CN104449154A - Water-based chromium-free fingerprint-resistant paint for galvanized steel plate - Google Patents
Water-based chromium-free fingerprint-resistant paint for galvanized steel plate Download PDFInfo
- Publication number
- CN104449154A CN104449154A CN201410707170.3A CN201410707170A CN104449154A CN 104449154 A CN104449154 A CN 104449154A CN 201410707170 A CN201410707170 A CN 201410707170A CN 104449154 A CN104449154 A CN 104449154A
- Authority
- CN
- China
- Prior art keywords
- parts
- monomer mixture
- methyl
- water
- mixtures
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based chromium-free fingerprint-resistant paint for a galvanized steel plate. The paint comprises raw materials in parts by weight as follows: 30.0-55.0 parts of a fluorine-modified water-based self-crosslinking acrylate emulsion, 0.1-1.5 parts of a neutralizer, 0.5-1.0 part of a silane coupling agent, 0.1-0.2 parts of laurocapram, 0.6-1.0 part of chlorinated paraffin, 4.0-8.0 parts of inorganic sol, 1.5-3.5 parts of metal salt, 0.1-0.3 parts of glycerin, 0.1-0.2 parts of sodium carboxymethylcellulose, 0.1-0.2 parts of polydimethylsiloxane, 1.5-5.5 parts of a cosolvent, 1.0-2.5 parts of aluminium dihydrogen phosphate and 40-50 parts of water; the curing temperature is as low as 40-60 DEG C, and energy consumption is reduced. The fluorine-modified water-based self-crosslinking acrylate emulsion is adopted to enable a film to have weather-resistant, waterproof and self-cleaning performance and the like, the film has a self-repairing function when damaged, and the forming processability is greatly improved. Low VOC (volatile organic compounds) emission is realized, and the problem of chromium passivation pollution is solved.
Description
Technical field
The present invention relates generally to paint field, particularly relates to a kind of aqueous chromium-free fingerprint-resistant coating for steel plate galvanized.
Background technology
Zinc-plated is one of the most widely used metal surface treating method, and zinc layers has excellent processing and use properties.But zinc layers self chemical property is comparatively active, and occur the defects such as white rust because of corrosion in a humidity environment, therefore zinc coating needs to carry out Passivation Treatment, improve its result of use further.Since a very long time, because chromating has the features such as technique is simple, excellent anti-corrosion performance, cost are low, and be generally used.But there is great hazardness containing free sexavalent chrome to environment and human body in chromium passivation film, prohibited in RoHS standard and adopted chromating process.
Along with the progressively enforcement of environmental protection act, the use of chromium passivating is subject to more and more stricter restriction.Current chromium-free deactivation technical study becomes domestic and international research focus and achieves certain achievement.Patent 201010277648.5 discloses a kind of non-chrome water-based organic fingerprint-resistant coating and preparation method thereof, the steel plate galvanized of this invention process has excellent anti-fingerprint and the oilness of punching press, but when steel surface coating damage without self-repair function, so that breakage corrosion can spread fast; Patent 201080054392.X discloses a kind of acidic aqueous chrome free composition for galvanized steel sheet surface corrosion-resistance treatment, this invention has positive effect in raising sheet material erosion resistance, but in punching course, do not reach self-lubricating effect, performance after punching press cannot be ensured; Patent US5068134 discloses a kind of containing inorganic silicate, organosilicate and SiO
2the chromium-free passivation liquid being applicable to galvanized sheet surface of colloidal sol etc., reaches the effect of alternative chromaking liquid substantially, but film-forming temperature requires more than 125 DEG C, requires too high, and cause energy dissipation to production line ability to cure.
The invention provides a kind of cryogenic curing, excellent erosion resistance and molding processibility, and there is the aqueous chromium-free fingerprint-resistant coating of self-repair function, meet the passivation user demand of steel plate galvanized completely.
Summary of the invention
The object of the invention is exactly to provide a kind of aqueous chromium-free fingerprint-resistant coating for steel plate galvanized.
