CN106118327A - A kind of building external paint and preparation method thereof - Google Patents
A kind of building external paint and preparation method thereof Download PDFInfo
- Publication number
- CN106118327A CN106118327A CN201610499176.5A CN201610499176A CN106118327A CN 106118327 A CN106118327 A CN 106118327A CN 201610499176 A CN201610499176 A CN 201610499176A CN 106118327 A CN106118327 A CN 106118327A
- Authority
- CN
- China
- Prior art keywords
- building external
- external paint
- styrene
- calcium carbonate
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of building external paint, its component and content (percentage by weight) is: acrylic resin 30%~35%, vinyl acetate 15%~25%, acrylate 10%~15%, styrene 8%~10%, cellulose ether 6%~8%, calcium carbonate 3%~5%, titanium dioxide 2%~5%, zinc sulfide 2%~5%, barium sulfate 2%~4%, remaining is distilled water.By having the beneficial effect that this technological means present invention obtains; this building external paint corrosion resistance is high; avoid corruption problem occurring exposing to wind and rain; its service life is long; need not often supplement coating; save great amount of cost, and do not had decolouring and fade overall attractive in appearance of situation, preferably protection external wall.
Description
Technical field
The present invention relates to technical field of chemical paint, be specifically related to a kind of building external paint and preparation method thereof.
Background technology
Along with expanding economy, people's life housing condition is constantly improved, and building is the most gradually stood in great numbers and streets and lanes,
Using anticorrosion to improve the attractive in appearance of life-span and exterior wall to build, external wall coats different types of exterior wall paint.But due to
Various places weather is different, i.e. rainfall, and the various factors such as rainwater composition and illuminance, common exterior coating is the most fully tested
Checking, cause exterior wall often occur crackle, decolour, the phenomenon such as corruption, ultimately result in the destruction completely of coating.In order to avoid these
Situation, some external wall is directly against upper ceramic tile, although effectively avoid the above-mentioned type problem using exterior coating to occur, but
Being as the passage of time, ceramic tile also there will be and comes off, and often occurs that outdoor tile pounds the casualty accident of people.Therefore, as
What produces one can preferably prevent corrosion, can protect again the building external paint of color throughout the year, be we be badly in need of solving one big
A difficult problem.
Summary of the invention
For solving above-mentioned technical problem, the invention provides a kind of corrosion resistance degree high, use outside the building of cycle length
Wall coating, and the manufacture method of this building external paint.
A kind of building external paint, its component and content (percentage by weight) is: acrylic resin 30%~35%, acetic acid second
Alkene 15%~25%, acrylate 10%~15%, styrene 8%~10%, cellulose ether 6%~8%, calcium carbonate 3%~5%, titanium dioxide
Titanium 2%~5%, zinc sulfide 2%~5%, barium sulfate 2%~4%, remaining is distilled water.
Further, this building external paint: its component and content (percentage by weight) is: acrylic resin 30%, acetic acid second
Alkene 15%, acrylate 10%, styrene 8%, cellulose ether 6%, calcium carbonate 3%, titanium dioxide 2%, zinc sulfide 2%, barium sulfate 2%,
Remaining is water.
Further, this building external paint: its component and content (percentage by weight) is: acrylic resin 32%, acetic acid second
Alkene 18%, acrylate 12%, styrene 8%, cellulose ether 7%, calcium carbonate 5%, titanium dioxide 4%, zinc sulfide 3%, barium sulfate 3%,
Remaining is water.
Further, this building external paint: its component and content (percentage by weight) is: acrylic resin 35%, acetic acid second
Alkene 20%, acrylate 15%, styrene 8%, cellulose ether 8%, calcium carbonate 5%, titanium dioxide 5%, zinc sulfide 5%, barium sulfate 4%,
Remaining is water.
The manufacture method of a kind of building external paint: comprise the steps:
(1) modulation base material: add by said components with containing measuring olefin(e) acid resin, vinyl acetate, acrylate, styrene and calcium carbonate
Entering stirs in distilled water is completely dissolved and is contained in container A, stand-by;
(2) modulation nutriment: stir by said components with containing measuring in titanium dioxide, zinc sulfide and barium sulfate addition distilled water
It is completely dissolved and is contained in container B, stand-by;
(3) polyreaction: the solution in cellulose ether, container A and the solution in container B are put in reactor and carry out polymerization instead
Should;
(4) pack: the finished product completed is packed.
By having the beneficial effect that this technological means present invention obtains, this building external paint corrosion resistance is high, it is to avoid
Exposing to wind and rain and corruption problem occur, its service life is long, it is not necessary to often supplement coating, has saved great amount of cost, and will not
Occur that decolouring is faded situation, preferably overall attractive in appearance of protection external wall.Additionally this building external paint manufacture method step
Simply, it is easy to operation, using equipment few, saved production cost, and then the price of reduction building external paint, applicable popularization makes
With.
Detailed description of the invention
The applicant is through lot of experiment validation, and carries out depth analysis research, sums up and draws the present invention.Illustrate below into
Row explanation, example is served only for explaining invention, is not intended to limit the scope of the present invention.
