，搅拌并研磨2-3小时，形成混悬液待用；
(3)将混悬液与改性二氧化钛混合，800-1000转/分下搅拌10-15分钟，烘干、粉碎成超细粉末即得。
本发明的有益效果是：本发明配方合理，生产工艺简单，添加了分散性能优异的易分散纤维以及改性二氧化钛，而且使用高分子聚合物对其表面进行改性，含有的不饱和双键可以与橡胶、塑料、涂料中的成膜物质发生交联反应，产生很强的结合力，大量添加也不会降低产品的性能，用于用于塑料添加剂、颜料、涂料助剂等产品。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种分散度高的改性碳酸钙，由下列重量份(公斤)的原料制备制成：碳酸钙85、扩散剂NNO1、衣康酸4、双丙酮丙烯酰胺5、马来酸二丁基锡1、聚丁二酸丁二醇酯4、聚合氯化铝2、云母粉2、易分散纤维2、秸秆灰烬2、改性二氧化钛3；
所述改性二氧化钛由以下重量份(公斤)的原料制成：氢氧化铝2、纳米二氧化钛50、碳化硅4、甲基丙烯酸甲酯5、三氧化二锑3、对苯二甲酸3、马来酸二辛酯3、乙二醇5、水50；制备方法是首先加入甲基丙烯酸甲酯、纳米二氧化钛、氢氧化铝、乙二醇、水搅拌均匀，形成悬浮液，在45-50℃下烘干至含水量2-3％，然后立即加入对苯二甲酸、马来酸二辛酯混合搅拌25-35分钟，然后加入其余剩余成分，在1200-1500转/分条件下搅拌，在50-60℃下烘干，粉碎成超细粉末即得。
本发明所述一种分散度高的改性碳酸钙，由以下具体步骤制成：
(1)将碳酸钙、碳酸钙、扩散剂NNO、衣康酸、双丙酮丙烯酰胺、马来酸二丁基锡、云母粉加入高速捏合机中，升温至70-80℃之间，保温搅拌半小时，继续添加除改性二氧化钛、聚合氯化铝、易分散纤维之外的其余剩余成分，继续升温至110-130℃，保温15-20分钟后倒出；
(2)将趁热将倒出物料加入适量的去离子水以及聚合氯化铝、易分散纤维，搅拌并研磨2-3小时，形成混悬液待用；
(3)将混悬液与改性二氧化钛混合，800-1000转/分下搅拌10-15分钟，烘干、粉碎成超细粉末即得。
对本发明的改性碳酸钙和普通碳酸钙的性能检测比较如下：
首先测量改性前、后碳酸钙的堆积密度，然后将改性好的碳酸钙和未改性的重质碳酸钙分别按15％的比例加入到PVC树脂中，制成样品，分别测试两者的力学性能，对比结果见下表：
由上表可以看出，改性后的碳酸钙的松散堆积密度变小，说明碳酸钙分体充分分散，还可以看出改性后碳酸钙的各项力学性能都得到提高。

Claims (2)

1.一种分散度高的改性碳酸钙，其特征在于，由下列重量份的原料制备制成：碳酸钙85-90、扩散剂NNO 1-2、衣康酸4-6、双丙酮丙烯酰胺5-6、马来酸二丁基锡1-2、聚丁二酸丁二醇酯4-6、聚合氯化铝2-3、云母粉2-4、易分散纤维2-4、秸秆灰烬2-3、改性二氧化钛3-4；
所述改性二氧化钛由以下重量份的原料制成：氢氧化铝2-4、纳米二氧化钛50-60、碳化硅4-6、甲基丙烯酸甲酯5-7、三氧化二锑3-4、对苯二甲酸3-4、马来酸二辛酯3-5、乙二醇5-6、水50-60；制备方法是首先加入甲基丙烯酸甲酯、纳米二氧化钛、氢氧化铝、乙二醇、水搅拌均匀，形成悬浮液，在45-50℃下烘干至含水量2-3%，然后立即加入对苯二甲酸、马来酸二辛酯混合搅拌25-35分钟，然后加入其余剩余成分，在1200-1500转/分条件下搅拌，在50-60℃下烘干，粉碎成超细粉末即得。
2.根据权利要求1所述一种分散度高的改性碳酸钙，其特征在于，由以下具体步骤制成：
（1）将碳酸钙、碳酸钙、扩散剂NNO、衣康酸、双丙酮丙烯酰胺、马来酸二丁基锡、云母粉加入高速捏合机中，升温至70-80℃之间，保温搅拌半小时，继续添加除改性二氧化钛、聚合氯化铝、易分散纤维之外的其余剩余成分，继续升温至110-130℃，保温15-20分钟后倒出；
（2）将趁热将倒出物料加入适量的去离子水以及聚合氯化铝、易分散纤维，搅拌并研磨2-3小时，形成混悬液待用；
（3）将混悬液与改性二氧化钛混合，800-1000转/分下搅拌10-15分钟，烘干、粉碎成超细粉末即得。
CN201410214666.7A 2014-05-20 2014-05-20 一种分散度高的改性碳酸钙及其制备方法 Expired - Fee Related CN104031418B (zh)