CN107698265A - A kind of adhesive of ceramic batch - Google Patents
A kind of adhesive of ceramic batch Download PDFInfo
- Publication number
- CN107698265A CN107698265A CN201710808667.8A CN201710808667A CN107698265A CN 107698265 A CN107698265 A CN 107698265A CN 201710808667 A CN201710808667 A CN 201710808667A CN 107698265 A CN107698265 A CN 107698265A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive
- heated
- ceramic batch
- modifying agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of adhesive of ceramic batch, it is related to ceramic fabrication technique field, the present invention is using flake asbestos, paraffin, sepiolite powder as primary raw material, plus polyurethane, oxidic polyethylene, activated carbon, nitrile rubber, and it is aided with the auxiliary materials such as rosin, epoxidized soybean oil, lignin fiber, modifying agent, obtained adhesive viscosities are high, fine and smooth, the feature of environmental protection is good, and has preferable heat-resisting quantity and fastness.
Description
Technical field:
The present invention relates to ceramic fabrication technique field, and in particular to a kind of adhesive of ceramic batch.
Background technology:
Ceramics are the general names of pottery and porcelain.Common ceramic material has clay, aluminum oxide, kaolin etc..Ceramic material
General hardness is higher, but plasticity is poor.Except being used in feeder, on decoration in addition to, ceramics science, technology development in also play the part of
Drill key player.Ceramic raw material is that the original ample resources clay of the earth forms by quenching to take.And the property tool toughness of clay,
Normal temperature chance water is plastic, and micro- do can carve, absolutely dry to grind;Water can be filled into pottery by burning to 700 degree;Burn to 1230 degree of then porcelain, can be several
Do not absorb water completely and corrosion-and high-temp-resistant.The elasticity of its usage, there is the application of various intention in culture today science and technology.
Ceramic batch is in manufacturing process, it is necessary to which stronger viscosity is in order to the shaping of blank, the higher blank warp of viscosity
After calcining, toughness is high, and wearability is good, is not easy to break.
The content of the invention:
The technical problems to be solved by the invention are to provide a kind of adhesive of ceramic batch.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of adhesive of ceramic batch, is made up of the raw material of following parts by weight:
Flake asbestos 25-30 parts, paraffin 12-15 parts, sepiolite powder 10-15 parts, polyurethane 8-11 parts, oxidic polyethylene 6-10
Part, activated carbon 5-8 parts, nitrile rubber 5-8 parts, curing accelerator 4-6 parts, rosin 3-5 parts, epoxidized soybean oil 3-5 parts, lignin are fine
Tie up 2-3 parts, sulphur 1-2 parts, modifying agent 3-6 parts, water 100-150 parts.
Further, the adhesive of the ceramic batch, it is made up of the raw material of following parts by weight:
28 parts of flake asbestos, 13 parts of paraffin, 12 parts of sepiolite powder, 10 parts of polyurethane, 8 parts of oxidic polyethylene, 7 parts of activated carbon,
7 parts of nitrile rubber, 5 parts of curing accelerator, 4 parts of rosin, 4 parts of epoxidized soybean oil, 3 parts of lignin fiber, 2 parts of sulphur, modifying agent 5
Part, 125 parts of water.
Further, the modifying agent is made up of the component of following parts by weight:Potato starch 3-5 parts, cornstarch 3-5
Part, tapioca 3-5 parts, wheat bran 1-3 parts, glutinous rice flour 2-4 parts, alkali lye 4-8 parts, borax 2-3 parts.
Further, the component of the preferably following parts by weight of the modifying agent is formed:4 parts of potato starch, 4 parts of cornstarch,
4 parts of tapioca, 2 parts of wheat bran, 3 parts of glutinous rice flour, 6 parts of alkali lye, 2 parts of borax.
