CN106083010B - The ceramic preparation of celadon smooth surface and crack surface - Google Patents

The ceramic preparation of celadon smooth surface and crack surface Download PDF

Info

Publication number
CN106083010B
CN106083010B CN201610450762.0A CN201610450762A CN106083010B CN 106083010 B CN106083010 B CN 106083010B CN 201610450762 A CN201610450762 A CN 201610450762A CN 106083010 B CN106083010 B CN 106083010B
Authority
CN
China
Prior art keywords
parts
celadon
smooth surface
crack
crack surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610450762.0A
Other languages
Chinese (zh)
Other versions
CN106083010A (en
Inventor
马协初
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YIXING GOLDFISH CERAMICS CO Ltd
Original Assignee
YIXING GOLDFISH CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIXING GOLDFISH CERAMICS CO Ltd filed Critical YIXING GOLDFISH CERAMICS CO Ltd
Priority to CN201610450762.0A priority Critical patent/CN106083010B/en
Publication of CN106083010A publication Critical patent/CN106083010A/en
Application granted granted Critical
Publication of CN106083010B publication Critical patent/CN106083010B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to ceramic field, the pug ingredient of the smooth surface (lower layer or upper layer) of the specially ceramic preparation not hacking of celadon smooth surface and crack surface includes SiO269.26 part, AL2O319.25 part, Fe2O30.86 part, 0.81 part of CaO, 0.51 part of MgO, K22.90 parts of O, Na21.30 parts of O；The pug ingredient of the crack surface (upper layer or lower layer) of hacking includes SiO262.56 part, AL2O325.44 part, Fe2O30.82 part, 0.7 part of CaO, 4.25 parts of MgO, K22.20 parts of O, Na21.20 parts of O；It is bonded together level above and below smooth surface and crack surface to form whole base with intermediate mud layer, whole base utilizes shuttle kiln, and the atmosphere of reducing flame is burnt into.The celadon of traditional smooth surface is combined with crack surface celadon, is showed on same part celadon pottery, and be not in cracking defect by the ceramic preparation of celadon smooth surface and crack surface provided by the invention, creates the high-grade celadon art work.

