CN103467067A - Polished crystal tile - Google Patents
Polished crystal tile Download PDFInfo
- Publication number
- CN103467067A CN103467067A CN201310355471XA CN201310355471A CN103467067A CN 103467067 A CN103467067 A CN 103467067A CN 201310355471X A CN201310355471X A CN 201310355471XA CN 201310355471 A CN201310355471 A CN 201310355471A CN 103467067 A CN103467067 A CN 103467067A
- Authority
- CN
- China
- Prior art keywords
- powder
- hour
- parts
- adobe
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polished crystal tile. The polished crystal tile is made through using the following raw materials, by weight, 15-25 parts of highly plastic clay, 15-20 parts of kaolinite powder, 10-15 parts of pyrophillite powder, 20-30 parts of porcelain stone powder, 10-15 parts of feldspar powder, 5-10 parts of quartz powder, 1-3 parts of talcum, 2-4 parts of a modified carbide slag particle and a proper amount of water.
Description
Technical field
The present invention relates to the brickmaking field, is exactly the brilliant brick of a kind of throwing.
Background technology
Throwing brilliant brick is a kind of a kind of bright and clean bright brick become by surface finish, and its clear patterns is true to nature, and hard wear resistant is applicable to various decorations, and existing throwing glazed brick is incomparable from hardness.
Summary of the invention
The object of the present invention is to provide a kind of ultimate compression strength high, hardness is good, and anti-soil is effective, and brightness surpasses more than 95%, the brilliant brick of the throwing that glossiness is good.
Above-mentioned purpose realizes by following scheme:
The brilliant brick of a kind of throwing is characterized in that: it is that raw material by following weight parts makes: highly plastic clay 15-25, kaolinite powder 15-20, pyrophyllite powder 10-15, porcelain stone powder 20-30, Feldspar Powder 10-15, silica powder 5-10, talcum 1-3, modified carbide slag particle 2-4, water is appropriate.
The brilliant brick of described a kind of throwing is characterized in that:
The preparation method is the fragmentation of (1) power taking rock ballast, soak 8-9 hour in the sodium-chlor that the gained powder is 3-5% in concentration, 800-900 ℃ of lower sintering 3-4 hour, speed with 5-10 ℃ of per minute cooled to 500-550 ℃ of insulation after 1-2 hour again, take out, cooling, add the calcium formiate that is equivalent to powder gross weight 1-2%, the Sumstar 190 of 1-2%, the silane coupling agent kh570 of 1-2%, and suitable quantity of water, under 1800-2000rpm after high speed shear 10-15 minute, take out, dry, grind, cross the 100-200 mesh sieve, add amount of water after adding again the white glue with vinyl that is equivalent to above-mentioned powder gross weight 1-2% to stir, granulation, grain diameter is at 3-5mm, then after the particle made being fired to 20-30 minute under 200-300 ℃, obtain the modified carbide slag particle standby,
(2) by weight by each raw material blending, three-roll grinder grinds 1-2 hour, and compression moulding, obtain adobe, by carrying out surface after brick bat drying, throws the base processing, obtains the adobe that surface has clear texture;
(3) again according to common process through glazing, printing ornament, execute the clear frit powder, burn till, after polishing, adobe is entered to klining becomes and polishing and get final product.
The brilliant brick of described a kind of throwing is characterized in that: firing time is 2-4 hour, and firing temperature is 1100-1300 ℃.
Beneficial effect of the present invention is: of the present invention by adding the modified carbide slag particle, rationally batching, make ultimate compression strength high, and hardness is good, anti-soil is effective, and brightness surpasses more than 95%, and glossiness is good, and wear resistance is good simultaneously, the decorative applications scope is wide, and energy consumption level is low, with short production cycle.There is no macroscopic bubble in the brilliant brick of throwing after the gained polishing, homogeneity is good.Use the waste materials such as carbide slag, ceramic polished waste residue powder, turn waste into wealth.
Embodiment
The brilliant brick of a kind of throwing, it is that raw material by following weight parts (kg) makes: highly plastic clay 25, kaolinite powder 20, pyrophyllite powder 15, porcelain stone powder 30, Feldspar Powder 15, silica powder 10, talcum 3, modified carbide slag particle 4, water is appropriate.
The brilliant brick of described a kind of throwing,
The preparation method is
(1) power taking rock ballast fragmentation, in the sodium-chlor that the gained powder is 4% in concentration, soak 9 hours, 870 ℃ of lower sintering 3 hours, speed with 10 ℃ of per minutes cooled to 500 ℃ of insulations after 2 hours again, take out, cooling, add the calcium formiate that is equivalent to powder gross weight 2%, 1% Sumstar 190, 1% silane coupling agent kh570, and suitable quantity of water, under 1800rpm, high speed shear is after 15 minutes, take out, dry, grind, cross 200 mesh sieves, add amount of water after adding again the white glue with vinyl that is equivalent to above-mentioned powder gross weight 1% to stir, granulation, grain diameter is at 3-5mm, then after the particle made being fired to 30 minutes under 300 ℃, obtain the modified carbide slag particle standby,
(2) by weight by each raw material blending, three-roll grinder grinds 2 hours, and compression moulding, obtain adobe, by carrying out surface after brick bat drying, throws the base processing, obtains the adobe that surface has clear texture;
(3) again according to common process through glazing, printing ornament, execute the clear frit powder, burn till, after polishing, adobe is entered to klining becomes and polishing and get final product; Described firing time is 3 hours, and firing temperature is 1300 ℃.
The present embodiment ultimate compression strength is 17-20MPA, and proportion is 0.5-0.6, and folding strength is 8.3MPA.
Claims (3)
1. throw brilliant brick for one kind, it is characterized in that: it is that raw material by following weight parts makes: highly plastic clay 15-25, kaolinite powder 15-20, pyrophyllite powder 10-15, porcelain stone powder 20-30, Feldspar Powder 10-15, silica powder 5-10, talcum 1-3, modified carbide slag particle 2-4, carclazyte 1-2, ceramic polished waste residue powder 1-2, cullet powder 1-2, water is appropriate.
2. the brilliant brick of a kind of throwing according to claim 1 is characterized in that:
The preparation method is:
(1) power taking rock ballast fragmentation, soak 8-9 hour in the sodium-chlor that the gained powder is 3-5% in concentration, 800-900 ℃ of lower sintering 3-4 hour, speed with 5-10 ℃ of per minute cooled to 500-550 ℃ of insulation after 1-2 hour again, take out, cooling, add the calcium formiate that is equivalent to powder gross weight 1-2%, the Sumstar 190 of 1-2%, the silane coupling agent kh570 of 1-2%, and suitable quantity of water, under 1800-2000rpm after high speed shear 10-15 minute, take out, dry, grind, cross the 100-200 mesh sieve, add amount of water after adding again the white glue with vinyl that is equivalent to above-mentioned powder gross weight 1-2% to stir, granulation, grain diameter is at 3-5mm, then after the particle made being fired to 20-30 minute under 200-300 ℃, obtain the modified carbide slag particle standby,
(2) by weight by each raw material blending, three-roll grinder grinds 1-2 hour, and compression moulding, obtain adobe, by carrying out surface after brick bat drying, throws the base processing, obtains the adobe that surface has clear texture;
(3) again according to common process through glazing, printing ornament, execute the clear frit powder, burn till, after polishing, adobe is entered to klining becomes and polishing and get final product.
3. the brilliant brick of a kind of throwing according to claim 2, it is characterized in that: firing time is 2-4 hour, firing temperature is 1100-1300 ℃.