The present invention is achieved by the following technical solutions:
For an aqueous chromium-free fingerprint-resistant coating for steel plate galvanized, it is characterized in that what it was made up of the raw material of following weight parts:
Fluorine modified aqueous self-crosslinking acrylic ester emulsion 30.0-55.0, neutralizing agent 0.1-1.5, silane coupling agent 0.5-1.0, azone 0.1-0.2, clorafin 0.6-1.0, inorganic sol 4.0-8.0, metal-salt 1.5-3.5, glycerine 0.1-0.3, Xylo-Mucine 0.1-0.2, dimethyl silicone oil 0.1-0.2, solubility promoter 1.5-5.5, aluminium dihydrogen phosphate 1.0-2.5, water 40-50;
Described neutralizing agent is one or more mixtures in ammoniacal liquor, triethylamine, dimethylethanolamine, N, N-dimethylethanolamine, AMP-95;
Described inorganic sol is MgO, CaO, SiO
2, ZnO, Al
2o
3in one or more mixtures;
Described metal-salt is one or more mixtures in four (trolamine) zirconate, methyl ethyl diketone zirconium, sodium fluozirconate, potassium fluozirconate, Sodium orthomolybdate, potassium molybdate, ammonium molybdate;
Described solubility promoter is one or more mixtures in methyl alcohol, ether, ethanol, Virahol, propyl carbinol, ethylene glycol monomethyl ether, ethylene glycol ethyl ether, butyl glycol ether, propylene glycol monomethyl ether, propandiol butyl ether, (two) toluene;
Described silane coupling agent is one or more mixtures in APTES, 3-(2,3-epoxy third oxygen) propyl trimethoxy silicane, γ-mercaptopropyl trimethoxysilane, vinyltrimethoxy silane;
Described fluorine modified aqueous self-crosslinking acrylic ester emulsion is made up of the raw material of following weight parts:
Emulsifying agent 0.2-1.0, monomer mixture 35.0-55.0, initiator 0.2-0.5, water 50-70;
(1) pre-emulsification: under room temperature, joins emulsifying agent in above-mentioned water, obtains emulsifier solution after stirring and dissolving, and the 25-75% getting emulsifier solution weight mixes with monomer mixture, and high-speed stirring evenly obtains pre-emulsion afterwards, for subsequent use;
(2) seed priming: remaining emulsifier solution is mixed with remaining monomer mixture, stir, add the 10-15% of above-mentioned pre-emulsion weight, 55-65 DEG C is warming up under 4-5 DEG C/min speed, add the 20-25% of above-mentioned initiator weight, continue to be warming up to 80-85 DEG C, seed reaction is complete;
(3) be polymerized: maintenance temperature is 80-85 DEG C, drip off each raw material of residue in 3-4h, insulation 3-4h, adjustment pH is 4.5-5.5, obtains final product;
Described monomer mixture is made up of following:
(1) one or more acrylic monomers, account for the 40.0-65.0% of monomer mixture total amount, comprising: (methyl) vinylformic acid, (methyl) Hydroxyethyl acrylate, (methyl) Propylene glycol monoacrylate, (methyl) methyl acrylate, (methyl) n-butyl acrylate, Isooctyl acrylate monomer, glycidyl methacrylate;
(2) one or more vinyl monomers, account for monomer mixture total amount 25.0-35.0%, comprising: vinylbenzene, tertiary ethylene carbonate, Vinyl toluene, norbornylene;
(3) one or more cross-linking monomers, account for monomer mixture total amount 0-4.0%, comprising: diacetone-acryloamide(DAA), acrylamide, N hydroxymethyl acrylamide, Ethylene glycol dimethacrylate;
(4) one or more fluorochemical monomers, account for monomer mixture total amount 1.0-5.0%, comprising: dodecafluoroheptyl methacrylate, trifluoroethyl methacrylate, Hexafluorobutyl mathacrylate, vinylformic acid hexafluoro butyl ester;
Described emulsifying agent is; One or more mixtures in alkylphenol polyoxyethylene, sodium lauryl sulphate, alkylamide vinyl sulfonic acid sodium;
Described initiator is: at least one in Potassium Persulphate, Sodium Persulfate, ammonium persulphate;
As claimed in claim 1 for a preparation method for the aqueous chromium-free fingerprint-resistant coating of steel plate galvanized, it is characterized in that comprising the following steps:
Joined in above-mentioned water by fluorine modified aqueous self-crosslinking acrylic ester emulsion, stir, add each raw material of residue, 1000-1600 rev/min of dispersed with stirring 20-30 minute, agitation and filtration obtains finished product.
Advantage of the present invention is:
(1) solidification value is low to moderate 40-60 DEG C, reduces energy consumption.Adopt fluorine modified aqueous self-crosslinking acrylic ester class emulsion, impel rete to have the performances such as weathering resistance, water tolerance and automatically cleaning.
(2) when rete is damaged, there is self-repair function, greatly improve moulding processability.
(3) low VOC discharge, and solve chromium passivating pollution problem.
