CN105885272A - 一种蒙脱土增韧聚氯乙烯的制备方法 - Google Patents
一种蒙脱土增韧聚氯乙烯的制备方法 Download PDFInfo
- Publication number
- CN105885272A CN105885272A CN201410745723.4A CN201410745723A CN105885272A CN 105885272 A CN105885272 A CN 105885272A CN 201410745723 A CN201410745723 A CN 201410745723A CN 105885272 A CN105885272 A CN 105885272A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- montmorillonite
- preparation
- toughening
- agent powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种蒙脱土增韧聚氯乙烯的制备方法，包括制备改性增韧剂和复合材料制备两步骤。使用改性纳米蒙脱土和丙烯酸酯类抗冲击改性剂再聚合中进行复核并增韧聚氯乙烯，不仅可以提高型材的韧性，还能在少损失拉伸强度同事提高材料的抗蠕变能力和刚性，力学性能佳。
Description
技术领域
本发明涉及塑料领域，具体涉及一种蒙脱土增韧聚氯乙烯的制备方法。
背景技术
聚氯乙烯(PVC)是由氯乙烯在引发剂作用下聚合而成的热塑性树脂。是氯乙烯的均聚物。有优异的介电性能。但对光和热的稳定性差，在100℃以上或经长时间阳光曝晒，就会分解而产生氯化氢，并进一步自动催化分解，引起变色，物理机械性能也迅速下降，在实际应用中必须加入稳定剂以提高对热和光的稳定性。
树脂产量大，价格便宜，综合性能相对较好，但是缺点是质脆，要想扩大应用领域，如何有效对其增韧是关键。PVC型材中所用增韧剂多是丙烯酸酯类抗冲击改性剂和氯化聚乙烯。但这两种增韧剂增韧时都存在PVC型材拉伸强度损失多、使用过程中蠕变严重的问题。蒙脱土在PVC中的分散度不佳，从而导致PVC复合材料的稳定性差。
发明内容
本发明的目的在于克服现有技术中存在的缺陷，提供一种力学性能好的蒙脱土增韧聚氯乙烯的制备方法。
为实现上述技术效果，本发明的技术方案为：一种蒙脱土增韧聚氯乙烯的制备方法，其特征在于，所述方法包括以下步骤：
S1：制备改性增韧剂，将纳米蒙脱土加入装有去离子水的反应器中，搅拌分散，加入丙烯酸丁酯和十二烷基硫酸钠，氮气保护下升温至70～80℃，保温反应2～3h，经破乳、抽滤、洗涤和干燥即得改性剂粉料；
S2：将S1所得改性剂粉料和PVC树脂颗粒在双辊开炼机上熔融共混5～10min，开炼机温度为170～180℃，然后将混合料置于190～200℃的平板硫化剂上压制5～10min，得蒙脱土增韧聚氯乙烯片材。
其中，所述改性剂粉料中纳米蒙脱土的含量为0.2～0.8％。
其中，蒙脱土增韧聚氯乙烯中改性剂粉料所占的重量百分比为7～11％。
本发明的优点和有益效果在于：
使用改性纳米蒙脱土和丙烯酸酯类抗冲击改性剂再聚合中进行复核并增韧聚氯乙烯，不仅可以提高型材的韧性，还能在少损失拉伸强度同事提高材料的抗蠕变能力和刚性，力学性能佳。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
实施例1的蒙脱土增韧聚氯乙烯的制备方法，包括以下步骤：
S1：制备改性增韧剂，将纳米蒙脱土加入装有去离子水的反应器中，搅拌分散，加入丙烯酸丁酯和十二烷基硫酸钠，氮气保护下升温至70～80℃，保温反应2～3h，经破乳、抽滤、洗涤和干燥即得改性剂粉料；
S2：将S1所得改性剂粉料和PVC树脂颗粒在双辊开炼机上熔融共混5～10min，开炼机温度为170～180℃，然后将混合料置于190～200℃的平板硫化剂上压制5～10min，得蒙脱土增韧聚氯乙烯片材。
其中，改性剂粉料中纳米蒙脱土的含量为0.2～0.8％。
其中，蒙脱土增韧聚氯乙烯中改性剂粉料所占的重量百分比为7～11％。
实施例2
实施例2的蒙脱土增韧聚氯乙烯的制备方法，包括以下步骤：
S1：制备改性增韧剂，将纳米蒙脱土加入装有去离子水的反应器中，搅拌分散，加入丙烯酸丁酯和十二烷基硫酸钠，氮气保护下升温至70～80℃，保温反应2～3h，经破乳、抽滤、洗涤和干燥即得改性剂粉料；
S2：将S1所得改性剂粉料和PVC树脂颗粒在双辊开炼机上熔融共混5～10min，开炼机温度为170～180℃，然后将混合料置于190～200℃的平板硫化剂上压制5～10min，得蒙脱土增韧聚氯乙烯片材。
其中，改性剂粉料中纳米蒙脱土的含量为0.2～0.8％。
其中，蒙脱土增韧聚氯乙烯中改性剂粉料所占的重量百分比为7～11％。
实施例3
实施例3的蒙脱土增韧聚氯乙烯的制备方法，包括以下步骤：
S1：制备改性增韧剂，将纳米蒙脱土加入装有去离子水的反应器中，搅拌分散，加入丙烯酸丁酯和十二烷基硫酸钠，氮气保护下升温至70～80℃，保温反应2～3h，经破乳、抽滤、洗涤和干燥即得改性剂粉料；
S2：将S1所得改性剂粉料和PVC树脂颗粒在双辊开炼机上熔融共混5～10min，开炼机温度为170～180℃，然后将混合料置于190～200℃的平板硫化剂上压制5～10min，得蒙脱土增韧聚氯乙烯片材。
其中，改性剂粉料中纳米蒙脱土的含量为0.2～0.8％。
其中，蒙脱土增韧聚氯乙烯中改性剂粉料所占的重量百分比为7～11％。
经实施例方法制得的改性剂中，丙烯酸丁酯单体小分子能够充分渗透到纳米蒙脱土的片层微缝隙中间并在层间被引发聚合反应，聚合得到的聚丙烯酸丁酯大分子链因为体积不断长大，会将纳米蒙脱土的层间距也胀大。
改性剂中的纳米蒙脱土直接表现是降低了橡胶弹性，间接影响结果是降低了对PVC树脂的增韧能力。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (3)
1.一种蒙脱土增韧聚氯乙烯的制备方法，其特征在于，所述方法包括以下步骤：
S1：制备改性增韧剂，将纳米蒙脱土加入装有去离子水的反应器中，搅拌分散，加入丙烯酸丁酯和十二烷基硫酸钠，氮气保护下升温至70～80℃，保温反应2～3h，经破乳、抽滤、洗涤和干燥即得改性剂粉料；
S2：将S1所得改性剂粉料和PVC树脂颗粒在双辊开炼机上熔融共混5～10min，开炼机温度为170～180℃，然后将混合料置于190～200℃的平板硫化剂上压制5～10min，得蒙脱土增韧聚氯乙烯片材。
2.根据权利要求1所述的蒙脱土增韧聚氯乙烯的制备方法，其特征在于，所述改性剂粉料中纳米蒙脱土的含量为0.2～0.8％。
3.根据权利要求1所述的蒙脱土增韧聚氯乙烯的制备方法，其特征在于，蒙脱土增韧聚氯乙烯中改性剂粉料所占的重量百分比为7～11％。