Embodiment 1:
Building external paint: its component and content (percentage by weight) is: acrylic resin 30%, vinyl acetate 15%, acrylic acid
Ester 10%, styrene 8%, cellulose ether 6%, calcium carbonate 3%, titanium dioxide 2%, zinc sulfide 2%, barium sulfate 2%, remaining is water.
The method making this building external paint: comprise the steps:
(1) modulation base material: add by said components with containing measuring olefin(e) acid resin, vinyl acetate, acrylate, styrene and calcium carbonate
Entering stirs in distilled water is completely dissolved and is contained in container A, stand-by;
(2) modulation nutriment: stir by said components with containing measuring in titanium dioxide, zinc sulfide and barium sulfate addition distilled water
It is completely dissolved and is contained in container B, stand-by;
(3) polyreaction: the solution in cellulose ether, container A and the solution in container B are put in reactor and carry out polymerization instead
Should;
(4) pack: the finished product completed is packed.
Embodiment 2:
Building external paint: its component and content (percentage by weight) is: acrylic resin 32%, vinyl acetate 18%, acrylic acid
Ester 12%, styrene 8%, cellulose ether 7%, calcium carbonate 5%, titanium dioxide 4%, zinc sulfide 3%, barium sulfate 3%, remaining is water.
Building external paint the most according to claim 1: it is characterized in that: its component and content (percentage by weight)
For: acrylic resin 35%, vinyl acetate 20%, acrylate 15%, styrene 8%, cellulose ether 8%, calcium carbonate 5%, titanium dioxide
Titanium 5%, zinc sulfide 5%, barium sulfate 4%, remaining is water.
The method making this building external paint: comprise the steps:
(1) modulation base material: add by said components with containing measuring olefin(e) acid resin, vinyl acetate, acrylate, styrene and calcium carbonate
Entering stirs in distilled water is completely dissolved and is contained in container A, stand-by;
(2) modulation nutriment: stir by said components with containing measuring in titanium dioxide, zinc sulfide and barium sulfate addition distilled water
It is completely dissolved and is contained in container B, stand-by;
(3) polyreaction: the solution in cellulose ether, container A and the solution in container B are put in reactor and carry out polymerization instead
Should;
(4) pack: the finished product completed is packed.
Embodiment 3:
Building external paint: its component and content (percentage by weight) is: acrylic resin 35%, vinyl acetate 20%, acrylic acid
Ester 15%, styrene 8%, cellulose ether 8%, calcium carbonate 5%, titanium dioxide 5%, zinc sulfide 5%, barium sulfate 4%, remaining is water.
The method making this building external paint: comprise the steps:
(1) modulation base material: add by said components with containing measuring olefin(e) acid resin, vinyl acetate, acrylate, styrene and calcium carbonate
Entering stirs in distilled water is completely dissolved and is contained in container A, stand-by;
(2) modulation nutriment: stir by said components with containing measuring in titanium dioxide, zinc sulfide and barium sulfate addition distilled water
It is completely dissolved and is contained in container B, stand-by;
(3) polyreaction: the solution in cellulose ether, container A and the solution in container B are put in reactor and carry out polymerization instead
Should;
(4) pack: the finished product completed is packed.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (5)
1. a building external paint, it is characterised in that: its component and content (percentage by weight) is: acrylic resin 30%~
35%, vinyl acetate 15%~25%, acrylate 10%~15%, styrene 8%~10%, cellulose ether 6%~8%, calcium carbonate 3%~
5%, titanium dioxide 2%~5%, zinc sulfide 2%~5%, barium sulfate 2%~4%, remaining is distilled water.
Building external paint the most according to claim 1: it is characterized in that: its component and content (percentage by weight) is:
Acrylic resin 30%, vinyl acetate 15%, acrylate 10%, styrene 8%, cellulose ether 6%, calcium carbonate 3%, titanium dioxide
2%, zinc sulfide 2%, barium sulfate 2%, remaining is water.
Building external paint the most according to claim 1: it is characterized in that: its component and content (percentage by weight) is:
Acrylic resin 32%, vinyl acetate 18%, acrylate 12%, styrene 8%, cellulose ether 7%, calcium carbonate 5%, titanium dioxide
4%, zinc sulfide 3%, barium sulfate 3%, remaining is water.
Building external paint the most according to claim 1: it is characterized in that: its component and content (percentage by weight) is:
Acrylic resin 35%, vinyl acetate 20%, acrylate 15%, styrene 8%, cellulose ether 8%, calcium carbonate 5%, titanium dioxide
5%, zinc sulfide 5%, barium sulfate 4%, remaining is water.
5. according to the manufacture method of the arbitrary described building external paint of Claims 1-4: it is characterized in that: include walking as follows
Rapid:
(1) modulation base material: add by said components with containing measuring olefin(e) acid resin, vinyl acetate, acrylate, styrene and calcium carbonate
Entering stirs in distilled water is completely dissolved and is contained in container A, stand-by;
(2) modulation nutriment: stir by said components with containing measuring in titanium dioxide, zinc sulfide and barium sulfate addition distilled water
It is completely dissolved and is contained in container B, stand-by;
(3) polyreaction: the solution in cellulose ether, container A and the solution in container B are put in reactor and carry out polymerization instead
Should;
(4) pack: the finished product completed is packed.