Description

The ceramic preparation of celadon smooth surface and crack surface
Technical field
The present invention relates to ceramic fields, the specially ceramic preparation of celadon smooth surface and crack surface.
Background technique
Yixing celadon such as lotus flower when fully open, it is pure and fresh to scoop, it is known as " oriental hyacinth, exquisite jasper device ", currently, celadon Product has more than 1000 a kinds such as vase, flowerpot, tea set, tableware, drinking utensils, ashtray, lamp holder and all kinds of industrial art decorative ceramics. Glaze colours is also added to yellow eel Huang, black pigment used by women in ancient times to paint their eyebrows blueness, Mei Qing, bluish white, ultramarine, emerald green blueness, pale blue, shadow blueness, calipash, reddish black, grey green more than 10, In especially using yellow eel yellow, pale blue as top grade.Decoration on other than traditional texturing, embossment stippling, hundred fragments, there are also Ye Luowen, A variety of new decorations such as flower, screen printing, transmutation, crimson are brushed under spraying decoration, colored glaze, bluish white combination, glaze.Wherein hundred traditional fragments, Piece line staggered " roe line " and " crab line " on old china circle term, overlapping such as ice is named " cracked ice pattern ", and lines is crisscross freely, Glaze colours is simple and honest strong.
It as consumer is to the diversity requirement of ceramic, needs to break through traditional technique, a variety of skill is combined, make Make richer ceramic.Making best artistic effect is the foundation and target that we set up the project.
Summary of the invention
To solve the above-mentioned problems, the present invention provides the technique that a kind of celadon of smooth surface is combined with crack surface celadon, knot Traditional handicraft and modern technologies are closed, a kind of new celadon is provided, the higher level requirement of client is met.
The specific technical proposal is:
The ceramic preparation of celadon smooth surface and crack surface, including following procedure:
The pug ingredient of the smooth surface (lower layer or upper layer) of not hacking is formed according to following parts by weight:
SiO269.26 part, AL2O319.25 part, Fe2O30.86 part, 0.81 part of CaO, 0.51 part of MgO, K2O 2.90 Part, Na21.30 parts of O；
The pug ingredient of the crack surface (upper layer or lower layer) of hacking is formed according to following parts by weight:
SiO262.56 part, AL2O325.44 part, Fe2O30.82 part, 0.7 part of CaO, 4.25 parts of MgO, K2O 2.20 Part, Na21.20 parts of O；
Be bonded together level above and below smooth surface and crack surface to form whole base with intermediate mud layer, the pug of intermediate mud layer at Divide and formed according to following parts by weight:
SiO266.43 part, AL2O322.66 part, Fe2O30.83 part, 0.80 part of CaO, 2.02 parts of MgO, K2O 2.50 Part, Na21.20 parts of O；
Whole base utilizes shuttle kiln, and the atmosphere of reducing flame is burnt into, firing temperature: 1250~1320 DEG C, when firing Between: 10~12 hours.
The ceramic preparation of celadon smooth surface and crack surface provided by the invention, by the celadon and crack surface of traditional smooth surface Celadon combines, and is showed on same part celadon pottery, and be not in cracking defect, and high-grade celadon is created The art work.
Specific embodiment
It is described in conjunction with the embodiments the specific embodiment of the invention.
Embodiment 1
The pug ingredient of the smooth surface (lower layer or upper layer) of not hacking is formed according to following parts by weight:
SiO269.26 part, AL2O319.25 part, Fe2O30.86 part, 0.81 part of CaO, 0.51 part of MgO, K2O 2.90 Part, Na21.30 parts of O；
The pug ingredient of the crack surface (upper layer or lower layer) of hacking is formed according to following parts by weight:
SiO262.56 part, AL2O325.44 part, Fe2O30.82 part, 0.7 part of CaO, 4.25 parts of MgO, K2O 2.20 Part, Na21.20 parts of O；
Be bonded together level above and below smooth surface and crack surface to form whole base with intermediate mud layer, the pug of intermediate mud layer at Divide and formed according to following parts by weight:
SiO266.43 part, AL2O322.66 part, Fe2O30.83 part, 0.80 part of CaO, 2.02 parts of MgO, K2O 2.50 Part, Na21.20 parts of O；
Whole base utilizes shuttle kiln, and the atmosphere of reducing flame is burnt into, firing temperature: 1250~1320 DEG C, when firing Between: 10~12 hours.

Claims (1)

1. the ceramic preparation of celadon smooth surface and crack surface, which is characterized in that including following procedure:
The pug ingredient of the smooth surface of not hacking is formed according to following parts by weight:
SiO269.26 part, AL2O319.25 part, Fe2O30.86 part, 0.81 part of CaO, 0.51 part of MgO, K22.90 parts of O, Na21.30 parts of O；
The pug ingredient of the crack surface of hacking is formed according to following parts by weight:
SiO262.56 part, AL2O325.44 part, Fe2O30.82 part, 0.7 part of CaO, 4.25 parts of MgO, K22.20 parts of O, Na2O 1.20 part；
It is bonded together smooth surface and crack surface to form whole base with intermediate mud layer, whole base utilizes shuttle kiln, the gas of reducing flame Atmosphere is burnt into, firing temperature: 1250~1320 DEG C, firing time: 10~12 hours；
The pug ingredient of the intermediate mud layer is formed according to following parts by weight:
SiO266.43 part, AL2O322.66 part, Fe2O30.83 part, 0.80 part of CaO, 2.02 parts of MgO, K22.50 parts of O, Na21.20 parts of O.
CN201610450762.0A 2016-06-22 2016-06-22 The ceramic preparation of celadon smooth surface and crack surface Active CN106083010B (en)