Its preparation method comprises the following steps:
(1) flake asbestos and sepiolite powder are added into water, immersion 30min is heated to reflux state isothermal holding 15min, then
Lignin fiber and rosin are added, continues isothermal holding 10min, produces material I;
(2) paraffin, polyurethane and oxidic polyethylene are sufficiently mixed, add nitrile rubber and epoxidized soybean oil, carried out
Heating stirring, 120-140 DEG C of insulated and stirred 10min is first heated to, then proceedes to be heated to 150-180 DEG C of insulated and stirred 5min,
Mixing speed is 400-500r/min, produces material II;
(3) material II, activated carbon, curing accelerator, modifying agent are added into material I, with stirring after being sufficiently mixed uniformly
Machine is quickly stirred, mixing speed 1000-1200r/min;
(4) material being stirred is added in ball mill, is milled to fineness less than 15 μm.
Further, the preparation method of the modifying agent comprises the following steps:
Potato starch, cornstarch, tapioca, wheat bran, glutinous rice flour, alkali lye, borax are mixed, mixture is beaten
Breakdown mill processing, the mixture after grinding is heated, and heating-up temperature is 120-150 degree, and the heat time is 20-30 minutes,
The mixture heated is added in agitator and carries out insulated and stirred, mixing speed 1200-1400r/min, keeping temperature is
80-90 degree.
The beneficial effects of the invention are as follows:The present invention using flake asbestos, paraffin, sepiolite powder as primary raw material, plus polyurethane,
Oxidic polyethylene, activated carbon, nitrile rubber, and it is aided with the auxiliary materials such as rosin, epoxidized soybean oil, lignin fiber, modifying agent, it is obtained
Adhesive viscosities are high, and fine and smooth, the feature of environmental protection is good, and has preferable heat-resisting quantity and fastness.
Embodiment:
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of adhesive of ceramic batch, is made up of the raw material of following parts by weight:
25 parts of flake asbestos, 12 parts of paraffin, 10 parts of sepiolite powder, 8 parts of polyurethane, 6 parts of oxidic polyethylene, 5 parts of activated carbon, fourth
Fine 5 parts of rubber, 4 parts of curing accelerator, 3 parts of rosin, 3 parts of epoxidized soybean oil, 2 parts of lignin fiber, 1 part of sulphur, 3 parts of modifying agent,
100 parts of water.
Further, the modifying agent is made up of the component of following parts by weight:3 parts of potato starch, 3 parts of cornstarch, wood
3 parts of sweet potato starch, 1 part of wheat bran, 2 parts of glutinous rice flour, 4 parts of alkali lye, 2 parts of borax.
Its preparation method comprises the following steps:
(1) flake asbestos and sepiolite powder are added into water, immersion 30min is heated to reflux state isothermal holding 15min, then
Lignin fiber and rosin are added, continues isothermal holding 10min, produces material I;
(2) paraffin, polyurethane and oxidic polyethylene are sufficiently mixed, add nitrile rubber and epoxidized soybean oil, carried out
Heating stirring, 120 DEG C of insulated and stirred 10min are first heated to, then proceed to be heated to 150 DEG C of insulated and stirred 5min, mixing speed
For 400r/min, material II is produced;
(3) material II, activated carbon, curing accelerator, modifying agent are added into material I, with stirring after being sufficiently mixed uniformly
Machine is quickly stirred, mixing speed 1000r/min;
(4) material being stirred is added in ball mill, is milled to fineness less than 15 μm.
Further, the preparation method of the modifying agent comprises the following steps:
Potato starch, cornstarch, tapioca, wheat bran, glutinous rice flour, alkali lye, borax are mixed, mixture is beaten
Breakdown mill processing, the mixture after grinding is heated, and heating-up temperature is 120 degree, and the heat time is 20 minutes, will be heated
Mixture add in agitator and carry out insulated and stirred, mixing speed 1200r/min, keeping temperature is 80 degree.
Embodiment 2
A kind of adhesive of ceramic batch, is made up of the raw material of following parts by weight:
30 parts of flake asbestos, 15 parts of paraffin, 15 parts of sepiolite powder, 11 parts of polyurethane, 10 parts of oxidic polyethylene, 8 parts of activated carbon,
8 parts of nitrile rubber, 6 parts of curing accelerator, 5 parts of rosin, 5 parts of epoxidized soybean oil, 3 parts of lignin fiber, 2 parts of sulphur, modifying agent 6
Part, 150 parts of water.
