CN106111890A - 一种蜡模制作工艺 - Google Patents

一种蜡模制作工艺 Download PDF

Info

Publication number
CN106111890A
CN106111890A CN201610603957.4A CN201610603957A CN106111890A CN 106111890 A CN106111890 A CN 106111890A CN 201610603957 A CN201610603957 A CN 201610603957A CN 106111890 A CN106111890 A CN 106111890A
Authority
CN
China
Prior art keywords
wax
pattern
slack
processing technology
stirring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610603957.4A
Other languages
English (en)
Inventor
何拥军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liuzhou Jin Te Abrasion Resistance Material Limited-Liability Co
Original Assignee
Liuzhou Jin Te Abrasion Resistance Material Limited-Liability Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liuzhou Jin Te Abrasion Resistance Material Limited-Liability Co filed Critical Liuzhou Jin Te Abrasion Resistance Material Limited-Liability Co
Priority to CN201610603957.4A priority Critical patent/CN106111890A/zh
Publication of CN106111890A publication Critical patent/CN106111890A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种蜡模制作工艺，包括以下步骤：蜡料配比，制作蜡膏，注蜡，取模。用本发明的方法制作蜡模，能使蜡模质量达到很大的提高，节约了人力和物力，提高了利用价值。

Description

一种蜡模制作工艺
技术领域
本发明属于铝合金压铸工艺技术领域，特别涉及一种蜡模制作工艺。
背景技术
目前，金属铸造工艺中，蜡模的制作非常重要，但是在制作过程中往往存在不同程度的缺陷，能很好的解决该问题则使铸件的质量能得到很大的提高。
发明内容
为了解决铸造中蜡模质量出现很多的问题，本发明提供一种蜡模制作工艺。
本发明的技术方案是：一种蜡模制作工艺，其特征在于：包括以下步骤：（1）蜡料配比：石蜡重量百分比10%-50%，硬脂酸重量百分比10%-50%；（2）将上述步骤中配好的液蜡和蜡屑送到搅拌蜡缸内搅拌，使蜡膏搅拌充分并均匀、无气，得到合乎要求的蜡膏，搅拌时始终沿同一方向搅拌，搅拌速度为30cm/s，搅拌过程中加热温度为30-40℃；（3）压蜡缸循环水温度为50-55℃，压蜡压力3-6Kg；（4）注蜡时保压时间1-2小时，注满蜡的模具放置于模型冷却池中冷却，当冷却池水温度升高后可用冰块降温；（5）取模；所述步骤（5）中取出的蜡模完全冷却后，放在预先制作好的两个型腔中的一个内，两个型腔组合到一起与标准蜡模完全相同，且二者组合处为在蜡模有飞边和分型线的位置，在该组合处两个型腔上均设置刀刃，飞边和分型线通过两个型腔组合时被切掉，取出蜡模再用砂纸打磨残留的飞边和分型线的痕迹，最后再次吹干净蜡模上的蜡屑和水份，分类整齐地摆放到蜡模架上。
进一步地，所述步骤（2）中如果蜡膏太稀,可再加适量的蜡屑,如果太稠，可加入少量蜡液,继续搅拌，如果蜡膏粗,可延长搅拌时间,直至拌出合乎要求的蜡膏为止。
进一步地，所述步骤（4）中浇注完成后，取下注蜡枪时要及时封堵注蜡嘴，以防蜡膏倒流造蜡模缺陷。
本发明的有益效果：用本发明的方法制作蜡模，能使蜡模质量达到很大的提高，节约了人力和物力，提高了利用价值。
具体实施方式
对本发明提供的实施方式作进一步详细的说明：
一种蜡模制作工艺，包括以下步骤：（1）蜡料配比：石蜡重量百分比10%-50%，硬脂酸重量百分比10%-50%；（2）将上述步骤中配好的液蜡和蜡屑送到搅拌蜡缸内搅拌，使蜡膏搅拌充分并均匀、无气，得到合乎要求的蜡膏，搅拌时始终沿同一方向搅拌，搅拌速度为30cm/s，搅拌过程中加热温度为30-40℃；（3）压蜡缸循环水温度为50-55℃，压蜡压力3-6Kg；（4）注蜡时保压时间1-2小时，注满蜡的模具放置于模型冷却池中冷却，当冷却池水温度升高后可用冰块降温；（5）取模；所述步骤（5）中取出的蜡模完全冷却后，放在预先制作好的两个型腔中的一个内，两个型腔组合到一起与标准蜡模完全相同，且二者组合处为在蜡模有飞边和分型线的位置，在该组合处两个型腔上均设置刀刃，飞边和分型线通过两个型腔组合时被切掉，取出蜡模再用砂纸打磨残留的飞边和分型线的痕迹，最后再次吹干净蜡模上的蜡屑和水份，分类整齐地摆放到蜡模架上。
所述步骤（2）中如果蜡膏太稀,可再加适量的蜡屑,如果太稠，可加入少量蜡液,继续搅拌，如果蜡膏粗,可延长搅拌时间,直至拌出合乎要求的蜡膏为止。
所述步骤（4）中浇注完成后，取下注蜡枪时要及时封堵注蜡嘴，以防蜡膏倒流造蜡模缺陷。
在此说明书中，本发明已参照其特定的实施例作了描述。但是，很显然仍可以作出各种修改和变换而不背离本发明的精神和范围。因此，说明书应被认为是说明性的而非限制性的。

Claims (3)

1.一种蜡模制作工艺，其特征在于：包括以下步骤：（1）蜡料配比：石蜡重量百分比10%-50%，硬脂酸重量百分比10%-50%；（2）将上述步骤中配好的液蜡和蜡屑送到搅拌蜡缸内搅拌，使蜡膏搅拌充分并均匀、无气，得到合乎要求的蜡膏，搅拌时始终沿同一方向搅拌，搅拌速度为30cm/s，搅拌过程中加热温度为30-40℃；（3）压蜡缸循环水温度为50-55℃，压蜡压力3-6Kg；（4）注蜡时保压时间1-2小时，注满蜡的模具放置于模型冷却池中冷却，当冷却池水温度升高后可用冰块降温；（5）取模；所述步骤（5）中取出的蜡模完全冷却后，放在预先制作好的两个型腔中的一个内，两个型腔组合到一起与标准蜡模完全相同，且二者组合处为在蜡模有飞边和分型线的位置，在该组合处两个型腔上均设置刀刃，飞边和分型线通过两个型腔组合时被切掉，取出蜡模再用砂纸打磨残留的飞边和分型线的痕迹，最后再次吹干净蜡模上的蜡屑和水份，分类整齐地摆放到蜡模架上。
2.根据权利要求1所述的蜡模制作工艺，其特征在于：所述步骤（2）中如果蜡膏太稀,可再加适量的蜡屑,如果太稠，可加入少量蜡液,继续搅拌，如果蜡膏粗,可延长搅拌时间,直至拌出合乎要求的蜡膏为止。
3.根据权利要求1所述的蜡模制作工艺，其特征在于：所述步骤（4）中浇注完成后，取下注蜡枪时要及时封堵注蜡嘴，以防蜡膏倒流造蜡模缺陷。
CN201610603957.4A 2016-07-28 2016-07-28 一种蜡模制作工艺 Pending CN106111890A (zh)