CN106083010A - Celadon bright finish and the ceramic preparation of crack surface - Google Patents

Celadon bright finish and the ceramic preparation of crack surface Download PDF

Info

Publication number
CN106083010A
CN106083010A CN201610450762.0A CN201610450762A CN106083010A CN 106083010 A CN106083010 A CN 106083010A CN 201610450762 A CN201610450762 A CN 201610450762A CN 106083010 A CN106083010 A CN 106083010A
Authority
CN
China
Prior art keywords
parts
celadon
crack surface
bright finish
cao
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610450762.0A
Other languages
Chinese (zh)
Other versions
CN106083010B (en
Inventor
马协初
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YIXING GOLDFISH CERAMICS CO Ltd
Original Assignee
YIXING GOLDFISH CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIXING GOLDFISH CERAMICS CO Ltd filed Critical YIXING GOLDFISH CERAMICS CO Ltd
Priority to CN201610450762.0A priority Critical patent/CN106083010B/en
Publication of CN106083010A publication Critical patent/CN106083010A/en
Application granted granted Critical
Publication of CN106083010B publication Critical patent/CN106083010B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to ceramic field, specially celadon bright finish and the ceramic preparation of crack surface, the pug composition of the bright finish not hacked (lower floor or upper strata) includes SiO269.26 part, AL2O319.25 part, Fe2O3 0.86 part, CaO 0.81 part, MgO 0.51 part, K2O 2.90 parts, NA2O 1.30 parts；The pug composition of the crack surface (upper strata or lower floor) hacked includes SiO262.56 part, AL2O325.44 part, Fe2O3 0.82 part, CaO 0.7 part, MgO 4.25 parts, K2O 2.20 parts, NA2O 1.20 parts；Middle to bright finish and the upper and lower aspect of crack surface mud layer is bonded together the overall base of formation, and overall base utilizes shuttle kiln, and the atmosphere of reducing flame is burnt till.The celadon bright finish that the present invention provides and the ceramic preparation of crack surface, combine the celadon of traditional bright finish with crack surface celadon, show, and do not have cracking defect on same part celadon pottery, create the celadon art work of top grade.