Further, the modifying agent is made up of the component of following parts by weight:5 parts of potato starch, 5 parts of cornstarch, wood
5 parts of sweet potato starch, 3 parts of wheat bran, 4 parts of glutinous rice flour, 8 parts of alkali lye, 3 parts of borax.
Its preparation method comprises the following steps:
(1) flake asbestos and sepiolite powder are added into water, immersion 30min is heated to reflux state isothermal holding 15min, then
Lignin fiber and rosin are added, continues isothermal holding 10min, produces material I;
(2) paraffin, polyurethane and oxidic polyethylene are sufficiently mixed, add nitrile rubber and epoxidized soybean oil, carried out
Heating stirring, 140 DEG C of insulated and stirred 10min are first heated to, then proceed to be heated to 180 DEG C of insulated and stirred 5min, mixing speed
For 500r/min, material II is produced;
(3) material II, activated carbon, curing accelerator, modifying agent are added into material I, with stirring after being sufficiently mixed uniformly
Machine is quickly stirred, mixing speed 1200r/min;
(4) material being stirred is added in ball mill, is milled to fineness less than 15 μm.
Further, the preparation method of the modifying agent comprises the following steps:
Potato starch, cornstarch, tapioca, wheat bran, glutinous rice flour, alkali lye, borax are mixed, mixture is beaten
Breakdown mill processing, the mixture after grinding is heated, and heating-up temperature is 150 degree, and the heat time is 30 minutes, will be heated
Mixture add in agitator and carry out insulated and stirred, mixing speed 1400r/min, keeping temperature is 90 degree.
Control group 1
A kind of adhesive of ceramic batch, is made up of the raw material of following parts by weight:
25 parts of flake asbestos, 12 parts of paraffin, 10 parts of sepiolite powder, 8 parts of polyurethane, 6 parts of oxidic polyethylene, 5 parts of activated carbon, fourth
Fine 5 parts of rubber, 4 parts of curing accelerator, 3 parts of rosin, 3 parts of epoxidized soybean oil, 2 parts of lignin fiber, 1 part of sulphur, 100 parts of water.
Its preparation method comprises the following steps:
(1) flake asbestos and sepiolite powder are added into water, immersion 30min is heated to reflux state isothermal holding 15min, then
Lignin fiber and rosin are added, continues isothermal holding 10min, produces material I;
(2) paraffin, polyurethane and oxidic polyethylene are sufficiently mixed, add nitrile rubber and epoxidized soybean oil, carried out
Heating stirring, 120 DEG C of insulated and stirred 10min are first heated to, then proceed to be heated to 150 DEG C of insulated and stirred 5min, mixing speed
For 400r/min, material II is produced;
(3) material II, activated carbon, curing accelerator are added into material I, is carried out soon with mixer after being sufficiently mixed uniformly
Speed stirring, mixing speed 1000r/min;
(4) material being stirred is added in ball mill, is milled to fineness less than 15 μm.
Control group 2
A kind of adhesive of ceramic batch, is made up of the raw material of following parts by weight:
30 parts of flake asbestos, 15 parts of paraffin, 15 parts of sepiolite powder, 11 parts of polyurethane, 10 parts of oxidic polyethylene, 8 parts of activated carbon,
8 parts of nitrile rubber, 6 parts of curing accelerator, 5 parts of rosin, 5 parts of epoxidized soybean oil, 3 parts of lignin fiber, 2 parts of sulphur, modifying agent 6
Part, 150 parts of water.
Further, the modifying agent is made up of the component of following parts by weight:5 parts of potato starch, 5 parts of cornstarch, wood
5 parts of sweet potato starch, 3 parts of wheat bran, 4 parts of glutinous rice flour, 8 parts of alkali lye, 3 parts of borax.
Its preparation method comprises the following steps:
(1) flake asbestos, sepiolite powder, lignin fiber and rosin are added into water, immersion 30min is heated to reflux state guarantor
Temperature processing 15min, produces material I;
(2) paraffin, polyurethane and oxidic polyethylene are sufficiently mixed, add nitrile rubber and epoxidized soybean oil, carried out
Heating, 180 DEG C of insulation 5min are heated to, produce material II;
(3) material II, activated carbon, curing accelerator, modifying agent are added into material I, is sufficiently mixed uniformly;
(4) material being stirred is added in ball mill, is milled to fineness less than 15 μm.
