CN106044847A - 一种氧化锌的制备方法 - Google Patents
一种氧化锌的制备方法 Download PDFInfo
- Publication number
- CN106044847A CN106044847A CN201610498404.7A CN201610498404A CN106044847A CN 106044847 A CN106044847 A CN 106044847A CN 201610498404 A CN201610498404 A CN 201610498404A CN 106044847 A CN106044847 A CN 106044847A
- Authority
- CN
- China
- Prior art keywords
- zinc oxide
- zinc nitrate
- zinc
- parts
- nitrate solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种氧化锌制备方法，由以下步骤组成：取硝酸锌30~40份加入去离子水中，充分搅拌后得到硝酸锌溶液；取硫酸30~40份，与硝酸锌溶液混合，置于加热器中，在磁力搅拌下，形成沉淀；将沉淀过滤出来，用纯净水洗涤过后，放入干燥机干燥得到氧化锌。本发明具有反应简单，低成本，无污染，反应可控制等优点。
Description
技术领域
本发明涉及一种氧化锌的制备方法。
背景技术
氧化锌是一种常用的化学添加剂，广泛地应用于塑料、硅酸盐制品、合成橡胶、润滑油、油漆涂料、药膏、粘合剂、食品、电池、阻燃剂等产品的制作中，主要用于橡胶或电缆工业作补强剂和活性剂。
发明内容
为了充分利用上述氧化锌的功能，本发明的目的是提供一种氧化锌的制备方法。
本发明是采取以下技术方案来实现的：一种氧化锌制备方法，由以下步骤组成：
（1）取硝酸锌30~40份加入去离子水中，充分搅拌后得到硝酸锌溶液；
（2）取硫酸30~40份，与硝酸锌溶液混合，置于加热器中，在磁力搅拌下，形成沉淀；
（3）将步骤（2）中的沉淀过滤出来，用纯净水洗涤过后，放入干燥机干燥得到氧化锌。
上述的一种氧化锌制备方法，所述硝酸锌与硫酸的摩尔比为1:1。
上述的一种氧化锌制备方法，所述加热器的温度设置为60~80℃
综上所述本发明具有以下有益效果：本发明具有反应简单，低成本，无污染，反应可控制等优点。
具体实施方式
一种氧化锌制备方法，由以下步骤组成：
（1）取硝酸锌30~40份加入去离子水中，充分搅拌后得到硝酸锌溶液；
（2）取硫酸30~40份，与硝酸锌溶液混合，置于加热器中，在磁力搅拌下，形成沉淀；
（3）将步骤（2）中的沉淀过滤出来，用纯净水洗涤过后，放入干燥机干燥得到氧化锌。
上述的一种氧化锌制备方法，所述硝酸锌与硫酸的摩尔比为1:1。
上述的一种氧化锌制备方法，所述加热器的温度设置为60~80℃
综上所述本发明具有以下有益效果：本发明具有反应简单，低成本，无污染，反应可控制等优点。
以上所述是本发明的实施例，故凡依本发明申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。
Claims (3)
1.一种氧化锌制备方法，其特征在于，由以下步骤组成：
（1）取硝酸锌30~40份加入去离子水中，充分搅拌后得到硝酸锌溶液；
（2）取硫酸30~40份，与硝酸锌溶液混合，置于加热器中，在磁力搅拌下，形成沉淀；
（3）将步骤（2）中的沉淀过滤出来，用纯净水洗涤过后，放入干燥机干燥得到氧化锌。
2.根据权利要求1所述的一种氧化锌制备方法，其特征在于，所述硝酸锌与硫酸的摩尔比为1:1。
3.根据权利要求1所述的一种氧化锌制备方法，其特征在于，所述加热器的温度设置为60~80℃。