Embodiment
Embodiment 1
For an aqueous chromium-free fingerprint-resistant coating for steel plate galvanized, it is characterized in that what it was made up of the raw material of following weight parts:
Fluorine modified aqueous self-crosslinking acrylic ester emulsion 30.0-55.0, neutralizing agent 0.1-1.5, silane coupling agent 0.5-1.0, azone 0.1-0.2, clorafin 0.6-1.0, inorganic sol 4.0-8.0, metal-salt 1.5-3.5, glycerine 0.1-0.3, Xylo-Mucine 0.1-0.2, dimethyl silicone oil 0.1-0.2, solubility promoter 1.5-5.5, aluminium dihydrogen phosphate 1.0-2.5, water 40-50;
Described neutralizing agent is one or more mixtures in ammoniacal liquor, triethylamine, dimethylethanolamine, N, N-dimethylethanolamine, AMP-95;
Described inorganic sol is MgO, CaO, SiO
2, ZnO, Al
2o
3in one or more mixtures;
Described metal-salt is one or more mixtures in four (trolamine) zirconate, methyl ethyl diketone zirconium, sodium fluozirconate, potassium fluozirconate, Sodium orthomolybdate, potassium molybdate, ammonium molybdate;
Described solubility promoter is one or more mixtures in methyl alcohol, ether, ethanol, Virahol, propyl carbinol, ethylene glycol monomethyl ether, ethylene glycol ethyl ether, butyl glycol ether, propylene glycol monomethyl ether, propandiol butyl ether, (two) toluene;
Described silane coupling agent is one or more mixtures in APTES, 3-(2,3-epoxy third oxygen) propyl trimethoxy silicane, γ-mercaptopropyl trimethoxysilane, vinyltrimethoxy silane;
Described fluorine modified aqueous self-crosslinking acrylic ester emulsion is made up of the raw material of following weight parts:
Emulsifying agent 1.0, monomer mixture 55.0, initiator 0.5, water 50;
(1) pre-emulsification: under room temperature, joins emulsifying agent in above-mentioned water, obtains emulsifier solution after stirring and dissolving, and get emulsifier solution weight 75% mixes with monomer mixture, and high-speed stirring evenly obtains pre-emulsion afterwards, for subsequent use;
(2) seed priming: mixed with remaining monomer mixture by remaining emulsifier solution, stir, adds 15% of above-mentioned pre-emulsion weight, 65 DEG C are warming up under 5 DEG C/min speed, add 25% of above-mentioned initiator weight, continue to be warming up to 85 DEG C, seed reaction is complete;
(3) be polymerized: keep temperature to be 85 DEG C, in 3-4h, drip off each raw material of residue, insulation 3-4h, and regulate pH to be 5.5, obtain final product;
Described monomer mixture is made up of following:
(1) one or more acrylic monomers, account for 56% of monomer mixture total amount, comprising: (methyl) vinylformic acid, (methyl) Hydroxyethyl acrylate, (methyl) Propylene glycol monoacrylate, (methyl) methyl acrylate, (methyl) n-butyl acrylate, Isooctyl acrylate monomer, glycidyl methacrylate;
(2) one or more vinyl monomers, account for monomer mixture total amount 35.0%, comprising: vinylbenzene, tertiary ethylene carbonate, Vinyl toluene, norbornylene;
(3) one or more cross-linking monomers, account for monomer mixture total amount 4.0%, comprising: diacetone-acryloamide(DAA), acrylamide, N hydroxymethyl acrylamide, Ethylene glycol dimethacrylate;
(4) one or more fluorochemical monomers, account for monomer mixture total amount 5.0%, comprising: dodecafluoroheptyl methacrylate, trifluoroethyl methacrylate, Hexafluorobutyl mathacrylate, vinylformic acid hexafluoro butyl ester;
Described emulsifying agent is; One or more mixtures in alkylphenol polyoxyethylene, sodium lauryl sulphate, alkylamide vinyl sulfonic acid sodium;
Described initiator is: at least one in Potassium Persulphate, Sodium Persulfate, ammonium persulphate;
For a preparation method for the aqueous chromium-free fingerprint-resistant coating of steel plate galvanized, it is characterized in that comprising the following steps:
Joined in above-mentioned water by fluorine modified aqueous self-crosslinking acrylic ester emulsion, stir, add each raw material of residue, 1600 revs/min of dispersed with stirring 30 minutes, agitation and filtration obtains finished product.
