CN105400408A - Transparent type water-borne woodenware coating capable of purifying indoor air quality - Google Patents
Transparent type water-borne woodenware coating capable of purifying indoor air quality Download PDFInfo
- Publication number
- CN105400408A CN105400408A CN201510941337.7A CN201510941337A CN105400408A CN 105400408 A CN105400408 A CN 105400408A CN 201510941337 A CN201510941337 A CN 201510941337A CN 105400408 A CN105400408 A CN 105400408A
- Authority
- CN
- China
- Prior art keywords
- type
- water
- coating
- tego
- borne
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a transparent type water-borne woodenware coating capable of purifying indoor air quality. The coating is prepared by compounding a colorless and transparent nano silver solution, a colorless transparent anion solution, 2-amino-2-methyl-1-propanol, an AGITAN-208 type defoamer, dipropylene glycol butyl ether, dipropylene glycol methyl ether, a Kh-570 type silane coupling agent, a Tego-270 type substrate wetting agent, a Tego-410 type levelling agent, a wax emulsion, urea, a photocatalyst, an Kh-570 type silane coupling agent, a water-borne PUA emulsion, a polyacrylate thickener, Kathon, water and other raw materials. When the coating is used, a woodenware material brushed with a water-borne woodenware primer is directly coated with the product through a spray-coating or roll-coating way, so that not only can the shortcomings of solvent type woodenware coatings be overcome, but also the indoor air quality can be improved.
Description
Technical field
The present invention relates to Material Field, particularly a kind of transparent type has the water-borne wood coating of the quality that purifies the air of a room.
Background technology
Traditional woodwork coating generally uses solvent based coating, and it has following shortcoming: 1. it is generally organic solvent, volatile, inflammable and explosive; 2. it is generally containing free TDI, HDI and heavy metal, exists endanger human body and environment; 3. its general polycomponent product, needs allotment evenly, and because of containing solidifying agent, must construct as early as possible complete after can opening before construction, and irritant smell of constructing, must wear a gas mask.And water-borne wood coating adopts water to be solvent, it can overcome the shortcoming that solvent wood coatings exists, and is embodied in: 1. it generally adopts water to be solvent, does not fire not quick-fried; 2. it is negligible for the free TDI in product, HDI and heavy metal content, to human body and environment, it does not exist harm; 3. its general single-component product, construction is simple, and after can opening, product is stablized, and the engineering time does not limit, and without the need to wearing a gas mask, the symptoms such as workmen can not produce dizziness, cough.
Woodenware is the article often used during people live, and when the woodenware having brushed solvent based coating is used in indoor, more or less discharges the material be harmful to people in addition, and uses water-borne wood coating can overcome this shortcoming.There is water-borne wood coating in the market, also comprised the water-borne wood coating of the transparency, but it only has decoration functions, but seldom there are other functions.
For above situation, our company develops the water-borne wood coating that a kind of transparent type has the quality that purifies the air of a room, and not only can overcome the shortcoming of solvent wood coatings, can also improve IAQ (indoor air quality).
Summary of the invention
The technical problem to be solved in the present invention is to provide the water-borne wood coating that a kind of transparent type has the quality that purifies the air of a room, and it not only can overcome the shortcoming of solvent wood coatings, can also improve IAQ (indoor air quality).
The technical scheme that the present invention solves the problems of the technologies described above is: the water-borne wood coating that a kind of transparent type has the quality that purifies the air of a room adopts following weight percent formula.
Water white transparency Nano silver solution 0.5 ~ 3%, water white transparency negative solution 0.5 ~ 1%, 2-amino-2-methyl-1-propanol 0.1 ~ 0.3%, AGITAN-208 type defoamer 0.1 ~ 0.3%, waterborne PUA emulsion 65 ~ 80%, dipropylene 1 ~ 3%, dipropylene glycol methyl ether 1 ~ 3%, Kh-570 type silane coupling agent 0.1 ~ 0.3%, Tego-270 type substrate wetting agents 0.3 ~ 0.6%, Tego-410 type flow agent 0.3 ~ 0.6%, Polyacrylate thickeners 0.2 ~ 0.5%, wax emulsion 0.5 ~ 2%, photocatalyst 2 ~ 5%, urea 2 ~ 5%, Kathon CG 0.1 ~ 0.3%, water surplus.
The water-borne wood coating that a kind of transparent type of the present invention has the quality that purifies the air of a room adopts following steps to process.
Water is added in proportion in stirring tank, add water white transparency Nano silver solution, water white transparency negative solution, 2-amino-2-methyl-1-propanol, AGITAN-208 type defoamer, dipropylene, dipropylene glycol methyl ether, Kh-570 type silane coupling agent, Tego-270 type substrate wetting agents, Tego-410 type flow agent, wax emulsion, urea, photocatalyst and Kathon CG more in proportion, and stir.
After slowly dripping Kh-570 type silane coupling agent in proportion, then add waterborne PUA emulsion in proportion, slowly add Polyacrylate thickeners afterwards, stir.
During use, product of the present invention is directly coated in be coated with is brushed on the woodenware material of aqueous wooden ware priming paint by spraying or roller applications.
In the present invention, a kind of transparent type has the usage quantity of the water-borne wood coating of the quality that purifies the air of a room is every square metre of woodenware material coating 0.08 ~ 0.2kg.
Product of the present invention is verified after being used in woodenware material after tested, and woodenware material has antibacterial, the functions such as objectionable impurities such as anion releasing, decomposing formaldehyde, thus can realize improving IAQ (indoor air quality).
