CN105713545A - Adhesive for handles of ceramic cups - Google Patents
Adhesive for handles of ceramic cups Download PDFInfo
- Publication number
- CN105713545A CN105713545A CN201610196422.XA CN201610196422A CN105713545A CN 105713545 A CN105713545 A CN 105713545A CN 201610196422 A CN201610196422 A CN 201610196422A CN 105713545 A CN105713545 A CN 105713545A
- Authority
- CN
- China
- Prior art keywords
- parts
- sufficiently mixed
- add
- adhesive
- adhesion promoter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive for handles of ceramic cups and relates to the technical field of manufacturing of ceramic products. The adhesive is prepared from raw materials in parts by weight as follows: 15-20 parts of polyoxyethylene, 10-15 parts of terpene resin, 8-12 parts of fumed silica, 6-10 parts of sepiolite powder, 6-10 parts of polyacrylamide, 5-8 parts of an adhesion promoter, 4-6 parts of hydrogenated castor oil, 3-5 parts of molecular sieve raw powder, 3-5 parts of microcrystalline wax, 2-3 parts of gelatin and 60-80 parts of water. The adhesive is moderate in viscosity, clear, bright and good in high-temperature resistance, the handles can be firmly bonded to ceramic cup bodies, harmful substances and gases cannot be produced after the adhesive is subjected to high-temperature sintering, and the phenomenon of peeling-off of the handles under the effect of high temperatures can be avoided.
Description
Technical field:
The present invention relates to ceramic article manufacturing technology field, be specifically related to a kind of ceramic cup bonding agent.
Background technology:
Ceramic cup is the conventional ceramic of one way of life, and safe and harmless, main component is Kaolin, clay, porcelain stone, china clay, coloring agent, blue and white material, lime glaze, Calx alkali glaze etc., has significantly high corrosion resistance and scour resistance.In ceramic cup manufacture process, generally first manufacture cup, finally by cup bonding on cup.Traditional handicraft be directly by cup bonding to after moistening on cup, it is easy to cup occurs dropping phenomenon.
Summary of the invention:
The technical problem to be solved is in that to provide a kind of viscosity is suitable, caking property is good, easy to use ceramic cup bonding agent.
The technical problem to be solved adopts following technical scheme to realize:
A kind of ceramic cup, bonding agent, is made up of the raw material of following parts by weight:
Polyethylene glycol oxide 15-20 part, terpene resin 10-15 part, gas-phase silica 8-12 part, sepiolite powder 6-10 part, polyacrylamide 6-10 part, adhesion promoter 5-8 part, castor oil hydrogenated 4-6 part, molecular screen primary powder 3-5 part, microwax 3-5 part, gelatin 2-3 part, water 60-80 part;
Its preparation method is as follows:
(1) terpene resin and microwax are added to the water, be then heated to fluidized state insulation 15min, add polyethylene glycol oxide and gelatin, after being sufficiently mixed under microwave frequency 2450MHz, power 800W microwave treatment 10min, obtain material I;
(2) gas-phase silica, sepiolite powder and molecular screen primary powder are sufficiently mixed, first heat to 100-110 DEG C of insulation mixing 15min, at 0-5 DEG C, stand 30min, obtain material II;
(3) in material I, add material II, polyacrylamide, adhesion promoter and castor oil hydrogenated, be sufficiently mixed after uniformly and add in ball mill, be milled to fineness less than 50 μm.
Described adhesion promoter is made up of the raw material of following parts by weight: stearic acid 9-13 part, spermol 7-11 part, butadiene rubber 5-8 part, polyoxyethylene lauryl ether 3-6 part, emulsified silicone oil 3-6 part, fluorocarbon resin 2-4 part, tributyl citrate 1-2 part, vaseline 1-2 part, carbamide 0.5-1 part, rare earth 0.05-0.1 part, its preparation method is: by stearic acid, spermol and vaseline are slowly heated after being sufficiently mixed, add butadiene rubber and tributyl citrate until completely melted, mixture is in supersonic frequency 40kHz, supersound process 15min under power 50W, then at microwave frequency 2450MHz, microwave treatment 10min under power 800W, it is subsequently adding emulsified silicone oil and fluorocarbon resin, continue microwave treatment 10min, after temperature is down to 60-70 DEG C naturally, finally add polyoxyethylene lauryl ether, carbamide and rare earth, it is sufficiently mixed uniformly.
The invention has the beneficial effects as follows: the present invention, with polyethylene glycol oxide and terpene resin for primary raw material, is aided with multiple auxiliary agent and prepares bonding agent, this binding agent modest viscosity, clarify bright, steady for cup adhering can be connected on pottery cup;Heat-resisting quantity is good, will not produce harmful substance and gas, and do not have because high temperature affects cup peeling phenomenon after high temperature sintering, and the cup of made ceramic cup finished product is firmly, easy to use.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be easy to understand, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) 10 parts of terpene resins and 3 parts of microwaxes are added in 60 parts of water, it is then heated to fluidized state insulation 15min, add 18 parts of polyethylene glycol oxides and 2 parts of gelatin, after being sufficiently mixed under microwave frequency 2450MHz, power 800W microwave treatment 10min, obtain material I;
(2) 8 parts of gas-phase silicas, 8 parts of sepiolite powders and 3 parts of molecular screen primary powders are sufficiently mixed, first heat to 100-110 DEG C of insulation mixing 15min, at 0-5 DEG C, stand 30min, obtain material II;
(3) in material I, add material II, 6 parts of polyacrylamides, 7 parts of adhesion promoters and 4 parts of castor oil hydrogenated, be sufficiently mixed after uniformly and add in ball mill, be milled to fineness less than 50 μm.