Its physicals tested by gained coating and properties of coating evaluation is as follows:
Physicals:
Test item | Detection method | Unit | This Product checking result | Commercially available prod |
Solid content | Weighting method, 120 DEG C, 30min | % | 15±1 | 16±1 |
Viscosity | Be coated with-4 glasss, 25 DEG C | s | 12±1 | 13±1 |
Proportion | m/V,25℃ | g/mL | 1.02±0.03 | 1.0±0.03 |
PH value | PH meter, 25 DEG C | — | 5.0±1 | 4.5±1 |
Properties of coating is evaluated:
Claims (2)
1., for an aqueous chromium-free fingerprint-resistant coating for steel plate galvanized, it is characterized in that what it was made up of the raw material of following weight parts:
Fluorine modified aqueous self-crosslinking acrylic ester emulsion 30.0-55.0, neutralizing agent 0.1-1.5, silane coupling agent 0.5-1.0, azone 0.1-0.2, clorafin 0.6-1.0, inorganic sol 4.0-8.0, metal-salt 1.5-3.5, glycerine 0.1-0.3, Xylo-Mucine 0.1-0.2, dimethyl silicone oil 0.1-0.2, solubility promoter 1.5-5.5, aluminium dihydrogen phosphate 1.0-2.5, water 40-50;
Described neutralizing agent is one or more mixtures in ammoniacal liquor, triethylamine, dimethylethanolamine, N, N-dimethylethanolamine, AMP-95;
Described inorganic sol is MgO, CaO, SiO
2, ZnO, Al
2o
3in one or more mixtures;
Described metal-salt is one or more mixtures in four (trolamine) zirconate, methyl ethyl diketone zirconium, sodium fluozirconate, potassium fluozirconate, Sodium orthomolybdate, potassium molybdate, ammonium molybdate;
Described solubility promoter is one or more mixtures in methyl alcohol, ether, ethanol, Virahol, propyl carbinol, ethylene glycol monomethyl ether, ethylene glycol ethyl ether, butyl glycol ether, propylene glycol monomethyl ether, propandiol butyl ether, (two) toluene;
Described silane coupling agent is APTES, 3-(2,3-epoxy third oxygen) propyl trimethoxy silicane, γ-mercaptopropyl trimethoxysilane, one or more mixtures in vinyltrimethoxy silane;
Described fluorine modified aqueous self-crosslinking acrylic ester emulsion is made up of the raw material of following weight parts:
Emulsifying agent 0.2-1.0, monomer mixture 35.0-55.0, initiator 0.2-0.5, water 50-70;
(1) pre-emulsification: under room temperature, joins emulsifying agent in above-mentioned water, obtains emulsifier solution after stirring and dissolving, and the 25-75% getting emulsifier solution weight mixes with monomer mixture, and high-speed stirring evenly obtains pre-emulsion afterwards, for subsequent use;
(2) seed priming: remaining emulsifier solution is mixed with remaining monomer mixture, stir, add the 10-15% of above-mentioned pre-emulsion weight, 55-65 DEG C is warming up under 4-5 DEG C/min speed, add the 20-25% of above-mentioned initiator weight, continue to be warming up to 80-85 DEG C, seed reaction is complete;
(3) be polymerized: maintenance temperature is 80-85 DEG C, drip off each raw material of residue in 3-4h, insulation 3-4h, adjustment pH is 4.5-5.5, obtains final product;
Described monomer mixture is made up of following:
(1) one or more acrylic monomers, account for the 40.0-65.0% of monomer mixture total amount, comprising: (methyl) vinylformic acid, (methyl) Hydroxyethyl acrylate, (methyl) Propylene glycol monoacrylate, (methyl) methyl acrylate, (methyl) n-butyl acrylate, Isooctyl acrylate monomer, glycidyl methacrylate;
(2) one or more vinyl monomers, account for monomer mixture total amount 25.0-35.0%, comprising: vinylbenzene, tertiary ethylene carbonate, Vinyl toluene, norbornylene;
(3) one or more cross-linking monomers, account for monomer mixture total amount 0-4.0%, comprising: diacetone-acryloamide(DAA), acrylamide, N hydroxymethyl acrylamide, Ethylene glycol dimethacrylate;
(4) one or more fluorochemical monomers, account for monomer mixture total amount 1.0-5.0%, comprising: dodecafluoroheptyl methacrylate, trifluoroethyl methacrylate, Hexafluorobutyl mathacrylate, vinylformic acid hexafluoro butyl ester;
Described emulsifying agent is; One or more mixtures in alkylphenol polyoxyethylene, sodium lauryl sulphate, alkylamide vinyl sulfonic acid sodium;
Described initiator is: at least one in Potassium Persulphate, Sodium Persulfate, ammonium persulphate.
2., as claimed in claim 1 for a preparation method for the aqueous chromium-free fingerprint-resistant coating of steel plate galvanized, it is characterized in that comprising the following steps:
Joined in above-mentioned water by fluorine modified aqueous self-crosslinking acrylic ester emulsion, stir, add each raw material of residue, 1000-1600 rev/min of dispersed with stirring 20-30 minute, agitation and filtration obtains finished product.