Embodiment
Embodiment 1
16.4 parts of water are added at stirring tank, 3 parts of water white transparency Nano silver solutions, 0.5 part of water white transparency negative solution, 0.3 part of 2-amino-2-methyl-1-propanol, 0.1 part of AGITAN-208 type defoamer, 1 part of dipropylene, 3 parts of dipropylene glycol methyl ethers, 0.1 part of Kh-570 type silane coupling agent, 0.6 part of Tego-270 type substrate wetting agents, 0.3 part of Tego-410 type flow agent, 2 parts of wax emulsions, 5 parts of urea, 2 parts of photocatalysts and 0.1 part of Kathon CG, and stir, after slowly dripping 0.1 part of Kh-570 type silane coupling agent again, add 65 parts of waterborne PUA emulsions, slowly add 0.5 part of Polyacrylate thickeners afterwards, stir, i.e. the present embodiment 1.
Embodiment 2
11.2 parts of water are added at stirring tank, 1.5 parts of water white transparency Nano silver solutions, 0.8 part of water white transparency negative solution, 0.2 part of 2-amino-2-methyl-1-propanol, 0.2 part of AGITAN-208 type defoamer, 2 parts of dipropylene, 2 parts of dipropylene glycol methyl ethers, 0.2 part of Kh-570 type silane coupling agent, 0.5 part of Tego-270 type substrate wetting agents, 0.5 part of Tego-410 type flow agent, 1.2 parts of wax emulsions, 3 parts of urea, 3 parts of photocatalysts and 0.2 part of Kathon CG, and stir, after slowly dripping 0.2 part of Kh-570 type silane coupling agent again, add 73 parts of waterborne PUA emulsions, slowly add 0.3 part of Polyacrylate thickeners afterwards, stir, i.e. the present embodiment 2.
Embodiment 3
4.6 parts of water are added at stirring tank, 0.5 part of water white transparency Nano silver solution, 1 part of water white transparency negative solution, 0.1 part of 2-amino-2-methyl-1-propanol, 0.3 part of AGITAN-208 type defoamer, 3 parts of dipropylene, 1 part of dipropylene glycol methyl ether, 0.3 part of Kh-570 type silane coupling agent, 0.3 part of Tego-270 type substrate wetting agents, 0.6 part of Tego-410 type flow agent, 0.5 part of wax emulsion, 2 parts of urea, 5 parts of photocatalysts and 0.3 part of Kathon CG, and stir, after slowly dripping 0.3 part of Kh-570 type silane coupling agent again, add 80 parts of waterborne PUA emulsions, slowly add 0.2 part of Polyacrylate thickeners afterwards, stir, i.e. the present embodiment 3.
In order to verify whether product of the present invention meets GB/T23999-2009 " indoor decorating use woodwork coating ", sample is delivered to third party and is detected feeler mechanism and detect by the present inventor, and test result gathers as follows.
Known by third party's detected result, inventive samples meets the standard-required of GB/T23999-2009 " indoor decorating use woodwork coating ".
In order to verify whether product of the present invention meets GB/T24410-2009 " in indoor decorating and refurnishing materials water-borne wood coating limits of harmful substances ", sample is delivered to third party and is detected feeler mechanism and detect by the present inventor, and test result gathers as follows.
Known by third party's detected result, inventive samples meets the standard-required of GB/T24410-2009 " in indoor decorating and refurnishing materials water-borne wood coating limits of harmful substances ".
In order to verify the properties of product of the present invention further, the present inventor detects with sample prepared by embodiment 1 ~ 3, and test result gathers as follows.
From test result: the embodiment of the present invention 1 ~ 3 all has antibacterial, purifying formaldehyde and the function such as toluene and anion releasing.
Claims (3)
1. transparent type has a water-borne wood coating for the quality that purifies the air of a room, it is characterized in that, it adopts following weight percent formula:
Water white transparency Nano silver solution 0.5 ~ 3%, water white transparency negative solution 0.5 ~ 1%, 2-amino-2-methyl-1-propanol 0.1 ~ 0.3%, AGITAN-208 type defoamer 0.1 ~ 0.3%, waterborne PUA emulsion 65 ~ 80%, dipropylene 1 ~ 3%, dipropylene glycol methyl ether 1 ~ 3%, Kh-570 type silane coupling agent 0.1 ~ 0.3%, Tego-270 type substrate wetting agents 0.3 ~ 0.6%, Tego-410 type flow agent 0.3 ~ 0.6%, Polyacrylate thickeners 0.2 ~ 0.5%, wax emulsion 0.5 ~ 2%, photocatalyst 2 ~ 5%, urea 2 ~ 5%, Kathon CG 0.1 ~ 0.3%, water surplus.
2. transparent type has a water-borne wood coating for the quality that purifies the air of a room, it is characterized in that, it adopts following steps to process:
A. in stirring tank, water is added in proportion, add water white transparency Nano silver solution, water white transparency negative solution, 2-amino-2-methyl-1-propanol, AGITAN-208 type defoamer, dipropylene, dipropylene glycol methyl ether, Kh-570 type silane coupling agent, Tego-270 type substrate wetting agents, Tego-410 type flow agent, wax emulsion, urea, photocatalyst and Kathon CG more in proportion, and stir;
B. after slowly dripping Kh-570 type silane coupling agent in proportion, then add waterborne PUA emulsion in proportion, slowly add Polyacrylate thickeners afterwards, stir.
3. transparent type has a water-borne wood coating for the quality that purifies the air of a room, it is characterized in that, the usage quantity of water-borne wood coating is every square metre of woodenware material coating 0.08 ~ 0.2kg.