Further, the preparation method of the modifying agent comprises the following steps:
Potato starch, cornstarch, tapioca, wheat bran, glutinous rice flour, alkali lye, borax are mixed, mixture is beaten
Heated after broken, heating-up temperature is 150 degree, and the heat time is 30 minutes.
Table 1 is the present invention and the Experimental Comparison result of control group
The adhesive for the ceramic batch that the present invention produces, viscosity is high, and fine and smooth, the feature of environmental protection is good, has preferable high temperature resistant
Property and fastness, are a kind of adhesives of high-quality ceramic batch.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (6)
1. a kind of adhesive of ceramic batch, is made up of the raw material of following parts by weight:
Flake asbestos 25-30 parts, paraffin 12-15 parts, sepiolite powder 10-15 parts, polyurethane 8-11 parts, oxidic polyethylene 6-10 parts,
Activated carbon 5-8 parts, nitrile rubber 5-8 parts, curing accelerator 4-6 parts, rosin 3-5 parts, epoxidized soybean oil 3-5 parts, lignin fiber
2-3 parts, sulphur 1-2 parts, modifying agent 3-6 parts, water 100-150 parts.
2. the adhesive of ceramic batch according to claim 1, it is characterised in that the adhesive of the ceramic batch, by
The raw material of following parts by weight is made:28 parts of flake asbestos, 13 parts of paraffin, 12 parts of sepiolite powder, 10 parts of polyurethane, oxidic polyethylene
8 parts, 7 parts of activated carbon, 7 parts of nitrile rubber, 5 parts of curing accelerator, 4 parts of rosin, 4 parts of epoxidized soybean oil, 3 parts of lignin fiber, sulphur
2 parts of sulphur, 5 parts of modifying agent, 125 parts of water.
3. the adhesive of ceramic batch according to claim 1, it is characterised in that the modifying agent is by following parts by weight
Component is formed:Potato starch 3-5 parts, cornstarch 3-5 parts, tapioca 3-5 parts, wheat bran 1-3 parts, glutinous rice flour 2-4 parts, alkali lye
4-8 parts, borax 2-3 parts.
4. the adhesive of ceramic batch according to claim 3, it is characterised in that 4 parts of potato starch, 4 parts of cornstarch,
4 parts of tapioca, 2 parts of wheat bran, 3 parts of glutinous rice flour, 6 parts of alkali lye, 2 parts of borax.
5. the adhesive of ceramic batch according to claim 1 or 2, it is characterised in that its preparation method includes following step
Suddenly:
(1) flake asbestos and sepiolite powder are added into water, immersion 30min is heated to reflux state isothermal holding 15min, added
Lignin fiber and rosin, continue isothermal holding 10min, produce material I;
(2) paraffin, polyurethane and oxidic polyethylene are sufficiently mixed, add nitrile rubber and epoxidized soybean oil, heated
Stirring, is first heated to 120-140 DEG C of insulated and stirred 10min, then proceedes to be heated to 150-180 DEG C of insulated and stirred 5min, stirs
Speed is 400-500r/min, produces material II;
(3) material II, activated carbon, curing accelerator, modifying agent are added into material I, is entered after being sufficiently mixed uniformly with mixer
The quick stirring of row, mixing speed 1000-1200r/min;
(4) material being stirred is added in ball mill, is milled to fineness less than 15 μm.
6. the adhesive of the ceramic batch according to claim 3 or 4, it is characterised in that the preparation method of the modifying agent
Comprise the following steps:Potato starch, cornstarch, tapioca, wheat bran, glutinous rice flour, alkali lye, borax are mixed, by mixture
Carry out smashing milled processed, the mixture after grinding is heated, heating-up temperature is 120-150 degree, heat time 20-30
Minute, the mixture heated is added in agitator and carries out insulated and stirred, mixing speed 1200-1400r/min, keeps temperature
Spend for 80-90 degree.