The preparation of adhesion promoter: by 12 parts of stearic acid, 9 parts of spermols and 1 part of vaseline are slowly heated after being sufficiently mixed, add 6 parts of butadiene rubbers and 2 parts of tributyl citrate until completely melted, mixture is in supersonic frequency 40kHz, supersound process 15min under power 50W, then at microwave frequency 2450MHz, microwave treatment 10min under power 800W, it is subsequently adding 6 parts of emulsified silicone oils and 2 parts of fluorocarbon resins, continue microwave treatment 10min, after temperature is down to 60-70 DEG C naturally, finally add 5 parts of polyoxyethylene lauryl ether, 1 part of carbamide and 0.05 part of rare earth, it is sufficiently mixed uniformly.
Embodiment 2
(1) 15 parts of terpene resins and 5 parts of microwaxes are added in 80 parts of water, it is then heated to fluidized state insulation 15min, add 15 parts of polyethylene glycol oxides and 3 parts of gelatin, after being sufficiently mixed under microwave frequency 2450MHz, power 800W microwave treatment 10min, obtain material I;
(2) 10 parts of gas-phase silicas, 6 parts of sepiolite powders and 4 parts of molecular screen primary powders are sufficiently mixed, first heat to 100-110 DEG C of insulation mixing 15min, at 0-5 DEG C, stand 30min, obtain material II;
(3) in material I, add material II, 8 parts of polyacrylamides, 5 parts of adhesion promoters and 5 parts of castor oil hydrogenated, be sufficiently mixed after uniformly and add in ball mill, be milled to fineness less than 50 μm.
The preparation of adhesion promoter: by 10 parts of stearic acid, 7 parts of spermols and 2 parts of vaseline are slowly heated after being sufficiently mixed, add 5 parts of butadiene rubbers and 1 part of tributyl citrate until completely melted, mixture is in supersonic frequency 40kHz, supersound process 15min under power 50W, then at microwave frequency 2450MHz, microwave treatment 10min under power 800W, it is subsequently adding 4 parts of emulsified silicone oils and 3 parts of fluorocarbon resins, continue microwave treatment 10min, after temperature is down to 60-70 DEG C naturally, finally add 3 parts of polyoxyethylene lauryl ether, 0.5 part of carbamide and 0.05 part of rare earth, it is sufficiently mixed uniformly.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.Skilled person will appreciate that of the industry; the present invention is not restricted to the described embodiments; described in above-described embodiment and description is that principles of the invention is described; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements both fall within the claimed scope of the invention.Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. a ceramic cup is bonding agent, it is characterised in that be made up of the raw material of following parts by weight:
Polyethylene glycol oxide 15-20 part, terpene resin 10-15 part, gas-phase silica 8-12 part, sepiolite powder 6-10 part, polyacrylamide 6-10 part, adhesion promoter 5-8 part, castor oil hydrogenated 4-6 part, molecular screen primary powder 3-5 part, microwax 3-5 part, gelatin 2-3 part, water 60-80 part;
Its preparation method is as follows:
(1) terpene resin and microwax are added to the water, be then heated to fluidized state insulation 15min, add polyethylene glycol oxide and gelatin, after being sufficiently mixed under microwave frequency 2450MHz, power 800W microwave treatment 10min, obtain material I;
(2) gas-phase silica, sepiolite powder and molecular screen primary powder are sufficiently mixed, first heat to 100-110 DEG C of insulation mixing 15min, at 0-5 DEG C, stand 30min, obtain material II;
(3) in material I, add material II, polyacrylamide, adhesion promoter and castor oil hydrogenated, be sufficiently mixed after uniformly and add in ball mill, be milled to fineness less than 50 μm.
2. ceramic cup according to claim 1 is bonding agent, it is characterized in that, described adhesion promoter is made up of the raw material of following parts by weight: stearic acid 9-13 part, spermol 7-11 part, butadiene rubber 5-8 part, polyoxyethylene lauryl ether 3-6 part, emulsified silicone oil 3-6 part, fluorocarbon resin 2-4 part, tributyl citrate 1-2 part, vaseline 1-2 part, carbamide 0.5-1 part, rare earth 0.05-0.1 part, its preparation method is: by stearic acid, spermol and vaseline are slowly heated after being sufficiently mixed, add butadiene rubber and tributyl citrate until completely melted, mixture is in supersonic frequency 40kHz, supersound process 15min under power 50W, then at microwave frequency 2450MHz, microwave treatment 10min under power 800W, it is subsequently adding emulsified silicone oil and fluorocarbon resin, continue microwave treatment 10min, after temperature is down to 60-70 DEG C naturally, finally add polyoxyethylene lauryl ether, carbamide and rare earth, it is sufficiently mixed uniformly.