Description

Celadon bright finish and the ceramic preparation of crack surface
Technical field
The present invention relates to ceramic field, specially celadon bright finish and the ceramic preparation of crack surface.
Background technology
Yixing celadon such as lotus flower when fully open, pure and fresh scoops, and is described as " oriental hyacinth, exquisite jasper device ", at present, celadon More than 1000 kinds such as the existing vase of product, flowerpot, tea set, tableware, drinking utensils, ashtray, lamp socket and all kinds of industrial art decorative ceramics. Glaze colours is also added to Monopteri albi Huang, black pigment used by women in ancient times to paint their eyebrows green grass or young crops, Mei Qing, bluish white, ultramarine, emerald green green grass or young crops, pale blue, shadow green grass or young crops, calipash, blue or green more than 10 kinds reddish black, grey, its In especially yellow with Monopteri albi, pale blue be top grade.Decoration in addition to traditional texturing, embossment stippling, hundred fragments, also Ye Luowen, Flower, screen printing, transmutation, the multiple new decoration such as crimson is brushed under spraying decoration, colored glaze, bluish white combination, glaze.Hundred the most traditional fragments, " the roe stricture of vagina " and " Eriocheir sinensis stricture of vagina " that sheet stricture of vagina is staggered on old china circle term, overlapping crying " cracked ice pattern " such as ice, lines is crisscross freely, Glaze colours is simple and honest effectively.
Along with consumer's diversity requirement to ceramic, need to break through traditional technique, multiple skill is combined, system Make more rich ceramic., making optimal artistic effect is our foundation set up the project and target.
Summary of the invention
In order to solve the problems referred to above, the present invention provides the technique that the celadon of a kind of bright finish combines with crack surface celadon, knot Close traditional handicraft and modern technologies, it is provided that a kind of new celadon, meet the requirement that client is higher level.
Concrete technical scheme is:
Celadon bright finish and the ceramic preparation of crack surface, including procedure below:
The pug composition of the bright finish (lower floor or upper strata) not hacked forms according to following parts by weight:
SiO269.26 part, AL2O319.25 part, Fe2O3 0.86 part, CaO 0.81 part, MgO 0.51 part, K2O 2.90 parts, NA2O 1.30 parts；
The pug composition of the crack surface (upper strata or lower floor) hacked forms according to following parts by weight:
SiO262.56 part, AL2O325.44 part, Fe2O3 0.82 part, CaO 0.7 part, MgO 4.25 parts, K2O 2.20 parts, NA2O 1.20 parts；
Middle to bright finish and the upper and lower aspect of crack surface mud layer is bonded together the overall base of formation, and the pug composition of middle mud layer is pressed Form according to following parts by weight:
SiO266.43 part, AL2O322.66 part, Fe2O3 0.83 part, CaO 0.80 part, MgO 2.02 parts, K2O 2.50 parts, NA2O 1.20 parts；
Overall base utilizes shuttle kiln, and the atmosphere of reducing flame is burnt till, firing temperature: 1250 ~ 1320 DEG C, firing time: 10 ~ 12 hours.
The celadon bright finish of present invention offer and the ceramic preparation of crack surface, by celadon and the crack surface of traditional bright finish Celadon combines, and shows, and do not have cracking defect on same part celadon pottery, creates the celadon of top grade The art work.
Detailed description of the invention
It is described in conjunction with the embodiments the specific embodiment of the invention.
Embodiment 1
The pug composition of the bright finish (lower floor or upper strata) not hacked forms according to following parts by weight:
SiO269.26 part, AL2O319.25 part, Fe2O3 0.86 part, CaO 0.81 part, MgO 0.51 part, K2O 2.90 parts, NA2O 1.30 parts；
The pug composition of the crack surface (upper strata or lower floor) hacked forms according to following parts by weight:
SiO262.56 part, AL2O325.44 part, Fe2O3 0.82 part, CaO 0.7 part, MgO 4.25 parts, K2O 2.20 parts, NA2O 1.20 parts；
Middle to bright finish and the upper and lower aspect of crack surface mud layer is bonded together the overall base of formation, and the pug composition of middle mud layer is pressed Form according to following parts by weight:
SiO266.43 part, AL2O322.66 part, Fe2O3 0.83 part, CaO 0.80 part, MgO 2.02 parts, K2O 2.50 parts, NA2O 1.20 parts；
Overall base utilizes shuttle kiln, and the atmosphere of reducing flame is burnt till, firing temperature: 1250 ~ 1320 DEG C, firing time: 10 ~ 12 hours.

Claims (2)

1. the ceramic preparation of celadon bright finish and crack surface, it is characterised in that include procedure below:
The pug composition of the bright finish not hacked forms according to following parts by weight:
SiO269.26 part, AL2O319.25 part, Fe2O3 0.86 part, CaO 0.81 part, MgO 0.51 part, K2O 2.90 parts, NA2O 1.30 parts；
The pug composition of the crack surface hacked forms according to following parts by weight:
SiO262.56 part, AL2O325.44 part, Fe2O3 0.82 part, CaO 0.7 part, MgO 4.25 parts, K2O 2.20 parts, NA2O 1.20 part；
Middle to bright finish and crack surface mud layer is bonded together the overall base of formation, and overall base utilizes shuttle kiln, the gas of reducing flame Atmosphere, burns till, firing temperature: 1250 ~ 1320 DEG C, firing time: 10 ~ 12 hours.
Celadon bright finish the most according to claim 1 and the ceramic preparation of crack surface, it is characterised in that described centre The pug composition of mud layer forms according to following parts by weight:
SiO266.43 part, AL2O322.66 part, Fe2O3 0.83 part, CaO 0.80 part, MgO 2.02 parts, K2O 2.50 parts, NA2O 1.20 parts.
CN201610450762.0A 2016-06-22 2016-06-22 The ceramic preparation of celadon smooth surface and crack surface Active CN106083010B (en)